3D Printing Info

Filament comparison

PAHT-CF vs PC-ESD

Compare printing settings, strength, heat resistance, dated prices and sources.

High-temperature CF nylon (PAHT-CF) guideESD-safe PC guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PAHT-CF comparisonsMore PC-ESD comparisons
PAHT-CF vs PC-ESD — documented properties and sources
PropertyHigh-temperature CF nylon (PAHT-CF)PAESD-safe PCPC
Market snapshot
Listing priceUSD/kg; dated snapshots$59.98/kg median; $49.99–$69.98/kg across 2 dated product listings$180.00/kg median; $180.00–$180.00/kg across 1 dated product listings
Identity & Market
Base polymer / chemistryHigh-temperature carbon-fibre nylon. Bambu Lab's PAHT-CF and Polymaker's PA612-CF15 both use a long-chain polyamide matrix for lower moisture uptake than PA6[1][2]Polycarbonate compounded with a conductive filler for static-dissipative parts[3]
Densityg/cm³1.03 (Polymaker PA612-CF15) and 1.06 (Bambu Lab), ISO 1183[1][2]1.24 (ISO 1183, 3DXTech); Stratasys specific gravity 1.195 (ASTM D792)[3][4]
Typical priceUSD/kg1 kg-equivalent spools cluster near 60[1][5]1 kg-equivalent spools cluster near 180[6]
Price range across brandsUSD/kg50–70 across brands; Bambu Lab 50, Polymaker Fiberon PA612-CF15 70[1][5]180 at 3DXTech's 750 g pricing — the most expensive material in this group[6]
Market availability1–5Available from several mainstream brands[1][5]Special order, 1–2 makers worldwide[6]
Spool sizes & diameters1.75 mm; 0.5 and 1 kg spools[5][1]1.75 and 2.85 mm; 750 g spools plus Stratasys-compatible cartridges[6]
Typical applicationsUnder-bonnet and near-motor parts needing 170 °C-plus heat deflection with less humidity drift than PA6[1][2]Electronics fixtures and trays that need PC heat resistance and static dissipation together[3]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[1]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[1]Enclosure required (passive)[7][8]
Recommended chamber temperature°C45–60 (Bambu Lab)[1]Not documented
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[9][10]PEI with a glue stick or a commercial adhesive[11]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][12]Not documented
Warping tendency1–5Not documentedSevere — heated chamber needed[7][8]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[9]Needs a specific surface plus adhesive[11][13]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[10]Moderate — retraction tuning needed; Polymaker flags stringing as a common PC problem[13]
Overall printing difficulty1–5Expert / industrial hardware only[1][14]Advanced — enclosure, hardware upgrades, tuning[7]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[1]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-CF15 and recommends hardened steel or ruby[2]Hardened steel required[3]
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-CF15[2]Moderately abrasive — conductive carbon filler[3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[14]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a 120 °C pre-dry[15]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[9]Slightly sensitive[11]
Hotend requirementMay require an all-metal hot end (Simplify3D)[9]All-metal hot end required (Simplify3D)[11]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — 0.88 % saturated at 25 °C / 55 % RH for Bambu Lab PAHT-CF, a third of its PA6-CF; Polymaker's PA612-CF15 reaches 2.2 % equilibrium[1][2][16]Low (0.1–0.3 %) — the PC matrix takes up 0.15–0.25 % and 3DXTech specifies a 120 °C, 4 h pre-dry[17][18][15]
Equilibrium moisture content at ~50 % RH%0.88 saturated at 25 °C / 55 % RH (Bambu Lab PAHT-CF); 2.2 equilibrium (Polymaker PA612-CF15)[1][2]Not documented
Drying temperature & time80 °C for 8–12 h (Bambu Lab)[1]Not documented
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing and a rough surface[14]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA612-CF15 itself: at 2.57 % moisture tensile falls only 91.9 → 83.1 MPa and modulus 5137 → 3991 MPa — the PA612 backbone absorbs far less than PA6[2][19]No dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[13][14]
Storage requirementSealed below 20 % RH with desiccant[14]Airtight containers with desiccant to prevent reabsorption[13]
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[20][21]Not documented
Mechanical Properties
Tensile strength (XY)MPa92 ± 7 (Bambu Lab) and 91.9 ± 2.0 (Polymaker PA612-CF15, dry/annealed) printed XY, ISO 527; the Polymaker grade only falls to 83.1 ± 2.2 conditioned to 2.57 % moisture[1][2]68 at break (printed XY, ISO 527, 3DXTech) — above the 58 of 3DXTech's unfilled ezPC; Stratasys prints 47.6-49.4 at yield in XZ (ASTM D638)[3][22][4]
Young's modulusMPa3860 ± 230 (Bambu Lab) and 5137 ± 192 (Polymaker PA612-CF15, dry) printed XY, ISO 527; Polymaker 3991 ± 137 conditioned[1][2]2300 (printed XY, ISO 527); Stratasys prints 1960 in XZ and 1810-1910 in ZX (ASTM D638)[3][4]
Elongation at break%2.6 ± 0.2 dry (Polymaker PA612-CF15) to 8.4 ± 1.8 (Bambu Lab) printed XY, ISO 527; Polymaker 4.1 ± 0.3 conditioned[1][2]6 at break (printed XY, ISO 527), against 14 for the unfilled grade[3][22]
Flexural strengthMPaNot documented95 (printed XY, ISO 178); Stratasys prints 82.6-83.2 at break in XZ against 46.3-49.5 in ZX (ASTM D790)[3][4]
Flexural modulusMPa4230 ± 210 printed XY, ISO 178 (Bambu Lab)[1]2310 (printed XY, ISO 178)[3]
Charpy impact, notchedkJ/m²8.1 ± 0.8 printed XY dry and 7.7 ± 0.5 conditioned, ISO 179 notched (Polymaker PA612-CF15)[2]Not documented
Other impact dataCharpy unnotched 57.5 ± 3.4 and notched 22.8 ± 1.8 printed XY (Bambu Lab, ISO 179)[1]Not documented
Layer adhesion / Z tensileMPa47 ± 5 (Bambu Lab) and 48.3 ± 3.9 (Polymaker PA612-CF15, dry) printed Z, ISO 527; Polymaker 35.6 ± 3.0 conditioned[1][2]32.5-37.9 at yield printed ZX (Stratasys, ASTM D638 on the Fortus 450mc and F900)[4]
Brittleness1–5Moderate[1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre long-chain nylon filament[23]Rockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for an ESD grade[24]
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load with 110 °C continuous service; the long-chain PA612 matrix takes up 0.88 % at saturation, a third of the same maker's PA6-CF, so it holds dimension better[25][2]Excellent — holds load for years. Moulded unfilled PC was still running unbroken under 41 MPa tensile creep at room temperature when the test was stopped, and the conductive filler leaves the glass transition unchanged at 142 °C, so the creep mechanism is polycarbonate's[26][4]
Fatigue / repeated-flex resistance1–5Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[25]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%51 (Bambu Lab) to 53 (Polymaker PA612-CF15), printed[1][2]68-77 (Stratasys ZX against XZ tensile yield, ASTM D638)[4]
Thermal Properties
HDT at 0.45 MPa°C175 (Polymaker PA612-CF15) and 194 (Bambu Lab), ISO 75 at 0.45 MPa[1][2]143-146 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 66 psi); 135 moulded[4]
HDT at 1.8 MPa°C114 (Polymaker PA612-CF15) and 170 (Bambu Lab), ISO 75 at 1.8 MPa[1][2]140-144 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 264 psi); 124 moulded[4]
Glass transition (Tg)°C70 (Bambu Lab, DSC)[1]143 (DSC, 3DXTech) and 142 (Stratasys, ASTM D7426)[3][4]
Melting point / Vicat°C210 (Polymaker PA612-CF15) and 225 (Bambu Lab) melting, DSC; Vicat 206 (Polymaker)[1][2]Not documented
Continuous service temperature°CNot documented113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[18]
Thermal expansion (CTE)µm/m·KNot documented68.4 on extruded unfilled PC stock (ASTM D696; source states 3.8e-5 in/in/°F); no figure is published for a conductive-filled grade[24]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[20]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[10]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[10]Withstands oils, solvents and fuels; Polymaker rates it good against weak acids[13]
Water / humidity resistance in service1–5Absorbs water, properties shift — less than PA6 but more than PA12[19][1]Not documented
Food contactNot food-contact certified as filament[10]Bisphenol-A polycarbonate is not offered as food-contact filament[13]
Biodegradability / compostabilityNot biodegradable[10]Not biodegradable[13]
RecyclabilityNot accepted in household plastic collection[10]Mechanically recyclable but not accepted in household plastic collection[13]
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker PA612-CF15, ANSI/ESD S11.11)[2]Surface resistance 10⁷–10⁹ ohm/sq, the static-dissipative band (ASTM D257), against above 10¹³ for unfilled ezPC[3][22]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[27]Moderate — measurable VOCs and UFPs, ventilation advised[27]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[27]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[27]≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[27]
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[27]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[27]Ventilated room or enclosure recommended[27][7]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[20]Conductive carbon filler is bound in the matrix; avoid inhaling sanding dust[3]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[9]Sands and machines well; the toughness means it cuts rather than chips[11]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[9]Cyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[11]
Vapour / chemical smoothingNo practical vapour smoothing[9]No practical vapour smoothing[11]
Support material pairingNot documentedPrints its own supports; 3DXTech sells a dedicated PC break-away support[11]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[28]Dichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[29]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[28]Methanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[29]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[28]Dichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[30]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet — PAHT-CF Bambu Lab · 2026-08 · tds
  2. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  3. 3DXSTAT ESD-PC Technical Data Sheet 3DXTech · 2026-08 · tds
  4. PC-ESD — FDM Material Data Sheet Stratasys · 2024-10 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  8. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  9. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  10. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  11. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  12. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  13. PC — material basics Polymaker Wiki · 2026-08 · doc
  14. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  15. 3DXSTAT ESD-PC — product page (print recommendations) 3DXTech · 2026-08 · doc
  16. Bambu Filament Technical Data Sheet — PA6-CF Bambu Lab · 2026-08 · tds
  17. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  18. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  19. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  20. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  21. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  22. ezPC Polycarbonate Technical Data Sheet 3DXTech · 2026-08 · tds
  23. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  24. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  25. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  26. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  27. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  28. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  29. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  30. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds