3D Printing Info

Filament comparison

PC vs POM

Compare printing settings, strength, heat resistance, dated prices and sources.

Polycarbonate (PC) guidePOM (acetal) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC comparisonsMore POM comparisons
PC vs POM — documented properties and sources
PropertyPolycarbonate (PC)PCPOM (acetal)ENGINEERING
Market snapshot
Listing priceUSD/kg; dated snapshots$39.99/kg median; $29.99–$92.00/kg across 9 dated product listingsNot documented
Identity & Market
Base polymer / chemistryBisphenol-A polycarbonate — an amorphous engineering thermoplastic[1][2]Polyoxymethylene, normally the copolymer POM-C. Apium's filament grade is POM-C with antistatic additives; no unfilled POM filament was found on sale[3][4]
Densityg/cm³1.19 (Polymaker) to 1.22 (Prusament), ISO 1183; Bambu Lab 1.20; Stratasys specific gravity 1.20 (ASTM D792)[1][5][6][7]1.41 (extruded POM-C stock)[3]
Typical priceUSD/kg1 kg spools cluster near 40[6][8][9]Not documented
Price range across brandsUSD/kg30–92 across brands; Polymaker PolyLite 30, Bambu Lab 40, Polymaker PolyMax 52, Prusament 59, 3DXTech ezPC 64 and 3DXMAX PC 92[8][6][9][10]Not documented
Market availability1–5Available from several mainstream brands[6][8][10][9]Special order, 1-2 makers worldwide — Apium sells a POM-C ESD filament through its own shop and states its printers are the only ones able to process POM-C; no POM filament appears in the 3DJAKE or igo3d product sitemaps, at MatterHackers or at Printed Solid[4][11][12][9]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75, 0.9, 1 and 3 kg spools[8][10][9]Not documented
Typical applicationsLight guides, lenses, under-bonnet automotive parts and impact-loaded housings that must hold shape above 110 °C[2][1]Gears, bushings, bearings, conveyor and food-machinery parts; Apium markets its POM-C ESD grade for semiconductor insulators, aerospace fasteners and sliding parts[3][4]
Diameter tolerance± mm±0.03 (Prusament PC Blend)[5]Not documented
Printing Parameters
Nozzle temperature°C250–280 across brands; Prusament 275 ± 10, Bambu Lab 260–280, Polymaker 250–270. Polymaker's material guide gives a wider 260–310 for PC and its composites[5][6][1][2]Not documented
Bed temperature°C90–115; Prusament 110 ± 10, Bambu Lab 90–110, Polymaker 90–105[5][6][1]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive) — Polymaker specifies a 70–100 °C chamber, Bambu Lab 45–60 °C and rules out its P1P and A-series machines[1][6][13]Not documented
Recommended chamber temperature°C70–100 (Polymaker); 45–60 (Bambu Lab)[1][6]Not documented
Part cooling fanOff or very low — Polymaker specifies off, Prusament 20 % within a 0–30 % range, Bambu Lab 0–60 %[1][5][6]Not documented
Bed surface & adhesion aidTextured PEI with glue when needed (Polymaker); smooth or textured PEI (Bambu Lab)[1][14]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s24 at Bambu Lab's 300 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer; Polymaker allows 50–200 mm/s and its material guide advises 30–60 for layer adhesion[6][1][2][15]Not documented
Warping tendency1–5Severe — heated chamber needed[1][2][13]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[1][13]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[2]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[2][13]Not documented
Extruder requirementAll-metal hotend rated to 300 °C; Polymaker advises larger nozzles and high chamber temperatures to improve bonding[2]Apium states that the adaptive heating system on its industrial machines is what makes POM-C printable, and that no other 3D printer can process it[4]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[13]Not documented
Abrasiveness1–5Non-abrasive[1]Not documented
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle[2]Not documented
Heat-creep / jam sensitivity1–5Slightly sensitive[16]Not documented
Hotend requirementAll-metal hot end required (Simplify3D); Polymaker advises a hot end rated above 300 °C[16][2]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low — 0.25 % saturated at 25 °C / 55 % RH (Bambu Lab); Prusa measures 0.15 % after 7 days at 22 % RH. Polymaker nonetheless calls PC highly hygroscopic in service[6][5][2]Low (0.1-0.3 %) — extruded POM-C stock takes up 0.18 % in 24 h and 0.80 % at saturation (ASTM D570)[3]
Equilibrium moisture content at ~50 % RH%0.25 saturated at 25 °C / 55 % RH (Bambu Lab); 0.15 after 7 days at 24 °C / 22 % RH (Prusa)[6][5]Not documented
Drying temperature & time80 °C for 8 h (Bambu Lab); 75 °C for 6 h (Polymaker); 70–80 °C for 6–8 h (Polymaker material guide)[6][1][2]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing, rough surface and weak layers[17]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[2][17]Not documented
Storage requirementAirtight containers with desiccant to prevent reabsorption[2]Not documented
Mechanical Properties
Tensile strength (XY)MPa53.4 (PolyMax) to 69.1 (PolyLite) printed XY, ISO 527; Bambu Lab 62 +/- 2 and Prusament 63 +/- 1 at yield; Stratasys 62.3-64.6 at yield printed XZ, ASTM D638 (its PC White table duplicates the Antero 840CN03 figures and was not used)[1][18][6][5][19][7]66.9 at break and 64.1 at yield (extruded POM-C stock, ASTM D638; converted from 9700 and 9300 psi)[3]
Young's modulusMPa2110 (Bambu Lab) to 2497 (PolyLite) printed XY, ISO 527; Prusament 1900, 3DXTech 2180[6][1][5][19]2275 (extruded POM-C stock, ASTM D638; converted from 330,000 psi)[3]
Elongation at break%3.8 (Bambu Lab) to 4.8 (PolyLite) at break, printed XY, ISO 527; 3DXTech quotes 14 at break, Prusament 5.8 at yield[6][1][19][5]40 at break and 9 at yield (extruded POM-C stock, ASTM D638)[3]
Flexural strengthMPa81.3 (PolyMax) to 108 (Bambu Lab) printed XY, ISO 178; Prusament 88 ± 1, PolyLite 106.1[18][6][5][1]89.6 (extruded POM-C stock, ASTM D790; converted from 13,000 psi)[3]
Flexural modulusMPa2050 (PolyMax) to 2640 (PolyLite) printed XY, ISO 178; Prusament 2100[18][1][5]2758 (extruded POM-C stock, ASTM D790; converted from 400,000 psi)[3]
Charpy impact, notchedkJ/m²4.1 (PolyLite) to 21.3 (PolyMax) printed XY, ISO 179, notched; Prusament 12 ± 1[1][18][5]Not documented
Other impact dataCharpy unnotched does not break on Prusa's pendulum in either orientation (ISO 179-1); PolyMax PC retains 9.2 kJ/m2 notched at -30 °C. Stratasys PC Black gives 85.3 MPa flexural strength at break in ZX against no break in XZ (ASTM D790, printed)[5][18][7]Izod 53 J/m on extruded POM-C stock, converted from 1.0 ft-lb/in[3]
Layer adhesion / Z tensileMPa37.1-45.3 at yield printed ZX (Stratasys PC Black and Red, ASTM D638); 41.4 (PolyMax) to 56 (Bambu Lab) printed Z; Prusa's interlayer adhesion test gives 21 +/- 2[5][18][6][7]Not documented
Brittleness1–5Tough — absorbs impact, yields before breaking[2][5]Tough — absorbs impact, yields before breaking; extruded stock elongates 40 % before failing. No printed figure is published[3]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 79 (Prusa Polymers method) and Shore D 79 on extruded PC stock (ASTM D2240); Rockwell 70 (118) — the source does not name the scales[5][20]Rockwell 86 (and R120) — the source names only the R scale on extruded POM-C stock (ASTM D785)[3]
Creep resistance / sustained load1–5Excellent — holds load for years. Room-temperature tensile creep of moulded PC was still running unbroken at 41 MPa when the experiment was stopped for time; specimens failed within the test window only at 47-52 MPa (ASTM D638)[21]Not documented
Fatigue / repeated-flex resistance1–5Good[5][2]Not documented
Elasticity / flexibility1–5Rigid[1]Not documented
Z strength as % of XY%59-73 (Stratasys PC Black and Red, ZX against XZ tensile yield, ASTM D638); 76 for PolyLite PC and 90 for Bambu Lab (printed Z against XY tensile)[6][1][7]Not documented
Wear resistance & frictionNot documentedWear factor 65e-10 in3*min/(ft*lb*h) and a dynamic coefficient of friction of 0.21 at 40 psi and 50 fpm (ASTM D3702, extruded stock) — the properties that make acetal the default gear and bushing plastic; Apium lists good sliding properties as the reason for its grade[3][4]
Thermal Properties
HDT at 0.45 MPa°C110 (PolyMax PC-FR) to 114 (PolyMax PC), ISO 75 at 0.45 MPa; Bambu Lab 112, PolyLite 111, Prusament 113. Stratasys FDM PC reaches 144 printed (ASTM D648 Method B at 66 psi)[18][1][6][5][7]158 (extruded POM-C stock, ASTM D648 at 66 psi; converted from 316 °F)[3]
HDT at 1.8 MPa°C93 (Prusament) to 117 (Bambu Lab), ISO 75 at 1.8 MPa; PolyLite 107, PolyMax 99. Stratasys FDM PC reaches 141 printed (ASTM D648 Method B at 264 psi)[5][6][1][18][7]110 (extruded POM-C stock, ASTM D648 at 264 psi; converted from 230 °F)[3]
Glass transition (Tg)°C113 (Polymaker, DSC), 142.5 (Stratasys, ASTM D7426 inflection point) and 145 (Bambu Lab, DSC); Polymaker's material guide quotes 150[1][6][2][7]Not documented
Melting point / Vicat°CAmorphous — no melting point; Vicat 117–120 (Polymaker, ISO 306); decomposition above 360 °C[1][18]165 melting (extruded POM-C stock; converted from 329 °F)[3]
Continuous service temperature°C113 — Prusa publishes this as the temperature resistance of Prusament PC Blend; extruded PC stock is rated 121 long term (converted from 250 °F)[5][20]91 long term and 141 intermittent (extruded POM-C stock; converted from 195 °F and 285 °F)[3]
Annealing response90 °C for 2 h (Polymaker)[1]Not documented
Thermal expansion (CTE)µm/m·K51.6 in XY over -50 to 30 °C, falling to 35.8 over 30-75 °C and 11.5 over 75-130 °C; 49.2 in XZ over -50 to 120 °C (printed, ASTM E831). Extruded PC stock gives 68.4 (ASTM D696)[7][20]84.6 (extruded POM-C stock, ASTM D696; source states 4.7e-5 in/in/°F)[3]
Flammability / UL 94Flammable; no UL 94 rating on standard PC, though V-0 grades exist[22][1]UL 94 HB on extruded POM-C stock[3]
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors — unstabilised PC yellows and embrittles under UV[2]Not documented
Chemical resistanceWithstands oils, solvents and fuels; Polymaker rates it good against weak acids[2]Good chemical resistance, particularly to bases; Apium lists resistance to bases as a headline property[3][4]
Water / humidity resistance in service1–5Good — minor absorption[6]Good — minor absorption; 0.80 % water at saturation (ASTM D570, extruded stock)[3]
Food contactBisphenol-A polycarbonate is not offered as food-contact filament[2]Not documented
Biodegradability / compostabilityNot biodegradable[2]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[2]Not documented
Electrical & ESD propertiesSurface resistance above 10¹³ ohm/sq — an electrical insulator, which Polymaker lists as a headline advantage[19][2]Volume resistance 1e14 ohm-cm, dielectric strength 500 V/mil and dielectric constant 3.7 at 60 Hz on extruded stock (ASTM D257, D149, D150); Apium's filament grade adds antistatic agents[3][4]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[23]Not documented
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[23]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[23][13]Not documented
Post-Processing
Sanding & machiningSands and machines well; the toughness means it cuts rather than chips[16]Easy to machine — Ensinger lists machinability as a headline property of POM-C stock[3]
Painting & finishingOptical clarity survives printing, so transparent parts are usually left unpainted[2]Not documented
Gluing & solvent weldingCyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[16]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[16]Not documented
Support material pairingPrints its own supports; 3DXTech sells a dedicated PC break-away support[16]Not documented
Dimensional accuracy & detailWarping is the dominant accuracy limit; light transmission 89 % on PolyLite PC (GB/T 2410)[1][2]Not documented
Solvents & Solubility
Soluble inDichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[24]Hexafluoroisopropanol dissolves it at room temperature; NMP and DMF only when hot. Laboratory reagents.[25]
Softened or crazed byMethanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[24]Acids, oxidants, halogens and hot concentrated zinc chloride attack it; alcohols, ketones and esters do not.[25][26]
Solvent welding & smoothing agentDichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[27]None — no solvent softens POM below its melting point, which is why it is bolted or heat-welded rather than glued.[25]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  2. PC — material basics Polymaker Wiki · 2026-08 · doc
  3. TECAFORM AH natural (POM-C) — stock shape properties Ensinger · 2026-08 · tds
  4. POM-C ESD 3D printing — material page Apium 3D Technologies · 2026-08 · doc
  5. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  6. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  7. PC (Polycarbonate) — FDM Material Data Sheet Stratasys · 2026-04 · tds
  8. Polymaker product catalogue Polymaker · 2026-08 · vendor
  9. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  10. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  11. 3DJAKE product catalogue 3DJAKE · 2026-08 · vendor
  12. igo3d product sitemap (17452 product URLs) igo3d · 2026-08 · vendor
  13. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  14. Bambu Filament Technical Data Sheet V1.0 — PC FR Bambu Lab · 2026-08 · tds
  15. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  16. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  18. PolyMax PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  19. ezPC Polycarbonate Technical Data Sheet 3DXTech · 2026-08 · tds
  20. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  21. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  22. PolyMax PC-FR Technical Data Sheet V5.5 Polymaker · 2024-11 · tds
  23. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  24. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  25. Resistance of Ultramid, Ultraform and Ultradur to chemicals (TI-KTU/AS-28 e) BASF · 2000-10 · tds
  26. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  27. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds