LW-PLA vs PEI 9085

Compare printing settings, strength, heat resistance, dated prices and sources.

Lightweight / foaming PLA (LW-PLA) guidePEI (ULTEM 9085) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore LW-PLA comparisonsMore PEI 9085 comparisons
LW-PLA vs PEI 9085 — documented properties and sources
PropertyLightweight / foaming PLA (LW-PLA)PLAPEI (ULTEM 9085)HIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$47.48/kg median; $37.49–$50.00/kg across 4 dated product listings$309.80/kg median; $220.00–$392.00/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryPLA with a blowing agent. Two distinct types: active-foaming grades that expand at the nozzle (Bambu Lab PLA Aero, colorFabb LW-PLA) and pre-foamed grades that do not (Polymaker PolyLite LW-PLA, PolyWood)[1][2][3][4]Polyetherimide, ULTEM 9085 grade — the flame-retardant PEI used for aircraft interiors[5]
Densityg/cm³Filament 1.21 (Bambu Lab) and 1.24 (colorFabb); pre-foamed filament 0.8 (PolyWood, at 21.5 °C) and 0.9 (Polymaker LW-PLA); foamed prints reach 0.40[1][2][3][4]1.34 (ISO 1183, 3DXTech) against 1.27 specific gravity on moulded plaques (ASTM D792, Stratasys) — the two suppliers disagree[5][6]
Typical priceUSD/kg1 kg-equivalent spools cluster near 45[7][2][8]1 kg-equivalent spools cluster near 298[9][10][11][12]
Price range across brandsUSD/kg37–50 across brands; Polymaker LW-PLA 37, Bambu Lab Aero 45, colorFabb 50, PolyWood 50[8][7][2]220-392 across brands and formats; 3DXTech ThermaX PEI 9085 220 at 2 kg, 3D4Makers 270 at 2 kg, Fiberlogy 298 at 500 g, Kimya 321 at 500 g, IEMAI 3D 385 at 1 kg, 3DXTech CarbonX PEI 9085+CF 392[9][10][11][12][13]
Market availability1–5Available from several mainstream brands[7][8][2]Niche, a handful of specialist brands[9][10][11][12]
Spool sizes & diameters1.75 and 2.85 mm; 0.6, 0.75, 0.8 and 1 kg spools[8][2]1.75 and 2.85 mm; 250 g to 2 kg spools, plus Stratasys canisters[9][12][6]
Typical applicationsRC aircraft, drone airframes and large props where mass matters more than strength[1][2]Aircraft interior parts and rail rolling stock, where the flame, smoke and toxicity rating is the requirement[5]
Printing Parameters
Nozzle temperature°C210–260 (Bambu Lab, foaming); 195–260 (colorFabb, foaming); 190–210 (Polymaker, pre-foamed)[1][2][3]Not documented
Bed temperature°C35–45 (Bambu Lab); 50–60 (colorFabb); 25–60 (Polymaker)[1][2][3]130–140 (3DXTech)[5]
Enclosure / chamber requirement1–5Open frame is fine[3]Actively heated chamber required[14][15]
Part cooling fanFan on[1][3]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s3.2–8 at the 40–100 mm/s colorFabb specifies and the 50–100 mm/s Polymaker specifies, on a 0.4 mm nozzle at 0.2 mm layer[3][2][16]Not documented
Warping tendency1–5Not documentedSevere — heated chamber needed[14]
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; flow has to be cut to match the expansion[2]Expert / industrial hardware only[14][15]
Extruder requirementBambu Lab PLA Aero is 0.4 mm nozzle only on the store and wiki, while its own TDS lists 0.4, 0.6 and 0.8[1][17]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[3][4]Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[14]
Abrasiveness1–5Non-abrasive[3][4]Non-abrasive when unfilled[5]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles; Bambu Lab warns the foamed extrudate swells and easily clogs the nozzle, and rules out 0.2 mm nozzles[17]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[18]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.45 % saturated at 25 °C / 55 % RH (Bambu Lab); 0.40 % equilibrium (Polymaker)[1][3]Not documented
Equilibrium moisture content at ~50 % RH%0.45 saturated at 25 °C / 55 % RH (Bambu Lab); 0.40 equilibrium (Polymaker)[1][3]Not documented
Drying temperature & time55 °C for 6–8 h[1][3]Not documented
Effect of moisture on strengthPolymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[19]No dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[18]
Mechanical Properties
Tensile strength (XY)MPa24 ± 2 (Bambu Lab) and 24.4 (Polymaker) printed XY, ISO 527; colorFabb falls from 43.1 unfoamed to 10.8 at 45 % flow[1][3][2]63-77 at break (printed XZ, ASTM D638, Stratasys F900/F3300/Fortus 450mc, three tips and two colours); 54 (printed XY, ISO 527, 3DXTech)[6][5]
Young's modulusMPa1350 ± 250 (Bambu Lab) and 1689 (Polymaker) printed XY, ISO 527; colorFabb falls from 3334 unfoamed to 864 foamed[1][3][2]2040-2540 (printed XZ, ASTM D638, Stratasys); 2050 (printed XY, ISO 527, 3DXTech)[6][5]
Elongation at break%2.6 ± 0.7 (Bambu Lab) and 8.8 (Polymaker) printed XY, ISO 527[1][3]5.4-9.1 at break (printed XZ, ASTM D638, Stratasys); 1.9-4.3 in ZX; 3DXTech quotes 3 (ISO 527)[6][5]
Flexural strengthMPa45 ± 4 (Bambu Lab) and 50.2 (Polymaker) printed XY, ISO 178[1][3]104-116 at break (printed XZ, ASTM D790 Procedure A, Stratasys); 72-98 in ZX; 3DXTech quotes 90 (ISO 178)[6][5]
Flexural modulusMPa1690 ± 120 (Bambu Lab) and 1959 (Polymaker) printed XY, ISO 178[1][3]2400-2550 (printed XZ, ASTM D790, Stratasys F900 T16 and T16A) against 2120-2130 in ZX; 3DXTech quotes 2170 (ISO 178)[6][5]
Charpy impact, notchedkJ/m²8.2 ± 0.7 printed XY, ISO 179, notched (Bambu Lab); colorFabb 3.67 foamed[1][2]Not documented
Other impact dataCharpy unnotched 28.8 printed XY (Bambu Lab); colorFabb 5.46 foamed[1][2]Izod notched 88.5-140 J/m XZ against 37-80 J/m ZX; unnotched 647-2260 J/m XZ against 169-633 J/m ZX (printed, ASTM D256/D4812, Stratasys, across three printers and three tips)[6]
Layer adhesion / Z tensileMPa18 ± 3 printed Z, ISO 527 (Bambu Lab); flexural Z collapses to 17 against 45 in XY[1]39-63 at break (printed ZX, ASTM D638, Stratasys); the low end is the F900 T16 baseline, the high end the F3300 N500 hot end[6]
Brittleness1–5Brittle — snaps with little warning; elongation at break 2.6 % in XY and 1.2 % in Z[1]Brittle — snaps with little warning[5]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell M110 / R126 on extruded PEI stock (ASTM D785)[20]
Creep resistance / sustained load1–5Poor — no foamed-grade creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg, and the foam carries less solid[21][22][23]Excellent — holds load for years. Printed ZX coupons keep 87 % of room-temperature tensile strength at 104 °C and 70 % at 132 °C (ASTM D638); extruded PEI stock is rated 170 °C long-term service[6][20]
Fatigue / repeated-flex resistance1–5Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and elongation at break falls to 2.6 % in XY and 1.2 % in Z[24][1]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[5]
Z strength as % of XY%75 by tensile, 38 by flexural (printed, Bambu Lab)[1]56-86 (Stratasys ZX against XZ tensile at break, ASTM D638, across F900/F3300/Fortus 450mc and T16/T20/T40A tips); 58 on the F900 T16 baseline[6]
Thermal Properties
HDT at 0.45 MPa°C53 (Bambu Lab) and 54 (Polymaker), ISO 75 at 0.45 MPa[1][3]158 (printed XY, ISO 75 at 0.45 MPa, 3DXTech) to 178 (printed XY 178.2 and ZX 178.4, ASTM D648 Method B at 66 psi, Stratasys); moulded 176.9[5][6]
HDT at 1.8 MPa°C48 (Bambu Lab) and 50 (Polymaker), ISO 75 at 1.8 MPa[1][3]170-173 (printed XY 170.2 and ZX 172.6, ASTM D648 Method B at 264 psi); moulded 172.9[6]
Glass transition (Tg)°C55 (Bambu Lab) and 59 (Polymaker), DSC[1][3]177 (moulded plaque, ASTM D7426 inflection point, Stratasys); 186 (DSC, 3DXTech)[6][5][25]
Melting point / Vicat°C150 peak melt (Polymaker, DSC); Vicat 60 °C[3]Not documented
Continuous service temperature°CNot documented170 long-term service on extruded PEI stock, converted from 338 °F; 200 short term[20]
Annealing responseBambu Lab advises against annealing thin, low-infill Aero prints[1]Not documented
Thermal expansion (CTE)µm/m·KNot documented44.9 (printed XY, -50 to 80 °C, ASTM E831), falling to 31.4 over 80-160 °C; ZX gives 44.5 over -50 to 60 °C. Black pigment raises it to 51.9[6]
Flammability / UL 94Not documentedUL 94 V-0 at 1.5 mm on the base resin. Printed parts are tested to 14 CFR 25.853, BSS 7238 and 7239 and AITM 2.0007B and 3.0005 covering 60 s and 12 s vertical burn, 15 s horizontal burn, smoke density, toxic gas emission and OSU heat release[5][6]
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors[26]Good — years with some colour shift. 1000 h of QUV cycling to ASTM G154 left printed ZX coupons at 55.5 MPa yield against 56.0 unexposed, with elongation and modulus unchanged[6]
Health & Safety
Fume toxicity1–5Low hazard — minimal VOC and particle emission[27]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[27]
Ventilation / filtration requirement1–5None needed in a normal room[27]Ventilated room or enclosure recommended[27]
Post-Processing
Dimensional accuracy & detailFoamed surfaces are rough and matte; dimensional accuracy depends on holding the foaming temperature steady[1][2]Not documented
Solvents & Solubility
Soluble inChloroform dissolves the PLA matrix; the foamed wall wicks solvent right through instead of only skinning over.[28]Chlorinated hydrocarbons — dichloromethane and chloroform — are solvents for polyetherimide. Laboratory reagents.[29][30]
Softened or crazed byAcetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[28][31]Acetone, MEK, benzene, toluene and butyl acetate craze or stress-crack it; alcohols, fuels and dilute acids do not.[30][29]
Solvent welding & smoothing agentChloroform vapour reaches only the resin skin; no workshop-safe smoothing agent exists for PLA of any kind.[32][31]Dichloromethane is the only welding route, and it is a controlled carcinogen rather than a workshop material.[29][30]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet V4.0 — PLA Aero Bambu Lab · 2026-08 · tds
  2. LW-PLA technical data sheet colorFabb · 2026-08 · tds
  3. PolyLite LW-PLA Technical Data Sheet (V7.0) Polymaker · 2026-08 · tds
  4. PolyWood Technical Data Sheet Version 4.0 (Nov 2018) Polymaker (copy hosted by 3Dee) · 2018-11 · tds
  5. ThermaX PEI 9085 Technical Data Sheet v4 3DXTech · 2026-08 · tds
  6. ULTEM 9085 Resin — FDM Material Data Sheet Stratasys · 2026-04 · tds
  7. PLA Aero — product page Bambu Lab US Store · 2026-08 · vendor
  8. Polymaker product catalogue Polymaker · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. Kimya PEI-9085 Natural 2.85 mm 500 g igo3d · 2026-08 · vendor
  11. Fiberlogy PEI 9085 Natural, 1.75 mm / 500 g 3DJAKE · 2026-08 · vendor
  12. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  13. IEMAI 3D PEI 9085 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  14. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  15. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. PLA Usage Guide Bambu Lab Wiki · 2026-08 · doc
  18. THERMAX PEI 9085 — product page (print recommendations) 3DXTech · 2026-08 · doc
  19. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  20. TECAPEI natural (PEI) — stock shape properties Ensinger · 2026-08 · tds
  21. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  22. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  23. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  24. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  25. ThermaX PEI 1010 Technical Data Sheet v4 3DXTech · 2026-08 · tds
  26. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  27. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  28. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  29. Radel PPSU, Veradel PESU, Acudel modified PPSU Design Guide — environmental stress cracking tables Solvay Specialty Polymers · 2026-08 · tds
  30. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  31. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  32. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper