Filament comparison

PLA-GF vs PLA Matte

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PLA (PLA-GF) guideMatte PLA guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PLA-GF comparisonsMore PLA Matte comparisons
PLA-GF vs PLA Matte — documented properties and sources
PropertyGlass-fibre PLA (PLA-GF)PLAMatte PLAPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$44.99/kg median; $29.99–$59.99/kg across 2 dated product listings$19.09/kg median; $10.99–$32.16/kg across 10 dated product listings
Identity & Market
Base polymer / chemistryPLA filled with chopped glass fibre — 12 wt% (Polymaker HT-PLA-GF), 15–20 wt% (eSUN PLA-GF). Bambu Lab PLA Galaxy uses glass microspheres, not fibre, and is not equivalent[1][2][3]PLA compounded with a mineral filler — Fiberlogy names chalk — that scatters light into a diffuse finish[4][5]
Densityg/cm³1.31 (eSUN) to 1.337 (Polymaker), ISO 1183 / GB/T 1033[1][2]1.31 (Bambu Lab, ISO 1183) to 1.38 (Fiberlogy PLA Mineral, method not stated) — above plain PLA from the filler[5][4]
Typical priceUSD/kg1 kg spools cluster near 30[6][7]Mainstream 1 kg spools cluster near 21[8][9][10]
Price range across brandsUSD/kg30–60 across brands; Polymaker 30, Proto-pasta 60[6][7]11–32 across brands; budget house brands 11–19, Fiberlogy PLA Mineral 32[11][9][12]
Market availability1–5Niche, a handful of specialist brands[6][7][2]Stocked by most mainstream brands[11][10][8]
Spool sizes & diameters1.75 mm; 0.5 and 1 kg spools[7][13]1.75 mm; 1 kg spools plus spool-less refills[8][14]
Typical applicationsStiff brackets and fixtures; the Polymaker grade is aimed at parts annealed for heat resistance[1]Display models and visible parts where a matte, non-reflective finish matters[5]
Diameter tolerance± mmNot documented±0.03 (Bambu Lab)[15]
Printing Parameters
Nozzle temperature°C210–230 (Polymaker HT-PLA-GF)[1]190–230 (Bambu Lab); 190–210 (Fiberlogy PLA Mineral)[5][4]
Bed temperature°C25–60 (Polymaker HT-PLA-GF)[1]35–45 (Bambu Lab); 60 (Fiberlogy)[5][4]
Enclosure / chamber requirement1–5Open frame is fine[1]Open frame is fine[5][4]
Part cooling fanFan on — eSUN specifies 100 %[2]Fan on; Fiberlogy specifies 75–100 %[5][4]
Bed surface & adhesion aidNot documentedCool plate, high-temperature plate or textured PEI with glue (Bambu Lab); smooth PEI, textured PEI or glass (Fiberlogy)[5][4]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s28 at Polymaker's stated 350 mm/s on a 0.4 mm nozzle at 0.2 mm layer; eSUN prints its specimens at 60 mm/s[1][2][16]Not documented
Warping tendency1–5Not documentedNone[5]
Bed-adhesion difficulty1–5Not documentedSticks to anything[17]
Shrinkage%0.05 in X-Y and Z, 0.10 diagonal (Polymaker HT-PLA-GF)[1]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[1]Beginner — prints on any machine out of the box[5][4]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[1]Brass fine indefinitely[18][5][4]
Abrasiveness1–5Highly abrasive — standard GF composite[1]Slightly abrasive — mineral filler pushes density from 1.24 to 1.31–1.38[4][5][19]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[20]Very low[18]
Heat-creep / jam sensitivity1–5Not documentedModerate — good heatbreak cooling needed; PLA softens below 60 °C[21]
Hotend requirementHardened steel or ruby nozzle; Polymaker's own slicer preset sets a minimum nozzle hardness of 40 HRC[1]No special hot-end required[17]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — the PLA matrix takes up 0.40–0.51 % saturated; no glass-filled grade publishes its own figure[19][22]Moderate — 0.40 % saturated at 25 °C / 55 % RH[5]
Equilibrium moisture content at ~50 % RH%Not documented0.40 saturated at 25 °C / 55 % RH (Bambu Lab)[5]
Drying temperature & time60 °C for 6 h (Polymaker HT-PLA-GF)[1]50 °C for 8 h in a forced-air dryer, or 60–70 °C for 12 h on an X1 heatbed; Fiberlogy specifies 50 °C for 6 h[5][4][23]
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing, rough surface and weak layers[24]
Effect of moisture on strengthPolymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[24]Polymaker rates PLA low-sensitivity — the loss shows as poor layer adhesion and brittle layers rather than a published strength figure[24]
Storage requirementNot documentedSealed with desiccant below 20 % RH; shelf life at ambient is long[19][17]
Mechanical Properties
Tensile strength (XY)MPa50.1 as printed and 50.2 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 59.3 by GB/T 1040[1][2]30 (printed XY, ISO 527, Bambu Lab); 35.1 on My Tech Fun bars for PolyTerra PLA[5][25]
Young's modulusMPa3794 as printed, 4207 annealed, printed XY, ISO 527 (Polymaker)[1]1960 (Bambu Lab, printed XY, ISO 527); Fiberlogy PLA Mineral quotes 3500 (ISO 527, specimen type not stated)[5][4]
Elongation at break%2.77 as printed, 2.3 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 7.99[1][2]14.8 (printed XY, ISO 527)[5]
Flexural strengthMPa86.4 printed XY, ISO 178 (Polymaker)[1]53 (printed XY, ISO 178) — 30 % below PLA Basic at 76[5][19]
Flexural modulusMPa3685 printed XY, ISO 178 (Polymaker); eSUN quotes 4415 flexural modulus by GB/T 9341[1][2]2360 (printed XY, ISO 178)[5]
Charpy impact, notchedkJ/m²5.31 ± 0.46 as printed and 4.92 ± 0.50 annealed (printed XY, ISO 179, notched); Z 4.28 ± 0.18[1]6.3 (printed XY, ISO 179, notched); unnotched 19.2[5]
Other impact dataIzod 10.16 kJ/m² (eSUN, GB/T 1843)[2]Izod 6.1 kJ/m² on My Tech Fun printed bars for PolyTerra PLA[25]
Layer adhesion / Z tensileMPa23.7 as printed, 22.5 annealed, printed Z, ISO 527 (Polymaker)[1]22 (printed Z, ISO 527); flexural Z falls to 29 against 53 in XY; 12.9 on My Tech Fun layer-adhesion bars[5][25]
Brittleness1–5Very brittle — elongation at break 2.77 % in XY and 0.85 % in Z[1]Brittle — snaps with little warning[5]
Creep resistance / sustained load1–5Poor — no GF-grade creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[26][27][28]Poor — 12 mm bar sagged to 18.7 mm over 5 days at 1.25 kg[25]
Fatigue / repeated-flex resistance1–5Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and elongation at break falls to 2.77 % in XY and 0.85 % in Z[29][1]Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength (R = 0.2)[29][21]
Elasticity / flexibility1–5Rigid[1]Rigid[5]
Z strength as % of XY%47 as printed (23.7 Z against 50.1 XY), printed[1]73 by tensile, 55 by flexural (printed, Bambu Lab)[5]
Wear resistance & frictioneSUN describes high wear resistance and positions the grade for wear parts[2]Not documented
Thermal Properties
HDT at 0.45 MPa°C75.5 as printed, 114.7 after annealing (ISO 75, 0.45 MPa) — the point of the material[1]58 (Bambu Lab) and 48 (Fiberlogy PLA Mineral), ISO 75 at 0.45 MPa[5][4]
HDT at 1.8 MPa°C59.7 as printed, 84 after annealing (ISO 75, 1.8 MPa)[1]52 (ISO 75, 1.8 MPa)[5]
Glass transition (Tg)°C59.8 (DSC)[1]61 (DSC)[5]
Melting point / Vicat°C174.9 peak melt (DSC); Vicat 148.9 as printed, 148.3 annealed[1]163 peak melt (DSC); Vicat 63 °C[5]
Continuous service temperature°CNot documented54 — loaded bars begin to move at this temperature[25]
Annealing responseAnnealing lifts HDT at 0.45 MPa from 75.5 to 114.7 °C and modulus from 3794 to 4207 MPa[1]50–60 °C for 6–12 h; some prints deform or warp, and a forced-air oven is required[5]
Flammability / UL 94Not documentedFlammable; no UL 94 rating published by the major brands[19][22]
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors[21]Degrades within weeks outdoors[21][30]
Chemical resistanceNot documentedGood against weak acids, oils and grease; poor against strong acids and alkalis; dissolved by chloroform, THF and hot benzene[22][21]
Water / humidity resistance in service1–5Not documentedGood — insoluble in water[19]
Food contactNot documentedBase resin is food-contact grade, but printed layer grooves harbour bacteria; Prusa advises against food use[21]
Biodegradability / compostabilityNot documentedIndustrially compostable only — needs sustained 55 °C; not home compostable[31][21]
RecyclabilityNot documentedMechanically recyclable; not accepted in household plastic collection[31]
Health & Safety
Fume toxicity1–5Low hazard — minimal VOC and particle emission[32]Low hazard — minimal VOC and particle emission[32]
Ventilation / filtration requirement1–5None needed in a normal room[32]None needed in a normal room[32]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[33]Not documented
Post-Processing
Sanding & machiningNot documentedWet sanding — dry sanding heats the surface by friction and smears it[30][21]
Gluing & solvent weldingNot documentedCyanoacrylate for most joints; some grades partially dissolve and bond with acetone[21][34]
Vapour / chemical smoothingNot documentedNo practical vapour smoothing — only chloroform, hot benzene or THF, which are laboratory-only[21]
Support material pairingNot documentedSupport for PLA (Bambu Lab)[5]
Dimensional accuracy & detailNear-zero shrinkage — 0.05 % in X-Y and Z (Polymaker)[1]Matte surface hides layer lines; 55° overhangs and 30 mm bridges as for plain PLA[5]
Solvents & Solubility
Soluble inChloroform dissolves the PLA matrix (10 % w/v, 2–4 h at 23 °C) and leaves the filler as loose sludge; laboratory reagent.[35]Chloroform: 10 % w/v in 2–4 h at 23 °C, every grade and morphology; THF and DMF only at 65 °C. Laboratory reagents.[35]
Softened or crazed byAcetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[35][36]Acetone, ethyl acetate and toluene plasticise it but dissolve <1 % even at 65 °C; submersion in acetone crazes and destroys parts.[35][36]
Solvent welding & smoothing agentChloroform vapour attacks only the resin fraction, so the filler is left standing proud; no workshop-safe agent exists.[37][36]Chloroform vapour smooths and welds PLA at the cost of tensile strength; acetone does not smooth it at all.[37][36]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Polymaker HT-PLA-GF Technical Data Sheet V1.1 Polymaker · 2026-08 · tds
  2. eSUN ePLA-GF Technical Data Sheet V1.0 (Nov 2023) eSUN (copy hosted on 3d.nice-cdn.com) · 2023-11 · tds
  3. Bambu Filament Technical Data Sheet V1.0 — PLA Galaxy Bambu Lab · 2026-08 · tds
  4. PLA Mineral — product and technical data Fiberlogy · 2026-08 · tds
  5. Bambu Filament Technical Data Sheet V3.0 — PLA Matte Bambu Lab · 2026-08 · tds
  6. Polymaker HT-PLA-GF — product page Polymaker Shop · 2026-08 · vendor
  7. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  8. Polymaker Panchroma Matte PLA — product listing 3DJake International · 2026-08 · vendor
  9. Overture Matte PLA 1.75mm Overture3D · 2026-08 · vendor
  10. Matte PLA filament collection Anycubic Official Store · 2026-08 · vendor
  11. Matte PLA filament collection Sunlu Official Store · 2026-08 · vendor
  12. Fiberlogy PLA Mineral — product listing 3DJake International · 2026-08 · vendor
  13. Polymaker product catalogue Polymaker · 2026-08 · vendor
  14. Extrudr PLA NX2 Matt — product listing 3DJake International · 2026-08 · vendor
  15. PLA Basic — product page Bambu Lab US Store · 2026-08 · vendor
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. PLA — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  19. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  20. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  21. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  22. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  23. Filament Drying Recommendations Bambu Lab Wiki · 2026-08 · doc
  24. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  25. PolyTerra PLA vs PLA+ — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  27. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  28. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  29. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  30. Prusament PLA Technical Data Sheet v1.0 Prusa Polymers · 2018-09 · tds
  31. Filamentive PLA (recycled) — product page Filamentive · 2026-08 · vendor
  32. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  33. StoneFil safety data sheet Formfutura · 2026-08 · msds
  34. Prusament rPLA Corn Pigment 1kg — product page Prusa Research · 2026-08 · vendor
  35. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  36. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  37. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper