PEKK vs HT soluble — documented properties and sources
PropertyPEKKHIGHTEMPHigh-temperature supportSUPPORT
Market snapshot
Listing priceUSD/kg; dated snapshots$525.00/kg median; $332.50–$771.12/kg across 6 dated product listings$209.00/kg median; $100.00–$290.00/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryPolyether ketone ketone, amorphous grade — a polyaryletherketone that stays amorphous, so it does not need PEEK's crystallisation control. Stratasys sells it as Antero 800NA and Antero 840CN03; category numbers below are unfilled unless a carbon grade is named[1][2]Break-away support compounded to survive high-temperature print chambers; 3DXTech sells separate grades for PC/ABS and for the PAEK and PEI class[3][4]
Densityg/cm³1.28 unfilled (ASTM D792, Antero 800NA; 1.31 annealed) and 1.33 for CarbonX PEKK-A CF15 (ISO 1183)[2][1]1.37 (3DXTech THERMAX HTS1, ISO 1183)[3]
Typical priceUSD/kg1 kg-equivalent spools cluster near 550[5][6][7]1 kg-equivalent spools cluster near 168[5]
Price range across brandsUSD/kg333-771 across grades and formats; 3DXTech CarbonX PEKK-A+CF15 333 at 2 kg, 3D4Makers unfilled PEKK-A 485 at 2 kg, IEMAI 3D 500 at 1 kg, Kimya PEKK Carbon 771 at 500 g[5][6][7][8][9]100–290 across grades; 3DXTech THERMAX MTS1 100 at 2 kg, HTS2 168 at 250 g, HTS1 250 at 500 g, IEMAI 3D HT-SP 290 at 1 kg[5][10]
Market availability1–5Niche, a handful of specialist brands[5][6][7]Niche, a handful of specialist brands[5][10]
Spool sizes & diameters1.75 and 2.85 mm; 200 g to 2 kg spools, plus Stratasys canisters[5][6][2]1.75 mm; 250 g, 500 g, 1 kg and 2 kg spools[5]
Typical applicationsAerospace interior and structural parts; 3DXTech labels its carbon-filled PEKK-A grade AERO and Stratasys certifies Antero 800NA for outgassing and FST[1][2]Support for PEEK, PEI and PC-class prints, where PVA and PLA-based supports would decompose[3][4]
Printing Parameters
Bed temperature°C140 (3DXTech CarbonX PEKK-A CF15)[1]Not documented
Enclosure / chamber requirement1–5Actively heated chamber required[11][12]Actively heated chamber required — it is used inside high-temperature builds[3]
Overall printing difficulty1–5Expert / industrial hardware only[11][12]Expert / industrial hardware only[3]
Extruder requirementNot documentedA dual-extruder machine rated for high-temperature materials; 3DXTech states the grade is intended for dual-extruder printers designed to print high-temp materials[13]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — the category spans unfilled PEKK, where brass is acceptable, and the carbon-filled aerospace grades that make up most of the market[1][2]Brass fine indefinitely[3]
Abrasiveness1–5Highly abrasive — most PEKK filament sold is carbon-filled; unfilled Antero 800NA and ThermaX PEKK-A are non-abrasive[1][2]Non-abrasive[3]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[14]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry for HTS1 and 80 °C for MTS1[13][15]
Moisture Behaviour
Effect of moisture on strengthNo dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[14]No dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry for HTS1 and 80 °C for MTS1 because trapped water flashes to steam at these nozzle temperatures[13][15]
Mechanical Properties
Tensile strength (XY)MPa86.7-90.0 at yield and 73.0 at break (printed XZ, ASTM D638, Antero 800NA on the F900 and Fortus 450mc); 88.8 at break annealed; 126 at break for CarbonX PEKK-A CF15 (printed XY, ISO 527)[2][1]Not documented
Young's modulusMPa2640-3870 (printed XZ, ASTM D638, Antero 800NA; upper figure annealed); 9125 for CarbonX PEKK-A CF15 (printed XY, ISO 527)[2][1]Not documented
Elongation at break%6.1 at break (printed XZ, ASTM D638, Antero 800NA); 2.3 in ZX; 3.15 for CarbonX PEKK-A CF15 (ISO 527)[2][1]Not documented
Flexural strengthMPa136 at 5 % strain (printed XZ, ASTM D790, Antero 800NA); 178 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[2][1]Not documented
Flexural modulusMPa3200 (printed XZ, ASTM D790, Antero 800NA); 8817 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[2][1]Not documented
Other impact dataIzod notched 41.1 J/m XZ and 33.3 J/m ZX; unnotched 1730 J/m XZ against 203 J/m ZX (printed, ASTM D256/D4812, Antero 800NA)[2]Not documented
Layer adhesion / Z tensileMPa50.1-59.4 at yield (printed ZX, ASTM D638, Antero 800NA); 56.0 for the ESD grade Antero 840CN03[2][16]Not documented
Brittleness1–5Moderate unfilled — 6.1 % elongation at break in plane; brittle in the carbon-filled grades at 3.15 %[2][1]Not documented
Creep resistance / sustained load1–5Excellent — holds load for years. Antero 800NA still holds 82 % of its room-temperature ZX tensile strength at 104 °C and 63 % at 132 °C (printed, ASTM D638)[2]Not documented
Elasticity / flexibility1–5Rigid[1]Not documented
Z strength as % of XY%56-82 (Antero 800NA and 840CN03 printed on the F900 and Fortus 450mc, ZX against XZ tensile yield and break, ASTM D638)[2][16]Not documented
Wear resistance & frictionNot documented3DXTech marks tensile strength, modulus and elongation as not applicable for its support grades — they are not characterised as structural materials[3]
Thermal Properties
HDT at 0.45 MPa°C158 (printed XY and ZX, ASTM D648 Method B at 66 psi, Antero 800NA); 285 for CarbonX PEKK-A CF15 (ISO 75 at 0.45 MPa)[2][1]Not documented
HDT at 1.8 MPa°C156-157 (printed, ASTM D648 Method B at 264 psi, Antero 800NA); moulded 147[2]205 (THERMAX HTS1, printed XY, ISO 75 at 1.8 MPa)[3]
Glass transition (Tg)°C156 (ASTM D7426, Antero 800NA); 165 for CarbonX PEKK-A CF15 (DSC)[2][1]225 (3DXTech THERMAX HTS1, DSC) — high enough to stay solid inside a PEI or PEEK build[3]
Melting point / Vicat°C300 melt point (ASTM D7426 peak heat, Antero 800NA); 305 for CarbonX PEKK-A CF15 (DSC)[2][1]Not documented
Thermal expansion (CTE)µm/m·K36.1 in XY and 50.2 in ZX (printed, 40-140 °C, ASTM E831, Antero 800NA); 47.4 and 51.2 for the ESD grade Antero 840CN03[2][16]Not documented
Environment & Chemical
UV resistance1–5Good — years with some colour shift. 1000 h of QUV cycling to ASTM G154 left Antero 800NA's yield strength unchanged at 57 MPa and raised stress at break 3.6 %[2]Not documented
Electrical & ESD propertiesUnfilled PEKK is an insulator at above 1.4e14 ohm-cm (ASTM D257); CarbonX PEKK-A CF15 sits above 10^7 ohm/sq, and the Antero 840CN03 ESD grade is specified at 10^4-10^9 ohm-cm[2][1][16]Surface resistance above 10^13 ohm/sq on all three THERMAX support grades (ASTM D257) — insulating[3][17][4]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[18]Low hazard — minimal VOC and particle emission; none of these materials was in the chamber study[18]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[18]Open a window / occasional ventilation[18]
Dust & fibre handling hazardCarbon fibre is bound in the matrix; sanding dust should not be inhaled[1]Not documented
Post-Processing
Support material pairingNot documentedThis is the support material. MTS1 is matched to PC/ABS and PC; HTS1 and HTS2 to the higher-temperature classes[4][3]
Solvents & Solubility
Soluble inConcentrated sulphuric acid, as for PEEK; no common organic solvent touches a polyaryletherketone.[19][20]Aqueous alkali, not water: IEMAI specifies an alkaline bath in an ultrasonic cleaner until the support dissolves.[10]
Softened or crazed byConcentrated sulphuric acid and liquid Freon are the entries Ensinger marks not resistant; acetone, MEK and toluene do nothing.[19]Not documented
Solvent welding & smoothing agentNone — no solvent softens a polyaryletherketone.[19]None — the alkaline bath dissolves the support rather than welding anything.[10]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. CarbonX Carbon Fiber PEKK-A CF15 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  2. Antero 800NA — FDM Material Data Sheet (PEKK-based) Stratasys · 2025-08 · tds
  3. THERMAX HTS1 Break Away Support Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  4. THERMAX MTS1 Break Away Support Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  5. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  6. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  7. Kimya PEKK-A Natural 1.75 mm 500 g igo3d · 2026-08 · vendor
  8. Kimya PEKK Carbon Grey 1.75 mm 500 g igo3d · 2026-08 · vendor
  9. IEMAI 3D PEKK 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  10. IEMAI 3D HT-SP alkaline-soluble support filament — store page IEMAI 3D · 2026-08 · vendor
  11. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  12. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  13. THERMAX HTS1 — product page 3DXTech · 2026-08 · vendor
  14. THERMAX PEKK-A — product page (print recommendations) 3DXTech · 2026-08 · doc
  15. THERMAX MTS1 — product page 3DXTech · 2026-08 · vendor
  16. Antero 840CN03 — FDM Material Data Sheet (PEKK, ESD) Stratasys · 2024-08 · tds
  17. THERMAX HTS2 Break Away Support Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  18. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  19. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  20. The Effects of Sulfonated Poly(ether ether ketone) Ion Exchange Preparation Conditions on Membrane Properties Yee, Zhang & Ladewig, Membranes 3(3) 182–195 · 2013-07 · paper