3D Printing Info

Filament comparison

PAHT-CF vs PLA HS

Compare printing settings, strength, heat resistance, dated prices and sources.

High-temperature CF nylon (PAHT-CF) guideHigh-Speed PLA guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PAHT-CF comparisonsMore PLA HS comparisons
PAHT-CF vs PLA HS — documented properties and sources
PropertyHigh-temperature CF nylon (PAHT-CF)PAHigh-Speed PLAPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$59.98/kg median; $49.99–$69.98/kg across 2 dated product listings$19.99/kg median; $11.49–$32.99/kg across 10 dated product listings
Identity & Market
Base polymer / chemistryHigh-temperature carbon-fibre nylon. Bambu Lab's PAHT-CF and Polymaker's PA612-CF15 both use a long-chain polyamide matrix for lower moisture uptake than PA6[1][2]PLA with rheology and crystallisation tuned for high volumetric flow; melt index 15.4 g/10 min vs 7–11 for standard PLA[3][4]
Densityg/cm³1.03 (Polymaker PA612-CF15) and 1.06 (Bambu Lab), ISO 1183[1][2]1.23 (ISO 1183, at 21.5 °C)[3]
Typical priceUSD/kg1 kg-equivalent spools cluster near 60[1][5]Mainstream 1 kg spools cluster near 20[6][7][8]
Price range across brandsUSD/kg50–70 across brands; Bambu Lab 50, Polymaker Fiberon PA612-CF15 70[1][5]11–33 across brands; budget house brands 11–18, Prusament 33[9][10][11]
Market availability1–5Available from several mainstream brands[1][5]Stocked by most mainstream brands[12][8][13]
Spool sizes & diameters1.75 mm; 0.5 and 1 kg spools[5][1]1.75 mm; 1 kg spools[6][8]
Typical applicationsUnder-bonnet and near-motor parts needing 170 °C-plus heat deflection with less humidity drift than PA6[1][2]Large or repetitive prints on printers that can sustain high flow[14][12]
Diameter tolerance± mmNot documented±0.03 (Bambu Lab PLA Basic, rated to 258 mm/s)[15]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[1]210–230 for high-speed work; 190–210 at classic speeds[3][12]
Bed temperature°CNot documented30–60 (Polymaker); 35–45 (Bambu Lab)[3][16]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[1]Open frame is fine[3]
Recommended chamber temperature°C45–60 (Bambu Lab)[1]Not documented
Part cooling fanNot documentedFan on[3]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[17][18]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][19]≈24 at 300 mm/s with a 0.4 mm nozzle and 0.2 mm layer; 30 % more flow than regular PLA at the same temperature[3][12][14][19]
Warping tendency1–5Not documentedNone[3]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[17]Sticks to anything[20]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[18]Not documented
Overall printing difficulty1–5Expert / industrial hardware only[1][21]Easy — minor profile tuning; needs a printer that can actually reach the flow rate[12][3]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[1]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-CF15 and recommends hardened steel or ruby[2]Brass fine indefinitely[22]
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-CF15[2]Non-abrasive[23][22]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[21]Very low[22]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[17]Moderate — good heatbreak cooling needed; PLA softens below 60 °C[24]
Hotend requirementMay require an all-metal hot end (Simplify3D)[17]No special hot-end required[20]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — 0.88 % saturated at 25 °C / 55 % RH for Bambu Lab PAHT-CF, a third of its PA6-CF; Polymaker's PA612-CF15 reaches 2.2 % equilibrium[1][2][25]Moderate — 0.40 % equilibrium at 23 °C / 70 % RH[3]
Equilibrium moisture content at ~50 % RH%0.88 saturated at 25 °C / 55 % RH (Bambu Lab PAHT-CF); 2.2 equilibrium (Polymaker PA612-CF15)[1][2]0.40 equilibrium at 23 °C / 70 % RH (Polymaker PolySonic)[3]
Drying temperature & time80 °C for 8–12 h (Bambu Lab)[1]55 °C for 6 h; 50 °C for 8 h (Bambu Lab)[3][16]
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing, rough surface and weak layers[21]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA612-CF15 itself: at 2.57 % moisture tensile falls only 91.9 → 83.1 MPa and modulus 5137 → 3991 MPa — the PA612 backbone absorbs far less than PA6[2][26]Polymaker rates PLA low-sensitivity — the loss shows as poor layer adhesion and brittle layers rather than a published strength figure[21]
Storage requirementSealed below 20 % RH with desiccant[21]Sealed with desiccant below 20 % RH; shelf life at ambient is long[16][20]
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[27][28]Not documented
Mechanical Properties
Tensile strength (XY)MPa92 ± 7 (Bambu Lab) and 91.9 ± 2.0 (Polymaker PA612-CF15, dry/annealed) printed XY, ISO 527; the Polymaker grade only falls to 83.1 ± 2.2 conditioned to 2.57 % moisture[1][2]43.9 at 300 mm/s and 46.0 at 46.7 mm/s (printed XY, ISO 527); 58.6 on My Tech Fun bars for Creality Hyper PLA[3][29]
Young's modulusMPa3860 ± 230 (Bambu Lab) and 5137 ± 192 (Polymaker PA612-CF15, dry) printed XY, ISO 527; Polymaker 3991 ± 137 conditioned[1][2]2650 at 300 mm/s, 2878 at classic speed (printed XY, ISO 527)[3]
Elongation at break%2.6 ± 0.2 dry (Polymaker PA612-CF15) to 8.4 ± 1.8 (Bambu Lab) printed XY, ISO 527; Polymaker 4.1 ± 0.3 conditioned[1][2]15.1 at 300 mm/s, 21.5 at classic speed (printed XY, ISO 527)[3]
Flexural strengthMPaNot documented71.4 at 300 mm/s, 76.5 at classic speed (printed XY, ISO 178)[3]
Flexural modulusMPa4230 ± 210 printed XY, ISO 178 (Bambu Lab)[1]2798 at 300 mm/s, 2868 at classic speed (printed XY, ISO 178)[3]
Charpy impact, notchedkJ/m²8.1 ± 0.8 printed XY dry and 7.7 ± 0.5 conditioned, ISO 179 notched (Polymaker PA612-CF15)[2]5.0 at 300 mm/s, 6.1 at classic speed (printed XY, ISO 179, notched)[3]
Other impact dataCharpy unnotched 57.5 ± 3.4 and notched 22.8 ± 1.8 printed XY (Bambu Lab, ISO 179)[1]Printing at 300 mm/s instead of 46.7 mm/s costs 4.6 % tensile strength and 18 % notched Charpy[3]
Layer adhesion / Z tensileMPa47 ± 5 (Bambu Lab) and 48.3 ± 3.9 (Polymaker PA612-CF15, dry) printed Z, ISO 527; Polymaker 35.6 ± 3.0 conditioned[1][2]32.4 at 300 mm/s, 37.3 at classic speed (printed Z, ISO 527); 35.3 for Creality Hyper PLA vs 23.0 for average PLA on identical bars[3][29]
Brittleness1–5Moderate[1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre long-chain nylon filament[30]78.7 Shore D measured on printed bars for Sunlu PLA Meta (My Tech Fun), against 75.3 for the same maker's plain PLA[31]
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load with 110 °C continuous service; the long-chain PA612 matrix takes up 0.88 % at saturation, a third of the same maker's PA6-CF, so it holds dimension better[32][2]Poor — 12 mm bar sagged to 17.7 mm over 6 days at 1.25 kg[29]
Fatigue / repeated-flex resistance1–5Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[32]Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength (R = 0.2)[33][24]
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%51 (Bambu Lab) to 53 (Polymaker PA612-CF15), printed[1][2]74 at 300 mm/s, 81 at classic speed (printed)[3]
Thermal Properties
HDT at 0.45 MPa°C175 (Polymaker PA612-CF15) and 194 (Bambu Lab), ISO 75 at 0.45 MPa[1][2]53 (ISO 75, 0.45 MPa)[3]
HDT at 1.8 MPa°C114 (Polymaker PA612-CF15) and 170 (Bambu Lab), ISO 75 at 1.8 MPa[1][2]52 (ISO 75, 1.8 MPa)[3]
Glass transition (Tg)°C70 (Bambu Lab, DSC)[1]59 (DSC)[3]
Melting point / Vicat°C210 (Polymaker PA612-CF15) and 225 (Bambu Lab) melting, DSC; Vicat 206 (Polymaker)[1][2]164 peak melt (DSC); crystallisation 96 °C, Vicat 61 °C[3]
Continuous service temperature°CNot documented53 — loaded bars begin to move at this temperature[29]
Thermal expansion (CTE)µm/m·KNot documented96–99 for plain printed PLA (fibre Bragg grating, 25–50 °C); no grade-specific measurement published[34]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[27]Flammable; no UL 94 rating published by the major brands[16][4]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[18]Degrades within weeks outdoors[24][35]
Chemical resistanceWithstands oils, fuels and alkalis[18]Good against weak acids, oils and grease; poor against strong acids and alkalis[3]
Water / humidity resistance in service1–5Absorbs water, properties shift — less than PA6 but more than PA12[26][1]Good — insoluble in water[16]
Food contactNot food-contact certified as filament[18]Base resin is food-contact grade, but printed layer grooves harbour bacteria; Prusa advises against food use[24]
Biodegradability / compostabilityNot biodegradable[18]Industrially compostable only — needs sustained 55 °C; not home compostable[36][24]
RecyclabilityNot accepted in household plastic collection[18]Mechanically recyclable; not accepted in household plastic collection[36]
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker PA612-CF15, ANSI/ESD S11.11)[2]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[37]Low hazard — minimal VOC and particle emission[37]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[37]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[37]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[37]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[37]None needed in a normal room[37]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[27]Not documented
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[17]Wet sanding — dry sanding heats the surface by friction and smears it[35][24]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[17]Cyanoacrylate for most joints; some grades partially dissolve and bond with acetone[24][38]
Vapour / chemical smoothingNo practical vapour smoothing[17]No practical vapour smoothing — only chloroform, hot benzene or THF, which are laboratory-only[24]
Support material pairingNot documentedPolySupport and PolyDissolve S1 (Polymaker)[3]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[39]Chloroform: 10 % w/v in 2–4 h at 23 °C, every grade and morphology; THF and DMF only at 65 °C. Laboratory reagents.[40]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[39]Acetone, ethyl acetate and toluene plasticise it but dissolve <1 % even at 65 °C; submersion in acetone crazes and destroys parts.[40][41]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[39]Chloroform vapour smooths and welds PLA at the cost of tensile strength; acetone does not smooth it at all.[42][41]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet — PAHT-CF Bambu Lab · 2026-08 · tds
  2. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  3. PolySonic PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  4. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. PolySonic PLA 1.75mm/1kg — product page Polymaker Shop · 2026-08 · vendor
  7. Overture High Speed PLA 1.75mm Overture3D · 2026-08 · vendor
  8. High Speed PLA filament collection Anycubic Official Store · 2026-08 · vendor
  9. PLA Meta filament collection Sunlu Official Store · 2026-08 · vendor
  10. QIDI PLA Rapido 1.75mm 1kg 3D Printers Depot · 2026-08 · vendor
  11. Prusament PLA Prusa Pro Green 1kg (NFC) Prusa Research · 2026-08 · vendor
  12. PolySonic PLA — product page Polymaker · 2026-08 · vendor
  13. Creality PLA filament collection Creality Official Store · 2026-08 · vendor
  14. Polymaker Launches New High-Speed 3D Printing Filament — PolySonic PLA & PLA Pro Polymaker · 2023-11 · doc
  15. PLA Basic — product page Bambu Lab US Store · 2026-08 · vendor
  16. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  17. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  19. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  20. PLA — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  21. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  22. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  23. Prusament PLA — material page Prusa Polymers · 2026-08 · doc
  24. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  25. Bambu Filament Technical Data Sheet — PA6-CF Bambu Lab · 2026-08 · tds
  26. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  27. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  28. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  29. Creality Hyper PLA filament review — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  30. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  31. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  32. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  33. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  34. Characterization of Thermal Expansion Coefficient of 3D Printing Polymeric Materials Using Fiber Bragg Grating Sensors Materials 17(18):4668 · 2024-09 · paper
  35. Prusament PLA Technical Data Sheet v1.0 Prusa Polymers · 2018-09 · tds
  36. Filamentive PLA (recycled) — product page Filamentive · 2026-08 · vendor
  37. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  38. Prusament rPLA Corn Pigment 1kg — product page Prusa Research · 2026-08 · vendor
  39. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  40. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  41. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  42. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper