Compare printing settings, strength, heat resistance, dated prices and sources.

High-temperature CF nylon (PAHT-CF) guideGlass-fibre PLA (PLA-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PAHT-CF comparisonsMore PLA-GF comparisons
PAHT-CF vs PLA-GF — documented properties and sources
PropertyHigh-temperature CF nylon (PAHT-CF)PAGlass-fibre PLA (PLA-GF)PLA
Market snapshot
Listing priceUSD/kg; dated snapshots$59.98/kg median; $49.99–$69.98/kg across 2 dated product listings$44.99/kg median; $29.99–$59.99/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryHigh-temperature carbon-fibre nylon. Bambu Lab's PAHT-CF and Polymaker's PA612-CF15 both use a long-chain polyamide matrix for lower moisture uptake than PA6[1][2]PLA filled with chopped glass fibre — 12 wt% (Polymaker HT-PLA-GF), 15–20 wt% (eSUN PLA-GF). Bambu Lab PLA Galaxy uses glass microspheres, not fibre, and is not equivalent[3][4][5]
Densityg/cm³1.03 (Polymaker PA612-CF15) and 1.06 (Bambu Lab), ISO 1183[1][2]1.31 (eSUN) to 1.337 (Polymaker), ISO 1183 / GB/T 1033[3][4]
Typical priceUSD/kg1 kg-equivalent spools cluster near 60[1][6]1 kg spools cluster near 30[7][8]
Price range across brandsUSD/kg50–70 across brands; Bambu Lab 50, Polymaker Fiberon PA612-CF15 70[1][6]30–60 across brands; Polymaker 30, Proto-pasta 60[7][8]
Market availability1–5Available from several mainstream brands[1][6]Niche, a handful of specialist brands[7][8][4]
Spool sizes & diameters1.75 mm; 0.5 and 1 kg spools[6][1]1.75 mm; 0.5 and 1 kg spools[8][6]
Typical applicationsUnder-bonnet and near-motor parts needing 170 °C-plus heat deflection with less humidity drift than PA6[1][2]Stiff brackets and fixtures; the Polymaker grade is aimed at parts annealed for heat resistance[3]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[1]210–230 (Polymaker HT-PLA-GF)[3]
Bed temperature°CNot documented25–60 (Polymaker HT-PLA-GF)[3]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[1]Open frame is fine[3]
Recommended chamber temperature°C45–60 (Bambu Lab)[1]Not documented
Part cooling fanNot documentedFan on — eSUN specifies 100 %[4]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[9][10]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][11]28 at Polymaker's stated 350 mm/s on a 0.4 mm nozzle at 0.2 mm layer; eSUN prints its specimens at 60 mm/s[3][4][11]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[9]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[10]Not documented
Shrinkage%Not documented0.05 in X-Y and Z, 0.10 diagonal (Polymaker HT-PLA-GF)[3]
Overall printing difficulty1–5Expert / industrial hardware only[1][12]Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[3]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[1]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-CF15 and recommends hardened steel or ruby[2]Hardened steel required[3]
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-CF15[2]Highly abrasive — standard GF composite[3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[12]Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[13]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[9]Not documented
Hotend requirementMay require an all-metal hot end (Simplify3D)[9]Hardened steel or ruby nozzle; Polymaker's own slicer preset sets a minimum nozzle hardness of 40 HRC[3]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — 0.88 % saturated at 25 °C / 55 % RH for Bambu Lab PAHT-CF, a third of its PA6-CF; Polymaker's PA612-CF15 reaches 2.2 % equilibrium[1][2][14]Moderate — the PLA matrix takes up 0.40–0.51 % saturated; no glass-filled grade publishes its own figure[15][16]
Equilibrium moisture content at ~50 % RH%0.88 saturated at 25 °C / 55 % RH (Bambu Lab PAHT-CF); 2.2 equilibrium (Polymaker PA612-CF15)[1][2]Not documented
Drying temperature & time80 °C for 8–12 h (Bambu Lab)[1]60 °C for 6 h (Polymaker HT-PLA-GF)[3]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA612-CF15 itself: at 2.57 % moisture tensile falls only 91.9 → 83.1 MPa and modulus 5137 → 3991 MPa — the PA612 backbone absorbs far less than PA6[2][17]Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[12]
Storage requirementSealed below 20 % RH with desiccant[12]Not documented
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[18][19]Not documented
Mechanical Properties
Tensile strength (XY)MPa92 ± 7 (Bambu Lab) and 91.9 ± 2.0 (Polymaker PA612-CF15, dry/annealed) printed XY, ISO 527; the Polymaker grade only falls to 83.1 ± 2.2 conditioned to 2.57 % moisture[1][2]50.1 as printed and 50.2 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 59.3 by GB/T 1040[3][4]
Young's modulusMPa3860 ± 230 (Bambu Lab) and 5137 ± 192 (Polymaker PA612-CF15, dry) printed XY, ISO 527; Polymaker 3991 ± 137 conditioned[1][2]3794 as printed, 4207 annealed, printed XY, ISO 527 (Polymaker)[3]
Elongation at break%2.6 ± 0.2 dry (Polymaker PA612-CF15) to 8.4 ± 1.8 (Bambu Lab) printed XY, ISO 527; Polymaker 4.1 ± 0.3 conditioned[1][2]2.77 as printed, 2.3 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 7.99[3][4]
Flexural strengthMPaNot documented86.4 printed XY, ISO 178 (Polymaker)[3]
Flexural modulusMPa4230 ± 210 printed XY, ISO 178 (Bambu Lab)[1]3685 printed XY, ISO 178 (Polymaker); eSUN quotes 4415 flexural modulus by GB/T 9341[3][4]
Charpy impact, notchedkJ/m²8.1 ± 0.8 printed XY dry and 7.7 ± 0.5 conditioned, ISO 179 notched (Polymaker PA612-CF15)[2]5.31 ± 0.46 as printed and 4.92 ± 0.50 annealed (printed XY, ISO 179, notched); Z 4.28 ± 0.18[3]
Other impact dataCharpy unnotched 57.5 ± 3.4 and notched 22.8 ± 1.8 printed XY (Bambu Lab, ISO 179)[1]Izod 10.16 kJ/m² (eSUN, GB/T 1843)[4]
Layer adhesion / Z tensileMPa47 ± 5 (Bambu Lab) and 48.3 ± 3.9 (Polymaker PA612-CF15, dry) printed Z, ISO 527; Polymaker 35.6 ± 3.0 conditioned[1][2]23.7 as printed, 22.5 annealed, printed Z, ISO 527 (Polymaker)[3]
Brittleness1–5Moderate[1]Very brittle — elongation at break 2.77 % in XY and 0.85 % in Z[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre long-chain nylon filament[20]Not documented
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load with 110 °C continuous service; the long-chain PA612 matrix takes up 0.88 % at saturation, a third of the same maker's PA6-CF, so it holds dimension better[21][2]Poor — no GF-grade creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[22][23][24]
Fatigue / repeated-flex resistance1–5Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[21]Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and elongation at break falls to 2.77 % in XY and 0.85 % in Z[25][3]
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%51 (Bambu Lab) to 53 (Polymaker PA612-CF15), printed[1][2]47 as printed (23.7 Z against 50.1 XY), printed[3]
Wear resistance & frictionNot documentedeSUN describes high wear resistance and positions the grade for wear parts[4]
Thermal Properties
HDT at 0.45 MPa°C175 (Polymaker PA612-CF15) and 194 (Bambu Lab), ISO 75 at 0.45 MPa[1][2]75.5 as printed, 114.7 after annealing (ISO 75, 0.45 MPa) — the point of the material[3]
HDT at 1.8 MPa°C114 (Polymaker PA612-CF15) and 170 (Bambu Lab), ISO 75 at 1.8 MPa[1][2]59.7 as printed, 84 after annealing (ISO 75, 1.8 MPa)[3]
Glass transition (Tg)°C70 (Bambu Lab, DSC)[1]59.8 (DSC)[3]
Melting point / Vicat°C210 (Polymaker PA612-CF15) and 225 (Bambu Lab) melting, DSC; Vicat 206 (Polymaker)[1][2]174.9 peak melt (DSC); Vicat 148.9 as printed, 148.3 annealed[3]
Annealing responseNot documentedAnnealing lifts HDT at 0.45 MPa from 75.5 to 114.7 °C and modulus from 3794 to 4207 MPa[3]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[18]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[10]Degrades within weeks outdoors[26]
Chemical resistanceWithstands oils, fuels and alkalis[10]Not documented
Water / humidity resistance in service1–5Absorbs water, properties shift — less than PA6 but more than PA12[17][1]Not documented
Food contactNot food-contact certified as filament[10]Not documented
Biodegradability / compostabilityNot biodegradable[10]Not documented
RecyclabilityNot accepted in household plastic collection[10]Not documented
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker PA612-CF15, ANSI/ESD S11.11)[2]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[27]Low hazard — minimal VOC and particle emission[27]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[27]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[27]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[27]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[27]None needed in a normal room[27]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[18]Glass fibre is bound in the matrix; avoid inhaling sanding dust[28]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[9]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[9]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[9]Not documented
Dimensional accuracy & detailNot documentedNear-zero shrinkage — 0.05 % in X-Y and Z (Polymaker)[3]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[29]Chloroform dissolves the PLA matrix (10 % w/v, 2–4 h at 23 °C) and leaves the filler as loose sludge; laboratory reagent.[30]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[29]Acetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[30][31]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[29]Chloroform vapour attacks only the resin fraction, so the filler is left standing proud; no workshop-safe agent exists.[32][31]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet — PAHT-CF Bambu Lab · 2026-08 · tds
  2. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  3. Polymaker HT-PLA-GF Technical Data Sheet V1.1 Polymaker · 2026-08 · tds
  4. eSUN ePLA-GF Technical Data Sheet V1.0 (Nov 2023) eSUN (copy hosted on 3d.nice-cdn.com) · 2023-11 · tds
  5. Bambu Filament Technical Data Sheet V1.0 — PLA Galaxy Bambu Lab · 2026-08 · tds
  6. Polymaker product catalogue Polymaker · 2026-08 · vendor
  7. Polymaker HT-PLA-GF — product page Polymaker Shop · 2026-08 · vendor
  8. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  9. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  10. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  11. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  12. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  13. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  14. Bambu Filament Technical Data Sheet — PA6-CF Bambu Lab · 2026-08 · tds
  15. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  16. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  17. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  18. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  19. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  20. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  21. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  22. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  23. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  24. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  26. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  27. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  28. StoneFil safety data sheet Formfutura · 2026-08 · msds
  29. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  30. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  31. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  32. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper