3D Printing Info

Filament comparison

ASA-CF vs PAHT-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

Carbon-fibre ASA (ASA-CF) guideHigh-temperature CF nylon (PAHT-CF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ASA-CF comparisonsMore PAHT-CF comparisons
ASA-CF vs PAHT-CF — documented properties and sources
PropertyCarbon-fibre ASA (ASA-CF)ASAHigh-temperature CF nylon (PAHT-CF)PA
Market snapshot
Listing priceUSD/kg; dated snapshots$36.99/kg median; $25.00–$90.00/kg across 5 dated product listings$59.98/kg median; $49.99–$69.98/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryASA reinforced with chopped carbon fibre — Formfutura's ApolloX CF10 is 10 wt%[1][2][3]High-temperature carbon-fibre nylon. Bambu Lab's PAHT-CF and Polymaker's PA612-CF15 both use a long-chain polyamide matrix for lower moisture uptake than PA6[4][5]
Densityg/cm³1.02 (Bambu Lab), 1.1 (Formfutura ApolloX CF10) and 1.11 (3DXTech), ISO 1183[1][2][3]1.03 (Polymaker PA612-CF15) and 1.06 (Bambu Lab), ISO 1183[4][5]
Typical priceUSD/kg1 kg spools cluster near 37[6][7]1 kg-equivalent spools cluster near 60[4][7]
Price range across brandsUSD/kg25–90 across brands; IEMAI 25, Ambrosia 33, Bambu Lab 37, Polymaker Fiberon 40, 3DXTech 90[8][6][7][9][10]50–70 across brands; Bambu Lab 50, Polymaker Fiberon PA612-CF15 70[4][7]
Market availability1–5Available from several mainstream brands[6][7][9][8]Available from several mainstream brands[4][7]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75 and 1 kg spools[7][9][6]1.75 mm; 0.5 and 1 kg spools[7][4]
Typical applicationsOutdoor structural parts, drone and antenna mounts where stiffness and UV stability both matter[1][2]Under-bonnet and near-motor parts needing 170 °C-plus heat deflection with less humidity drift than PA6[4][5]
Printing Parameters
Nozzle temperature°C250–280 (Bambu Lab)[1]260–290 (Bambu Lab)[4]
Bed temperature°C80–100 (Bambu Lab)[1]Not documented
Enclosure / chamber requirement1–5Enclosure recommended — Bambu Lab specifies a 45–60 °C chamber[1][11]Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[4]
Recommended chamber temperature°C45–60 (Bambu Lab)[1]45–60 (Bambu Lab)[4]
Part cooling fanFan on (Bambu Lab)[1]Not documented
Bed surface & adhesion aidPEI sheet, BuildTak or an adhesion aid such as Magigoo (Polymaker); Simplify3D also lists Kapton tape and ASA slurry[12][13]PEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[14][15]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s20 at Bambu Lab's 250 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][16]8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[4][16]
Warping tendency1–5Moderate — needs adhesion aid or draught shield; the fibre reduces warping against unfilled ASA[11]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[12]Needs a specific surface plus adhesive[14]
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[12]Moderate — retraction tuning needed[15]
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[11]Expert / industrial hardware only[4][17]
Extruder requirementNot documented0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[4]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[11]Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-CF15 and recommends hardened steel or ruby[5]
Abrasiveness1–5Highly abrasive — standard CF composite[11]Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-CF15[5]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for fibre-filled composites and Simplify3D a higher tendency to clog[18][19]High — jams from moisture, heat creep or particles[17]
Heat-creep / jam sensitivity1–5Slightly sensitive[13]Moderate — good heatbreak cooling needed[14]
Hotend requirementNo special hotend required[13]May require an all-metal hot end (Simplify3D)[14]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.33 % saturated at 25 °C / 55 % RH (Bambu Lab)[1]High (0.8–2 %) — 0.88 % saturated at 25 °C / 55 % RH for Bambu Lab PAHT-CF, a third of its PA6-CF; Polymaker's PA612-CF15 reaches 2.2 % equilibrium[4][5][20]
Equilibrium moisture content at ~50 % RH%0.33 saturated at 25 °C / 55 % RH (Bambu Lab)[1]0.88 saturated at 25 °C / 55 % RH (Bambu Lab PAHT-CF); 2.2 equilibrium (Polymaker PA612-CF15)[4][5]
Drying temperature & time80 °C for 8 h (Bambu Lab)[1]80 °C for 8–12 h (Bambu Lab)[4]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[17]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published; Polymaker groups the styrenics as moderate-sensitivity and absorbed water shows as bubbling and poor layer adhesion[17]Polymaker publishes dry and wet printed blocks for PA612-CF15 itself: at 2.57 % moisture tensile falls only 91.9 → 83.1 MPa and modulus 5137 → 3991 MPa — the PA612 backbone absorbs far less than PA6[5][21]
Storage requirementSealed with desiccant; Polymaker rates the styrenics moderate-sensitivity[17]Sealed below 20 % RH with desiccant[17]
Hydrolysis at melt temperatureNot documentedPolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[22][23]
Mechanical Properties
Tensile strength (XY)MPa34 ± 3 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 48 at break and Formfutura 79 at 23 °C[1][2][3]92 ± 7 (Bambu Lab) and 91.9 ± 2.0 (Polymaker PA612-CF15, dry/annealed) printed XY, ISO 527; the Polymaker grade only falls to 83.1 ± 2.2 conditioned to 2.57 % moisture[4][5]
Young's modulusMPa4200 ± 270 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 5355 and Formfutura 7580[1][2][3]3860 ± 230 (Bambu Lab) and 5137 ± 192 (Polymaker PA612-CF15, dry) printed XY, ISO 527; Polymaker 3991 ± 137 conditioned[4][5]
Elongation at break%9.6 ± 1.4 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 3 at break and Formfutura 1.8[1][2][3]2.6 ± 0.2 dry (Polymaker PA612-CF15) to 8.4 ± 1.8 (Bambu Lab) printed XY, ISO 527; Polymaker 4.1 ± 0.3 conditioned[4][5]
Flexural strengthMPa72 ± 5 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 78[1][2]Not documented
Flexural modulusMPa3740 ± 130 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 5210[1][2]4230 ± 210 printed XY, ISO 178 (Bambu Lab)[4]
Charpy impact, notchedkJ/m²6.2 ± 1.4 printed XY, ISO 179, notched (Bambu Lab) — a third of unfilled Bambu Lab ASA's 19.6[1][24]8.1 ± 0.8 printed XY dry and 7.7 ± 0.5 conditioned, ISO 179 notched (Polymaker PA612-CF15)[5]
Other impact dataCharpy unnotched 14.0 ± 2.2 printed XY (Bambu Lab, ISO 179), against 41.0 for unfilled Bambu Lab ASA[1][24]Charpy unnotched 57.5 ± 3.4 and notched 22.8 ± 1.8 printed XY (Bambu Lab, ISO 179)[4]
Layer adhesion / Z tensileMPa30 ± 4 printed Z, ISO 527 (Bambu Lab); flexural Z falls to 33 against 72 in XY[1]47 ± 5 (Bambu Lab) and 48.3 ± 3.9 (Polymaker PA612-CF15, dry) printed Z, ISO 527; Polymaker 35.6 ± 3.0 conditioned[4][5]
Brittleness1–5Brittle — snaps with little warning[1][2]Moderate[4]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre long-chain nylon filament[25]
Creep resistance / sustained load1–5Good — no creep test found; chopped carbon fibre lifts modulus to 4200 MPa against 2379–2450 for unfilled ASA[1][26]Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load with 110 °C continuous service; the long-chain PA612 matrix takes up 0.88 % at saturation, a third of the same maker's PA6-CF, so it holds dimension better[27][5]
Fatigue / repeated-flex resistance1–5Below average — no CF-grade S-N curve; notched Charpy falls to 6.2 kJ/m² against 19.6 for unfilled Bambu Lab ASA[1][24]Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[27]
Elasticity / flexibility1–5Rigid[1]Rigid[4]
Z strength as % of XY%88 by tensile, 46 by flexural (printed, Bambu Lab)[1]51 (Bambu Lab) to 53 (Polymaker PA612-CF15), printed[4][5]
Thermal Properties
HDT at 0.45 MPa°C110 (ISO 75, 0.45 MPa, Bambu Lab) against 100 for unfilled Bambu Lab ASA[1][24]175 (Polymaker PA612-CF15) and 194 (Bambu Lab), ISO 75 at 0.45 MPa[4][5]
HDT at 1.8 MPa°C102 (ISO 75, 1.8 MPa, Bambu Lab) against 92 for unfilled Bambu Lab ASA[1][24]114 (Polymaker PA612-CF15) and 170 (Bambu Lab), ISO 75 at 1.8 MPa[4][5]
Glass transition (Tg)°CNot documented70 (Bambu Lab, DSC)[4]
Melting point / Vicat°CNot documented210 (Polymaker PA612-CF15) and 225 (Bambu Lab) melting, DSC; Vicat 206 (Polymaker)[4][5]
Continuous service temperature°C93 — Prusa publishes this as the temperature resistance of Prusament ASA[28]Not documented
Flammability / UL 94Flammable; no UL 94 rating published[24]Flammable; no UL 94 rating published for the grades surveyed[22]
Environment & Chemical
UV resistance1–5Excellent — designed for permanent outdoor use; the acrylate rubber phase is unchanged by the fibre[29][12]Months outdoors before embrittlement — unstabilised polyamide yellows under UV[15]
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[26]Withstands oils, fuels and alkalis[15]
Water / humidity resistance in service1–5Not documentedAbsorbs water, properties shift — less than PA6 but more than PA12[21][4]
Food contactNot food safe[12]Not food-contact certified as filament[15]
Biodegradability / compostabilityNot biodegradable[12]Not biodegradable[15]
RecyclabilityNot accepted in household plastic collection[12]Not accepted in household plastic collection[15]
Electrical & ESD propertiesSurface resistance above 10⁹ ohm/sq — not static-dissipative (3DXTech, ASTM D257)[2]Surface resistivity above 10¹² ohm — insulating (Polymaker PA612-CF15, ANSI/ESD S11.11)[5]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[30][11]Moderate — measurable VOCs and UFPs, ventilation advised[30]
VOC emission rateµg/minNot documentedUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[30]
Ultrafine-particle emission rateparticles/minNot documented≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[30]
Hazardous species emittedStyrene. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea. Azimi et al. measured styrene from every styrenic filament tested but did not test ASA itself[11][30]Caprolactam, at up to 180 µg/min from nylon filament[30]
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration[30][11]Ventilated room or enclosure recommended[30]
Dust & fibre handling hazardCarbon fibre is bound in the matrix; sanding dust should not be inhaled[2]Fibre is bound in the matrix; sanding dust should not be inhaled[22]
Post-Processing
Sanding & machiningSands well and takes filler before painting[12]Sands poorly — gums rather than powders[14]
Painting & finishingPaints readily; ASA holds colour outdoors so many parts are left unpainted[12]Not documented
Gluing & solvent weldingSolvent-welds with acetone[26]Cyanoacrylate; no common solvent welds polyamide[14]
Vapour / chemical smoothingAcetone vapour smoothing works[26]No practical vapour smoothing[14]
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a Support for ABS that also serves ASA[11]Not documented
Dimensional accuracy & detailMatte fibre-filled finish hides layer lines[1]Not documented
Solvents & Solubility
Soluble inAcetone dissolves the resin and leaves the fibre; MEK, THF, ethyl acetate and chlorinated solvents attack the styrenic backbone.[31][26]Formic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[32]
Softened or crazed byLimonene attacks some grades — Prusa reports Prusament ASA Orange flaking apart as layer adhesion fails.[33]Zinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[32]
Solvent welding & smoothing agentAcetone vapour reaches only the resin fraction, so the fibre is left standing proud of the smoothed surface.[34][26]None — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[32]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet V1.0 — ASA-CF Bambu Lab · 2026-08 · tds
  2. CarbonX Carbon Fiber ASA Technical Data Sheet 3DXTech · 2026-08 · tds
  3. ApolloX CF10 Technical Data Sheet Formfutura · 2026-08 · tds
  4. Bambu Filament Technical Data Sheet — PAHT-CF Bambu Lab · 2026-08 · tds
  5. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  6. ASA-CF — product page Bambu Lab US Store · 2026-08 · vendor
  7. Polymaker product catalogue Polymaker · 2026-08 · vendor
  8. Filastruder product catalogue Filastruder · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. IEMAI CF-ASA 3D Printing Filament product page IEMAI 3D · 2026-08 · vendor
  11. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  12. ASA — material basics Polymaker Wiki · 2026-08 · doc
  13. ASA — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  14. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  15. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  18. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  19. Carbon Fiber Filled — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  20. Bambu Filament Technical Data Sheet — PA6-CF Bambu Lab · 2026-08 · tds
  21. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  22. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  23. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  24. Bambu Filament Technical Data Sheet V3.0 — ASA Bambu Lab · 2026-08 · tds
  25. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  26. PolyLite ASA Technical Data Sheet Polymaker · 2024-11 · tds
  27. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  28. Prusament ASA — material page Prusa Polymers · 2026-08 · doc
  29. ASA — FDM Material Data Sheet (includes 1000 h QUV exposure results) Stratasys · 2026-08 · tds
  30. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  31. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  32. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  33. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  34. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc