3D Printing Info

Filament comparison

PC-CF vs PPS-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

Carbon-fibre PC (PC-CF) guideFibre-reinforced PPS guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC-CF comparisonsMore PPS-CF comparisons
PC-CF vs PPS-CF — documented properties and sources
PropertyCarbon-fibre PC (PC-CF)PCFibre-reinforced PPSHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$62.58/kg median; $34.99–$117.33/kg across 6 dated product listings$139.98/kg median; $119.98–$174.17/kg across 5 dated product listings
Identity & Market
Base polymer / chemistryPolycarbonate reinforced with chopped carbon fibre[1][2]Carbon-fibre reinforced PPS — Polymaker's Fiberon grade is nominally 10 wt%[3]
Densityg/cm³1.22 (Prusament) and 1.36 (3DXTech), ISO 1183[1][2]1.29 (Fiberon PPS-CF10) and 1.36 (Fiberon PPS-GF20), ISO 1183[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 35–117; the middle of the market is about 63[5][6][7][8][9]1 kg-equivalent spools span 93–174; the middle of the market is about 140[10][11][12][13]
Price range across brandsUSD/kg35–117 across brands; Ambrosia 35, IEMAI 39, YXPOLYER 55, Spectrum PC CF 70, Prusament 94, 3DXTech 117[5][6][7][8][9]93-174 across brands and formats; Polymaker Fiberon PPS-GF20 93 at 3 kg, IEMAI 3D CF-PPS 131 at 750 g, LEHVOSS Luvocom 3F PPS CF 9938 164 at 2.3 kg, Bambu Lab PPS-CF 174 at 750 g[10][11][12][13]
Market availability1–5Available from several mainstream brands[5][7][14]Available from several mainstream brands[10][11][12]
Spool sizes & diameters1.75 and 2.85 mm; 0.75, 0.8 and 1 kg spools[5][7]1.75 mm; 0.5 kg spools[10]
Typical applicationsStiff high-temperature structural parts — jigs, drone frames and under-bonnet brackets[1][2]Chemical and automotive parts needing PPS chemistry with structural stiffness[3]
Diameter tolerance± mm±0.04 (Prusament PC Blend Carbon Fiber)[1]Not documented
Printing Parameters
Nozzle temperature°C285 ± 10 (Prusament)[1]Not documented
Bed temperature°C110 ± 10 (Prusament)[1]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive)[1][15]Enclosure required (passive) — Polymaker states its Fiberon PPS-CF10 needs no heated chamber, unlike the unfilled sulfones and PAEKs[3]
Part cooling fanOff — Prusa allows 0–20 % and warns cooling significantly reduces interlayer adhesion[1]Not documented
Bed surface & adhesion aidPEI with a glue stick or a commercial adhesive[16]Not documented
Warping tendency1–5High — enclosure needed for reliable large parts; the fibre reduces warping against unfilled PC[1][15]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[16][17]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed; Polymaker flags stringing as a common PC problem[17]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning; hardened nozzle mandatory[15][1]Expert / industrial hardware only[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[15]Hardened steel required[3]
Abrasiveness1–5Highly abrasive — standard CF composite[15]Highly abrasive — standard CF composite[3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles; PC already absorbs water from the air and 3DXTech adds a hardened 0.4 mm minimum nozzle, 0.25 mm layers and a 120 °C pre-dry[18][16][19]High — jams from moisture, heat creep or particles; Polymaker specifies hardened steel or ruby nozzles for carbon-filled PPS and Prusa lists composites as a higher clogging risk[20][19]
Heat-creep / jam sensitivity1–5Slightly sensitive[16]Not documented
Hotend requirementAll-metal hot end required (Simplify3D)[16]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low (0.1–0.3 %) — the PC matrix takes up 0.15–0.25 % and 3DXTech specifies a 120 °C, 4 h pre-dry[21][22][18]Low (0.1–0.3 %) — 0.225 % equilibrium for Fiberon PPS-CF10 and 0.11 % for PPS-GF20[3][4]
Equilibrium moisture content at ~50 % RH%0.11 after 7 days at 24 °C / 22 % RH (Prusa Polymers)[1]0.225 equilibrium (Fiberon PPS-CF10); 0.11 (PPS-GF20)[3][4]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[23]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[17][23]No dry-versus-conditioned figures are published; equilibrium uptake is 0.225 % and Polymaker specifies a 100 °C, 10 h dry[3]
Storage requirementAirtight containers with desiccant to prevent reabsorption[17]Not documented
Mechanical Properties
Tensile strength (XY)MPa64 ± 3 printed horizontal and 70 ± 3 printed vertical at yield, ISO 527-1 (Prusament); 3DXTech quotes 73 at break[1][2]59.4 ± 1.3 (PPS-CF10) and 64.1 ± 2.1 (PPS-GF20) printed XY, ISO 527[3][4]
Young's modulusMPa2600 printed horizontal and 3200 printed vertical, ISO 527-1 (Prusament); 3DXTech quotes 6980[1][2]5446.7 ± 149.0 (PPS-CF10) and 4552.0 ± 54.6 (PPS-GF20) printed XY, ISO 527[3][4]
Elongation at break%4.6 at yield printed horizontal (Prusament); 3DXTech quotes 2.1 at break[1][2]1.4 ± 0.1 (PPS-CF10) and 2.0 ± 0.2 (PPS-GF20) printed XY, ISO 527 — the lowest elongation in the dataset[3][4]
Flexural strengthMPa94 ± 3 printed horizontal and 130 ± 2 printed vertical, ISO 178 (Prusament); 3DXTech quotes 85[1][2]Not documented
Flexural modulusMPa3500 printed horizontal and 4200 printed vertical, ISO 178 (Prusament); 3DXTech quotes 6540[1][2]Not documented
Charpy impact, notchedkJ/m²12 ± 1 printed horizontal and 17 ± 2 printed vertical, ISO 179-1 notched (Prusament)[1]5.3 ± 0.2 printed XY for PPS-CF10 and 7.3 ± 0.2 for PPS-GF20, ISO 179 notched[3][4]
Other impact dataCharpy unnotched 32 ± 5 printed horizontal and 35 ± 4 printed vertical (Prusament, ISO 179-1)[1]Not documented
Layer adhesion / Z tensileMPa23 ± 2 (Prusa Polymers interlayer adhesion test) — above the 21 ± 2 of unfilled Prusament PC Blend[1][22]32.0 ± 5.1 (PPS-CF10) and 22.9 ± 0.8 (PPS-GF20) printed Z, ISO 527[3][4]
Brittleness1–5Moderate[1][2]Very brittle — cracks or shatters easily; elongation at break 1.4 %[3]
Hardness (scale-specific)Shore A / Shore D / Rockwell83 Shore D (Prusa Polymers method), against 79 for unfilled Prusament PC Blend[1][22]Rockwell 105 (and R124) on extruded unfilled PPS stock (ASTM D785); no figure is published for a fibre-filled PPS filament[24]
Creep resistance / sustained load1–5Excellent — holds load for years. Room-temperature tensile creep of moulded unfilled PC ran unbroken at 41 MPa until the test was stopped; short carbon fibre raises the flexural modulus from about 2.1 to 3.5-6.5 GPa, which reduces creep strain further[25][1]Excellent — holds load for years. Ensinger lists high creep resistance for unfilled PPS stock and Spectrum states creep resistance is unchanged under continuous load at high temperature; the fibre raises heat deflection to 252 °C at 0.45 MPa[24][26][3]
Fatigue / repeated-flex resistance1–5Good. No fatigue test data was found for a carbon-fibre PC filament; the unfilled polymer is rated Good on the same scale[25]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%Not documented54 (PPS-CF10) and 36 (PPS-GF20), printed[3][4]
Thermal Properties
HDT at 0.45 MPa°C114 (ISO 75, 0.45 MPa, Prusament)[1]252.5 (PPS-CF10) and 236.3 (PPS-GF20), printed, ISO 75 at 0.45 MPa[3][4]
HDT at 1.8 MPa°C106 (ISO 75, 1.8 MPa, Prusament), against 93 for unfilled Prusament PC Blend[1][22]133 (PPS-CF10) and 125.8 (PPS-GF20), printed, ISO 75 at 1.8 MPa[3][4]
Glass transition (Tg)°C127 (3DXTech, DSC)[2]97.7 (PPS-CF10) and 95.0 (PPS-GF20), DSC[3][4]
Melting point / Vicat°CNot documented279.7 (PPS-CF10) and 279.6 (PPS-GF20) melting, DSC; Vicat 267.5 and 272.5 (ISO 306)[3][4]
Continuous service temperature°C113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[22]170 long-term service on extruded PPS stock, converted from 338 °F; no figure published for the carbon-filled grade[24]
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors unless stabilised[17]Not documented
Chemical resistanceWithstands oils, solvents and fuels; Polymaker rates it good against weak acids[17]Outstanding — PPS resists essentially all solvents below 200 °C[20]
Food contactBisphenol-A polycarbonate is not offered as food-contact filament[17]Not documented
Biodegradability / compostabilityNot biodegradable[17]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[17]Not documented
Electrical & ESD propertiesSurface resistance above 10⁹ ohm/sq — not static-dissipative (3DXTech, ASTM D257)[2]Surface resistivity above 10¹² ohm — insulating (ANSI/ESD S11.11)[3][4]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[27]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[27]
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[27]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[27][15]Ventilated room or enclosure recommended[27]
Dust & fibre handling hazardCarbon fibre is bound in the matrix; sanding dust should not be inhaled[2]Fibre is bound in the matrix; sanding dust should not be inhaled[3]
Post-Processing
Sanding & machiningSands and machines well; the toughness means it cuts rather than chips[16]Not documented
Gluing & solvent weldingCyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[16]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[16]Not documented
Support material pairingPrints its own supports; 3DXTech sells a dedicated PC break-away support[16]Not documented
Solvents & Solubility
Soluble inDichloromethane and chloroform dissolve the matrix and leave the fibre; DMF and dioxane do the same (Covestro).[28]None — PPS does not dissolve in any known solvent below 200 °C.[29][30]
Softened or crazed byMethanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[28]Nothing at 23 °C; Ensinger rates it only conditionally resistant to benzene, dichloromethane, toluene and pyridine.[30]
Solvent welding & smoothing agentDichloromethane cement welds the resin, but the fibre keeps the joint from flowing closed. Controlled carcinogen.[31]None — no solvent welds or smooths PPS.[29]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Prusament PC Blend Carbon Fiber Technical Datasheet v2.0 Prusa Polymers · 2023-04 · tds
  2. CarbonX Carbon Fiber ezPC Polycarbonate Technical Data Sheet 3DXTech · 2026-08 · tds
  3. Fiberon PPS-CF10 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  4. Fiberon PPS-GF20 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  5. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  6. Spectrum PC CF Carbon Black, 1.75 mm / 250 g 3DJAKE · 2026-08 · vendor
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. IEMAI CF-PC 3D Printing Filament product page IEMAI 3D · 2026-08 · vendor
  9. YXPOLYER PC CF product page YXPOLYER · 2026-08 · vendor
  10. Polymaker product catalogue Polymaker · 2026-08 · vendor
  11. Bambu Lab PPS-CF Black, spool (750 g) 3DJAKE · 2026-08 · vendor
  12. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  13. IEMAI 3D CF-PPS 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  14. Filastruder product catalogue Filastruder · 2026-08 · vendor
  15. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  16. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. PC — material basics Polymaker Wiki · 2026-08 · doc
  18. CARBONX ezPC+CF — product page (print recommendations) 3DXTech · 2026-08 · doc
  19. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  20. PPS — material basics Polymaker Wiki · 2026-08 · doc
  21. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  22. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  23. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  24. TECATRON natural (PPS) — stock shape properties Ensinger · 2026-08 · tds
  25. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  26. Spectrum PPS AM230 Technical Data Sheet Spectrum Filaments · 2022-04 · tds
  27. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  28. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  29. PPS (Polyphenylene sulfide) — Knowledge Base Prusa Research · 2026-08 · doc
  30. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  31. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds