3D Printing Info

Filament comparison

PEKK vs PLA Wood

Compare printing settings, strength, heat resistance, dated prices and sources.

PEKK guideWood-filled PLA guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PEKK comparisonsMore PLA Wood comparisons
PEKK vs PLA Wood — documented properties and sources
PropertyPEKKHIGHTEMPWood-filled PLAPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$525.00/kg median; $332.50–$771.12/kg across 6 dated product listings$34.49/kg median; $13.99–$76.40/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryPolyether ketone ketone, amorphous grade — a polyaryletherketone that stays amorphous, so it does not need PEEK's crystallisation control. Stratasys sells it as Antero 800NA and Antero 840CN03; category numbers below are unfilled unless a carbon grade is named[1][2]PLA filled with wood powder — 10–18 wt% (Bambu Lab SDS); colorFabb woodFill uses a PLA/PHA base with recycled wood fibre[3][4]
Densityg/cm³1.28 unfilled (ASTM D792, Antero 800NA; 1.31 annealed) and 1.33 for CarbonX PEKK-A CF15 (ISO 1183)[2][1]1.15 (colorFabb) to 1.23 (Fiberlogy), ISO 1183; Bambu Lab 1.21[5][4][6]
Typical priceUSD/kg1 kg-equivalent spools cluster near 550[7][8][9]1 kg spools cluster near 25; counting the 0.5 kg specialty spools the middle of the market is about 34[10][11][12]
Price range across brandsUSD/kg333-771 across grades and formats; 3DXTech CarbonX PEKK-A+CF15 333 at 2 kg, 3D4Makers unfilled PEKK-A 485 at 2 kg, IEMAI 3D 500 at 1 kg, Kimya PEKK Carbon 771 at 500 g[7][8][9][13][14]14–76 across brands; SUNLU 14, ELEGOO 19, Bambu Lab 25, Prusament 44, Filament PM 49 on 0.5 kg spools, colorFabb 76[11][10][15][16][17][12]
Market availability1–5Niche, a handful of specialist brands[7][8][9]Stocked by most mainstream brands[10][11][16][6]
Spool sizes & diameters1.75 and 2.85 mm; 200 g to 2 kg spools, plus Stratasys canisters[7][8][2]1.75 and 2.85 mm; 0.6, 0.85 and 1 kg spools[16][6][10]
Typical applicationsAerospace interior and structural parts; 3DXTech labels its carbon-filled PEKK-A grade AERO and Stratasys certifies Antero 800NA for outgassing and FST[1][2]Decorative and model-making prints that are sanded and stained like timber[5][4]
Diameter tolerance± mmNot documented±0.03 (Bambu Lab)[5]
Printing Parameters
Nozzle temperature°CNot documented190–240 (Bambu Lab); colorFabb advises 195–220 for its PLA/PHA base[5][4]
Bed temperature°C140 (3DXTech CarbonX PEKK-A CF15)[1]35–45 (Bambu Lab); 50–70 (Fiberlogy)[5][6]
Enclosure / chamber requirement1–5Actively heated chamber required[18][19]Open frame is fine[5]
Part cooling fanNot documentedFan on[5]
Warping tendency1–5Not documentedNone[5]
Overall printing difficulty1–5Expert / industrial hardware only[18][19]Easy — minor profile tuning; pre-drying is required and the wood content chars if it sits hot[20][5]
Extruder requirementNot documentedNozzles below 0.4 mm are not compatible; Bambu Lab does not recommend the AMS lite[20]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — the category spans unfilled PEKK, where brass is acceptable, and the carbon-filled aerospace grades that make up most of the market[1][2]Brass acceptable; hardened steel for volume work — Bambu Lab's PLA compatibility table lists no hardened-nozzle requirement, but its nozzle guide names wood among the abrasive filaments hardened steel exists for[20][21]
Abrasiveness1–5Highly abrasive — most PEKK filament sold is carbon-filled; unfilled Antero 800NA and ThermaX PEKK-A are non-abrasive[1][2]Moderately abrasive — wood fill[20]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[22]Moderate — needs dry filament and a clean nozzle; wood particles char and block small nozzles[20]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Not documentedHigh — 1.25 % saturated at 25 °C / 55 % RH, the highest in the PLA family[5]
Equilibrium moisture content at ~50 % RH%Not documented1.25 saturated at 25 °C / 55 % RH (Bambu Lab)[5]
Drying temperature & timeNot documented55 °C for 8 h in a forced-air dryer; Bambu Lab lists pre-drying as required[5][20]
Symptoms when wetNot documentedBambu Lab flags pre-drying and ventilation as specific requirements for this grade[20]
Effect of moisture on strengthNo dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[22]No dry-versus-conditioned figures are published. At 1.25 % saturated uptake the practical loss shows as poor layer adhesion, rough surface and weak layers[23][5]
Mechanical Properties
Tensile strength (XY)MPa86.7-90.0 at yield and 73.0 at break (printed XZ, ASTM D638, Antero 800NA on the F900 and Fortus 450mc); 88.8 at break annealed; 126 at break for CarbonX PEKK-A CF15 (printed XY, ISO 527)[2][1]26 ± 5 (Bambu Lab) and 28.4 (colorFabb) printed XY, ISO 527; Fiberlogy quotes 35 at yield[5][4][6]
Young's modulusMPa2640-3870 (printed XZ, ASTM D638, Antero 800NA; upper figure annealed); 9125 for CarbonX PEKK-A CF15 (printed XY, ISO 527)[2][1]2360 ± 190 (Bambu Lab) and 2479 (colorFabb) printed XY, ISO 527; Fiberlogy 2950[5][4][6]
Elongation at break%6.1 at break (printed XZ, ASTM D638, Antero 800NA); 2.3 in ZX; 3.15 for CarbonX PEKK-A CF15 (ISO 527)[2][1]4.5 (colorFabb) to 15.3 (Bambu Lab) printed XY, ISO 527; Fiberlogy 6.5[5][4][6]
Flexural strengthMPa136 at 5 % strain (printed XZ, ASTM D790, Antero 800NA); 178 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[2][1]55 ± 4 printed XY, ISO 178 (Bambu Lab)[5]
Flexural modulusMPa3200 (printed XZ, ASTM D790, Antero 800NA); 8817 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[2][1]2780 ± 120 printed XY, ISO 178 (Bambu Lab)[5]
Charpy impact, notchedkJ/m²Not documented3.81 (colorFabb) and 6.3 ± 2.2 (Bambu Lab) printed XY, ISO 179, notched[5][4]
Other impact dataIzod notched 41.1 J/m XZ and 33.3 J/m ZX; unnotched 1730 J/m XZ against 203 J/m ZX (printed, ASTM D256/D4812, Antero 800NA)[2]Charpy unnotched 12.28 (colorFabb) and 15.7 (Bambu Lab), printed, ISO 179[5][4]
Layer adhesion / Z tensileMPa50.1-59.4 at yield (printed ZX, ASTM D638, Antero 800NA); 56.0 for the ESD grade Antero 840CN03[2][24]15 ± 4 printed Z, ISO 527 (Bambu Lab); flexural Z falls to 28 against 55 in XY[5]
Brittleness1–5Moderate unfilled — 6.1 % elongation at break in plane; brittle in the carbon-filled grades at 3.15 %[2][1]Brittle — snaps with little warning[5]
Creep resistance / sustained load1–5Excellent — holds load for years. Antero 800NA still holds 82 % of its room-temperature ZX tensile strength at 104 °C and 63 % at 132 °C (printed, ASTM D638)[2]Poor — no wood-filled creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[25][26][27]
Fatigue / repeated-flex resistance1–5Not documentedPoor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and the wood filler cuts elongation and the parts snap without warning[28][5]
Elasticity / flexibility1–5Rigid[1]Rigid[5]
Z strength as % of XY%56-82 (Antero 800NA and 840CN03 printed on the F900 and Fortus 450mc, ZX against XZ tensile yield and break, ASTM D638)[2][24]58 by tensile, 51 by flexural (printed, Bambu Lab)[5]
Thermal Properties
HDT at 0.45 MPa°C158 (printed XY and ZX, ASTM D648 Method B at 66 psi, Antero 800NA); 285 for CarbonX PEKK-A CF15 (ISO 75 at 0.45 MPa)[2][1]60 (ISO 75, 0.45 MPa)[5]
HDT at 1.8 MPa°C156-157 (printed, ASTM D648 Method B at 264 psi, Antero 800NA); moulded 147[2]57 (ISO 75, 1.8 MPa)[5]
Glass transition (Tg)°C156 (ASTM D7426, Antero 800NA); 165 for CarbonX PEKK-A CF15 (DSC)[2][1]54 (Bambu Lab, DSC); Fiberlogy quotes 55–60[5][6]
Melting point / Vicat°C300 melt point (ASTM D7426 peak heat, Antero 800NA); 305 for CarbonX PEKK-A CF15 (DSC)[2][1]156 peak melt (DSC)[5]
Thermal expansion (CTE)µm/m·K36.1 in XY and 50.2 in ZX (printed, 40-140 °C, ASTM E831, Antero 800NA); 47.4 and 51.2 for the ESD grade Antero 840CN03[2][24]Not documented
Environment & Chemical
UV resistance1–5Good — years with some colour shift. 1000 h of QUV cycling to ASTM G154 left Antero 800NA's yield strength unchanged at 57 MPa and raised stress at break 3.6 %[2]Degrades within weeks outdoors[29]
Electrical & ESD propertiesUnfilled PEKK is an insulator at above 1.4e14 ohm-cm (ASTM D257); CarbonX PEKK-A CF15 sits above 10^7 ohm/sq, and the Antero 840CN03 ESD grade is specified at 10^4-10^9 ohm-cm[2][1][24]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[30]Low hazard — minimal VOC and particle emission[30]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[30]None needed in a normal room; Bambu Lab specifically advises ventilation for this grade[20]
Dust & fibre handling hazardCarbon fibre is bound in the matrix; sanding dust should not be inhaled[1]Not documented
Post-Processing
Sanding & machiningNot documentedSands and stains like timber — the usual reason for choosing it[4]
Support material pairingNot documentedSupport for PLA (Bambu Lab)[5]
Dimensional accuracy & detailNot documentedWood grain hides layer lines; colour darkens with nozzle temperature[5][4]
Solvents & Solubility
Soluble inConcentrated sulphuric acid, as for PEEK; no common organic solvent touches a polyaryletherketone.[31][32]Chloroform dissolves the PLA matrix (10 % w/v, 2–4 h at 23 °C) and leaves the filler as loose sludge; laboratory reagent.[33]
Softened or crazed byConcentrated sulphuric acid and liquid Freon are the entries Ensinger marks not resistant; acetone, MEK and toluene do nothing.[31]Acetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[33][34]
Solvent welding & smoothing agentNone — no solvent softens a polyaryletherketone.[31]Chloroform vapour attacks only the resin fraction, so the filler is left standing proud; no workshop-safe agent exists.[35][34]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. CarbonX Carbon Fiber PEKK-A CF15 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  2. Antero 800NA — FDM Material Data Sheet (PEKK-based) Stratasys · 2025-08 · tds
  3. Safety Data Sheet SDS20250723SA16 — Bambu PLA Wood Bambu Lab · 2025-07 · msds
  4. woodFill technical data sheet colorFabb · 2026-08 · tds
  5. Bambu Filament Technical Data Sheet — PLA Wood Bambu Lab · 2026-08 · tds
  6. FiberWood technical data sheet Fiberlogy · 2026-08 · tds
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  9. Kimya PEKK-A Natural 1.75 mm 500 g igo3d · 2026-08 · vendor
  10. PLA Wood — product page Bambu Lab US Store · 2026-08 · vendor
  11. ELEGOO product catalogue ELEGOO · 2026-08 · vendor
  12. PLA+ WOODJet - Natur (1,75 mm; 0,5 kg) Filament PM shop · 2026-08 · vendor
  13. Kimya PEKK Carbon Grey 1.75 mm 500 g igo3d · 2026-08 · vendor
  14. IEMAI 3D PEKK 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  15. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  16. woodFill — product page colorFabb US · 2026-08 · vendor
  17. SUNLU Optimized Wood PLA 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  18. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  19. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  20. PLA Usage Guide Bambu Lab Wiki · 2026-08 · doc
  21. Nozzles — material and compatibility Bambu Lab Wiki · 2026-08 · doc
  22. THERMAX PEKK-A — product page (print recommendations) 3DXTech · 2026-08 · doc
  23. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  24. Antero 840CN03 — FDM Material Data Sheet (PEKK, ESD) Stratasys · 2024-08 · tds
  25. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  27. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  28. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  29. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  30. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  31. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  32. The Effects of Sulfonated Poly(ether ether ketone) Ion Exchange Preparation Conditions on Membrane Properties Yee, Zhang & Ladewig, Membranes 3(3) 182–195 · 2013-07 · paper
  33. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  34. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  35. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper