PEI 9085 vs PLA-GF

Compare printing settings, strength, heat resistance, dated prices and sources.

PEI (ULTEM 9085) guideGlass-fibre PLA (PLA-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PEI 9085 comparisonsMore PLA-GF comparisons
PEI 9085 vs PLA-GF — documented properties and sources
PropertyPEI (ULTEM 9085)HIGHTEMPGlass-fibre PLA (PLA-GF)PLA
Market snapshot
Listing priceUSD/kg; dated snapshots$309.80/kg median; $220.00–$392.00/kg across 6 dated product listings$44.99/kg median; $29.99–$59.99/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryPolyetherimide, ULTEM 9085 grade — the flame-retardant PEI used for aircraft interiors[1]PLA filled with chopped glass fibre — 12 wt% (Polymaker HT-PLA-GF), 15–20 wt% (eSUN PLA-GF). Bambu Lab PLA Galaxy uses glass microspheres, not fibre, and is not equivalent[2][3][4]
Densityg/cm³1.34 (ISO 1183, 3DXTech) against 1.27 specific gravity on moulded plaques (ASTM D792, Stratasys) — the two suppliers disagree[1][5]1.31 (eSUN) to 1.337 (Polymaker), ISO 1183 / GB/T 1033[2][3]
Typical priceUSD/kg1 kg-equivalent spools cluster near 298[6][7][8][9]1 kg spools cluster near 30[10][11]
Price range across brandsUSD/kg220-392 across brands and formats; 3DXTech ThermaX PEI 9085 220 at 2 kg, 3D4Makers 270 at 2 kg, Fiberlogy 298 at 500 g, Kimya 321 at 500 g, IEMAI 3D 385 at 1 kg, 3DXTech CarbonX PEI 9085+CF 392[6][7][8][9][12]30–60 across brands; Polymaker 30, Proto-pasta 60[10][11]
Market availability1–5Niche, a handful of specialist brands[6][7][8][9]Niche, a handful of specialist brands[10][11][3]
Spool sizes & diameters1.75 and 2.85 mm; 250 g to 2 kg spools, plus Stratasys canisters[6][9][5]1.75 mm; 0.5 and 1 kg spools[11][13]
Typical applicationsAircraft interior parts and rail rolling stock, where the flame, smoke and toxicity rating is the requirement[1]Stiff brackets and fixtures; the Polymaker grade is aimed at parts annealed for heat resistance[2]
Printing Parameters
Nozzle temperature°CNot documented210–230 (Polymaker HT-PLA-GF)[2]
Bed temperature°C130–140 (3DXTech)[1]25–60 (Polymaker HT-PLA-GF)[2]
Enclosure / chamber requirement1–5Actively heated chamber required[14][15]Open frame is fine[2]
Part cooling fanNot documentedFan on — eSUN specifies 100 %[3]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented28 at Polymaker's stated 350 mm/s on a 0.4 mm nozzle at 0.2 mm layer; eSUN prints its specimens at 60 mm/s[2][3][16]
Warping tendency1–5Severe — heated chamber needed[14]Not documented
Shrinkage%Not documented0.05 in X-Y and Z, 0.10 diagonal (Polymaker HT-PLA-GF)[2]
Overall printing difficulty1–5Expert / industrial hardware only[14][15]Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[2]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[14]Hardened steel required[2]
Abrasiveness1–5Non-abrasive when unfilled[1]Highly abrasive — standard GF composite[2]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[17]Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[18]
Hotend requirementNot documentedHardened steel or ruby nozzle; Polymaker's own slicer preset sets a minimum nozzle hardness of 40 HRC[2]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Not documentedModerate — the PLA matrix takes up 0.40–0.51 % saturated; no glass-filled grade publishes its own figure[19][20]
Drying temperature & timeNot documented60 °C for 6 h (Polymaker HT-PLA-GF)[2]
Effect of moisture on strengthNo dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[17]Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[21]
Mechanical Properties
Tensile strength (XY)MPa63-77 at break (printed XZ, ASTM D638, Stratasys F900/F3300/Fortus 450mc, three tips and two colours); 54 (printed XY, ISO 527, 3DXTech)[5][1]50.1 as printed and 50.2 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 59.3 by GB/T 1040[2][3]
Young's modulusMPa2040-2540 (printed XZ, ASTM D638, Stratasys); 2050 (printed XY, ISO 527, 3DXTech)[5][1]3794 as printed, 4207 annealed, printed XY, ISO 527 (Polymaker)[2]
Elongation at break%5.4-9.1 at break (printed XZ, ASTM D638, Stratasys); 1.9-4.3 in ZX; 3DXTech quotes 3 (ISO 527)[5][1]2.77 as printed, 2.3 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 7.99[2][3]
Flexural strengthMPa104-116 at break (printed XZ, ASTM D790 Procedure A, Stratasys); 72-98 in ZX; 3DXTech quotes 90 (ISO 178)[5][1]86.4 printed XY, ISO 178 (Polymaker)[2]
Flexural modulusMPa2400-2550 (printed XZ, ASTM D790, Stratasys F900 T16 and T16A) against 2120-2130 in ZX; 3DXTech quotes 2170 (ISO 178)[5][1]3685 printed XY, ISO 178 (Polymaker); eSUN quotes 4415 flexural modulus by GB/T 9341[2][3]
Charpy impact, notchedkJ/m²Not documented5.31 ± 0.46 as printed and 4.92 ± 0.50 annealed (printed XY, ISO 179, notched); Z 4.28 ± 0.18[2]
Other impact dataIzod notched 88.5-140 J/m XZ against 37-80 J/m ZX; unnotched 647-2260 J/m XZ against 169-633 J/m ZX (printed, ASTM D256/D4812, Stratasys, across three printers and three tips)[5]Izod 10.16 kJ/m² (eSUN, GB/T 1843)[3]
Layer adhesion / Z tensileMPa39-63 at break (printed ZX, ASTM D638, Stratasys); the low end is the F900 T16 baseline, the high end the F3300 N500 hot end[5]23.7 as printed, 22.5 annealed, printed Z, ISO 527 (Polymaker)[2]
Brittleness1–5Brittle — snaps with little warning[1]Very brittle — elongation at break 2.77 % in XY and 0.85 % in Z[2]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M110 / R126 on extruded PEI stock (ASTM D785)[22]Not documented
Creep resistance / sustained load1–5Excellent — holds load for years. Printed ZX coupons keep 87 % of room-temperature tensile strength at 104 °C and 70 % at 132 °C (ASTM D638); extruded PEI stock is rated 170 °C long-term service[5][22]Poor — no GF-grade creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[23][24][25]
Fatigue / repeated-flex resistance1–5Not documentedPoor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and elongation at break falls to 2.77 % in XY and 0.85 % in Z[26][2]
Elasticity / flexibility1–5Rigid[1]Rigid[2]
Z strength as % of XY%56-86 (Stratasys ZX against XZ tensile at break, ASTM D638, across F900/F3300/Fortus 450mc and T16/T20/T40A tips); 58 on the F900 T16 baseline[5]47 as printed (23.7 Z against 50.1 XY), printed[2]
Wear resistance & frictionNot documentedeSUN describes high wear resistance and positions the grade for wear parts[3]
Thermal Properties
HDT at 0.45 MPa°C158 (printed XY, ISO 75 at 0.45 MPa, 3DXTech) to 178 (printed XY 178.2 and ZX 178.4, ASTM D648 Method B at 66 psi, Stratasys); moulded 176.9[1][5]75.5 as printed, 114.7 after annealing (ISO 75, 0.45 MPa) — the point of the material[2]
HDT at 1.8 MPa°C170-173 (printed XY 170.2 and ZX 172.6, ASTM D648 Method B at 264 psi); moulded 172.9[5]59.7 as printed, 84 after annealing (ISO 75, 1.8 MPa)[2]
Glass transition (Tg)°C177 (moulded plaque, ASTM D7426 inflection point, Stratasys); 186 (DSC, 3DXTech)[5][1][27]59.8 (DSC)[2]
Melting point / Vicat°CNot documented174.9 peak melt (DSC); Vicat 148.9 as printed, 148.3 annealed[2]
Continuous service temperature°C170 long-term service on extruded PEI stock, converted from 338 °F; 200 short term[22]Not documented
Annealing responseNot documentedAnnealing lifts HDT at 0.45 MPa from 75.5 to 114.7 °C and modulus from 3794 to 4207 MPa[2]
Thermal expansion (CTE)µm/m·K44.9 (printed XY, -50 to 80 °C, ASTM E831), falling to 31.4 over 80-160 °C; ZX gives 44.5 over -50 to 60 °C. Black pigment raises it to 51.9[5]Not documented
Flammability / UL 94UL 94 V-0 at 1.5 mm on the base resin. Printed parts are tested to 14 CFR 25.853, BSS 7238 and 7239 and AITM 2.0007B and 3.0005 covering 60 s and 12 s vertical burn, 15 s horizontal burn, smoke density, toxic gas emission and OSU heat release[1][5]Not documented
Environment & Chemical
UV resistance1–5Good — years with some colour shift. 1000 h of QUV cycling to ASTM G154 left printed ZX coupons at 55.5 MPa yield against 56.0 unexposed, with elongation and modulus unchanged[5]Degrades within weeks outdoors[28]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[29]Low hazard — minimal VOC and particle emission[29]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[29]None needed in a normal room[29]
Dust & fibre handling hazardNot documentedGlass fibre is bound in the matrix; avoid inhaling sanding dust[30]
Post-Processing
Dimensional accuracy & detailNot documentedNear-zero shrinkage — 0.05 % in X-Y and Z (Polymaker)[2]
Solvents & Solubility
Soluble inChlorinated hydrocarbons — dichloromethane and chloroform — are solvents for polyetherimide. Laboratory reagents.[31][32]Chloroform dissolves the PLA matrix (10 % w/v, 2–4 h at 23 °C) and leaves the filler as loose sludge; laboratory reagent.[33]
Softened or crazed byAcetone, MEK, benzene, toluene and butyl acetate craze or stress-crack it; alcohols, fuels and dilute acids do not.[32][31]Acetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[33][34]
Solvent welding & smoothing agentDichloromethane is the only welding route, and it is a controlled carcinogen rather than a workshop material.[31][32]Chloroform vapour attacks only the resin fraction, so the filler is left standing proud; no workshop-safe agent exists.[35][34]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. ThermaX PEI 9085 Technical Data Sheet v4 3DXTech · 2026-08 · tds
  2. Polymaker HT-PLA-GF Technical Data Sheet V1.1 Polymaker · 2026-08 · tds
  3. eSUN ePLA-GF Technical Data Sheet V1.0 (Nov 2023) eSUN (copy hosted on 3d.nice-cdn.com) · 2023-11 · tds
  4. Bambu Filament Technical Data Sheet V1.0 — PLA Galaxy Bambu Lab · 2026-08 · tds
  5. ULTEM 9085 Resin — FDM Material Data Sheet Stratasys · 2026-04 · tds
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. Kimya PEI-9085 Natural 2.85 mm 500 g igo3d · 2026-08 · vendor
  8. Fiberlogy PEI 9085 Natural, 1.75 mm / 500 g 3DJAKE · 2026-08 · vendor
  9. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  10. Polymaker HT-PLA-GF — product page Polymaker Shop · 2026-08 · vendor
  11. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  12. IEMAI 3D PEI 9085 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  13. Polymaker product catalogue Polymaker · 2026-08 · vendor
  14. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  15. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. THERMAX PEI 9085 — product page (print recommendations) 3DXTech · 2026-08 · doc
  18. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  19. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  20. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  21. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  22. TECAPEI natural (PEI) — stock shape properties Ensinger · 2026-08 · tds
  23. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  24. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  27. ThermaX PEI 1010 Technical Data Sheet v4 3DXTech · 2026-08 · tds
  28. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  29. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  30. StoneFil safety data sheet Formfutura · 2026-08 · msds
  31. Radel PPSU, Veradel PESU, Acudel modified PPSU Design Guide — environmental stress cracking tables Solvay Specialty Polymers · 2026-08 · tds
  32. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  33. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  34. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  35. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper