PC vs PETG-GF

Compare printing settings, strength, heat resistance, dated prices and sources.

Polycarbonate (PC) guideGlass-fibre polyester (PETG-GF / PET-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC comparisonsMore PETG-GF comparisons
PC vs PETG-GF — documented properties and sources
PropertyPolycarbonate (PC)PCGlass-fibre polyester (PETG-GF / PET-GF)PETG
Market snapshot
Listing priceUSD/kg; dated snapshots$39.99/kg median; $29.99–$92.00/kg across 9 dated product listings$27.38/kg median; $18.99–$29.99/kg across 3 dated product listings
Identity & Market
Base polymer / chemistryBisphenol-A polycarbonate — an amorphous engineering thermoplastic[1][2]Glass-fibre reinforced polyester. Polymaker's Fiberon PET-GF15 uses a PET rather than a PETG matrix and carries 15 wt% glass fibre[3]
Densityg/cm³1.19 (Polymaker) to 1.22 (Prusament), ISO 1183; Bambu Lab 1.20; Stratasys specific gravity 1.20 (ASTM D792)[1][4][5][6]1.43 (Fiberon PET-GF15, ISO 1183)[3]
Typical priceUSD/kg1 kg spools cluster near 40[5][7][8]1 kg spools cluster near 25[9][7]
Price range across brandsUSD/kg30–92 across brands; Polymaker PolyLite 30, Bambu Lab 40, Polymaker PolyMax 52, Prusament 59, 3DXTech ezPC 64 and 3DXMAX PC 92[7][5][8][10]19–30 across brands; ELEGOO 19, Polymaker Fiberon 30[9][7]
Market availability1–5Available from several mainstream brands[5][7][10][8]Niche, a handful of specialist brands[9][7]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75, 0.9, 1 and 3 kg spools[7][10][8]1.75 mm; 0.5 and 1 kg spools[7]
Typical applicationsLight guides, lenses, under-bonnet automotive parts and impact-loaded housings that must hold shape above 110 °C[2][1]Stiff, dimensionally stable fixtures; the Fiberon grade is designed to be annealed for heat resistance[3]
Diameter tolerance± mm±0.03 (Prusament PC Blend)[4]Not documented
Printing Parameters
Nozzle temperature°C250–280 across brands; Prusament 275 ± 10, Bambu Lab 260–280, Polymaker 250–270. Polymaker's material guide gives a wider 260–310 for PC and its composites[4][5][1][2]Not documented
Bed temperature°C90–115; Prusament 110 ± 10, Bambu Lab 90–110, Polymaker 90–105[4][5][1]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive) — Polymaker specifies a 70–100 °C chamber, Bambu Lab 45–60 °C and rules out its P1P and A-series machines[1][5][11]Not documented
Recommended chamber temperature°C70–100 (Polymaker); 45–60 (Bambu Lab)[1][5]Not documented
Part cooling fanOff or very low — Polymaker specifies off, Prusament 20 % within a 0–30 % range, Bambu Lab 0–60 %[1][4][5]Not documented
Bed surface & adhesion aidTextured PEI with glue when needed (Polymaker); smooth or textured PEI (Bambu Lab)[1][12]Textured PEI, satin or powder-coated sheets; on smooth PEI a glue stick acts as a release agent[13][14]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s24 at Bambu Lab's 300 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer; Polymaker allows 50–200 mm/s and its material guide advises 30–60 for layer adhesion[5][1][2][15]Not documented
Warping tendency1–5Severe — heated chamber needed[1][2][11]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[1][11]Needs the right surface or a thin adhesive — the problem is releasing the part, not sticking it[13][14]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[2]Moderate — retraction tuning needed; Polymaker names stringing as PETG's common quirk[14]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[2][11]Not documented
Extruder requirementAll-metal hotend rated to 300 °C; Polymaker advises larger nozzles and high chamber temperatures to improve bonding[2]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[11]Hardened steel required[3]
Abrasiveness1–5Non-abrasive[1]Highly abrasive — standard GF composite[3]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle[2]Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[16]
Heat-creep / jam sensitivity1–5Slightly sensitive[17]Slightly sensitive[18]
Hotend requirementAll-metal hot end required (Simplify3D); Polymaker advises a hot end rated above 300 °C[17][2]No special hot-end required[18]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low — 0.25 % saturated at 25 °C / 55 % RH (Bambu Lab); Prusa measures 0.15 % after 7 days at 22 % RH. Polymaker nonetheless calls PC highly hygroscopic in service[5][4][2]Moderate (0.3–0.8 %) — the PETG matrix reaches 0.40 % saturated at 25 °C / 55 % RH; no glass-filled grade publishes its own figure[13]
Equilibrium moisture content at ~50 % RH%0.25 saturated at 25 °C / 55 % RH (Bambu Lab); 0.15 after 7 days at 24 °C / 22 % RH (Prusa)[5][4]Not documented
Drying temperature & time80 °C for 8 h (Bambu Lab); 75 °C for 6 h (Polymaker); 70–80 °C for 6–8 h (Polymaker material guide)[5][1][2]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing, rough surface and weak layers[19]Bubbling and popping at the nozzle, stringing and a rough surface[19]
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[2][19]Polymaker groups PETG with nylon, PVA and TPU as highly hygroscopic; no dry-versus-conditioned strength figures are published for this grade and the loss shows as bubbling and poor layer adhesion[19]
Storage requirementAirtight containers with desiccant to prevent reabsorption[2]Sealed with desiccant; Polymaker groups PETG with the highly hygroscopic materials[19][14]
Mechanical Properties
Tensile strength (XY)MPa53.4 (PolyMax) to 69.1 (PolyLite) printed XY, ISO 527; Bambu Lab 62 +/- 2 and Prusament 63 +/- 1 at yield; Stratasys 62.3-64.6 at yield printed XZ, ASTM D638 (its PC White table duplicates the Antero 840CN03 figures and was not used)[1][20][5][4][21][6]59.9 ± 0.8 printed XY, ISO 527 (Fiberon PET-GF15)[3]
Young's modulusMPa2110 (Bambu Lab) to 2497 (PolyLite) printed XY, ISO 527; Prusament 1900, 3DXTech 2180[5][1][4][21]4144 ± 133 printed XY, ISO 527 (Fiberon PET-GF15)[3]
Elongation at break%3.8 (Bambu Lab) to 4.8 (PolyLite) at break, printed XY, ISO 527; 3DXTech quotes 14 at break, Prusament 5.8 at yield[5][1][21][4]4.0 ± 0.5 printed XY, ISO 527 (Fiberon PET-GF15)[3]
Flexural strengthMPa81.3 (PolyMax) to 108 (Bambu Lab) printed XY, ISO 178; Prusament 88 ± 1, PolyLite 106.1[20][5][4][1]104.2 ± 2.4 printed XY, ISO 178 (Fiberon PET-GF15)[3]
Flexural modulusMPa2050 (PolyMax) to 2640 (PolyLite) printed XY, ISO 178; Prusament 2100[20][1][4]3705 ± 85 printed XY, ISO 178 (Fiberon PET-GF15)[3]
Charpy impact, notchedkJ/m²4.1 (PolyLite) to 21.3 (PolyMax) printed XY, ISO 179, notched; Prusament 12 ± 1[1][20][4]8.7 ± 0.6 printed XY, ISO 179, notched (Fiberon PET-GF15)[3]
Other impact dataCharpy unnotched does not break on Prusa's pendulum in either orientation (ISO 179-1); PolyMax PC retains 9.2 kJ/m2 notched at -30 °C. Stratasys PC Black gives 85.3 MPa flexural strength at break in ZX against no break in XZ (ASTM D790, printed)[4][20][6]Charpy unnotched 27.2 ± 2.0 printed XY (Fiberon PET-GF15, ISO 179)[3]
Layer adhesion / Z tensileMPa37.1-45.3 at yield printed ZX (Stratasys PC Black and Red, ASTM D638); 41.4 (PolyMax) to 56 (Bambu Lab) printed Z; Prusa's interlayer adhesion test gives 21 +/- 2[4][20][5][6]48.2 ± 0.3 printed Z, ISO 527 (Fiberon PET-GF15)[3]
Brittleness1–5Tough — absorbs impact, yields before breaking[2][4]Brittle — snaps with little warning; elongation 4.0 % in XY and 2.6 % in Z[3]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 79 (Prusa Polymers method) and Shore D 79 on extruded PC stock (ASTM D2240); Rockwell 70 (118) — the source does not name the scales[4][22]Not documented
Creep resistance / sustained load1–5Excellent — holds load for years. Room-temperature tensile creep of moulded PC was still running unbroken at 41 MPa when the experiment was stopped for time; specimens failed within the test window only at 47-52 MPa (ASTM D638)[23]Below average — no GF-grade creep test; the CF grades sagged to 14.8–16.7 mm over 5 days at 1.25 kg against 17.1–20.4 mm unfilled[24][25][26]
Fatigue / repeated-flex resistance1–5Good[4][2]Below average — no GF-grade S-N curve; elongation at break falls to 4.0 % in XY against 5.2–9.3 % unfilled[3][27]
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%59-73 (Stratasys PC Black and Red, ZX against XZ tensile yield, ASTM D638); 76 for PolyLite PC and 90 for Bambu Lab (printed Z against XY tensile)[5][1][6]80 (Fiberon PET-GF15, printed Z against XY tensile)[3]
Thermal Properties
HDT at 0.45 MPa°C110 (PolyMax PC-FR) to 114 (PolyMax PC), ISO 75 at 0.45 MPa; Bambu Lab 112, PolyLite 111, Prusament 113. Stratasys FDM PC reaches 144 printed (ASTM D648 Method B at 66 psi)[20][1][5][4][6]81.6 as printed, 133.7 after annealing (ISO 75, 0.45 MPa)[3]
HDT at 1.8 MPa°C93 (Prusament) to 117 (Bambu Lab), ISO 75 at 1.8 MPa; PolyLite 107, PolyMax 99. Stratasys FDM PC reaches 141 printed (ASTM D648 Method B at 264 psi)[4][5][1][20][6]71.8 as printed, 87.3 after annealing (ISO 75, 1.8 MPa)[3]
Glass transition (Tg)°C113 (Polymaker, DSC), 142.5 (Stratasys, ASTM D7426 inflection point) and 145 (Bambu Lab, DSC); Polymaker's material guide quotes 150[1][5][2][6]59.5 (DSC)[3]
Melting point / Vicat°CAmorphous — no melting point; Vicat 117–120 (Polymaker, ISO 306); decomposition above 360 °C[1][20]231.6 melting (DSC); Vicat 232.6 (ISO 306)[3]
Continuous service temperature°C113 — Prusa publishes this as the temperature resistance of Prusament PC Blend; extruded PC stock is rated 121 long term (converted from 250 °F)[4][22]Not documented
Annealing response90 °C for 2 h (Polymaker)[1]Annealing lifts HDT at 0.45 MPa from 81.6 to 133.7 °C[3]
Thermal expansion (CTE)µm/m·K51.6 in XY over -50 to 30 °C, falling to 35.8 over 30-75 °C and 11.5 over 75-130 °C; 49.2 in XZ over -50 to 120 °C (printed, ASTM E831). Extruded PC stock gives 68.4 (ASTM D696)[6][22]20 along the print bead and 63–74 in the build direction at 30 °C (30 wt% GF, large-format printed, TMA)[28]
Flammability / UL 94Flammable; no UL 94 rating on standard PC, though V-0 grades exist[29][1]UL 94 HB at 1.5 mm (Fiberon PET-GF15)[3]
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors — unstabilised PC yellows and embrittles under UV[2]Not documented
Chemical resistanceWithstands oils, solvents and fuels; Polymaker rates it good against weak acids[2]Withstands acids, alkalis, oils and UV exposure[14]
Water / humidity resistance in service1–5Good — minor absorption[5]Not documented
Food contactBisphenol-A polycarbonate is not offered as food-contact filament[2]Not certified for food contact as filament[14]
Biodegradability / compostabilityNot biodegradable[2]Not biodegradable[14]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[2]Not accepted in household plastic collection[14]
Electrical & ESD propertiesSurface resistance above 10¹³ ohm/sq — an electrical insulator, which Polymaker lists as a headline advantage[21][2]Surface resistivity above 10¹² ohm — insulating (Fiberon PET-GF15, ANSI/ESD S11.11)[3]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[30]Moderate — measurable VOCs and UFPs, ventilation advised[30]
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[30]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[30][11]Open a window / occasional ventilation[30]
Dust & fibre handling hazardNot documentedGlass fibre is bound in the matrix; avoid inhaling sanding dust[3]
Post-Processing
Sanding & machiningSands and machines well; the toughness means it cuts rather than chips[17]Sands poorly — the material is tough and gums rather than powders[18]
Painting & finishingOptical clarity survives printing, so transparent parts are usually left unpainted[2]Not documented
Gluing & solvent weldingCyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[17]Cyanoacrylate; no common solvent welds PETG cleanly[18]
Vapour / chemical smoothingNo practical vapour smoothing[17]No practical vapour smoothing[18]
Support material pairingPrints its own supports; 3DXTech sells a dedicated PC break-away support[17]Prints its own supports; Polymaker rates PolyDissolve S1 for PETG[18]
Dimensional accuracy & detailWarping is the dominant accuracy limit; light transmission 89 % on PolyLite PC (GB/T 2410)[1][2]Not documented
Solvents & Solubility
Soluble inDichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[31]No common workshop solvent; dichloromethane — a carcinogen — dissolves the matrix surface, 1,2-dichloroethane destroys it in a week.[32][33]
Softened or crazed byMethanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[31]Acetone (+16 % weight over 1 year at 23 °C), ethyl acetate, toluene and DMF swell and soften it; methanol crazes it.[32]
Solvent welding & smoothing agentDichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[34]Dichloromethane reaches only the resin, so the fibre is left standing proud of the surface. Controlled carcinogen.[33]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  2. PC — material basics Polymaker Wiki · 2026-08 · doc
  3. Fiberon PET-GF15 Technical Data Sheet V1.0 Polymaker · 2026-08 · tds
  4. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  5. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  6. PC (Polycarbonate) — FDM Material Data Sheet Stratasys · 2026-04 · tds
  7. Polymaker product catalogue Polymaker · 2026-08 · vendor
  8. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  9. ELEGOO product catalogue ELEGOO · 2026-08 · vendor
  10. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  11. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  12. Bambu Filament Technical Data Sheet V1.0 — PC FR Bambu Lab · 2026-08 · tds
  13. Prusament PETG Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  14. PETG — material basics Polymaker Wiki · 2026-08 · doc
  15. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  16. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  17. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. PET and PETG — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  19. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  20. PolyMax PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  21. ezPC Polycarbonate Technical Data Sheet 3DXTech · 2026-08 · tds
  22. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  23. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  24. Extrudr PETG vs PCTG vs XPETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. Prusament PETG-CF vs PETG V0 vs PETG — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. BambuLab PETG Basic vs Translucent vs PETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  27. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  28. Effects of Fiber Orientation on the Coefficient of Thermal Expansion of Fiber-Filled Polymer Systems in Large Format Polymer Extrusion-Based Additive Manufacturing Materials 15(8):2764 · 2022-04 · paper
  29. PolyMax PC-FR Technical Data Sheet V5.5 Polymaker · 2024-11 · tds
  30. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  31. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  32. Eastman Spectar copolyester — Chemical resistance (unstressed bars, 1 year at 23 °C) Eastman Chemical Company · 2026-08 · tds
  33. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  34. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds