3D Printing Info

Filament comparison

PA6-GF vs PPS-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PA6 (PA6-GF) guideFibre-reinforced PPS guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA6-GF comparisonsMore PPS-CF comparisons
PA6-GF vs PPS-CF — documented properties and sources
PropertyGlass-fibre PA6 (PA6-GF)PAFibre-reinforced PPSHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$59.98/kg median; $39.99–$130.00/kg across 6 dated product listings$139.98/kg median; $119.98–$174.17/kg across 5 dated product listings
Identity & Market
Base polymer / chemistryPA6 reinforced with chopped glass fibre — Polymaker's grade is 25 wt%[1][2]Carbon-fibre reinforced PPS — Polymaker's Fiberon grade is nominally 10 wt%[3]
Densityg/cm³1.14 (Bambu Lab) and 1.20 (Polymaker Fiberon), ISO 1183[2][1]1.29 (Fiberon PPS-CF10) and 1.36 (Fiberon PPS-GF20), ISO 1183[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 40–130; the middle of the market is about 60[2][5][6]1 kg-equivalent spools span 93–174; the middle of the market is about 140[5][7][8][9]
Price range across brandsUSD/kg40–130 across brands; SUNLU 40, YXPOLYER 45, Polymaker Fiberon and Bambu Lab 60, 3DXTech FibreX 87, Obsidian Nylon 6+GF 130[5][2][10][6][11]93-174 across brands and formats; Polymaker Fiberon PPS-GF20 93 at 3 kg, IEMAI 3D CF-PPS 131 at 750 g, LEHVOSS Luvocom 3F PPS CF 9938 164 at 2.3 kg, Bambu Lab PPS-CF 174 at 750 g[5][7][8][9]
Market availability1–5Stocked by most mainstream brands[2][5][10][6][11]Available from several mainstream brands[5][7][8]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75 and 1 kg spools[5][10][2]1.75 mm; 0.5 kg spools[5]
Typical applicationsStiff, heat-resistant structural parts where a matte finish and lower cost beat carbon fibre[2][1]Chemical and automotive parts needing PPS chemistry with structural stiffness[3]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[2]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[2]Enclosure required (passive) — Polymaker states its Fiberon PPS-CF10 needs no heated chamber, unlike the unfilled sulfones and PAEKs[3]
Recommended chamber temperature°C45–60 (Bambu Lab)[2]Not documented
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[12][13]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s10 at Bambu Lab's 130 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][14]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[12]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[13]Not documented
Overall printing difficulty1–5Expert / industrial hardware only[2][15]Expert / industrial hardware only[3]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[2]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA6-GF25 and recommends hardened steel or ruby[1]Hardened steel required[3]
Abrasiveness1–5Highly abrasive — standard GF composite; Polymaker puts brass nozzle life at roughly 9 h on PA6-GF25[1]Highly abrasive — standard CF composite[3]
Nozzle clog risk1–5Very high — frequent jams without careful setup[15]High — jams from moisture, heat creep or particles; Polymaker specifies hardened steel or ruby nozzles for carbon-filled PPS and Prusa lists composites as a higher clogging risk[16][17]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[12]Not documented
Hotend requirementMay require an all-metal hot end (Simplify3D)[12]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Very high (>2 %) — 2.56 % saturated at 25 °C / 55 % RH (Bambu Lab) and 3.33 % equilibrium (Polymaker Fiberon), the highest in the dataset[2][1]Low (0.1–0.3 %) — 0.225 % equilibrium for Fiberon PPS-CF10 and 0.11 % for PPS-GF20[3][4]
Equilibrium moisture content at ~50 % RH%2.56 saturated at 25 °C / 55 % RH (Bambu Lab); 3.33 equilibrium (Polymaker Fiberon PA6-GF25)[2][1]0.225 equilibrium (Fiberon PPS-CF10); 0.11 (PPS-GF20)[3][4]
Drying temperature & time80 °C for 8–12 h (Bambu Lab)[2]Not documented
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[18]Not documented
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA6-GF25 itself: at 4.57 % moisture tensile falls 80.1 → 40.2 MPa and modulus 5357 → 1794 MPa, while notched Charpy rises 10.0 → 28.0 kJ/m²[1][18]No dry-versus-conditioned figures are published; equilibrium uptake is 0.225 % and Polymaker specifies a 100 °C, 10 h dry[3]
Storage requirementSealed below 20 % RH with desiccant[15]Not documented
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[19][20]Not documented
Mechanical Properties
Tensile strength (XY)MPa75 ± 6 (Bambu Lab) and 80.1 ± 1.8 (Polymaker Fiberon, dry/annealed) printed XY, ISO 527; Fiberon falls to 40.2 ± 2.1 conditioned to 4.57 % moisture. Stratasys FDM PA6/66-GF30-FR gives 60.2-61.1 at break and 61.7-62.3 at yield printed XZ (ASTM D638)[2][1][21]59.4 ± 1.3 (PPS-CF10) and 64.1 ± 2.1 (PPS-GF20) printed XY, ISO 527[3][4]
Young's modulusMPa2850 ± 260 (Bambu Lab) and 5357 ± 211 (Polymaker Fiberon, dry) printed XY, ISO 527; Fiberon falls to 1794 ± 84 conditioned. Stratasys FDM PA6/66-GF30-FR gives 5600-5830 printed XZ against 3050-3140 in ZX (ASTM D638)[2][1][21]5446.7 ± 149.0 (PPS-CF10) and 4552.0 ± 54.6 (PPS-GF20) printed XY, ISO 527[3][4]
Elongation at break%2.4 ± 0.2 dry (Polymaker Fiberon) to 3.9 ± 0.8 (Bambu Lab) printed XY, ISO 527; the Fiberon grade rises to 4.2 ± 0.7 conditioned[2][1]1.4 ± 0.1 (PPS-CF10) and 2.0 ± 0.2 (PPS-GF20) printed XY, ISO 527 — the lowest elongation in the dataset[3][4]
Flexural modulusMPa3670 ± 140 printed XY, ISO 178 (Bambu Lab)[2]Not documented
Charpy impact, notchedkJ/m²10.0 ± 0.7 printed XY dry and 28.0 ± 1.0 conditioned, ISO 179 notched (Polymaker Fiberon); Bambu Lab 7.2 ± 2.3[1][2]5.3 ± 0.2 printed XY for PPS-CF10 and 7.3 ± 0.2 for PPS-GF20, ISO 179 notched[3][4]
Other impact dataCharpy unnotched 27.2 ± 2.2 printed XY (Bambu Lab, ISO 179). Stratasys FDM PA6/66-GF30-FR gives Izod notched 74.6-77.1 J/m printed XZ against 17.2-22.1 in ZX (ASTM D256)[2][21]Not documented
Layer adhesion / Z tensileMPa27 ± 5 (Bambu Lab) and 60.7 ± 1.1 (Polymaker Fiberon, dry) printed Z, ISO 527 — the two makers differ by more than a factor of two; Fiberon falls to 26.3 ± 1.5 conditioned. Stratasys FDM PA6/66-GF30-FR gives 23.7-24.4 at break printed ZX (ASTM D638)[2][1][21]32.0 ± 5.1 (PPS-CF10) and 22.9 ± 0.8 (PPS-GF20) printed Z, ISO 527[3][4]
Brittleness1–5Brittle — snaps with little warning; elongation at break 2.4 % in XY[1]Very brittle — cracks or shatters easily; elongation at break 1.4 %[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785)[22]Rockwell 105 (and R124) on extruded unfilled PPS stock (ASTM D785); no figure is published for a fibre-filled PPS filament[23]
Creep resistance / sustained load1–5Good. Ensinger lists high creep resistance as a headline property of extruded PA66-GF30 stock; the rating is held below Excellent because equilibrium moisture uptake of 3.33 % softens the matrix in service[22][1]Excellent — holds load for years. Ensinger lists high creep resistance for unfilled PPS stock and Spectrum states creep resistance is unchanged under continuous load at high temperature; the fibre raises heat deflection to 252 °C at 0.45 MPa[23][24][3]
Fatigue / repeated-flex resistance1–5Good. Ensinger lists high fatigue strength as a headline property of extruded PA66-GF30 stock[22]Not documented
Elasticity / flexibility1–5Rigid[2]Rigid[3]
Z strength as % of XY%36 (Bambu Lab) to 76 (Polymaker Fiberon), printed; Stratasys FDM PA6/66-GF30-FR gives 39-41 (ZX against XZ tensile at break, ASTM D638)[2][1][21]54 (PPS-CF10) and 36 (PPS-GF20), printed[3][4]
Thermal Properties
HDT at 0.45 MPa°C182 (Bambu Lab) and 191 (Polymaker Fiberon), ISO 75 at 0.45 MPa. Stratasys FDM PA6/66-GF30-FR gives 161 printed XY and 185 XZ (ASTM D648 at 66 psi)[2][1][21]252.5 (PPS-CF10) and 236.3 (PPS-GF20), printed, ISO 75 at 0.45 MPa[3][4]
HDT at 1.8 MPa°C157 (Polymaker Fiberon) and 158 (Bambu Lab), ISO 75 at 1.8 MPa[2][1]133 (PPS-CF10) and 125.8 (PPS-GF20), printed, ISO 75 at 1.8 MPa[3][4]
Glass transition (Tg)°C67 (Bambu Lab) and 70.4 (Polymaker Fiberon), DSC; Stratasys measures 51.5 on FDM PA6/66-GF30-FR (ASTM D7426)[2][1][21]97.7 (PPS-CF10) and 95.0 (PPS-GF20), DSC[3][4]
Melting point / Vicat°C214.5 (Polymaker Fiberon) and 219 (Bambu Lab) melting, DSC; Vicat 210–212 (ISO 306)[2][1]279.7 (PPS-CF10) and 279.6 (PPS-GF20) melting, DSC; Vicat 267.5 and 272.5 (ISO 306)[3][4]
Continuous service temperature°CNot documented170 long-term service on extruded PPS stock, converted from 338 °F; no figure published for the carbon-filled grade[23]
Thermal expansion (CTE)µm/m·K48.6 on extruded PA66-GF30 stock (ASTM D696; source states 2.7e-5 in/in/°F). Stratasys measures much higher on printed FDM PA6/66-GF30-FR — 95.4 over -20 to 5 °C and 214 over 25 to 80 °C in XY (ASTM E831)[22][21]Not documented
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[19]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[13]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[13]Outstanding — PPS resists essentially all solvents below 200 °C[16]
Water / humidity resistance in service1–5Absorbs water, properties shift[18]Not documented
Food contactNot food-contact certified as filament[13]Not documented
Biodegradability / compostabilityNot biodegradable[13]Not documented
RecyclabilityNot accepted in household plastic collection[13]Not documented
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker Fiberon, ANSI/ESD S11.11)[1]Surface resistivity above 10¹² ohm — insulating (ANSI/ESD S11.11)[3][4]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[25]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[25]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[25]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[25]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[25]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[25]Ventilated room or enclosure recommended[25]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Fibre is bound in the matrix; sanding dust should not be inhaled[3]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[12]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[12]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[12]Not documented
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[26]None — PPS does not dissolve in any known solvent below 200 °C.[27][28]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[26]Nothing at 23 °C; Ensinger rates it only conditionally resistant to benzene, dichloromethane, toluene and pyridine.[28]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[26]None — no solvent welds or smooths PPS.[27]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  2. Bambu Filament Technical Data Sheet — PA6-GF Bambu Lab · 2026-08 · tds
  3. Fiberon PPS-CF10 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  4. Fiberon PPS-GF20 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. SUNLU Nylon-6 Glass Fiber (PA6-GF) 3D Printer Filament 1 kg — product page SUNLU · 2026-08 · vendor
  7. Bambu Lab PPS-CF Black, spool (750 g) 3DJAKE · 2026-08 · vendor
  8. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  9. IEMAI 3D CF-PPS 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  10. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  11. YXPOLYER PA6-GF Black 1 kg — product page YXPOLYER · 2026-08 · vendor
  12. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  13. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  14. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  15. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  16. PPS — material basics Polymaker Wiki · 2026-08 · doc
  17. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  18. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  19. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  20. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  21. FDM PA6/66-GF30-FR — Material Data Sheet Stratasys · 2026-07 · tds
  22. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  23. TECATRON natural (PPS) — stock shape properties Ensinger · 2026-08 · tds
  24. Spectrum PPS AM230 Technical Data Sheet Spectrum Filaments · 2022-04 · tds
  25. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  26. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  27. PPS (Polyphenylene sulfide) — Knowledge Base Prusa Research · 2026-08 · doc
  28. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds