ABS-GF vs PPSU — documented properties and sources
PropertyGlass-fibre ABS (ABS-GF)ABSPPSUHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$34.99/kg median; $24.49–$73.33/kg across 4 dated product listings$337.40/kg median; $223.00–$732.56/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryABS reinforced with chopped glass fibre — 3DXTech's grade is nominally 10 wt%[1][2]Polyphenylsulfone — an amorphous high-temperature sulfone polymer[3]
Densityg/cm³1.08 (Bambu Lab) and 1.15 (3DXTech), ISO 1183[2][1]1.28 (ISO 1183, 3DXTech; ASTM D792, Stratasys PPSF)[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 24–73; the middle of the market is about 35[5][6][7][8]1 kg-equivalent spools span 223–733; the middle of the market is about 425[6][9][10][11]
Price range across brandsUSD/kg24–73 across brands; Siraya Tech 24, Bambu Lab 30, SUNLU 40, 3DXTech 73[5][6][7][8]223-733 across brands; IEMAI 3D 223 at 1 kg, 3DXTech ThermaX PPSU 250 at 500 g, 3D4Makers 425 at 750 g, Kimya PPSU-S 733 at 500 g[6][9][10][11]
Market availability1–5Available from several mainstream brands[5][6]Niche, a handful of specialist brands[6][9][10]
Spool sizes & diameters1.75 and 2.85 mm; 750 g and 1 kg spools[6][5]1.75 and 2.85 mm; 200 g to 750 g spools[6][9][10]
Typical applicationsStiff, dimensionally stable enclosure and tooling parts; Bambu Lab notes the fibre blurs layer lines into a matte finish[2]Steam-sterilisable medical and dental tooling, and aircraft interior parts[3]
Printing Parameters
Nozzle temperature°C240–280 (Bambu Lab)[2]Not documented
Bed temperature°C80–100 (Bambu Lab)[2]130–150 (3DXTech)[3]
Enclosure / chamber requirement1–5Enclosure recommended — Bambu Lab specifies a 45–60 °C chamber[2][12]Actively heated chamber required[13][14]
Recommended chamber temperature°C45–60 (Bambu Lab)[2]Not documented
Part cooling fan0–80 % (Bambu Lab)[2]Not documented
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[12][15]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s14 at Bambu Lab's 180 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][16]Not documented
Warping tendency1–5Moderate — needs adhesion aid or draught shield; Bambu Lab positions the fibre as reducing warping[2]Severe — heated chamber needed[13]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[12]Not documented
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[17]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[12]Expert / industrial hardware only[13][14]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[12]Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[13]
Abrasiveness1–5Highly abrasive — standard GF composite[12]Non-abrasive when unfilled[3]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech specifies a hardened 0.4 mm minimum nozzle and 0.25 mm layers or higher for the glass-filled grade[18][19]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[20]
Heat-creep / jam sensitivity1–5Slightly sensitive[15]Not documented
Hotend requirementNo special hot-end required[15]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.53 % saturated at 25 °C / 55 % RH (Bambu Lab)[2]Not documented
Equilibrium moisture content at ~50 % RH%0.53 saturated at 25 °C / 55 % RH (Bambu Lab)[2]0.37 in 24 h and 1.1 at saturation on extruded stock (ASTM D570)[21]
Drying temperature & time80 °C for 8 h (Bambu Lab)[2]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[22]Not documented
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures; absorbed water flashes to steam in the hotend and shows as bubbling and poor layer adhesion[22]No dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[20]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[22]Not documented
Mechanical Properties
Tensile strength (XY)MPa36 ± 3 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 68 at break[2][1]55 (printed XY, ISO 527, 3DXTech) and 55 (printed on side long edge, ASTM D638, Stratasys PPSF); 79 at yield on extruded stock[3][4][21]
Young's modulusMPa3160 ± 170 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 4210[2][1]2100 (printed, ASTM D638, Stratasys PPSF) and 2310 (printed XY, ISO 527, 3DXTech); 2344 on extruded stock[3][4][21]
Elongation at break%6.3 ± 1.2 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 2 at break[2][1]3 (printed, ISO 527 and ASTM D638) against 60 on extruded stock — printing costs PPSU almost all of its ductility[3][4][21]
Flexural strengthMPa68 ± 4 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 70[2][1]110 (printed, ISO 178 and ASTM D790, 3DXTech and Stratasys PPSF agree); 91 on extruded stock[3][4][21]
Flexural modulusMPa2860 ± 130 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 4420[2][1]2200 (printed, ASTM D790, Stratasys PPSF) and 2215 (printed XY, ISO 178, 3DXTech)[3][4]
Charpy impact, notchedkJ/m²4.2 ± 1.1 printed XY, ISO 179, notched (Bambu Lab)[2]Not documented
Other impact dataCharpy unnotched 14.5 ± 1.5 printed XY (Bambu Lab, ISO 179)[2]Izod notched 58.7 J/m and unnotched 165.5 J/m (printed, ASTM D256 Method A, Stratasys PPSF); 160 J/m notched on extruded stock[4][21]
Layer adhesion / Z tensileMPa29 ± 3 printed Z, ISO 527 (Bambu Lab)[2]Not documented
Brittleness1–5Brittle — snaps with little warning; notched Charpy falls from 21.5 to 4.2 kJ/m² against unfilled Bambu Lab ABS[2][23]Brittle — snaps with little warning[3]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell M86 on printed PPSF (ASTM D785, Stratasys); M96 on extruded PPSU stock (and an unlabelled 123)[4][21]
Creep resistance / sustained load1–5Good — no creep test found; chopped glass fibre lifts modulus to 3160 MPa against 2200 for unfilled Bambu Lab ABS[2][23]Good. Printed PPSF holds 189 °C heat deflection at 1.8 MPa (ASTM D648) and extruded stock is rated 149 °C long-term service, but Ensinger does not claim the creep resistance it claims for PSU and PPS[4][21]
Fatigue / repeated-flex resistance1–5Below average — no S-N curve found; notched Charpy falls to 4.2 kJ/m² against 21.5 for unfilled Bambu Lab ABS[2][23]Not documented
Elasticity / flexibility1–5Rigid[2]Rigid[3]
Z strength as % of XY%81 (Bambu Lab, printed Z against XY tensile)[2]Not documented
Thermal Properties
HDT at 0.45 MPa°C99 (ISO 75, 0.45 MPa, Bambu Lab) against 87 for unfilled Bambu Lab ABS[2][23]190 (printed XY, ISO 75 at 0.45 MPa, 3DXTech)[3]
HDT at 1.8 MPa°C88 (ISO 75, 1.8 MPa, Bambu Lab) against 84 for unfilled Bambu Lab ABS[2][23]189 (printed, ASTM D648 at 264 psi, Stratasys PPSF); 207 on extruded stock, converted from 405 °F[4][21]
Glass transition (Tg)°CNot documented230 (DSC) — the highest glass transition in the dataset[3]
Continuous service temperature°CNot documented149 long-term service on extruded PPSU stock, converted from 300 °F[21]
Thermal expansion (CTE)µm/m·KNot documented55.0 (printed PPSF, ASTM D696; source states 5.5e-5 mm/mm/°C) and 55.8 on extruded stock (ASTM D696, from 3.1e-5 in/in/°F)[4][21]
Flammability / UL 94Not documentedUL 94 V-0 at 1.5 mm, rated on the base resin[3]
Environment & Chemical
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[24]Withstands repeated steam autoclaving, the usual reason to choose PPSU over PSU; Stratasys also lists PPSF as passing 24 h stress-crack exposure to antifreeze, petrol, motor oil, power-steering, transmission and washer fluid at 23 °C and 100 °C[3][4]
Food contactNot food safe — Polymaker cites potential chemical leaching[17]Not documented
Biodegradability / compostabilityNot biodegradable[17]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[17]Not documented
Electrical & ESD propertiesNot documentedVolume resistivity 5e13 to 1.5e14 ohm-cm and dielectric strength 80-290 V/mil on printed PPSF (ASTM D257, D149)[4]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[25][12]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[25]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[25]Not documented
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[25]Not documented
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[25][12]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[25][12]Ventilated room or enclosure recommended[25]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Not documented
Post-Processing
Sanding & machiningSands well and takes filler before painting[17]Not documented
Painting & finishingPaints readily after light abrasion[17]Not documented
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[26][12]Not documented
Dimensional accuracy & detailBambu Lab describes a smooth matte finish with micro-spot gloss that blurs layer lines[2]Not documented
Solvents & Solubility
Soluble inAcetone dissolves the resin and leaves the fibre as sludge; MEK, THF, ethyl acetate and chlorinated solvents do the same.[27][24]Dichloromethane dissolves it at 23 °C at every stress level; acetone solvates and softens unstressed PPSU (Solvay ESCR).[28]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[27][29]MEK ruptures stressed parts and toluene crazes them above 13.8 MPa; glass-filled grades survive where unfilled craze.[28]
Solvent welding & smoothing agentAcetone vapour reaches only the resin fraction, so the fibre is left standing proud of the smoothed surface.[30][24]Dichloromethane cements PPSU and NMP softens residual resin; both are laboratory reagents, not workshop stock.[28]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. FibreX ABS+GF10 Glass Fiber ABS Technical Data Sheet 3DXTech · 2026-08 · tds
  2. Bambu Filament Technical Data Sheet V1.0 — ABS-GF Bambu Lab · 2026-08 · tds
  3. ThermaX PPSU Technical Data Sheet v3 3DXTech · 2026-08 · tds
  4. PPSF (polyphenylsulfone) — FDM Data Sheet Stratasys · 2018-06 · tds
  5. ABS-GF — product page Bambu Lab US Store · 2026-08 · vendor
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. Siraya Tech Fibreheart ABS-GF Filament product page Siraya Tech · 2026-08 · vendor
  8. SUNLU ABS-GF (ABS Glass Fiber) 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  9. Kimya PPSU-S Natural 1.75 mm 500 g igo3d · 2026-08 · vendor
  10. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  11. IEMAI 3D PPSU 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  12. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  13. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  14. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  15. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. ABS — material basics Polymaker Wiki · 2026-08 · doc
  18. FIBREX ABS+GF — product page (print recommendations) 3DXTech · 2026-08 · doc
  19. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  20. THERMAX PPSU — product page (print recommendations) 3DXTech · 2026-08 · doc
  21. TECASON P black (PPSU) — stock shape properties Ensinger · 2026-08 · tds
  22. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  23. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  24. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  25. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  26. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  27. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  28. Radel PPSU, Veradel PESU, Acudel modified PPSU Design Guide — environmental stress cracking tables Solvay Specialty Polymers · 2026-08 · tds
  29. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  30. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc