PET-CF vs PLA Matte — documented properties and sources
PropertyCarbon-fibre PET (PET-CF)PETGMatte PLAPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$39.99/kg median; $26.00–$49.98/kg across 4 dated product listings$19.09/kg median; $10.99–$32.16/kg across 10 dated product listings
Identity & Market
Base polymer / chemistrySemi-crystalline PET reinforced with carbon fibre — a different polymer from PETG-CF, with the glycol modifier removed so the matrix can crystallise[1][2]PLA compounded with a mineral filler — Fiberlogy names chalk — that scatters light into a diffuse finish[3][4]
Densityg/cm³1.29 (Bambu Lab) and 1.34 (Fiberon PET-CF17), ISO 1183[1][2]1.31 (Bambu Lab, ISO 1183) to 1.38 (Fiberlogy PLA Mineral, method not stated) — above plain PLA from the filler[4][3]
Typical priceUSD/kg1 kg spools cluster near 45[1][5]Mainstream 1 kg spools cluster near 21[6][7][8]
Price range across brandsUSD/kg26–50 across brands; ELEGOO 26 in a 5 kg pack, Bambu Lab 45, Fiberon 50[9][1][5]11–32 across brands; budget house brands 11–19, Fiberlogy PLA Mineral 32[10][7][11]
Market availability1–5Available from several mainstream brands[1][5][9]Stocked by most mainstream brands[10][8][6]
Spool sizes & diameters1.75 mm; 0.5 and 1 kg spools[5][1]1.75 mm; 1 kg spools plus spool-less refills[6][12]
Typical applicationsLoad-bearing parts that must survive above PETG's 70 °C ceiling without moving to PA or PC[1][2]Display models and visible parts where a matte, non-reflective finish matters[4]
Diameter tolerance± mmNot documented±0.03 (Bambu Lab)[13]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[1]190–230 (Bambu Lab); 190–210 (Fiberlogy PLA Mineral)[4][3]
Bed temperature°C80–100 (Bambu Lab)[1]35–45 (Bambu Lab); 60 (Fiberlogy)[4][3]
Enclosure / chamber requirement1–5Enclosure recommended — Bambu Lab specifies a 45–60 °C chamber[1]Open frame is fine[4][3]
Recommended chamber temperature°C45–60 (Bambu Lab)[1]Not documented
Part cooling fan0–60 % (Bambu Lab)[1]Fan on; Fiberlogy specifies 75–100 %[4][3]
Bed surface & adhesion aidTextured PEI, satin or powder-coated sheets; on smooth PEI a glue stick acts as a release agent[14][15]Cool plate, high-temperature plate or textured PEI with glue (Bambu Lab); smooth PEI, textured PEI or glass (Fiberlogy)[4][3]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer — half the speed it allows for PETG-CF[1][16]Not documented
Warping tendency1–5Not documentedNone[4]
Bed-adhesion difficulty1–5Needs the right surface or a thin adhesive — the problem is releasing the part, not sticking it[14][15]Sticks to anything[17]
Stringing / oozing tendency1–5Moderate — retraction tuning needed; Polymaker names stringing as PETG's common quirk[15]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[1]Beginner — prints on any machine out of the box[4][3]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[1]Brass fine indefinitely[18][4][3]
Abrasiveness1–5Highly abrasive — standard CF composite[1]Slightly abrasive — mineral filler pushes density from 1.24 to 1.31–1.38[3][4][19]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for carbon-filled composites[20]Very low[18]
Heat-creep / jam sensitivity1–5Slightly sensitive[21]Moderate — good heatbreak cooling needed; PLA softens below 60 °C[22]
Hotend requirementNo special hot-end required[21]No special hot-end required[17]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.37 % saturated at 25 °C / 55 % RH (Bambu Lab); 0.53 % equilibrium (Fiberon)[1][2]Moderate — 0.40 % saturated at 25 °C / 55 % RH[4]
Equilibrium moisture content at ~50 % RH%0.37 saturated at 25 °C / 55 % RH (Bambu Lab); 0.53 equilibrium (Fiberon PET-CF17)[1][2]0.40 saturated at 25 °C / 55 % RH (Bambu Lab)[4]
Drying temperature & time80 °C for 8–12 h (Bambu Lab) — the longest and hottest dry in the polyester family; Fiberon specifies 100 °C for 10 h[1][2]50 °C for 8 h in a forced-air dryer, or 60–70 °C for 12 h on an X1 heatbed; Fiberlogy specifies 50 °C for 6 h[4][3][23]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[24]Bubbling and popping at the nozzle, stringing, rough surface and weak layers[24]
Effect of moisture on strengthBambu Lab publishes its whole mechanical table under the heading "Mechanical Properties (Dry state)" — the quoted figures apply only to dried filament[1]Polymaker rates PLA low-sensitivity — the loss shows as poor layer adhesion and brittle layers rather than a published strength figure[24]
Storage requirementSealed with desiccant; Polymaker groups PETG with the highly hygroscopic materials[24][15]Sealed with desiccant below 20 % RH; shelf life at ambient is long[19][17]
Hydrolysis at melt temperatureThe 80–100 °C dry both suppliers mandate is far above the 55–65 °C used for PETG, consistent with a melt-hydrolysis risk in the semi-crystalline PET matrix; neither publishes a molecular-weight loss figure[1][2]Not documented
Mechanical Properties
Tensile strength (XY)MPa65.9 (Fiberon) to 74 (Bambu Lab) printed XY, ISO 527[1][2]30 (printed XY, ISO 527, Bambu Lab); 35.1 on My Tech Fun bars for PolyTerra PLA[4][25]
Young's modulusMPa4730 ± 260 (Bambu Lab) and 5481 ± 224 (Fiberon) printed XY, ISO 527[1][2]1960 (Bambu Lab, printed XY, ISO 527); Fiberlogy PLA Mineral quotes 3500 (ISO 527, specimen type not stated)[4][3]
Elongation at break%2.4 ± 0.5 printed XY, ISO 527 (Fiberon PET-CF17)[2]14.8 (printed XY, ISO 527)[4]
Flexural strengthMPa109.3 ± 2.0 printed XY, ISO 178 (Fiberon PET-CF17)[2]53 (printed XY, ISO 178) — 30 % below PLA Basic at 76[4][19]
Flexural modulusMPa4744 ± 136 printed XY, ISO 178 (Fiberon PET-CF17)[2]2360 (printed XY, ISO 178)[4]
Charpy impact, notchedkJ/m²5.1 ± 0.2 printed XY, ISO 179 notched (Fiberon PET-CF17); unnotched 25.1 ± 2.8[2]6.3 (printed XY, ISO 179, notched); unnotched 19.2[4]
Other impact dataNot documentedIzod 6.1 kJ/m² on My Tech Fun printed bars for PolyTerra PLA[25]
Layer adhesion / Z tensileMPa27.9 (Fiberon) and 35 ± 5 (Bambu Lab) printed Z, ISO 527[1][2]22 (printed Z, ISO 527); flexural Z falls to 29 against 53 in XY; 12.9 on My Tech Fun layer-adhesion bars[4][25]
Brittleness1–5Very brittle — elongation at break 2.4 % in XY and 0.8 % in Z[2]Brittle — snaps with little warning[4]
Creep resistance / sustained load1–5Good — no creep test found; annealed PET-CF holds a 105 °C HDT at 1.8 MPa and a 4730–5481 MPa modulus against 1500–2311 for PETG[2][1]Poor — 12 mm bar sagged to 18.7 mm over 5 days at 1.25 kg[25]
Fatigue / repeated-flex resistance1–5Below average — no S-N curve; elongation at break is 2.4 % in XY and 0.8 % in Z, against 5.2–9.3 % for unfilled PETG[2]Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength (R = 0.2)[26][22]
Elasticity / flexibility1–5Rigid[1]Rigid[4]
Z strength as % of XY%42 (Fiberon) to 47 (Bambu Lab), printed[1][2]73 by tensile, 55 by flexural (printed, Bambu Lab)[4]
Thermal Properties
HDT at 0.45 MPa°C147.5 (Fiberon) and 205 (Bambu Lab), ISO 75 at 0.45 MPa[1][2]58 (Bambu Lab) and 48 (Fiberlogy PLA Mineral), ISO 75 at 0.45 MPa[4][3]
HDT at 1.8 MPa°C105 (Fiberon) and 182 (Bambu Lab), ISO 75 at 1.8 MPa[1][2]52 (ISO 75, 1.8 MPa)[4]
Glass transition (Tg)°C75 (Bambu Lab) and 79.3 (Fiberon), DSC[1][2]61 (DSC)[4]
Melting point / Vicat°C241.3 (Fiberon) and 250 (Bambu Lab) melting, DSC; Vicat 226–238[1][2]163 peak melt (DSC); Vicat 63 °C[4]
Continuous service temperature°CNot documented54 — loaded bars begin to move at this temperature[25]
Annealing responseThe PET matrix crystallises on annealing, which is what separates this grade from PETG-CF[2][1]50–60 °C for 6–12 h; some prints deform or warp, and a forced-air oven is required[4]
Flammability / UL 94Flammable; no UL 94 rating published for standard grades[27]Flammable; no UL 94 rating published by the major brands[19][28]
Environment & Chemical
UV resistance1–5Not documentedDegrades within weeks outdoors[22][29]
Chemical resistanceWithstands acids, alkalis, oils and UV exposure[15]Good against weak acids, oils and grease; poor against strong acids and alkalis; dissolved by chloroform, THF and hot benzene[28][22]
Water / humidity resistance in service1–5Not documentedGood — insoluble in water[19]
Food contactNot certified for food contact as filament[15]Base resin is food-contact grade, but printed layer grooves harbour bacteria; Prusa advises against food use[22]
Biodegradability / compostabilityNot biodegradable[15]Industrially compostable only — needs sustained 55 °C; not home compostable[30][22]
RecyclabilityNot accepted in household plastic collection[15]Mechanically recyclable; not accepted in household plastic collection[30]
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Fiberon PET-CF17, ANSI/ESD S11.11)[2]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[31]Low hazard — minimal VOC and particle emission[31]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[31][1]None needed in a normal room[31]
Dust & fibre handling hazardCarbon fibre is bound in the matrix; sanding dust should not be inhaled[2]Not documented
Post-Processing
Sanding & machiningSands poorly — the material is tough and gums rather than powders[21]Wet sanding — dry sanding heats the surface by friction and smears it[29][22]
Gluing & solvent weldingCyanoacrylate; no common solvent welds PETG cleanly[21]Cyanoacrylate for most joints; some grades partially dissolve and bond with acetone[22][32]
Vapour / chemical smoothingNo practical vapour smoothing[21]No practical vapour smoothing — only chloroform, hot benzene or THF, which are laboratory-only[22]
Support material pairingPrints its own supports; Polymaker rates PolyDissolve S1 for PETG[21]Support for PLA (Bambu Lab)[4]
Dimensional accuracy & detailBambu Lab markets it on low warping and shrinkage relative to other high-temperature composites[1]Matte surface hides layer lines; 55° overhangs and 30 mm bridges as for plain PLA[4]
Solvents & Solubility
Soluble inNone common; fluorinated solvents such as hexafluoroisopropanol dissolve linear polyester at 23 °C. Laboratory only.[33][34]Chloroform: 10 % w/v in 2–4 h at 23 °C, every grade and morphology; THF and DMF only at 65 °C. Laboratory reagents.[35]
Softened or crazed byEnsinger rates polyester not resistant to chloroform or dichloromethane and only conditionally resistant to acetone and MEK.[34]Acetone, ethyl acetate and toluene plasticise it but dissolve <1 % even at 65 °C; submersion in acetone crazes and destroys parts.[35][36]
Solvent welding & smoothing agentDichloromethane attacks polyester and can be brushed on, but the carbon fibre blocks any useful surface flow.[34][36]Chloroform vapour smooths and welds PLA at the cost of tensile strength; acetone does not smooth it at all.[37][36]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet — PET-CF Bambu Lab · 2026-08 · tds
  2. Fiberon PET-CF17 Technical Data Sheet V1.0 Polymaker · 2026-08 · tds
  3. PLA Mineral — product and technical data Fiberlogy · 2026-08 · tds
  4. Bambu Filament Technical Data Sheet V3.0 — PLA Matte Bambu Lab · 2026-08 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. Polymaker Panchroma Matte PLA — product listing 3DJake International · 2026-08 · vendor
  7. Overture Matte PLA 1.75mm Overture3D · 2026-08 · vendor
  8. Matte PLA filament collection Anycubic Official Store · 2026-08 · vendor
  9. ELEGOO product catalogue ELEGOO · 2026-08 · vendor
  10. Matte PLA filament collection Sunlu Official Store · 2026-08 · vendor
  11. Fiberlogy PLA Mineral — product listing 3DJake International · 2026-08 · vendor
  12. Extrudr PLA NX2 Matt — product listing 3DJake International · 2026-08 · vendor
  13. PLA Basic — product page Bambu Lab US Store · 2026-08 · vendor
  14. Prusament PETG Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  15. PETG — material basics Polymaker Wiki · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. PLA — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  19. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  20. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  21. PET and PETG — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  22. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  23. Filament Drying Recommendations Bambu Lab Wiki · 2026-08 · doc
  24. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  25. PolyTerra PLA vs PLA+ — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  27. Prusament PETG V0 Technical Datasheet Prusa Polymers · 2026-08 · tds
  28. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  29. Prusament PLA Technical Data Sheet v1.0 Prusa Polymers · 2018-09 · tds
  30. Filamentive PLA (recycled) — product page Filamentive · 2026-08 · vendor
  31. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  32. Prusament rPLA Corn Pigment 1kg — product page Prusa Research · 2026-08 · vendor
  33. Resistance of Ultramid, Ultraform and Ultradur to chemicals (TI-KTU/AS-28 e) BASF · 2000-10 · tds
  34. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  35. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  36. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  37. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper