3D Printing Info

Filament comparison

PA6-GF vs PPSU

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PA6 (PA6-GF) guidePPSU guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA6-GF comparisonsMore PPSU comparisons
PA6-GF vs PPSU — documented properties and sources
PropertyGlass-fibre PA6 (PA6-GF)PAPPSUHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$59.98/kg median; $39.99–$130.00/kg across 6 dated product listings$337.40/kg median; $223.00–$732.56/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryPA6 reinforced with chopped glass fibre — Polymaker's grade is 25 wt%[1][2]Polyphenylsulfone — an amorphous high-temperature sulfone polymer[3]
Densityg/cm³1.14 (Bambu Lab) and 1.20 (Polymaker Fiberon), ISO 1183[2][1]1.28 (ISO 1183, 3DXTech; ASTM D792, Stratasys PPSF)[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 40–130; the middle of the market is about 60[2][5][6]1 kg-equivalent spools span 223–733; the middle of the market is about 425[7][8][9][10]
Price range across brandsUSD/kg40–130 across brands; SUNLU 40, YXPOLYER 45, Polymaker Fiberon and Bambu Lab 60, 3DXTech FibreX 87, Obsidian Nylon 6+GF 130[5][2][7][6][11]223-733 across brands; IEMAI 3D 223 at 1 kg, 3DXTech ThermaX PPSU 250 at 500 g, 3D4Makers 425 at 750 g, Kimya PPSU-S 733 at 500 g[7][8][9][10]
Market availability1–5Stocked by most mainstream brands[2][5][7][6][11]Niche, a handful of specialist brands[7][8][9]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75 and 1 kg spools[5][7][2]1.75 and 2.85 mm; 200 g to 750 g spools[7][8][9]
Typical applicationsStiff, heat-resistant structural parts where a matte finish and lower cost beat carbon fibre[2][1]Steam-sterilisable medical and dental tooling, and aircraft interior parts[3]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[2]Not documented
Bed temperature°CNot documented130–150 (3DXTech)[3]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[2]Actively heated chamber required[12][13]
Recommended chamber temperature°C45–60 (Bambu Lab)[2]Not documented
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[14][15]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s10 at Bambu Lab's 130 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][16]Not documented
Warping tendency1–5Not documentedSevere — heated chamber needed[12]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[14]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[15]Not documented
Overall printing difficulty1–5Expert / industrial hardware only[2][17]Expert / industrial hardware only[12][13]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[2]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA6-GF25 and recommends hardened steel or ruby[1]Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[12]
Abrasiveness1–5Highly abrasive — standard GF composite; Polymaker puts brass nozzle life at roughly 9 h on PA6-GF25[1]Non-abrasive when unfilled[3]
Nozzle clog risk1–5Very high — frequent jams without careful setup[17]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[18]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[14]Not documented
Hotend requirementMay require an all-metal hot end (Simplify3D)[14]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Very high (>2 %) — 2.56 % saturated at 25 °C / 55 % RH (Bambu Lab) and 3.33 % equilibrium (Polymaker Fiberon), the highest in the dataset[2][1]Not documented
Equilibrium moisture content at ~50 % RH%2.56 saturated at 25 °C / 55 % RH (Bambu Lab); 3.33 equilibrium (Polymaker Fiberon PA6-GF25)[2][1]0.37 in 24 h and 1.1 at saturation on extruded stock (ASTM D570)[19]
Drying temperature & time80 °C for 8–12 h (Bambu Lab)[2]Not documented
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[20]Not documented
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA6-GF25 itself: at 4.57 % moisture tensile falls 80.1 → 40.2 MPa and modulus 5357 → 1794 MPa, while notched Charpy rises 10.0 → 28.0 kJ/m²[1][20]No dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[18]
Storage requirementSealed below 20 % RH with desiccant[17]Not documented
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[21][22]Not documented
Mechanical Properties
Tensile strength (XY)MPa75 ± 6 (Bambu Lab) and 80.1 ± 1.8 (Polymaker Fiberon, dry/annealed) printed XY, ISO 527; Fiberon falls to 40.2 ± 2.1 conditioned to 4.57 % moisture. Stratasys FDM PA6/66-GF30-FR gives 60.2-61.1 at break and 61.7-62.3 at yield printed XZ (ASTM D638)[2][1][23]55 (printed XY, ISO 527, 3DXTech) and 55 (printed on side long edge, ASTM D638, Stratasys PPSF); 79 at yield on extruded stock[3][4][19]
Young's modulusMPa2850 ± 260 (Bambu Lab) and 5357 ± 211 (Polymaker Fiberon, dry) printed XY, ISO 527; Fiberon falls to 1794 ± 84 conditioned. Stratasys FDM PA6/66-GF30-FR gives 5600-5830 printed XZ against 3050-3140 in ZX (ASTM D638)[2][1][23]2100 (printed, ASTM D638, Stratasys PPSF) and 2310 (printed XY, ISO 527, 3DXTech); 2344 on extruded stock[3][4][19]
Elongation at break%2.4 ± 0.2 dry (Polymaker Fiberon) to 3.9 ± 0.8 (Bambu Lab) printed XY, ISO 527; the Fiberon grade rises to 4.2 ± 0.7 conditioned[2][1]3 (printed, ISO 527 and ASTM D638) against 60 on extruded stock — printing costs PPSU almost all of its ductility[3][4][19]
Flexural strengthMPaNot documented110 (printed, ISO 178 and ASTM D790, 3DXTech and Stratasys PPSF agree); 91 on extruded stock[3][4][19]
Flexural modulusMPa3670 ± 140 printed XY, ISO 178 (Bambu Lab)[2]2200 (printed, ASTM D790, Stratasys PPSF) and 2215 (printed XY, ISO 178, 3DXTech)[3][4]
Charpy impact, notchedkJ/m²10.0 ± 0.7 printed XY dry and 28.0 ± 1.0 conditioned, ISO 179 notched (Polymaker Fiberon); Bambu Lab 7.2 ± 2.3[1][2]Not documented
Other impact dataCharpy unnotched 27.2 ± 2.2 printed XY (Bambu Lab, ISO 179). Stratasys FDM PA6/66-GF30-FR gives Izod notched 74.6-77.1 J/m printed XZ against 17.2-22.1 in ZX (ASTM D256)[2][23]Izod notched 58.7 J/m and unnotched 165.5 J/m (printed, ASTM D256 Method A, Stratasys PPSF); 160 J/m notched on extruded stock[4][19]
Layer adhesion / Z tensileMPa27 ± 5 (Bambu Lab) and 60.7 ± 1.1 (Polymaker Fiberon, dry) printed Z, ISO 527 — the two makers differ by more than a factor of two; Fiberon falls to 26.3 ± 1.5 conditioned. Stratasys FDM PA6/66-GF30-FR gives 23.7-24.4 at break printed ZX (ASTM D638)[2][1][23]Not documented
Brittleness1–5Brittle — snaps with little warning; elongation at break 2.4 % in XY[1]Brittle — snaps with little warning[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785)[24]Rockwell M86 on printed PPSF (ASTM D785, Stratasys); M96 on extruded PPSU stock (and an unlabelled 123)[4][19]
Creep resistance / sustained load1–5Good. Ensinger lists high creep resistance as a headline property of extruded PA66-GF30 stock; the rating is held below Excellent because equilibrium moisture uptake of 3.33 % softens the matrix in service[24][1]Good. Printed PPSF holds 189 °C heat deflection at 1.8 MPa (ASTM D648) and extruded stock is rated 149 °C long-term service, but Ensinger does not claim the creep resistance it claims for PSU and PPS[4][19]
Fatigue / repeated-flex resistance1–5Good. Ensinger lists high fatigue strength as a headline property of extruded PA66-GF30 stock[24]Not documented
Elasticity / flexibility1–5Rigid[2]Rigid[3]
Z strength as % of XY%36 (Bambu Lab) to 76 (Polymaker Fiberon), printed; Stratasys FDM PA6/66-GF30-FR gives 39-41 (ZX against XZ tensile at break, ASTM D638)[2][1][23]Not documented
Thermal Properties
HDT at 0.45 MPa°C182 (Bambu Lab) and 191 (Polymaker Fiberon), ISO 75 at 0.45 MPa. Stratasys FDM PA6/66-GF30-FR gives 161 printed XY and 185 XZ (ASTM D648 at 66 psi)[2][1][23]190 (printed XY, ISO 75 at 0.45 MPa, 3DXTech)[3]
HDT at 1.8 MPa°C157 (Polymaker Fiberon) and 158 (Bambu Lab), ISO 75 at 1.8 MPa[2][1]189 (printed, ASTM D648 at 264 psi, Stratasys PPSF); 207 on extruded stock, converted from 405 °F[4][19]
Glass transition (Tg)°C67 (Bambu Lab) and 70.4 (Polymaker Fiberon), DSC; Stratasys measures 51.5 on FDM PA6/66-GF30-FR (ASTM D7426)[2][1][23]230 (DSC) — the highest glass transition in the dataset[3]
Melting point / Vicat°C214.5 (Polymaker Fiberon) and 219 (Bambu Lab) melting, DSC; Vicat 210–212 (ISO 306)[2][1]Not documented
Continuous service temperature°CNot documented149 long-term service on extruded PPSU stock, converted from 300 °F[19]
Thermal expansion (CTE)µm/m·K48.6 on extruded PA66-GF30 stock (ASTM D696; source states 2.7e-5 in/in/°F). Stratasys measures much higher on printed FDM PA6/66-GF30-FR — 95.4 over -20 to 5 °C and 214 over 25 to 80 °C in XY (ASTM E831)[24][23]55.0 (printed PPSF, ASTM D696; source states 5.5e-5 mm/mm/°C) and 55.8 on extruded stock (ASTM D696, from 3.1e-5 in/in/°F)[4][19]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[21]UL 94 V-0 at 1.5 mm, rated on the base resin[3]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[15]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[15]Withstands repeated steam autoclaving, the usual reason to choose PPSU over PSU; Stratasys also lists PPSF as passing 24 h stress-crack exposure to antifreeze, petrol, motor oil, power-steering, transmission and washer fluid at 23 °C and 100 °C[3][4]
Water / humidity resistance in service1–5Absorbs water, properties shift[20]Not documented
Food contactNot food-contact certified as filament[15]Not documented
Biodegradability / compostabilityNot biodegradable[15]Not documented
RecyclabilityNot accepted in household plastic collection[15]Not documented
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker Fiberon, ANSI/ESD S11.11)[1]Volume resistivity 5e13 to 1.5e14 ohm-cm and dielectric strength 80-290 V/mil on printed PPSF (ASTM D257, D149)[4]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[25]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[25]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[25]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[25]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[25]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[25]Ventilated room or enclosure recommended[25]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Not documented
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[14]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[14]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[14]Not documented
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[26]Dichloromethane dissolves it at 23 °C at every stress level; acetone solvates and softens unstressed PPSU (Solvay ESCR).[27]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[26]MEK ruptures stressed parts and toluene crazes them above 13.8 MPa; glass-filled grades survive where unfilled craze.[27]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[26]Dichloromethane cements PPSU and NMP softens residual resin; both are laboratory reagents, not workshop stock.[27]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  2. Bambu Filament Technical Data Sheet — PA6-GF Bambu Lab · 2026-08 · tds
  3. ThermaX PPSU Technical Data Sheet v3 3DXTech · 2026-08 · tds
  4. PPSF (polyphenylsulfone) — FDM Data Sheet Stratasys · 2018-06 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. SUNLU Nylon-6 Glass Fiber (PA6-GF) 3D Printer Filament 1 kg — product page SUNLU · 2026-08 · vendor
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. Kimya PPSU-S Natural 1.75 mm 500 g igo3d · 2026-08 · vendor
  9. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  10. IEMAI 3D PPSU 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  11. YXPOLYER PA6-GF Black 1 kg — product page YXPOLYER · 2026-08 · vendor
  12. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  13. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  14. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  15. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  18. THERMAX PPSU — product page (print recommendations) 3DXTech · 2026-08 · doc
  19. TECASON P black (PPSU) — stock shape properties Ensinger · 2026-08 · tds
  20. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  21. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  22. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  23. FDM PA6/66-GF30-FR — Material Data Sheet Stratasys · 2026-07 · tds
  24. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  25. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  26. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  27. Radel PPSU, Veradel PESU, Acudel modified PPSU Design Guide — environmental stress cracking tables Solvay Specialty Polymers · 2026-08 · tds