3D Printing Info

Filament comparison

ASA-CF vs PC-ABS

Compare printing settings, strength, heat resistance, dated prices and sources.

Carbon-fibre ASA (ASA-CF) guidePC/ABS blend guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ASA-CF comparisonsMore PC-ABS comparisons
ASA-CF vs PC-ABS — documented properties and sources
PropertyCarbon-fibre ASA (ASA-CF)ASAPC/ABS blendPC
Market snapshot
Listing priceUSD/kg; dated snapshots$36.99/kg median; $25.00–$90.00/kg across 5 dated product listings$45.99/kg median; $34.99–$84.00/kg across 5 dated product listings
Identity & Market
Base polymer / chemistryASA reinforced with chopped carbon fibre — Formfutura's ApolloX CF10 is 10 wt%[1][2][3]Polycarbonate/ABS alloy — PC stiffness and heat resistance with ABS processability[4][5]
Densityg/cm³1.02 (Bambu Lab), 1.1 (Formfutura ApolloX CF10) and 1.11 (3DXTech), ISO 1183[1][2][3]1.10 (Polymaker) and 1.24 (3DXTech FR grade), ISO 1183; Stratasys specific gravity 1.10 (ASTM D792)[4][5][6]
Typical priceUSD/kg1 kg spools cluster near 37[7][8]1 kg spools cluster near 50[8][9]
Price range across brandsUSD/kg25–90 across brands; IEMAI 25, Ambrosia 33, Bambu Lab 37, Polymaker Fiberon 40, 3DXTech 90[10][7][8][9][11]35–84 across brands; Reli3D 35, SUNLU 46, Polymaker 50, 3DXMAX 84[8][9][12][13]
Market availability1–5Available from several mainstream brands[7][8][9][10]Available from several mainstream brands[8][9]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75 and 1 kg spools[8][9][7]1.75 and 2.85 mm; 0.5 and 1 kg spools[8][9]
Typical applicationsOutdoor structural parts, drone and antenna mounts where stiffness and UV stability both matter[1][2]Automotive interior and electronics housings that need PC heat resistance without PC's warping[4]
Printing Parameters
Nozzle temperature°C250–280 (Bambu Lab)[1]250–270 (Polymaker)[4]
Bed temperature°C80–100 (Bambu Lab)[1]90–105 (Polymaker)[4]
Enclosure / chamber requirement1–5Enclosure recommended — Bambu Lab specifies a 45–60 °C chamber[1][14]Enclosure required (passive) — Polymaker specifies a 90–100 °C chamber[4]
Recommended chamber temperature°C45–60 (Bambu Lab)[1]90–100 (Polymaker)[4]
Part cooling fanFan on (Bambu Lab)[1]Off (Polymaker)[4]
Bed surface & adhesion aidPEI sheet, BuildTak or an adhesion aid such as Magigoo (Polymaker); Simplify3D also lists Kapton tape and ASA slurry[15][16]PEI with a glue stick or a commercial adhesive[17]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s20 at Bambu Lab's 250 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][18]20 at Polymaker's 250 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[4][18]
Warping tendency1–5Moderate — needs adhesion aid or draught shield; the fibre reduces warping against unfilled ASA[14]High — enclosure needed for reliable large parts[4][14]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[15]Needs a specific surface plus adhesive[17][19]
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[15]Moderate — retraction tuning needed; Polymaker flags stringing as a common PC problem[19]
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[14]Advanced — enclosure, hardware upgrades, tuning[4][14]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[14]Brass fine indefinitely[14]
Abrasiveness1–5Highly abrasive — standard CF composite[14]Non-abrasive[4]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for fibre-filled composites and Simplify3D a higher tendency to clog[20][21]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a 120 °C pre-dry of 4 h or more[22]
Heat-creep / jam sensitivity1–5Slightly sensitive[16]Slightly sensitive[17]
Hotend requirementNo special hotend required[16]All-metal hot end required (Simplify3D)[17]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.33 % saturated at 25 °C / 55 % RH (Bambu Lab)[1]Low (0.1–0.3 %) — the PC matrix takes up 0.15–0.25 % and 3DXTech specifies a 120 °C, 4 h or more pre-dry[23][24][22]
Equilibrium moisture content at ~50 % RH%0.33 saturated at 25 °C / 55 % RH (Bambu Lab)[1]Not documented
Drying temperature & time80 °C for 8 h (Bambu Lab)[1]75 °C for 6 h (Polymaker)[4]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[25]Bubbling and popping at the nozzle, stringing and a rough surface[25]
Effect of moisture on strengthNo dry-versus-conditioned figures are published; Polymaker groups the styrenics as moderate-sensitivity and absorbed water shows as bubbling and poor layer adhesion[25]No dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[19][25]
Storage requirementSealed with desiccant; Polymaker rates the styrenics moderate-sensitivity[25]Airtight containers with desiccant to prevent reabsorption[19]
Mechanical Properties
Tensile strength (XY)MPa34 ± 3 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 48 at break and Formfutura 79 at 23 °C[1][2][3]39.9 ± 1.0 printed XY, ISO 527 (Polymaker); 3DXTech quotes 60 at break for its FR PC/ABS[4][5]
Young's modulusMPa4200 ± 270 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 5355 and Formfutura 7580[1][2][3]1835 ± 65 printed XY, ISO 527 (Polymaker); 3DXTech quotes 2250[4][5]
Elongation at break%9.6 ± 1.4 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 3 at break and Formfutura 1.8[1][2][3]4.2 ± 0.3 printed XY, ISO 527 (Polymaker); 3DXTech quotes 10 at break[4][5]
Flexural strengthMPa72 ± 5 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 78[1][2]66.3 ± 0.9 printed XY, ISO 178 (Polymaker); 3DXTech quotes 85[4][5]
Flexural modulusMPa3740 ± 130 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 5210[1][2]2081 ± 106 printed XY, ISO 178 (Polymaker); 3DXTech quotes 2300[4][5]
Charpy impact, notchedkJ/m²6.2 ± 1.4 printed XY, ISO 179, notched (Bambu Lab) — a third of unfilled Bambu Lab ASA's 19.6[1][26]25.8 ± 1.3 printed XY, ISO 179, notched (Polymaker) — above both unfilled PC and ABS[4]
Other impact dataCharpy unnotched 14.0 ± 2.2 printed XY (Bambu Lab, ISO 179), against 41.0 for unfilled Bambu Lab ASA[1][26]Notched Charpy still 13 ± 2 kJ/m² at −30 °C printed XY (Polymaker, ISO 179-1/1eA), against 1.5 in Z. Stratasys prints Izod notched at 241 J/m XZ against 34.0 J/m ZX, and unnotched 655 against 101 J/m (ASTM D256, F900 T16).[4][6]
Layer adhesion / Z tensileMPa30 ± 4 printed Z, ISO 527 (Bambu Lab); flexural Z falls to 33 against 72 in XY[1]25.9-30.2 at break printed ZX (Stratasys, ASTM D638 on the F900 and Fortus 450mc); 22.9 +/- 1.2 printed Z, ISO 527 (Polymaker)[4][6]
Brittleness1–5Brittle — snaps with little warning[1][2]Tough — absorbs impact, yields before breaking[4]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for a PC/ABS filament[27]
Creep resistance / sustained load1–5Good — no creep test found; chopped carbon fibre lifts modulus to 4200 MPa against 2379–2450 for unfilled ASA[1][28]Good. Room-temperature tensile creep of moulded PC/ABS was still running unbroken at 30 MPa when the experiment was stopped for time; specimens failed within the test window at 39-47 MPa (ASTM D638)[29]
Fatigue / repeated-flex resistance1–5Below average — no CF-grade S-N curve; notched Charpy falls to 6.2 kJ/m² against 19.6 for unfilled Bambu Lab ASA[1][26]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[4]
Z strength as % of XY%88 by tensile, 46 by flexural (printed, Bambu Lab)[1]75-86 (Stratasys ZX against XZ tensile at break, ASTM D638) against 57 (Polymaker, printed Z against XY tensile)[4][6]
Thermal Properties
HDT at 0.45 MPa°C110 (ISO 75, 0.45 MPa, Bambu Lab) against 100 for unfilled Bambu Lab ASA[1][26]112 (ISO 75 at 0.45 MPa, Polymaker); Stratasys prints 117.9 in XY and 126.1 in XZ (ASTM D648 Method B at 66 psi), against 125.0 moulded[4][6]
HDT at 1.8 MPa°C102 (ISO 75, 1.8 MPa, Bambu Lab) against 92 for unfilled Bambu Lab ASA[1][26]106 (ISO 75 at 1.8 MPa, Polymaker); Stratasys prints 107.5 in XY and 112.0 in XZ (ASTM D648 Method B at 264 psi), against 102.9 moulded[4][6]
Glass transition (Tg)°CNot documented109 (Polymaker) and 137 (3DXTech FR grade), DSC; Stratasys measures 105.3 (ASTM D7426 inflection point)[4][5][6]
Melting point / Vicat°CNot documentedAmorphous — no melting point; Vicat 135 (Polymaker, ISO 306)[4]
Continuous service temperature°C93 — Prusa publishes this as the temperature resistance of Prusament ASA[30]113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[24]
Annealing responseNot documented90 °C for 2 h (Polymaker)[4]
Thermal expansion (CTE)µm/m·KNot documented59.9 over -50 to 35 °C and 73.0 over -50 to 95 °C (printed XY, ASTM E831)[6]
Flammability / UL 94Flammable; no UL 94 rating published[26]Not documented
Environment & Chemical
UV resistance1–5Excellent — designed for permanent outdoor use; the acrylate rubber phase is unchanged by the fibre[31][15]Degrades within weeks outdoors[19]
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[28]Withstands oils, solvents and fuels; Polymaker rates it good against weak acids[19]
Food contactNot food safe[15]Bisphenol-A polycarbonate is not offered as food-contact filament[19]
Biodegradability / compostabilityNot biodegradable[15]Not biodegradable[19]
RecyclabilityNot accepted in household plastic collection[15]Mechanically recyclable but not accepted in household plastic collection[19]
Electrical & ESD propertiesSurface resistance above 10⁹ ohm/sq — not static-dissipative (3DXTech, ASTM D257)[2]Not documented
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[32][14]Moderate — measurable VOCs and UFPs, ventilation advised[32]
Ultrafine-particle emission rateparticles/minNot documented≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[32]
Hazardous species emittedStyrene. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea. Azimi et al. measured styrene from every styrenic filament tested but did not test ASA itself[14][32]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration[32][14]Ventilated room or enclosure recommended[32][14]
Dust & fibre handling hazardCarbon fibre is bound in the matrix; sanding dust should not be inhaled[2]Not documented
Post-Processing
Sanding & machiningSands well and takes filler before painting[15]Sands and machines well; the toughness means it cuts rather than chips[17]
Painting & finishingPaints readily; ASA holds colour outdoors so many parts are left unpainted[15]Not documented
Gluing & solvent weldingSolvent-welds with acetone[28]Cyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[17]
Vapour / chemical smoothingAcetone vapour smoothing works[28]Acetone attacks the ABS phase, so surface smoothing is partial rather than full[4]
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a Support for ABS that also serves ASA[14]Prints its own supports; 3DXTech sells a dedicated PC break-away support[17]
Dimensional accuracy & detailMatte fibre-filled finish hides layer lines[1]Not documented
Solvents & Solubility
Soluble inAcetone dissolves the resin and leaves the fibre; MEK, THF, ethyl acetate and chlorinated solvents attack the styrenic backbone.[33][28]Dichloromethane and chloroform dissolve the PC phase; acetone, MEK and THF dissolve the ABS phase.[34][33]
Softened or crazed byLimonene attacks some grades — Prusa reports Prusament ASA Orange flaking apart as layer adhesion fails.[35]Petrol, esters, ether and 1 % alkali stress-crack the PC phase; aromatics and esters soften the ABS phase.[34][33]
Solvent welding & smoothing agentAcetone vapour reaches only the resin fraction, so the fibre is left standing proud of the smoothed surface.[36][28]Acetone attacks only the ABS phase, so smoothing is partial; a dichloromethane cement welds the whole section.[4][37]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet V1.0 — ASA-CF Bambu Lab · 2026-08 · tds
  2. CarbonX Carbon Fiber ASA Technical Data Sheet 3DXTech · 2026-08 · tds
  3. ApolloX CF10 Technical Data Sheet Formfutura · 2026-08 · tds
  4. Polymaker PC-ABS Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  5. Firewire Flame Retardant PC/ABS Technical Data Sheet Rev 3.0 3DXTech · 2026-08 · tds
  6. PC-ABS — FDM Material Data Sheet Stratasys · 2023-08 · tds
  7. ASA-CF — product page Bambu Lab US Store · 2026-08 · vendor
  8. Polymaker product catalogue Polymaker · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. Filastruder product catalogue Filastruder · 2026-08 · vendor
  11. IEMAI CF-ASA 3D Printing Filament product page IEMAI 3D · 2026-08 · vendor
  12. Reli3D PC-ABS Filament, Black, 1000 g spool Reli3D (Amazon US) · 2026-08 · vendor
  13. SUNLU PC-ABS 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  14. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  15. ASA — material basics Polymaker Wiki · 2026-08 · doc
  16. ASA — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  19. PC — material basics Polymaker Wiki · 2026-08 · doc
  20. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  21. Carbon Fiber Filled — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  22. 3DXTech 3DXMAX ABS product page 3DXTech · 2026-08 · vendor
  23. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  24. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  25. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  26. Bambu Filament Technical Data Sheet V3.0 — ASA Bambu Lab · 2026-08 · tds
  27. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  28. PolyLite ASA Technical Data Sheet Polymaker · 2024-11 · tds
  29. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  30. Prusament ASA — material page Prusa Polymers · 2026-08 · doc
  31. ASA — FDM Material Data Sheet (includes 1000 h QUV exposure results) Stratasys · 2026-08 · tds
  32. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  33. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  34. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  35. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  36. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  37. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds