PA blend vs PC-ESD

Compare printing settings, strength, heat resistance, dated prices and sources.

PA6/66 copolymer blends guideESD-safe PC guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA blend comparisonsMore PC-ESD comparisons
PA blend vs PC-ESD — documented properties and sources
PropertyPA6/66 copolymer blendsPAESD-safe PCPC
Market snapshot
Listing priceUSD/kg; dated snapshots$65.62/kg median; $62.00–$113.33/kg across 4 dated product listings$180.00/kg median; $180.00–$180.00/kg across 1 dated product listings
Identity & Market
Base polymer / chemistryPA6/66 copolymer — a nylon alloy that lowers the melting point and improves printability against straight PA6[1][2]Polycarbonate compounded with a conductive filler for static-dissipative parts[3]
Densityg/cm³1.12 (ISO 1183, Polymaker CoPA)[1]1.24 (ISO 1183, 3DXTech); Stratasys specific gravity 1.195 (ASTM D792)[3][4]
Typical priceUSD/kg1 kg-equivalent spools cluster near 65[5][6][7]1 kg-equivalent spools cluster near 180[8]
Price range across brandsUSD/kg62–113 across brands; add:north Adura 62, PrimaCreator NylonPower PA6/66 65 at 500 g, Polymaker CoPA 67, 3DXTech AmideX Nylon 6-66 113[5][8][6][7]180 at 3DXTech's 750 g pricing — the most expensive material in this group[8]
Market availability1–5Available from several mainstream brands[5][8]Special order, 1–2 makers worldwide[8]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75 and 1 kg spools[5][8][6][7]1.75 and 2.85 mm; 750 g spools plus Stratasys-compatible cartridges[8]
Typical applicationsGeneral-purpose nylon parts and, unusually, CoPA can support itself if the support is removed before it absorbs moisture[1]Electronics fixtures and trays that need PC heat resistance and static dissipation together[3]
Printing Parameters
Nozzle temperature°C250–270 (Polymaker CoPA)[1]Not documented
Bed temperature°C25–50 (Polymaker CoPA)[1]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive) — Polymaker specifies a chamber at ambient temperature[1]Enclosure required (passive)[9][10]
Bed surface & adhesion aidNot documentedPEI with a glue stick or a commercial adhesive[11]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s16 at Polymaker's 200 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][12]Not documented
Warping tendency1–5Not documentedSevere — heated chamber needed[9][10]
Bed-adhesion difficulty1–5Not documentedNeeds a specific surface plus adhesive[11][13]
Stringing / oozing tendency1–5Not documentedModerate — retraction tuning needed; Polymaker flags stringing as a common PC problem[13]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning; must be kept below 20 % RH throughout[1][14]Advanced — enclosure, hardware upgrades, tuning[9]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades[15]Hardened steel required[3]
Abrasiveness1–5Non-abrasive when unfilled[15]Moderately abrasive — conductive carbon filler[3]
Nozzle clog risk1–5Very high — frequent jams without careful setup[16][14]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a 120 °C pre-dry[17]
Heat-creep / jam sensitivity1–5Not documentedSlightly sensitive[11]
Hotend requirementNot documentedAll-metal hot end required (Simplify3D)[11]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Very high (>2 %) — Polymaker's own wet-state specimens reached 6.16 % moisture content after 48 h immersion at 60 °C[1][14]Low (0.1–0.3 %) — the PC matrix takes up 0.15–0.25 % and 3DXTech specifies a 120 °C, 4 h pre-dry[18][19][17]
Drying temperature & time100 °C for 8 h (Polymaker CoPA)[1]Not documented
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[16]Bubbling and popping at the nozzle, stringing and a rough surface[14]
Effect of moisture on strengthMeasured dry against wet on printed specimens at 6.16 % moisture (Polymaker CoPA): tensile 78.0 → 34.3 MPa, Young's modulus 2703 → 724 MPa, flexural strength 109.8 → 22.6 MPa, while notched Charpy rises 6.9 → 27.7 kJ/m² and elongation 12.7 → 13.2 %[1][16]No dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[13][14]
Storage requirementPolymaker states CoPA must always be stored and used below 20 % relative humidity[1]Airtight containers with desiccant to prevent reabsorption[13]
Hydrolysis at melt temperaturePolymaker requires a 100 °C dry for 8 h and storage below 20 % RH; no molecular-weight loss figure is published, and the published wet data is conditioning rather than melt hydrolysis[1][20]Not documented
Mechanical Properties
Tensile strength (XY)MPa78.0 ± 0.7 printed XY dry and 34.3 ± 2.5 wet, ISO 527 (Polymaker CoPA)[1]68 at break (printed XY, ISO 527, 3DXTech) — above the 58 of 3DXTech's unfilled ezPC; Stratasys prints 47.6-49.4 at yield in XZ (ASTM D638)[3][21][4]
Young's modulusMPa2703 ± 259 printed XY dry and 724 ± 61 wet, ISO 527 (Polymaker CoPA)[1]2300 (printed XY, ISO 527); Stratasys prints 1960 in XZ and 1810-1910 in ZX (ASTM D638)[3][4]
Elongation at break%12.7 ± 2.1 printed XY dry and 13.2 ± 2.3 wet, ISO 527 (Polymaker CoPA)[1]6 at break (printed XY, ISO 527), against 14 for the unfilled grade[3][21]
Flexural strengthMPa109.8 ± 1.3 printed XY dry and 22.6 ± 0.5 wet, ISO 178 (Polymaker CoPA)[1]95 (printed XY, ISO 178); Stratasys prints 82.6-83.2 at break in XZ against 46.3-49.5 in ZX (ASTM D790)[3][4]
Flexural modulusMPa2510 ± 25 printed XY dry and 636 ± 11 wet, ISO 178 (Polymaker CoPA)[1]2310 (printed XY, ISO 178)[3]
Charpy impact, notchedkJ/m²6.9 ± 1.4 printed XY dry and 27.7 ± 1.2 wet, ISO 179 notched (Polymaker CoPA) — impact quadruples when conditioned[1]Not documented
Layer adhesion / Z tensileMPa45.8 ± 1.5 printed Z dry, falling to 13.7 ± 1.2 wet, ISO 527 (Polymaker CoPA)[1]32.5-37.9 at yield printed ZX (Stratasys, ASTM D638 on the Fortus 450mc and F900)[4]
Brittleness1–5Tough — absorbs impact, yields before breaking[1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 86 and Rockwell 85 (108) — the source does not name the scales on extruded unfilled PA66 stock (ASTM D2240, D785)[22]Rockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for an ESD grade[23]
Creep resistance / sustained load1–5Not documentedExcellent — holds load for years. Moulded unfilled PC was still running unbroken under 41 MPa tensile creep at room temperature when the test was stopped, and the conductive filler leaves the glass transition unchanged at 142 °C, so the creep mechanism is polycarbonate's[24][4]
Fatigue / repeated-flex resistance1–5Excellent — living hinges viable[15]Not documented
Elasticity / flexibility1–5Semi-flexible[16]Rigid[3]
Z strength as % of XY%59 dry (45.8 Z against 78.0 XY) and 40 wet, printed[1]68-77 (Stratasys ZX against XZ tensile yield, ASTM D638)[4]
Thermal Properties
HDT at 0.45 MPa°C111 (ISO 75, 0.45 MPa, Polymaker CoPA)[1]143-146 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 66 psi); 135 moulded[4]
HDT at 1.8 MPa°C70 (ISO 75, 1.8 MPa, Polymaker CoPA)[1]140-144 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 264 psi); 124 moulded[4]
Glass transition (Tg)°C66 (DSC, Polymaker CoPA)[1]143 (DSC, 3DXTech) and 142 (Stratasys, ASTM D7426)[3][4]
Melting point / Vicat°C189 melting (DSC); Vicat 180, crystallisation 148, decomposition 370 (Polymaker CoPA)[1]Not documented
Continuous service temperature°CNot documented113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[19]
Annealing response80 °C for 6 h (Polymaker CoPA)[1]Not documented
Thermal expansion (CTE)µm/m·K81.0 on extruded unfilled PA66 stock (ASTM D696; source states 4.5e-5 in/in/°F) — the same chemistry as a PA6/66 copolymer[22]68.4 on extruded unfilled PC stock (ASTM D696; source states 3.8e-5 in/in/°F); no figure is published for a conductive-filled grade[23]
Environment & Chemical
Chemical resistanceNot documentedWithstands oils, solvents and fuels; Polymaker rates it good against weak acids[13]
Water / humidity resistance in service1–5Absorbs water, properties shift — 6.16 % uptake cost 56 % of tensile strength and 73 % of modulus[1]Not documented
Food contactNot documentedBisphenol-A polycarbonate is not offered as food-contact filament[13]
Biodegradability / compostabilityNot documentedNot biodegradable[13]
RecyclabilityNot documentedMechanically recyclable but not accepted in household plastic collection[13]
Electrical & ESD propertiesNot documentedSurface resistance 10⁷–10⁹ ohm/sq, the static-dissipative band (ASTM D257), against above 10¹³ for unfilled ezPC[3][21]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[25]Moderate — measurable VOCs and UFPs, ventilation advised[25]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon; total VOC reached nearly 200 µg/min, the highest of the nine filaments tested[25]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median — low for ultrafine particles despite the highest VOC mass of any filament tested[25]≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[25]
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament — the largest single-VOC emission rate measured in the study[25]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[25]Ventilated room or enclosure recommended[25][9]
Dust & fibre handling hazardNot documentedConductive carbon filler is bound in the matrix; avoid inhaling sanding dust[3]
Post-Processing
Sanding & machiningNot documentedSands and machines well; the toughness means it cuts rather than chips[11]
Gluing & solvent weldingNot documentedCyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[11]
Vapour / chemical smoothingNot documentedNo practical vapour smoothing[11]
Support material pairingCoPA can support itself, but Polymaker warns the support bonds permanently if it absorbs moisture before removal[1]Prints its own supports; 3DXTech sells a dedicated PC break-away support[11]
Solvents & Solubility
Soluble inDissolved at 23 °C by formic acid above ~50 %, phenol, m-cresol, 96 % sulphuric acid or hexafluoroisopropanol — laboratory reagents.[26]Dichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[27]
Softened or crazed byZinc chloride solutions stress-crack it — 10 % marginal, 37 % not resistant; alcoholic calcium chloride dissolves it.[26]Methanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[27]
Solvent welding & smoothing agentNone — nylon's only solvents are formic acid, phenol and HFIP, all of which degrade the part they wet.[26]Dichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[28]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  2. AmideX Nylon 6-66 — product page 3DXTech · 2026-08 · vendor
  3. 3DXSTAT ESD-PC Technical Data Sheet 3DXTech · 2026-08 · tds
  4. PC-ESD — FDM Material Data Sheet Stratasys · 2024-10 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. add:north Adura product page add:north · 2026-08 · vendor
  7. PrimaCreator SELECT NylonPower PA6/66 product page PrimaCreator · 2026-08 · vendor
  8. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  9. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  10. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  11. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  12. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  13. PC — material basics Polymaker Wiki · 2026-08 · doc
  14. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  15. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  16. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  17. 3DXSTAT ESD-PC — product page (print recommendations) 3DXTech · 2026-08 · doc
  18. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  19. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  20. PolyMide CoPA — Technical Data Sheet page Polymaker Wiki · 2026-08 · tds
  21. ezPC Polycarbonate Technical Data Sheet 3DXTech · 2026-08 · tds
  22. TECAMID 66 natural (PA66) — stock shape properties Ensinger · 2026-08 · tds
  23. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  24. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  25. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  26. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  27. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  28. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds