3D Printing Info

Filament comparison

PC-ESD vs PLA-GF

Compare printing settings, strength, heat resistance, dated prices and sources.

ESD-safe PC guideGlass-fibre PLA (PLA-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC-ESD comparisonsMore PLA-GF comparisons
PC-ESD vs PLA-GF — documented properties and sources
PropertyESD-safe PCPCGlass-fibre PLA (PLA-GF)PLA
Market snapshot
Listing priceUSD/kg; dated snapshots$180.00/kg median; $180.00–$180.00/kg across 1 dated product listings$44.99/kg median; $29.99–$59.99/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryPolycarbonate compounded with a conductive filler for static-dissipative parts[1]PLA filled with chopped glass fibre — 12 wt% (Polymaker HT-PLA-GF), 15–20 wt% (eSUN PLA-GF). Bambu Lab PLA Galaxy uses glass microspheres, not fibre, and is not equivalent[2][3][4]
Densityg/cm³1.24 (ISO 1183, 3DXTech); Stratasys specific gravity 1.195 (ASTM D792)[1][5]1.31 (eSUN) to 1.337 (Polymaker), ISO 1183 / GB/T 1033[2][3]
Typical priceUSD/kg1 kg-equivalent spools cluster near 180[6]1 kg spools cluster near 30[7][8]
Price range across brandsUSD/kg180 at 3DXTech's 750 g pricing — the most expensive material in this group[6]30–60 across brands; Polymaker 30, Proto-pasta 60[7][8]
Market availability1–5Special order, 1–2 makers worldwide[6]Niche, a handful of specialist brands[7][8][3]
Spool sizes & diameters1.75 and 2.85 mm; 750 g spools plus Stratasys-compatible cartridges[6]1.75 mm; 0.5 and 1 kg spools[8][9]
Typical applicationsElectronics fixtures and trays that need PC heat resistance and static dissipation together[1]Stiff brackets and fixtures; the Polymaker grade is aimed at parts annealed for heat resistance[2]
Printing Parameters
Nozzle temperature°CNot documented210–230 (Polymaker HT-PLA-GF)[2]
Bed temperature°CNot documented25–60 (Polymaker HT-PLA-GF)[2]
Enclosure / chamber requirement1–5Enclosure required (passive)[10][11]Open frame is fine[2]
Part cooling fanNot documentedFan on — eSUN specifies 100 %[3]
Bed surface & adhesion aidPEI with a glue stick or a commercial adhesive[12]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented28 at Polymaker's stated 350 mm/s on a 0.4 mm nozzle at 0.2 mm layer; eSUN prints its specimens at 60 mm/s[2][3][13]
Warping tendency1–5Severe — heated chamber needed[10][11]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[12][14]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed; Polymaker flags stringing as a common PC problem[14]Not documented
Shrinkage%Not documented0.05 in X-Y and Z, 0.10 diagonal (Polymaker HT-PLA-GF)[2]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[10]Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[2]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[1]Hardened steel required[2]
Abrasiveness1–5Moderately abrasive — conductive carbon filler[1]Highly abrasive — standard GF composite[2]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a 120 °C pre-dry[15]Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[16]
Heat-creep / jam sensitivity1–5Slightly sensitive[12]Not documented
Hotend requirementAll-metal hot end required (Simplify3D)[12]Hardened steel or ruby nozzle; Polymaker's own slicer preset sets a minimum nozzle hardness of 40 HRC[2]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low (0.1–0.3 %) — the PC matrix takes up 0.15–0.25 % and 3DXTech specifies a 120 °C, 4 h pre-dry[17][18][15]Moderate — the PLA matrix takes up 0.40–0.51 % saturated; no glass-filled grade publishes its own figure[19][20]
Drying temperature & timeNot documented60 °C for 6 h (Polymaker HT-PLA-GF)[2]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[21]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[14][21]Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[21]
Storage requirementAirtight containers with desiccant to prevent reabsorption[14]Not documented
Mechanical Properties
Tensile strength (XY)MPa68 at break (printed XY, ISO 527, 3DXTech) — above the 58 of 3DXTech's unfilled ezPC; Stratasys prints 47.6-49.4 at yield in XZ (ASTM D638)[1][22][5]50.1 as printed and 50.2 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 59.3 by GB/T 1040[2][3]
Young's modulusMPa2300 (printed XY, ISO 527); Stratasys prints 1960 in XZ and 1810-1910 in ZX (ASTM D638)[1][5]3794 as printed, 4207 annealed, printed XY, ISO 527 (Polymaker)[2]
Elongation at break%6 at break (printed XY, ISO 527), against 14 for the unfilled grade[1][22]2.77 as printed, 2.3 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 7.99[2][3]
Flexural strengthMPa95 (printed XY, ISO 178); Stratasys prints 82.6-83.2 at break in XZ against 46.3-49.5 in ZX (ASTM D790)[1][5]86.4 printed XY, ISO 178 (Polymaker)[2]
Flexural modulusMPa2310 (printed XY, ISO 178)[1]3685 printed XY, ISO 178 (Polymaker); eSUN quotes 4415 flexural modulus by GB/T 9341[2][3]
Charpy impact, notchedkJ/m²Not documented5.31 ± 0.46 as printed and 4.92 ± 0.50 annealed (printed XY, ISO 179, notched); Z 4.28 ± 0.18[2]
Other impact dataNot documentedIzod 10.16 kJ/m² (eSUN, GB/T 1843)[3]
Layer adhesion / Z tensileMPa32.5-37.9 at yield printed ZX (Stratasys, ASTM D638 on the Fortus 450mc and F900)[5]23.7 as printed, 22.5 annealed, printed Z, ISO 527 (Polymaker)[2]
Brittleness1–5Moderate[1]Very brittle — elongation at break 2.77 % in XY and 0.85 % in Z[2]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for an ESD grade[23]Not documented
Creep resistance / sustained load1–5Excellent — holds load for years. Moulded unfilled PC was still running unbroken under 41 MPa tensile creep at room temperature when the test was stopped, and the conductive filler leaves the glass transition unchanged at 142 °C, so the creep mechanism is polycarbonate's[24][5]Poor — no GF-grade creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[25][26][27]
Fatigue / repeated-flex resistance1–5Not documentedPoor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and elongation at break falls to 2.77 % in XY and 0.85 % in Z[28][2]
Elasticity / flexibility1–5Rigid[1]Rigid[2]
Z strength as % of XY%68-77 (Stratasys ZX against XZ tensile yield, ASTM D638)[5]47 as printed (23.7 Z against 50.1 XY), printed[2]
Wear resistance & frictionNot documentedeSUN describes high wear resistance and positions the grade for wear parts[3]
Thermal Properties
HDT at 0.45 MPa°C143-146 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 66 psi); 135 moulded[5]75.5 as printed, 114.7 after annealing (ISO 75, 0.45 MPa) — the point of the material[2]
HDT at 1.8 MPa°C140-144 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 264 psi); 124 moulded[5]59.7 as printed, 84 after annealing (ISO 75, 1.8 MPa)[2]
Glass transition (Tg)°C143 (DSC, 3DXTech) and 142 (Stratasys, ASTM D7426)[1][5]59.8 (DSC)[2]
Melting point / Vicat°CNot documented174.9 peak melt (DSC); Vicat 148.9 as printed, 148.3 annealed[2]
Continuous service temperature°C113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[18]Not documented
Annealing responseNot documentedAnnealing lifts HDT at 0.45 MPa from 75.5 to 114.7 °C and modulus from 3794 to 4207 MPa[2]
Thermal expansion (CTE)µm/m·K68.4 on extruded unfilled PC stock (ASTM D696; source states 3.8e-5 in/in/°F); no figure is published for a conductive-filled grade[23]Not documented
Environment & Chemical
UV resistance1–5Not documentedDegrades within weeks outdoors[29]
Chemical resistanceWithstands oils, solvents and fuels; Polymaker rates it good against weak acids[14]Not documented
Food contactBisphenol-A polycarbonate is not offered as food-contact filament[14]Not documented
Biodegradability / compostabilityNot biodegradable[14]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[14]Not documented
Electrical & ESD propertiesSurface resistance 10⁷–10⁹ ohm/sq, the static-dissipative band (ASTM D257), against above 10¹³ for unfilled ezPC[1][22]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[30]Low hazard — minimal VOC and particle emission[30]
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[30]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[30][10]None needed in a normal room[30]
Dust & fibre handling hazardConductive carbon filler is bound in the matrix; avoid inhaling sanding dust[1]Glass fibre is bound in the matrix; avoid inhaling sanding dust[31]
Post-Processing
Sanding & machiningSands and machines well; the toughness means it cuts rather than chips[12]Not documented
Gluing & solvent weldingCyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[12]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[12]Not documented
Support material pairingPrints its own supports; 3DXTech sells a dedicated PC break-away support[12]Not documented
Dimensional accuracy & detailNot documentedNear-zero shrinkage — 0.05 % in X-Y and Z (Polymaker)[2]
Solvents & Solubility
Soluble inDichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[32]Chloroform dissolves the PLA matrix (10 % w/v, 2–4 h at 23 °C) and leaves the filler as loose sludge; laboratory reagent.[33]
Softened or crazed byMethanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[32]Acetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[33][34]
Solvent welding & smoothing agentDichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[35]Chloroform vapour attacks only the resin fraction, so the filler is left standing proud; no workshop-safe agent exists.[36][34]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. 3DXSTAT ESD-PC Technical Data Sheet 3DXTech · 2026-08 · tds
  2. Polymaker HT-PLA-GF Technical Data Sheet V1.1 Polymaker · 2026-08 · tds
  3. eSUN ePLA-GF Technical Data Sheet V1.0 (Nov 2023) eSUN (copy hosted on 3d.nice-cdn.com) · 2023-11 · tds
  4. Bambu Filament Technical Data Sheet V1.0 — PLA Galaxy Bambu Lab · 2026-08 · tds
  5. PC-ESD — FDM Material Data Sheet Stratasys · 2024-10 · tds
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. Polymaker HT-PLA-GF — product page Polymaker Shop · 2026-08 · vendor
  8. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  9. Polymaker product catalogue Polymaker · 2026-08 · vendor
  10. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  11. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  12. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  13. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  14. PC — material basics Polymaker Wiki · 2026-08 · doc
  15. 3DXSTAT ESD-PC — product page (print recommendations) 3DXTech · 2026-08 · doc
  16. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  17. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  18. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  19. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  20. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  21. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  22. ezPC Polycarbonate Technical Data Sheet 3DXTech · 2026-08 · tds
  23. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  24. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  25. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  27. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  28. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  29. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  30. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  31. StoneFil safety data sheet Formfutura · 2026-08 · msds
  32. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  33. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  34. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  35. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds
  36. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper