3D Printing Info

Filament comparison

PA6-GF vs rPETG

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PA6 (PA6-GF) guideRecycled PETG (rPETG) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA6-GF comparisonsMore rPETG comparisons
PA6-GF vs rPETG — documented properties and sources
PropertyGlass-fibre PA6 (PA6-GF)PARecycled PETG (rPETG)PETG
Market snapshot
Listing priceUSD/kg; dated snapshots$59.98/kg median; $39.99–$130.00/kg across 6 dated product listings$28.99/kg median; $17.24–$39.98/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryPA6 reinforced with chopped glass fibre — Polymaker's grade is 25 wt%[1][2]PETG regranulated from recycled polyester waste; Polymaker's Fiberon PETG-rCF08 adds 8 wt% recycled carbon fibre[3][4][5]
Densityg/cm³1.14 (Bambu Lab) and 1.20 (Polymaker Fiberon), ISO 1183[2][1]1.27 (Prusament) and 1.30 (Fiberon PETG-rCF08), ISO 1183[3][5]
Typical priceUSD/kg1 kg-equivalent spools span 40–130; the middle of the market is about 60[2][6][7]1 kg spools cluster near 29[8][9][6][10]
Price range across brandsUSD/kg40–130 across brands; SUNLU 40, YXPOLYER 45, Polymaker Fiberon and Bambu Lab 60, 3DXTech FibreX 87, Obsidian Nylon 6+GF 130[6][2][8][7][11]17–40 across brands; Filament PM RePETG 17, 3DXTech ECOMAX 26, GreenGate3D 32, Fiberon rCF08 40[8][9][6][10]
Market availability1–5Stocked by most mainstream brands[2][6][8][7][11]Available from several mainstream brands[8][9][6]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75 and 1 kg spools[6][8][2]1.75 and 2.85 mm; 0.5, 1 and 3 kg spools[6][9]
Typical applicationsStiff, heat-resistant structural parts where a matte finish and lower cost beat carbon fibre[2][1]Not documented
Diameter tolerance± mmNot documented±0.05 (Prusament PETG Recycled), against ±0.02 for virgin Prusament PETG[3][12]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[2]250 ± 10 (Prusament); 230–255 (Spectrum)[3][4]
Bed temperature°CNot documented80 ± 10 (Prusament); 60–80 (Spectrum)[3][4]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[2]Open frame is fine — Spectrum states a closed chamber is not necessary[4]
Recommended chamber temperature°C45–60 (Bambu Lab)[2]Not documented
Part cooling fanNot documented50 % (Prusament); up to 100 % (Spectrum)[3][4]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[13][14]Textured PEI, satin or powder-coated sheets; on smooth PEI a glue stick acts as a release agent[12][15]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s10 at Bambu Lab's 130 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][16]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[13]Needs the right surface or a thin adhesive — the problem is releasing the part, not sticking it[12][15]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[14]Moderate — retraction tuning needed; Polymaker names stringing as PETG's common quirk[15]
Overall printing difficulty1–5Expert / industrial hardware only[2][17]Easy — minor profile tuning; Spectrum describes printing as similar to standard PETG[4]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[2]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA6-GF25 and recommends hardened steel or ruby[1]Brass fine indefinitely[3]
Abrasiveness1–5Highly abrasive — standard GF composite; Polymaker puts brass nozzle life at roughly 9 h on PA6-GF25[1]Not documented
Nozzle clog risk1–5Very high — frequent jams without careful setup[17]Low — recycled PETG prints on the same hardware as virgin PETG: no special hot-end, no drybox and no hardened nozzle[18][19]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[13]Slightly sensitive[18]
Hotend requirementMay require an all-metal hot end (Simplify3D)[13]No special hot-end required[18]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Very high (>2 %) — 2.56 % saturated at 25 °C / 55 % RH (Bambu Lab) and 3.33 % equilibrium (Polymaker Fiberon), the highest in the dataset[2][1]Moderate (0.3–0.8 %) — recycled PETG shares the virgin matrix, which reaches 0.40 % saturated at 25 °C / 55 % RH[12]
Equilibrium moisture content at ~50 % RH%2.56 saturated at 25 °C / 55 % RH (Bambu Lab); 3.33 equilibrium (Polymaker Fiberon PA6-GF25)[2][1]0.07 after 24 h and 0.10 after 7 days at 24 °C / 22 % RH (Prusa Polymers)[3]
Drying temperature & time80 °C for 8–12 h (Bambu Lab)[2]Not documented
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[20]Bubbling and popping at the nozzle, stringing and a rough surface[17]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA6-GF25 itself: at 4.57 % moisture tensile falls 80.1 → 40.2 MPa and modulus 5357 → 1794 MPa, while notched Charpy rises 10.0 → 28.0 kJ/m²[1][20]Polymaker groups PETG with nylon, PVA and TPU as highly hygroscopic; no dry-versus-conditioned strength figures are published for this grade and the loss shows as bubbling and poor layer adhesion[17]
Storage requirementSealed below 20 % RH with desiccant[17]Sealed with desiccant; Polymaker groups PETG with the highly hygroscopic materials[17][15]
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[21][22]Not documented
Mechanical Properties
Tensile strength (XY)MPa75 ± 6 (Bambu Lab) and 80.1 ± 1.8 (Polymaker Fiberon, dry/annealed) printed XY, ISO 527; Fiberon falls to 40.2 ± 2.1 conditioned to 4.57 % moisture. Stratasys FDM PA6/66-GF30-FR gives 60.2-61.1 at break and 61.7-62.3 at yield printed XZ (ASTM D638)[2][1][23]43 ± 1.8 printed horizontal at yield, ISO 527-1 (Prusament), against 47 ± 2 for virgin Prusament PETG; Spectrum quotes 52 at yield on moulded specimens[3][12][4]
Young's modulusMPa2850 ± 260 (Bambu Lab) and 5357 ± 211 (Polymaker Fiberon, dry) printed XY, ISO 527; Fiberon falls to 1794 ± 84 conditioned. Stratasys FDM PA6/66-GF30-FR gives 5600-5830 printed XZ against 3050-3140 in ZX (ASTM D638)[2][1][23]1500 printed horizontal, 1600 printed vertical (Prusament, ISO 527-1) — the same as virgin Prusament PETG[3][12]
Elongation at break%2.4 ± 0.2 dry (Polymaker Fiberon) to 3.9 ± 0.8 (Bambu Lab) printed XY, ISO 527; the Fiberon grade rises to 4.2 ± 0.7 conditioned[2][1]4.5 at yield printed (Prusament); Spectrum quotes 400 at break on moulded specimens[3][4]
Flexural strengthMPaNot documented63 ± 1 printed horizontal, ISO 178 (Prusament), against 66 ± 2 for virgin Prusament PETG[3][12]
Flexural modulusMPa3670 ± 140 printed XY, ISO 178 (Bambu Lab)[2]1800 printed horizontal, ISO 178 (Prusament)[3]
Charpy impact, notchedkJ/m²10.0 ± 0.7 printed XY dry and 28.0 ± 1.0 conditioned, ISO 179 notched (Polymaker Fiberon); Bambu Lab 7.2 ± 2.3[1][2]12 ± 1 printed horizontal and 15 ± 3 printed vertical, ISO 179-1 notched (Prusament)[3]
Other impact dataCharpy unnotched 27.2 ± 2.2 printed XY (Bambu Lab, ISO 179). Stratasys FDM PA6/66-GF30-FR gives Izod notched 74.6-77.1 J/m printed XZ against 17.2-22.1 in ZX (ASTM D256)[2][23]Charpy unnotched 25 ± 3 printed horizontal and 38 ± 11 printed vertical (Prusament, ISO 179-1)[3]
Layer adhesion / Z tensileMPa27 ± 5 (Bambu Lab) and 60.7 ± 1.1 (Polymaker Fiberon, dry) printed Z, ISO 527 — the two makers differ by more than a factor of two; Fiberon falls to 26.3 ± 1.5 conditioned. Stratasys FDM PA6/66-GF30-FR gives 23.7-24.4 at break printed ZX (ASTM D638)[2][1][23]15 ± 5 (Prusa Polymers interlayer adhesion test), against 18 ± 4 for virgin Prusament PETG[3][12]
Brittleness1–5Brittle — snaps with little warning; elongation at break 2.4 % in XY[1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785)[24]74 Shore D (Prusa Polymers method) — the same as virgin Prusament PETG[3][12]
Creep resistance / sustained load1–5Good. Ensinger lists high creep resistance as a headline property of extruded PA66-GF30 stock; the rating is held below Excellent because equilibrium moisture uptake of 3.33 % softens the matrix in service[24][1]Below average — no recycled-grade creep test; virgin PETG sagged from 12 to 17.1–20.4 mm over 5 days at 1.25 kg[25][26][27][28]
Fatigue / repeated-flex resistance1–5Good. Ensinger lists high fatigue strength as a headline property of extruded PA66-GF30 stock[24]Moderate — no recycled-grade S-N curve; virgin printed PETG ran 79 000–193 000 cycles at 30 % of tensile strength[29]
Elasticity / flexibility1–5Rigid[2]Slightly flexible in thin sections[3]
Z strength as % of XY%36 (Bambu Lab) to 76 (Polymaker Fiberon), printed; Stratasys FDM PA6/66-GF30-FR gives 39-41 (ZX against XZ tensile at break, ASTM D638)[2][1][23]Not documented
Thermal Properties
HDT at 0.45 MPa°C182 (Bambu Lab) and 191 (Polymaker Fiberon), ISO 75 at 0.45 MPa. Stratasys FDM PA6/66-GF30-FR gives 161 printed XY and 185 XZ (ASTM D648 at 66 psi)[2][1][23]68 (ISO 75, 0.45 MPa) — the same as virgin Prusament PETG; Spectrum quotes 70[3][12][4]
HDT at 1.8 MPa°C157 (Polymaker Fiberon) and 158 (Bambu Lab), ISO 75 at 1.8 MPa[2][1]68 (ISO 75, 1.8 MPa)[3]
Glass transition (Tg)°C67 (Bambu Lab) and 70.4 (Polymaker Fiberon), DSC; Stratasys measures 51.5 on FDM PA6/66-GF30-FR (ASTM D7426)[2][1][23]Not documented
Melting point / Vicat°C214.5 (Polymaker Fiberon) and 219 (Bambu Lab) melting, DSC; Vicat 210–212 (ISO 306)[2][1]Not documented
Thermal expansion (CTE)µm/m·K48.6 on extruded PA66-GF30 stock (ASTM D696; source states 2.7e-5 in/in/°F). Stratasys measures much higher on printed FDM PA6/66-GF30-FR — 95.4 over -20 to 5 °C and 214 over 25 to 80 °C in XY (ASTM E831)[24][23]Not documented
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[21]Flammable; no UL 94 rating published for standard grades[30]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[14]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[14]Withstands acids, alkalis, oils and UV exposure[15]
Water / humidity resistance in service1–5Absorbs water, properties shift[20]Not documented
Food contactNot food-contact certified as filament[14]Not certified for food contact as filament[15]
Biodegradability / compostabilityNot biodegradable[14]Not biodegradable[15]
RecyclabilityNot accepted in household plastic collection[14]The feedstock itself — Spectrum describes collecting, shredding and re-homogenising PETG waste[4]
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker Fiberon, ANSI/ESD S11.11)[1]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[31]Moderate — measurable VOCs and UFPs, ventilation advised[31]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[31]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[31]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[31]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[31]Open a window / occasional ventilation[31]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Not documented
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[13]Sands poorly — the material is tough and gums rather than powders[18]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[13]Cyanoacrylate; no common solvent welds PETG cleanly[18]
Vapour / chemical smoothingNo practical vapour smoothing[13]No practical vapour smoothing[18]
Support material pairingNot documentedPrints its own supports; Polymaker rates PolyDissolve S1 for PETG[18]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[32]No common workshop solvent; 1,2-dichloroethane destroys it inside a week and dichloromethane — a carcinogen — dissolves the surface.[33][34]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[32]Acetone (+16 % weight over 1 year at 23 °C), ethyl acetate, toluene and DMF swell and soften it; methanol crazes it.[33]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[32]Dichloromethane brushed on is the only agent that smooths PETG — a controlled carcinogen, not workshop stock.[34]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  2. Bambu Filament Technical Data Sheet — PA6-GF Bambu Lab · 2026-08 · tds
  3. Prusament PETG Recycled Technical Datasheet Prusa Polymers · 2026-08 · tds
  4. Spectrum r-PETG Technical Data Sheet Spectrum Filaments · 2026-08 · tds
  5. Fiberon PETG-rCF08 Technical Data Sheet V1.0 Polymaker · 2026-08 · tds
  6. Polymaker product catalogue Polymaker · 2026-08 · vendor
  7. SUNLU Nylon-6 Glass Fiber (PA6-GF) 3D Printer Filament 1 kg — product page SUNLU · 2026-08 · vendor
  8. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  9. GreenGate3D Recycled PET-G — product data GreenGate3D · 2026-08 · vendor
  10. Filament PM RePETG technical data sheet Filament PM (Plasty Mladec) · 2026-08 · tds
  11. YXPOLYER PA6-GF Black 1 kg — product page YXPOLYER · 2026-08 · vendor
  12. Prusament PETG Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  13. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  14. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  15. PETG — material basics Polymaker Wiki · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  18. PET and PETG — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  19. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  20. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  21. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  22. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  23. FDM PA6/66-GF30-FR — Material Data Sheet Stratasys · 2026-07 · tds
  24. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  25. PCTG vs PETG comparison — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. Extrudr PETG vs PCTG vs XPETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  27. Prusament PETG-CF vs PETG V0 vs PETG — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  28. BambuLab PETG Basic vs Translucent vs PETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  29. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  30. Prusament PETG V0 Technical Datasheet Prusa Polymers · 2026-08 · tds
  31. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  32. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  33. Eastman Spectar copolyester — Chemical resistance (unstressed bars, 1 year at 23 °C) Eastman Chemical Company · 2026-08 · tds
  34. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc