Compare printing settings, strength, heat resistance, dated prices and sources.

ABS+ / Tough ABS guideTPU 98A / hard TPU guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS+ comparisonsMore TPU 98A comparisons
ABS+ vs TPU 98A — documented properties and sources
PropertyABS+ / Tough ABSABSTPU 98A / hard TPUFLEX
Market snapshot
Listing priceUSD/kg; dated snapshots$26.49/kg median; $15.99–$29.99/kg across 4 dated product listings$94.99/kg median; $34.99–$149.99/kg across 3 dated product listings
Identity & Market
Base polymer / chemistryABS reformulated for lower warping and a higher glass transition; Polymaker's ABS Pro and ABS Max reach Tg 114.9 and 126.3 °C against 101 °C for PolyLite ABS[1][2][3]Hard thermoplastic polyurethane at 98 Shore A to about 60 Shore D — the rigid end of the TPU range[4][5]
Densityg/cm³1.04 (ABS Pro) and 1.06 (ABS Max), ISO 1183[1][2]1.23 (Fillamentum Flexfill 98A); 1.2 (Extrudr FLEX HARD, ISO 2781)[4][5]
Typical priceUSD/kg1 kg spools cluster near 27[6]1 kg spools cluster near 150[7]
Price range across brandsUSD/kg16–30 across brands; SUNLU E-ABS 16, Polymaker ABS Pro 25, YXPOLYER ABS Enhanced 28, Polymaker ABS Max 30[6][8][9]95–150 across brands; Proto-pasta Clear Rigid TPU 95, Push Plastic TPU 100A 150[10][7]
Market availability1–5Available from several mainstream brands[6]Available from several mainstream brands[7][10][5]
Spool sizes & diameters1.75 and 2.85 mm; 1 kg spools[6]1.75 and 2.85 mm; 0.5, 0.75 and 1 kg spools[10][7]
Typical applicationsLarge enclosure and automotive parts where plain ABS warps or softens too early[1][2]Drive belts, wheels, snap-fits and bumpers that need to flex but hold shape under load[4]
Printing Parameters
Nozzle temperature°C270–290 (ABS Pro); 270–300 (ABS Max) — 25–35 °C above plain ABS[1][2]230–260 (Extrudr FLEX HARD)[5]
Bed temperature°C120 (ABS Max)[2]50–90 (Extrudr FLEX HARD)[5]
Enclosure / chamber requirement1–5Enclosure required (passive)[1][2][11]Open frame is fine[5]
Part cooling fanNot documented0–30 % (Extrudr FLEX HARD)[5]
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[11][12]PEI sheet or painter's tape; Polymaker warns TPU can over-stick and advises a glue stick as a release agent[13][14]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sUp to 250 mm/s (ABS Pro) and 200 mm/s (ABS Max), equivalent to 20 and 16 on a 0.4 mm nozzle at 0.2 mm layer[1][2][15]4.6 (Extrudr FLEX HARD, stated max volumetric speed on a 0.4 mm nozzle)[5]
Warping tendency1–5High — enclosure needed for reliable large parts[11]None[5]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[11]Not documented
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[16]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; the hotter nozzle rules out PTFE-lined hotends[1][2]Easy — minor profile tuning; at this hardness the filament pushes like a rigid material[5]
Extruder requirementNot documentedBowden viable at this hardness — Extrudr rates FLEX HARD to 100 mm/s where its soft grades cap lower[5]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[11]Brass fine indefinitely[5]
Abrasiveness1–5Non-abrasive[11]Non-abrasive[5]
Nozzle clog risk1–5Low — unfilled ABS compound; no special hot-end required and clogging is not among the listed drawbacks[12][17]Low[18]
Heat-creep / jam sensitivity1–5Slightly sensitive[12]Moderate — good heatbreak cooling needed[14]
Hotend requirementNo special hot-end required[12]No special hot-end required, but a direct-drive extruder is (Simplify3D)[13]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.51 % maximum water absorption (ABS Pro)[1]Moderate — the TPU family absorbs readily; Extrudr specifies a 12 h dry at 60 °C for FLEX HARD[5][18]
Equilibrium moisture content at ~50 % RH%0.51 maximum water absorption (Polymaker ABS Pro)[1]Not documented
Drying temperature & time70 °C for 6 h (ABS Max)[2]60 °C for 12 h (Extrudr FLEX HARD)[5]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[18]Bubbling and popping at the nozzle, stringing and a rough surface[18]
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures[18]Polymaker groups TPU with the highly hygroscopic materials; no dry-versus-conditioned figures are published[18]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[18]Sealed with desiccant; often kept in a dryer during the print[18]
Mechanical Properties
Tensile strength (XY)MPa34.9 (ABS Pro) and 35.7 (ABS Max) printed XY, ISO 527[1][2]53.7 at break (Fillamentum Flexfill 98A, DIN 53504)[4]
Young's modulusMPa2330 (ABS Pro) and 2320 (ABS Max) printed XY, ISO 527[1][2]Not documented
Elongation at break%6.7 (ABS Max) and 7.3 (ABS Pro) at break, printed XY, ISO 527[1][2]318 at break (Fillamentum Flexfill 98A, DIN 53504); Extrudr FLEX HARD 490 (ISO 527-2)[4][5]
Flexural strengthMPa60.1 (ABS Pro) and 63.3 (ABS Max) printed XY, ISO 178[1][2]Not documented
Flexural modulusMPa2330 (ABS Pro) and 2500 (ABS Max) printed XY, ISO 178[1][2]Not documented
Charpy impact, notchedkJ/m²10.5 (ABS Max) and 14.5 (ABS Pro) printed XY, ISO 179, notched[1][2]Not documented
Layer adhesion / Z tensileMPa21.9 (ABS Pro) and 25.4 (ABS Max) printed Z, ISO 527[1][2]Not documented
Brittleness1–5Tough — absorbs impact, yields before breaking[1][2]Very ductile — bends far before failing[4]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documented98 Shore A and 60 Shore D (Fillamentum, ISO 7619-1); Extrudr FLEX HARD 58 Shore D (ISO 868)[4][5]
Creep resistance / sustained load1–5Moderate — no creep test found; Tg of 115 °C (ABS Pro) and 126 °C (ABS Max) keeps room-temperature service far below softening[1][2]Poor — no 98A creep test; a printed 95A TPU bar crept from 74.5 to 82.7 mm over 5 days at 1.25 kg[19]
Fatigue / repeated-flex resistance1–5Moderate — no S-N curve found; 6.7–7.3 % elongation and 10.5–14.5 kJ/m² notched Charpy, below unfilled Bambu Lab ABS[1][2][20]Excellent — living hinges viable[14]
Elasticity / flexibility1–5Rigid[1]Semi-flexible[4][5]
Z strength as % of XY%63 (ABS Pro) and 71 (ABS Max), printed[1][2]Not documented
Wear resistance & frictionNot documentedAbrasion 23 mm³ (Fillamentum, ISO 4649 method A) and 26 mm³ (Extrudr FLEX HARD, ISO 4649-A) — the best abrasion figures in the group[4][5]
Thermal Properties
HDT at 0.45 MPa°C106.4 (ABS Pro) and 118.1 (ABS Max), ISO 75 at 0.45 MPa[1][2]Not documented
HDT at 1.8 MPa°C101.4 (ABS Pro) and 113.1 (ABS Max), ISO 75 at 1.8 MPa[1][2]Not documented
Glass transition (Tg)°C114.9 (ABS Pro) and 126.3 (ABS Max), DSC[1][2]Not documented
Melting point / Vicat°CAmorphous — no melting point; Vicat 116.1 (ABS Pro) and 127.4 (ABS Max), ISO 306[1][2]190–210 melting (Extrudr FLEX HARD, ISO 3146-C); Vicat A 140 (ISO 306)[5]
Thermal expansion (CTE)µm/m·K86–89 for printed unfilled ABS (fibre Bragg grating, 25–50 °C); no grade-specific measurement published[21]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement[16]Good — years with some colour shift; Polymaker lists UV exposure among the conditions TPU withstands[14]
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[3]Withstands industrial solvents and UV exposure (Polymaker)[14]
Food contactNot food safe — Polymaker cites potential chemical leaching[16]Not food safe without specific certification (Polymaker)[14]
Biodegradability / compostabilityNot biodegradable[16]Not biodegradable[14]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[16]Not accepted in household plastic collection[14]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[22][11]Low hazard — minimal VOC and particle emission; TPU was not among the nine filaments in the chamber study[22]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[22]Not documented
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[22]Not documented
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[22][11]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[22][11]Open a window / occasional ventilation[22]
Post-Processing
Sanding & machiningSands well and takes filler before painting[16]Difficult to sand or smooth; Polymaker limits post-processing to trimming or tumbling[14]
Painting & finishingPaints readily after light abrasion[16]Not documented
Gluing & solvent weldingNot documentedCyanoacrylate bonds TPU; no common solvent welds it[14]
Vapour / chemical smoothingAcetone vapour smoothing works[3]No practical vapour smoothing[14]
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[23][11]Polymaker warns TPU supports are often very difficult to remove[14]
Dimensional accuracy & detailNot documentedTear strength 170 kN/m (Fillamentum, ISO 34-1) and 175 kN/m (Extrudr FLEX HARD, ISO 34-1B)[4][5]
Solvents & Solubility
Soluble inAcetone dissolves it — the basis of ABS slurry; so do MEK, THF, ethyl acetate, chloroform, dichloromethane and toluene.[24][3]DMF, DMSO, NMP and THF dissolve TPU; acetone, MEK and cyclohexanone are partial solvents. All laboratory reagents.[25]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[24][26]Toluene and benzene swell it up to +50 % by weight at 23 °C; esters swell it severely; ethanol and IPA soften it.[25]
Solvent welding & smoothing agentAcetone: about 20 min of vapour at 80 °C over 5 mm of liquid. Prusa measured layer adhesion more than doubled.[27]None practical — the true solvents (DMF, THF, NMP) are laboratory reagents and leave the joint swollen and weak.[25]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Polymaker ABS Pro Technical Data Sheet V1 (2026-05-29) Polymaker · 2026-05 · tds
  2. Polymaker ABS Max Technical Data Sheet V1.1 (2026-06-01) Polymaker · 2026-06 · tds
  3. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  4. Flexfill TPU 98A Technical Data Sheet Fillamentum · 2019-08 · tds
  5. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  6. Polymaker product catalogue Polymaker · 2026-08 · vendor
  7. Push Plastic product catalogue Push Plastic · 2026-08 · vendor
  8. SUNLU E-ABS (Easy ABS) 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  9. YXPOLYER ABS Enhanced product page YXPOLYER · 2026-08 · vendor
  10. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  11. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  12. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  13. Flexible (TPE/TPU) — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  14. TPU — material basics Polymaker Wiki · 2026-08 · doc
  15. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  16. ABS — material basics Polymaker Wiki · 2026-08 · doc
  17. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  18. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  19. BambuLab TPU 95A HF vs Qidi TPU 95A HF — results spreadsheet My Tech Fun (Igor Gaspar) · 2024-02 · test
  20. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  21. Characterization of Thermal Expansion Coefficient of 3D Printing Polymeric Materials Using Fiber Bragg Grating Sensors Materials 17(18):4668 · 2024-09 · paper
  22. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  23. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  24. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  25. Elastollan — Chemical properties: swelling and chemical resistance BASF · 2026-08 · tds
  26. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  27. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc