3D Printing Info

Filament comparison

PC-ABS vs PEKK

Compare printing settings, strength, heat resistance, dated prices and sources.

PC/ABS blend guidePEKK guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC-ABS comparisonsMore PEKK comparisons
PC-ABS vs PEKK — documented properties and sources
PropertyPC/ABS blendPCPEKKHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$45.99/kg median; $34.99–$84.00/kg across 5 dated product listings$525.00/kg median; $332.50–$771.12/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryPolycarbonate/ABS alloy — PC stiffness and heat resistance with ABS processability[1][2]Polyether ketone ketone, amorphous grade — a polyaryletherketone that stays amorphous, so it does not need PEEK's crystallisation control. Stratasys sells it as Antero 800NA and Antero 840CN03; category numbers below are unfilled unless a carbon grade is named[3][4]
Densityg/cm³1.10 (Polymaker) and 1.24 (3DXTech FR grade), ISO 1183; Stratasys specific gravity 1.10 (ASTM D792)[1][2][5]1.28 unfilled (ASTM D792, Antero 800NA; 1.31 annealed) and 1.33 for CarbonX PEKK-A CF15 (ISO 1183)[4][3]
Typical priceUSD/kg1 kg spools cluster near 50[6][7]1 kg-equivalent spools cluster near 550[7][8][9]
Price range across brandsUSD/kg35–84 across brands; Reli3D 35, SUNLU 46, Polymaker 50, 3DXMAX 84[6][7][10][11]333-771 across grades and formats; 3DXTech CarbonX PEKK-A+CF15 333 at 2 kg, 3D4Makers unfilled PEKK-A 485 at 2 kg, IEMAI 3D 500 at 1 kg, Kimya PEKK Carbon 771 at 500 g[7][8][9][12][13]
Market availability1–5Available from several mainstream brands[6][7]Niche, a handful of specialist brands[7][8][9]
Spool sizes & diameters1.75 and 2.85 mm; 0.5 and 1 kg spools[6][7]1.75 and 2.85 mm; 200 g to 2 kg spools, plus Stratasys canisters[7][8][4]
Typical applicationsAutomotive interior and electronics housings that need PC heat resistance without PC's warping[1]Aerospace interior and structural parts; 3DXTech labels its carbon-filled PEKK-A grade AERO and Stratasys certifies Antero 800NA for outgassing and FST[3][4]
Printing Parameters
Nozzle temperature°C250–270 (Polymaker)[1]Not documented
Bed temperature°C90–105 (Polymaker)[1]140 (3DXTech CarbonX PEKK-A CF15)[3]
Enclosure / chamber requirement1–5Enclosure required (passive) — Polymaker specifies a 90–100 °C chamber[1]Actively heated chamber required[14][15]
Recommended chamber temperature°C90–100 (Polymaker)[1]Not documented
Part cooling fanOff (Polymaker)[1]Not documented
Bed surface & adhesion aidPEI with a glue stick or a commercial adhesive[16]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s20 at Polymaker's 250 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][17]Not documented
Warping tendency1–5High — enclosure needed for reliable large parts[1][18]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[16][19]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed; Polymaker flags stringing as a common PC problem[19]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[1][18]Expert / industrial hardware only[14][15]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[18]Hardened steel required — the category spans unfilled PEKK, where brass is acceptable, and the carbon-filled aerospace grades that make up most of the market[3][4]
Abrasiveness1–5Non-abrasive[1]Highly abrasive — most PEKK filament sold is carbon-filled; unfilled Antero 800NA and ThermaX PEKK-A are non-abrasive[3][4]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a 120 °C pre-dry of 4 h or more[20]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[21]
Heat-creep / jam sensitivity1–5Slightly sensitive[16]Not documented
Hotend requirementAll-metal hot end required (Simplify3D)[16]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low (0.1–0.3 %) — the PC matrix takes up 0.15–0.25 % and 3DXTech specifies a 120 °C, 4 h or more pre-dry[22][23][20]Not documented
Drying temperature & time75 °C for 6 h (Polymaker)[1]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[24]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[19][24]No dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[21]
Storage requirementAirtight containers with desiccant to prevent reabsorption[19]Not documented
Mechanical Properties
Tensile strength (XY)MPa39.9 ± 1.0 printed XY, ISO 527 (Polymaker); 3DXTech quotes 60 at break for its FR PC/ABS[1][2]86.7-90.0 at yield and 73.0 at break (printed XZ, ASTM D638, Antero 800NA on the F900 and Fortus 450mc); 88.8 at break annealed; 126 at break for CarbonX PEKK-A CF15 (printed XY, ISO 527)[4][3]
Young's modulusMPa1835 ± 65 printed XY, ISO 527 (Polymaker); 3DXTech quotes 2250[1][2]2640-3870 (printed XZ, ASTM D638, Antero 800NA; upper figure annealed); 9125 for CarbonX PEKK-A CF15 (printed XY, ISO 527)[4][3]
Elongation at break%4.2 ± 0.3 printed XY, ISO 527 (Polymaker); 3DXTech quotes 10 at break[1][2]6.1 at break (printed XZ, ASTM D638, Antero 800NA); 2.3 in ZX; 3.15 for CarbonX PEKK-A CF15 (ISO 527)[4][3]
Flexural strengthMPa66.3 ± 0.9 printed XY, ISO 178 (Polymaker); 3DXTech quotes 85[1][2]136 at 5 % strain (printed XZ, ASTM D790, Antero 800NA); 178 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[4][3]
Flexural modulusMPa2081 ± 106 printed XY, ISO 178 (Polymaker); 3DXTech quotes 2300[1][2]3200 (printed XZ, ASTM D790, Antero 800NA); 8817 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[4][3]
Charpy impact, notchedkJ/m²25.8 ± 1.3 printed XY, ISO 179, notched (Polymaker) — above both unfilled PC and ABS[1]Not documented
Other impact dataNotched Charpy still 13 ± 2 kJ/m² at −30 °C printed XY (Polymaker, ISO 179-1/1eA), against 1.5 in Z. Stratasys prints Izod notched at 241 J/m XZ against 34.0 J/m ZX, and unnotched 655 against 101 J/m (ASTM D256, F900 T16).[1][5]Izod notched 41.1 J/m XZ and 33.3 J/m ZX; unnotched 1730 J/m XZ against 203 J/m ZX (printed, ASTM D256/D4812, Antero 800NA)[4]
Layer adhesion / Z tensileMPa25.9-30.2 at break printed ZX (Stratasys, ASTM D638 on the F900 and Fortus 450mc); 22.9 +/- 1.2 printed Z, ISO 527 (Polymaker)[1][5]50.1-59.4 at yield (printed ZX, ASTM D638, Antero 800NA); 56.0 for the ESD grade Antero 840CN03[4][25]
Brittleness1–5Tough — absorbs impact, yields before breaking[1]Moderate unfilled — 6.1 % elongation at break in plane; brittle in the carbon-filled grades at 3.15 %[4][3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for a PC/ABS filament[26]Not documented
Creep resistance / sustained load1–5Good. Room-temperature tensile creep of moulded PC/ABS was still running unbroken at 30 MPa when the experiment was stopped for time; specimens failed within the test window at 39-47 MPa (ASTM D638)[27]Excellent — holds load for years. Antero 800NA still holds 82 % of its room-temperature ZX tensile strength at 104 °C and 63 % at 132 °C (printed, ASTM D638)[4]
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%75-86 (Stratasys ZX against XZ tensile at break, ASTM D638) against 57 (Polymaker, printed Z against XY tensile)[1][5]56-82 (Antero 800NA and 840CN03 printed on the F900 and Fortus 450mc, ZX against XZ tensile yield and break, ASTM D638)[4][25]
Thermal Properties
HDT at 0.45 MPa°C112 (ISO 75 at 0.45 MPa, Polymaker); Stratasys prints 117.9 in XY and 126.1 in XZ (ASTM D648 Method B at 66 psi), against 125.0 moulded[1][5]158 (printed XY and ZX, ASTM D648 Method B at 66 psi, Antero 800NA); 285 for CarbonX PEKK-A CF15 (ISO 75 at 0.45 MPa)[4][3]
HDT at 1.8 MPa°C106 (ISO 75 at 1.8 MPa, Polymaker); Stratasys prints 107.5 in XY and 112.0 in XZ (ASTM D648 Method B at 264 psi), against 102.9 moulded[1][5]156-157 (printed, ASTM D648 Method B at 264 psi, Antero 800NA); moulded 147[4]
Glass transition (Tg)°C109 (Polymaker) and 137 (3DXTech FR grade), DSC; Stratasys measures 105.3 (ASTM D7426 inflection point)[1][2][5]156 (ASTM D7426, Antero 800NA); 165 for CarbonX PEKK-A CF15 (DSC)[4][3]
Melting point / Vicat°CAmorphous — no melting point; Vicat 135 (Polymaker, ISO 306)[1]300 melt point (ASTM D7426 peak heat, Antero 800NA); 305 for CarbonX PEKK-A CF15 (DSC)[4][3]
Continuous service temperature°C113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[23]Not documented
Annealing response90 °C for 2 h (Polymaker)[1]Not documented
Thermal expansion (CTE)µm/m·K59.9 over -50 to 35 °C and 73.0 over -50 to 95 °C (printed XY, ASTM E831)[5]36.1 in XY and 50.2 in ZX (printed, 40-140 °C, ASTM E831, Antero 800NA); 47.4 and 51.2 for the ESD grade Antero 840CN03[4][25]
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors[19]Good — years with some colour shift. 1000 h of QUV cycling to ASTM G154 left Antero 800NA's yield strength unchanged at 57 MPa and raised stress at break 3.6 %[4]
Chemical resistanceWithstands oils, solvents and fuels; Polymaker rates it good against weak acids[19]Not documented
Food contactBisphenol-A polycarbonate is not offered as food-contact filament[19]Not documented
Biodegradability / compostabilityNot biodegradable[19]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[19]Not documented
Electrical & ESD propertiesNot documentedUnfilled PEKK is an insulator at above 1.4e14 ohm-cm (ASTM D257); CarbonX PEKK-A CF15 sits above 10^7 ohm/sq, and the Antero 840CN03 ESD grade is specified at 10^4-10^9 ohm-cm[4][3][25]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[28]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[28]
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[28]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[28][18]Ventilated room or enclosure recommended[28]
Dust & fibre handling hazardNot documentedCarbon fibre is bound in the matrix; sanding dust should not be inhaled[3]
Post-Processing
Sanding & machiningSands and machines well; the toughness means it cuts rather than chips[16]Not documented
Gluing & solvent weldingCyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[16]Not documented
Vapour / chemical smoothingAcetone attacks the ABS phase, so surface smoothing is partial rather than full[1]Not documented
Support material pairingPrints its own supports; 3DXTech sells a dedicated PC break-away support[16]Not documented
Solvents & Solubility
Soluble inDichloromethane and chloroform dissolve the PC phase; acetone, MEK and THF dissolve the ABS phase.[29][30]Concentrated sulphuric acid, as for PEEK; no common organic solvent touches a polyaryletherketone.[30][31]
Softened or crazed byPetrol, esters, ether and 1 % alkali stress-crack the PC phase; aromatics and esters soften the ABS phase.[29][30]Concentrated sulphuric acid and liquid Freon are the entries Ensinger marks not resistant; acetone, MEK and toluene do nothing.[30]
Solvent welding & smoothing agentAcetone attacks only the ABS phase, so smoothing is partial; a dichloromethane cement welds the whole section.[1][32]None — no solvent softens a polyaryletherketone.[30]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Polymaker PC-ABS Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  2. Firewire Flame Retardant PC/ABS Technical Data Sheet Rev 3.0 3DXTech · 2026-08 · tds
  3. CarbonX Carbon Fiber PEKK-A CF15 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  4. Antero 800NA — FDM Material Data Sheet (PEKK-based) Stratasys · 2025-08 · tds
  5. PC-ABS — FDM Material Data Sheet Stratasys · 2023-08 · tds
  6. Polymaker product catalogue Polymaker · 2026-08 · vendor
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  9. Kimya PEKK-A Natural 1.75 mm 500 g igo3d · 2026-08 · vendor
  10. Reli3D PC-ABS Filament, Black, 1000 g spool Reli3D (Amazon US) · 2026-08 · vendor
  11. SUNLU PC-ABS 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  12. Kimya PEKK Carbon Grey 1.75 mm 500 g igo3d · 2026-08 · vendor
  13. IEMAI 3D PEKK 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  14. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  15. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  16. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  18. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  19. PC — material basics Polymaker Wiki · 2026-08 · doc
  20. 3DXTech 3DXMAX ABS product page 3DXTech · 2026-08 · vendor
  21. THERMAX PEKK-A — product page (print recommendations) 3DXTech · 2026-08 · doc
  22. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  23. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  24. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  25. Antero 840CN03 — FDM Material Data Sheet (PEKK, ESD) Stratasys · 2024-08 · tds
  26. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  27. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  28. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  29. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  30. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  31. The Effects of Sulfonated Poly(ether ether ketone) Ion Exchange Preparation Conditions on Membrane Properties Yee, Zhang & Ladewig, Membranes 3(3) 182–195 · 2013-07 · paper
  32. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds