3D Printing Info

Filament comparison

ABS+ vs PPA-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

ABS+ / Tough ABS guidePPA-CF (carbon-fibre polyphthalamide) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS+ comparisonsMore PPA-CF comparisons
ABS+ vs PPA-CF — documented properties and sources
PropertyABS+ / Tough ABSABSPPA-CF (carbon-fibre polyphthalamide)PA
Market snapshot
Listing priceUSD/kg; dated snapshots$26.49/kg median; $15.99–$29.99/kg across 4 dated product listings$84.99/kg median; $21.99–$266.67/kg across 7 dated product listings
Identity & Market
Base polymer / chemistryABS reformulated for lower warping and a higher glass transition; Polymaker's ABS Pro and ABS Max reach Tg 114.9 and 126.3 °C against 101 °C for PolyLite ABS[1][2][3]Polyphthalamide — semi-aromatic nylon — with 10–15 wt% chopped carbon fibre; Bambu Lab lists the composition as semi-aromatic nylon plus carbon fibre, Raise3D and Siraya Tech state 15 wt%, Flashforge 10 %[4][5][6][7]
Densityg/cm³1.04 (ABS Pro) and 1.06 (ABS Max), ISO 1183[1][2]1.15 (Raise3D) to 1.25 (Bambu Lab and IEMAI 3D), ISO 1183; Flashforge 1.21–1.23[4][5][6][8]
Typical priceUSD/kg1 kg spools cluster near 27[9]1 kg-equivalent spools span 22–267; the middle of the market is about 85[10][11][12][13][14][15]
Price range across brandsUSD/kg16–30 across brands; SUNLU E-ABS 16, Polymaker ABS Pro 25, YXPOLYER ABS Enhanced 28, Polymaker ABS Max 30[9][16][17]22–267 across brands; CHCKX 22 on Amazon, IEMAI 3D 51, Siraya Tech 57 and 85, Bambu Lab 200 at 750 g, Raise3D 209, 3DXTech CarbonX HTN+CF 267 at 750 g[10][11][12][18][13][14][15]
Market availability1–5Available from several mainstream brands[9]Available from several mainstream brands[10][11][12][13][14]
Spool sizes & diameters1.75 and 2.85 mm; 1 kg spools[9]1.75 mm; 750 g, 1 kg, 2 kg and 2.5 kg spools[4][12][14]
Typical applicationsLarge enclosure and automotive parts where plain ABS warps or softens too early[1][2]Under-bonnet automotive brackets, jigs and end-use parts that must stay stiff above the 100 °C working ceiling of PA6-CF[5][6]
Diameter tolerance± mmNot documented0.05 (Bambu Lab and Siraya Tech, 1.75 mm)[4][7]
Printing Parameters
Nozzle temperature°C270–290 (ABS Pro); 270–300 (ABS Max) — 25–35 °C above plain ABS[1][2]280–310 (Bambu Lab and CHCKX); 280–320 (Siraya Tech)[4][7][15]
Bed temperature°C120 (ABS Max)[2]100–120 (Bambu Lab and CHCKX); Siraya Tech runs cooler at 70–90[4][7][15]
Enclosure / chamber requirement1–5Enclosure required (passive)[1][2][19]Enclosure required (passive) — Bambu Lab specifies a 50–80 °C chamber and Siraya Tech requires an enclosure, while Flashforge states its LUVOCOM-based grade prints on machines with no heated chamber[4][6][12]
Recommended chamber temperature°CNot documented50–80 (Bambu Lab); specimens were printed at a 52 °C chamber and Bambu Lab notes 70–80 °C raises Z properties[4]
Part cooling fanNot documentedBambu Lab turns the part fan on; Siraya Tech runs it off[4][7]
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[19][20]Smooth or textured PEI plate with a glue stick, or a PVP glue coating[4][7]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sUp to 250 mm/s (ABS Pro) and 200 mm/s (ABS Max), equivalent to 20 and 16 on a 0.4 mm nozzle at 0.2 mm layer[1][2][21]8–12 mm³/s at 300–320 °C (Siraya Tech)[7]
Warping tendency1–5High — enclosure needed for reliable large parts[19]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[19]Not documented
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[22]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; the hotter nozzle rules out PTFE-lined hotends[1][2]Advanced — enclosure, hardware upgrades, tuning; a 320 °C hot end and a hardened nozzle are the entry requirements[4][7]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[19]Hardened steel required — Siraya Tech and CHCKX specify hardened steel or better, Raise3D warns brass wears quickly[5][7][15]
Abrasiveness1–5Non-abrasive[19]Highly abrasive — standard CF/GF composites and glow fills[5][7]
Nozzle clog risk1–5Low — unfilled ABS compound; no special hot-end required and clogging is not among the listed drawbacks[20][23]Moderate — needs dry filament and a clean nozzle; Siraya Tech states nozzles below 0.4 mm will clog[7][12]
Heat-creep / jam sensitivity1–5Slightly sensitive[20]Not documented
Hotend requirementNo special hot-end required[20]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.51 % maximum water absorption (ABS Pro)[1]High (0.8–2 %) — 1.30 % saturated at 25 °C / 55 % RH for Bambu Lab and IEMAI 3D against 2.35 % for the same makers' PA6-CF, which is the whole reason to pay for PPA[4][8][24]
Equilibrium moisture content at ~50 % RH%0.51 maximum water absorption (Polymaker ABS Pro)[1]1.30 saturated at 25 °C / 55 % RH (Bambu Lab and IEMAI 3D) against 2.35 for their PA6-CF; Siraya Tech 1.37 and 1.09 by ISO 62, Raise3D 0.6 by ISO 62 Method 1, Flashforge below 0.1 at 23 °C / 24 h[4][5][6][7][25][8][24]
Drying temperature & time70 °C for 6 h (ABS Max)[2]100–140 °C for 8–12 h (Bambu Lab, hotter is better within that range); Siraya Tech 100 °C for 4–6 h; Raise3D 80–100 °C for 6–12 h[4][5][7]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[26]Not documented
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures[26]Not documented
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[26]Sealed below 20 % RH with desiccant (Bambu Lab); Raise3D keeps the spool in a dry box throughout the print[4][5]
Mechanical Properties
Tensile strength (XY)MPa34.9 (ABS Pro) and 35.7 (ABS Max) printed XY, ISO 527[1][2]95–168 (printed XY, ISO 527): Siraya Tech 95, Flashforge 108–112, Siraya Tech Core 112, Raise3D 122 conditioned and annealed, Bambu Lab and IEMAI 3D 168[4][5][6][7][25][8]
Young's modulusMPa2330 (ABS Pro) and 2320 (ABS Max) printed XY, ISO 527[1][2]7100–11800 (printed XY): Flashforge 7100–8000, Raise3D and Siraya Tech 7800, Siraya Tech Core 9300, Bambu Lab and IEMAI 3D 11800[4][5][6][7][25][8]
Elongation at break%6.7 (ABS Max) and 7.3 (ABS Pro) at break, printed XY, ISO 527[1][2]1.9–5 at break (printed XY): Raise3D 1.9, Siraya Tech 2, Siraya Tech Core 2.25, Bambu Lab and IEMAI 3D 3.2, Flashforge 3.5–5[4][5][6][7][25][8]
Flexural strengthMPa60.1 (ABS Pro) and 63.3 (ABS Max) printed XY, ISO 178[1][2]145–221 (printed XY, ISO 178): Siraya Tech 145, Siraya Tech Core 178, Raise3D 190, Bambu Lab and IEMAI 3D 208, Flashforge 210–221[4][5][6][7][25][8]
Flexural modulusMPa2330 (ABS Pro) and 2500 (ABS Max) printed XY, ISO 178[1][2]6500–9860 (printed XY, ISO 178): Flashforge 6500–7000, Siraya Tech 6800, Raise3D 8510, Siraya Tech Core 8700, Bambu Lab and IEMAI 3D 9860[4][5][6][7][25][8]
Charpy impact, notchedkJ/m²10.5 (ABS Max) and 14.5 (ABS Pro) printed XY, ISO 179, notched[1][2]6.5 notched Charpy XY (Bambu Lab and IEMAI 3D, ISO 179); Raise3D 7.8 and Siraya Tech 11 by ISO 179 without stating notched[4][5][7][8]
Other impact dataNot documentedBambu Lab and IEMAI 3D unnotched Charpy 41.7 kJ/m² XY against 4.3 in Z; Flashforge Izod 9–11 kJ/m² XY against 2.5–3 in Z[4][6][8]
Layer adhesion / Z tensileMPa21.9 (ABS Pro) and 25.4 (ABS Max) printed Z, ISO 527[1][2]57 printed Z (Bambu Lab and IEMAI 3D, ISO 527); Raise3D measures 30.2 by a custom mono-layer method[4][5][8]
Brittleness1–5Tough — absorbs impact, yields before breaking[1][2]Brittle — snaps with little warning; 2–3 % elongation at break is typical[4][5][7]
Creep resistance / sustained load1–5Moderate — no creep test found; Tg of 115 °C (ABS Pro) and 126 °C (ABS Max) keeps room-temperature service far below softening[1][2]Good — Flashforge cites outstanding creep resistance at high temperature and Raise3D high creep resistance, both against other nylons[5][6]
Fatigue / repeated-flex resistance1–5Moderate — no S-N curve found; 6.7–7.3 % elongation and 10.5–14.5 kJ/m² notched Charpy, below unfilled Bambu Lab ABS[1][2][27]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[4]
Z strength as % of XY%63 (ABS Pro) and 71 (ABS Max), printed[1][2]34 (Bambu Lab and IEMAI 3D, Z against XY tensile, ISO 527)[4][8]
Thermal Properties
HDT at 0.45 MPa°C106.4 (ABS Pro) and 118.1 (ABS Max), ISO 75 at 0.45 MPa[1][2]188–227 (ISO 75 at 0.45 MPa): Raise3D 188, Flashforge 220, Bambu Lab and IEMAI 3D 227; Siraya Tech reaches 192–199 only after annealing, 84.5–97 unannealed[4][5][6][7][25][8]
HDT at 1.8 MPa°C101.4 (ABS Pro) and 113.1 (ABS Max), ISO 75 at 1.8 MPa[1][2]113–196 (ISO 75 at 1.8 MPa): Raise3D 113, Bambu Lab and IEMAI 3D 196; Siraya Tech reaches 119–126 only after annealing, 82.5–84 unannealed[4][5][7][25][8]
Glass transition (Tg)°C114.9 (ABS Pro) and 126.3 (ABS Max), DSC[1][2]80 (Siraya Tech, ASTM D3418) to 85 (Bambu Lab and IEMAI 3D, DSC)[4][7][8]
Melting point / Vicat°CAmorphous — no melting point; Vicat 116.1 (ABS Pro) and 127.4 (ABS Max), ISO 306[1][2]Melting point 231 (Raise3D) to 258 (Bambu Lab and IEMAI 3D); Vicat softening 230–238 (ISO 306)[4][5][7][25][8]
Continuous service temperature°CNot documented120 (Flashforge, IEC 60216, LUVOCOM PPA-CF)[6]
Annealing responseNot documentedBambu Lab anneals at 120–140 °C for 6–12 h; Raise3D at 80–100 °C for 8 h and warns of up to 0.5 % Z shrinkage. On Siraya Tech's grades annealing lifts HDT at 0.45 MPa from 84.5 to 192 °C while notched Charpy falls from 11 to 6.3 kJ/m²[4][5][7]
Thermal expansion (CTE)µm/m·K86–89 for printed unfilled ABS (fibre Bragg grating, 25–50 °C); no grade-specific measurement published[28]Not documented
Flammability / UL 94Not documentedFlammable; Bambu Lab lists water, carbon oxides and nitrogen oxides as combustion products. No UL 94 rating is published for the filament grades surveyed[4]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement[22]Not documented
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[3]Better than general nylon against weak acids, weak alkalis, most organic solvents and most oils and greases (Bambu Lab); not resistant to strong acids or strong alkalis[4]
Water / humidity resistance in service1–5Not documentedGood — minor absorption; 1.3 % saturated moisture is roughly half what PA6-CF takes up[4][24]
Food contactNot food safe — Polymaker cites potential chemical leaching[22]Not documented
Biodegradability / compostabilityNot biodegradable[22]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[22]Not documented
Electrical & ESD propertiesNot documentedFlashforge's data sheet gives a surface resistance of 10³ Ω or below (IEC 60093) for its LUVOCOM-based PPA-CF — the carbon loading makes it conductive rather than merely dissipative[6]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[29][19]Not documented
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[29]Not documented
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[29]Not documented
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[29][19]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[29][19]Not documented
Dust & fibre handling hazardNot documentedChopped carbon fibre; dry sanding and cutting release respirable fibre-laden dust[30]
Post-Processing
Sanding & machiningSands well and takes filler before painting[22]Not documented
Painting & finishingPaints readily after light abrasion[22]Not documented
Vapour / chemical smoothingAcetone vapour smoothing works[3]Not documented
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[31][19]Bambu Lab pairs it with Support for PA/PET; Raise3D warns that PPA-CF used as its own support bonds permanently to the model once it takes up moisture, so supports must come off before annealing[4][5]
Solvents & Solubility
Soluble inAcetone dissolves it — the basis of ABS slurry; so do MEK, THF, ethyl acetate, chloroform, dichloromethane and toluene.[32][3]Formic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[33]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[32][34]Zinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[33]
Solvent welding & smoothing agentAcetone: about 20 min of vapour at 80 °C over 5 mm of liquid. Prusa measured layer adhesion more than doubled.[35]None — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[33]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Polymaker ABS Pro Technical Data Sheet V1 (2026-05-29) Polymaker · 2026-05 · tds
  2. Polymaker ABS Max Technical Data Sheet V1.1 (2026-06-01) Polymaker · 2026-06 · tds
  3. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  4. Bambu Filament Technical Data Sheet V1.0 — PPA-CF Bambu Lab · 2026-08 · tds
  5. Raise3D Industrial PPA CF Technical Data Sheet V2.0 Raise3D · 2022-04 · tds
  6. Flashforge PPA-CF Filament Technical Data Sheet (LUVOCOM PPA-CF, 10 % carbon fibre) Flashforge · 2026-08 · tds
  7. Siraya Tech Fibreheart PPA-CF Technical Data Sheet Siraya Tech · 2026-08 · tds
  8. IEMAI 3D CF-PPA Technical Data Sheet IEMAI 3D · 2025-04 · tds
  9. Polymaker product catalogue Polymaker · 2026-08 · vendor
  10. PPA-CF — Bambu Lab US Store Bambu Lab · 2026-08 · vendor
  11. Raise3D Industrial PPA CF Filament 1.75 mm (1 kg) — product listing MatterHackers · 2026-08 · vendor
  12. Fibreheart PPA-CF Filament — product page Siraya Tech · 2026-08 · vendor
  13. IEMAI 3D CF-PPA 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  14. CARBONX HTN+CF — product page 3DXTech · 2026-08 · vendor
  15. CHCKX PPA-CF 3D Printing Filament Matte Black 1 kg 1.75 mm 10 % Carbon Fiber — Amazon listing Amazon.com · 2026-08 · vendor
  16. SUNLU E-ABS (Easy ABS) 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  17. YXPOLYER ABS Enhanced product page YXPOLYER · 2026-08 · vendor
  18. Siraya Tech Fibreheart PPA-CF Core Filament — product page Siraya Tech · 2026-08 · vendor
  19. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  20. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  21. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  22. ABS — material basics Polymaker Wiki · 2026-08 · doc
  23. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  24. Bambu Filament Technical Data Sheet V3.0 — PA6-CF Bambu Lab · 2026-08 · tds
  25. Siraya Tech Fibreheart PPA-CF Core Technical Data Sheet Siraya Tech · 2026-08 · tds
  26. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  27. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  28. Characterization of Thermal Expansion Coefficient of 3D Printing Polymeric Materials Using Fiber Bragg Grating Sensors Materials 17(18):4668 · 2024-09 · paper
  29. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  30. PET-CF / PPA-CF / PPS-CF / PA6-CF carbon fibre filament usage guide Bambu Lab Wiki · 2026-08 · doc
  31. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  32. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  33. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  34. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  35. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc