PEI 1010 vs PEKK — documented properties and sources
PropertyPEI (ULTEM 1010)HIGHTEMPPEKKHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$281.22/kg median; $195.00–$698.00/kg across 6 dated product listings$525.00/kg median; $332.50–$771.12/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryPolyetherimide, ULTEM 1010 grade — the higher-temperature, food- and medical-contact PEI[1][2]Polyether ketone ketone, amorphous grade — a polyaryletherketone that stays amorphous, so it does not need PEEK's crystallisation control. Stratasys sells it as Antero 800NA and Antero 840CN03; category numbers below are unfilled unless a carbon grade is named[3][4]
Densityg/cm³1.27 (ISO 1183, 3DXTech and Prusament); 1.29 specific gravity on moulded plaques (ASTM D792, Stratasys)[1][2][5]1.28 unfilled (ASTM D792, Antero 800NA; 1.31 annealed) and 1.33 for CarbonX PEKK-A CF15 (ISO 1183)[4][3]
Typical priceUSD/kg1 kg-equivalent spools span 195–698; the middle of the market is about 270[6][7][8][9][10]1 kg-equivalent spools cluster near 550[6][9][11]
Price range across brandsUSD/kg195-698 across brands and grades; 3DXTech ThermaX PEI 1010 195 at 2 kg, IEMAI 3D 223 at 1 kg, 3D4Makers 270 at 2 kg, Prusament 292 at 500 g, Kimya 347 at 500 g, 3DXTech ESD-PEI 1010 698 at 500 g[6][7][8][9][10]333-771 across grades and formats; 3DXTech CarbonX PEKK-A+CF15 333 at 2 kg, 3D4Makers unfilled PEKK-A 485 at 2 kg, IEMAI 3D 500 at 1 kg, Kimya PEKK Carbon 771 at 500 g[6][9][11][12][13]
Market availability1–5Niche, a handful of specialist brands[6][7][8][9]Niche, a handful of specialist brands[6][9][11]
Spool sizes & diameters1.75 and 2.85 mm; 200 g to 2 kg spools, plus Stratasys canisters[6][9][5]1.75 and 2.85 mm; 200 g to 2 kg spools, plus Stratasys canisters[6][9][4]
Typical applicationsAutoclavable tooling, food-contact fixtures and parts that must hold load near 200 °C[2]Aerospace interior and structural parts; 3DXTech labels its carbon-filled PEKK-A grade AERO and Stratasys certifies Antero 800NA for outgassing and FST[3][4]
Printing Parameters
Nozzle temperature°C410 ± 10 (Prusament) — the hottest nozzle in the dataset[2]Not documented
Bed temperature°C140–160 (Prusament); 130–140 (3DXTech)[2][1]140 (3DXTech CarbonX PEKK-A CF15)[3]
Enclosure / chamber requirement1–5Actively heated chamber required — Prusa specifies 90 °C[2]Actively heated chamber required[2][14]
Recommended chamber temperature°C90 (Prusament)[2]Not documented
Bed surface & adhesion aidPA nylon sheet or powder-coated sheet with high-temperature glue (Prusament)[2]Not documented
Warping tendency1–5Severe — heated chamber needed[2]Not documented
Overall printing difficulty1–5Expert / industrial hardware only[2][14]Expert / industrial hardware only[2][14]
Extruder requirementA hot end rated to 420 °C, a heated chamber and a high-temperature bed; Prusa dries the filament at 150 °C for 6–8 h before printing[2]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[2]Hardened steel required — the category spans unfilled PEKK, where brass is acceptable, and the carbon-filled aerospace grades that make up most of the market[3][4]
Abrasiveness1–5Non-abrasive when unfilled[1]Highly abrasive — most PEKK filament sold is carbon-filled; unfilled Antero 800NA and ThermaX PEKK-A are non-abrasive[3][4]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 150 °C pre-dry before every print[15]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[16]
Moisture Behaviour
Equilibrium moisture content at ~50 % RH%0.4 in 24 h and 0.7 in 7 days at 24 °C and 22 % RH (Prusament)[2]Not documented
Drying temperature & time150 °C for 6–8 h (Prusament) — the hottest drying schedule in the dataset[2]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published; 3DXTech mandates a 150 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[15]No dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[16]
Mechanical Properties
Tensile strength (XY)MPa79-95 printed in plane: Stratasys 79.2 (F900 T14) to 91.6 (F3300 N500) at break in XZ, ASTM D638; Prusament 95 +/- 3.5 at yield printed horizontal, ISO 527-1; 3DXTech quotes 56 (ISO 527)[5][2][1]86.7-90.0 at yield and 73.0 at break (printed XZ, ASTM D638, Antero 800NA on the F900 and Fortus 450mc); 88.8 at break annealed; 126 at break for CarbonX PEKK-A CF15 (printed XY, ISO 527)[4][3]
Young's modulusMPa2300-3040 printed in plane: Prusament 2300 +/- 100 horizontal (ISO 527-1), Stratasys 2920-3040 in XZ (ASTM D638); 3DXTech quotes 2500[5][2][1]2640-3870 (printed XZ, ASTM D638, Antero 800NA; upper figure annealed); 9125 for CarbonX PEKK-A CF15 (printed XY, ISO 527)[4][3]
Elongation at break%4.0-4.1 at break in XZ (ASTM D638, Stratasys); Prusament gives 6.6 +/- 0.7 at yield printed horizontal (ISO 527-1); 3DXTech quotes 3[5][2][1]6.1 at break (printed XZ, ASTM D638, Antero 800NA); 2.3 in ZX; 3.15 for CarbonX PEKK-A CF15 (ISO 527)[4][3]
Flexural strengthMPa128 at 5 % strain (F900 T14) and 144 at break (F3300) printed XZ, ASTM D790; Prusament 98 +/- 6.5 horizontal and 138 +/- 5.3 vertical (ISO 178); 3DXTech quotes 110[5][2][1]136 at 5 % strain (printed XZ, ASTM D790, Antero 800NA); 178 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[4][3]
Flexural modulusMPa2910-3260 printed XZ (ASTM D790, Stratasys); Prusament 2300 horizontal and 2700 vertical (ISO 178); 3DXTech quotes 2510[5][2][1]3200 (printed XZ, ASTM D790, Antero 800NA); 8817 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[4][3]
Charpy impact, notchedkJ/m²3.4 ± 0.9 printed horizontal and 3.6 ± 0.4 printed vertical, ISO 179-1 notched (Prusament)[2]Not documented
Other impact dataIzod notched 26.6-36.3 J/m XZ against 21.7-27.2 J/m ZX; unnotched 260-406 J/m XZ against 68-116 J/m ZX (printed, ASTM D256/D4812, Stratasys). Charpy unnotched 19.7 +/- 4.3 horizontal and 39 +/- 10 vertical (Prusament, ISO 179-1)[5][2]Izod notched 41.1 J/m XZ and 33.3 J/m ZX; unnotched 1730 J/m XZ against 203 J/m ZX (printed, ASTM D256/D4812, Antero 800NA)[4]
Layer adhesion / Z tensileMPa28-37 at break (printed ZX, ASTM D638, Stratasys F900 and F3300) against 72 +/- 5 at yield printed vertical (ISO 527-1, Prusament on the Pro HT90 with a 0.6 mm nozzle and 90 °C chamber) — a fourfold spread driven by chamber temperature and bead size[5][2]50.1-59.4 at yield (printed ZX, ASTM D638, Antero 800NA); 56.0 for the ESD grade Antero 840CN03[4][17]
Brittleness1–5Brittle — snaps with little warning; notched Charpy only 3.4 kJ/m²[2]Moderate unfilled — 6.1 % elongation at break in plane; brittle in the carbon-filled grades at 3.15 %[4][3]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 83.5 (Prusa Polymers method); Rockwell M110 / R126 on extruded PEI stock (ASTM D785)[2][18]Not documented
Creep resistance / sustained load1–5Excellent — holds load for years. Printed coupons hold 215 °C heat deflection at 1.8 MPa (ASTM D648) and extruded PEI stock is rated 170 °C long-term service[5][18]Excellent — holds load for years. Antero 800NA still holds 82 % of its room-temperature ZX tensile strength at 104 °C and 63 % at 132 °C (printed, ASTM D638)[4]
Elasticity / flexibility1–5Rigid[2]Rigid[3]
Z strength as % of XY%36-40 (Stratasys ZX against XZ tensile at break, ASTM D638) against 76 (Prusament vertical against horizontal tensile yield, ISO 527-1)[5][2]56-82 (Antero 800NA and 840CN03 printed on the F900 and Fortus 450mc, ZX against XZ tensile yield and break, ASTM D638)[4][17]
Thermal Properties
HDT at 0.45 MPa°C207 (Prusament, ISO 75 at 0.45 MPa) to 217 (printed XY 216.9 and XZ 217.1, ASTM D648 Method B at 66 psi, Stratasys); 3DXTech quotes 208[2][5][1]158 (printed XY and ZX, ASTM D648 Method B at 66 psi, Antero 800NA); 285 for CarbonX PEKK-A CF15 (ISO 75 at 0.45 MPa)[4][3]
HDT at 1.8 MPa°C194 (Prusament, ISO 75 at 1.8 MPa) to 215 (printed XY 215.1 and XZ 214.5, ASTM D648 Method B at 264 psi, Stratasys) — the highest heat deflection in the dataset[2][5]156-157 (printed, ASTM D648 Method B at 264 psi, Antero 800NA); moulded 147[4]
Glass transition (Tg)°C209 (moulded plaque, ASTM D7426 inflection point, Stratasys); 217 (DSC, 3DXTech)[5][1]156 (ASTM D7426, Antero 800NA); 165 for CarbonX PEKK-A CF15 (DSC)[4][3]
Melting point / Vicat°CNot documented300 melt point (ASTM D7426 peak heat, Antero 800NA); 305 for CarbonX PEKK-A CF15 (DSC)[4][3]
Continuous service temperature°C170 long-term service on extruded PEI stock, converted from 338 °F; 200 short term[18]Not documented
Thermal expansion (CTE)µm/m·K36.1 (printed XY, -50 to 60 °C, ASTM E831), falling to 29.8 over 60-205 °C; ZX gives 32.5 over -50 to 110 °C and 16.2 over 110-165 °C[5]36.1 in XY and 50.2 in ZX (printed, 40-140 °C, ASTM E831, Antero 800NA); 47.4 and 51.2 for the ESD grade Antero 840CN03[4][17]
Flammability / UL 94UL 94 V-0 at 1.5 mm, rated on the base resin[1]Not documented
Environment & Chemical
UV resistance1–5Not documentedGood — years with some colour shift. 1000 h of QUV cycling to ASTM G154 left Antero 800NA's yield strength unchanged at 57 MPa and raised stress at break 3.6 %[4]
Electrical & ESD propertiesNot documentedUnfilled PEKK is an insulator at above 1.4e14 ohm-cm (ASTM D257); CarbonX PEKK-A CF15 sits above 10^7 ohm/sq, and the Antero 840CN03 ESD grade is specified at 10^4-10^9 ohm-cm[4][3][17]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[19]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[19]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[19]Ventilated room or enclosure recommended[19]
Dust & fibre handling hazardNot documentedCarbon fibre is bound in the matrix; sanding dust should not be inhaled[3]
Solvents & Solubility
Soluble inChlorinated hydrocarbons — dichloromethane and chloroform — are solvents for polyetherimide. Laboratory reagents.[20][21]Concentrated sulphuric acid, as for PEEK; no common organic solvent touches a polyaryletherketone.[21][22]
Softened or crazed byAcetone, MEK, benzene, toluene and butyl acetate craze or stress-crack it; alcohols, fuels and dilute acids do not.[21][20]Concentrated sulphuric acid and liquid Freon are the entries Ensinger marks not resistant; acetone, MEK and toluene do nothing.[21]
Solvent welding & smoothing agentDichloromethane is the only welding route, and it is a controlled carcinogen rather than a workshop material.[20][21]None — no solvent softens a polyaryletherketone.[21]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. ThermaX PEI 1010 Technical Data Sheet v4 3DXTech · 2026-08 · tds
  2. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  3. CarbonX Carbon Fiber PEKK-A CF15 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  4. Antero 800NA — FDM Material Data Sheet (PEKK-based) Stratasys · 2025-08 · tds
  5. ULTEM 1010 Resin — FDM Material Data Sheet Stratasys · 2026-06 · tds
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. Kimya PEI-1010 Amber Yellow 1.75 mm 500 g igo3d · 2026-08 · vendor
  8. Prusa Prusament PEI 1010 Natural (NFC), 1.75 mm / 500 g 3DJAKE · 2026-08 · vendor
  9. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  10. IEMAI 3D PEI 1010 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  11. Kimya PEKK-A Natural 1.75 mm 500 g igo3d · 2026-08 · vendor
  12. Kimya PEKK Carbon Grey 1.75 mm 500 g igo3d · 2026-08 · vendor
  13. IEMAI 3D PEKK 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  14. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  15. THERMAX PEI 1010 — product page (print recommendations) 3DXTech · 2026-08 · doc
  16. THERMAX PEKK-A — product page (print recommendations) 3DXTech · 2026-08 · doc
  17. Antero 840CN03 — FDM Material Data Sheet (PEKK, ESD) Stratasys · 2024-08 · tds
  18. TECAPEI natural (PEI) — stock shape properties Ensinger · 2026-08 · tds
  19. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  20. Radel PPSU, Veradel PESU, Acudel modified PPSU Design Guide — environmental stress cracking tables Solvay Specialty Polymers · 2026-08 · tds
  21. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  22. The Effects of Sulfonated Poly(ether ether ketone) Ion Exchange Preparation Conditions on Membrane Properties Yee, Zhang & Ladewig, Membranes 3(3) 182–195 · 2013-07 · paper