ABS-GF vs PLA-GF

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre ABS (ABS-GF) guideGlass-fibre PLA (PLA-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS-GF comparisonsMore PLA-GF comparisons
ABS-GF vs PLA-GF — documented properties and sources
PropertyGlass-fibre ABS (ABS-GF)ABSGlass-fibre PLA (PLA-GF)PLA
Market snapshot
Listing priceUSD/kg; dated snapshots$34.99/kg median; $24.49–$73.33/kg across 4 dated product listings$44.99/kg median; $29.99–$59.99/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryABS reinforced with chopped glass fibre — 3DXTech's grade is nominally 10 wt%[1][2]PLA filled with chopped glass fibre — 12 wt% (Polymaker HT-PLA-GF), 15–20 wt% (eSUN PLA-GF). Bambu Lab PLA Galaxy uses glass microspheres, not fibre, and is not equivalent[3][4][5]
Densityg/cm³1.08 (Bambu Lab) and 1.15 (3DXTech), ISO 1183[2][1]1.31 (eSUN) to 1.337 (Polymaker), ISO 1183 / GB/T 1033[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 24–73; the middle of the market is about 35[6][7][8][9]1 kg spools cluster near 30[10][11]
Price range across brandsUSD/kg24–73 across brands; Siraya Tech 24, Bambu Lab 30, SUNLU 40, 3DXTech 73[6][7][8][9]30–60 across brands; Polymaker 30, Proto-pasta 60[10][11]
Market availability1–5Available from several mainstream brands[6][7]Niche, a handful of specialist brands[10][11][4]
Spool sizes & diameters1.75 and 2.85 mm; 750 g and 1 kg spools[7][6]1.75 mm; 0.5 and 1 kg spools[11][12]
Typical applicationsStiff, dimensionally stable enclosure and tooling parts; Bambu Lab notes the fibre blurs layer lines into a matte finish[2]Stiff brackets and fixtures; the Polymaker grade is aimed at parts annealed for heat resistance[3]
Printing Parameters
Nozzle temperature°C240–280 (Bambu Lab)[2]210–230 (Polymaker HT-PLA-GF)[3]
Bed temperature°C80–100 (Bambu Lab)[2]25–60 (Polymaker HT-PLA-GF)[3]
Enclosure / chamber requirement1–5Enclosure recommended — Bambu Lab specifies a 45–60 °C chamber[2][13]Open frame is fine[3]
Recommended chamber temperature°C45–60 (Bambu Lab)[2]Not documented
Part cooling fan0–80 % (Bambu Lab)[2]Fan on — eSUN specifies 100 %[4]
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[13][14]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s14 at Bambu Lab's 180 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][15]28 at Polymaker's stated 350 mm/s on a 0.4 mm nozzle at 0.2 mm layer; eSUN prints its specimens at 60 mm/s[3][4][15]
Warping tendency1–5Moderate — needs adhesion aid or draught shield; Bambu Lab positions the fibre as reducing warping[2]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[13]Not documented
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[16]Not documented
Shrinkage%Not documented0.05 in X-Y and Z, 0.10 diagonal (Polymaker HT-PLA-GF)[3]
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[13]Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[13]Hardened steel required[3]
Abrasiveness1–5Highly abrasive — standard GF composite[13]Highly abrasive — standard GF composite[3]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech specifies a hardened 0.4 mm minimum nozzle and 0.25 mm layers or higher for the glass-filled grade[17][18]Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[18]
Heat-creep / jam sensitivity1–5Slightly sensitive[14]Not documented
Hotend requirementNo special hot-end required[14]Hardened steel or ruby nozzle; Polymaker's own slicer preset sets a minimum nozzle hardness of 40 HRC[3]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.53 % saturated at 25 °C / 55 % RH (Bambu Lab)[2]Moderate — the PLA matrix takes up 0.40–0.51 % saturated; no glass-filled grade publishes its own figure[19][20]
Equilibrium moisture content at ~50 % RH%0.53 saturated at 25 °C / 55 % RH (Bambu Lab)[2]Not documented
Drying temperature & time80 °C for 8 h (Bambu Lab)[2]60 °C for 6 h (Polymaker HT-PLA-GF)[3]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[21]Not documented
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures; absorbed water flashes to steam in the hotend and shows as bubbling and poor layer adhesion[21]Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[21]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[21]Not documented
Mechanical Properties
Tensile strength (XY)MPa36 ± 3 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 68 at break[2][1]50.1 as printed and 50.2 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 59.3 by GB/T 1040[3][4]
Young's modulusMPa3160 ± 170 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 4210[2][1]3794 as printed, 4207 annealed, printed XY, ISO 527 (Polymaker)[3]
Elongation at break%6.3 ± 1.2 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 2 at break[2][1]2.77 as printed, 2.3 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 7.99[3][4]
Flexural strengthMPa68 ± 4 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 70[2][1]86.4 printed XY, ISO 178 (Polymaker)[3]
Flexural modulusMPa2860 ± 130 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 4420[2][1]3685 printed XY, ISO 178 (Polymaker); eSUN quotes 4415 flexural modulus by GB/T 9341[3][4]
Charpy impact, notchedkJ/m²4.2 ± 1.1 printed XY, ISO 179, notched (Bambu Lab)[2]5.31 ± 0.46 as printed and 4.92 ± 0.50 annealed (printed XY, ISO 179, notched); Z 4.28 ± 0.18[3]
Other impact dataCharpy unnotched 14.5 ± 1.5 printed XY (Bambu Lab, ISO 179)[2]Izod 10.16 kJ/m² (eSUN, GB/T 1843)[4]
Layer adhesion / Z tensileMPa29 ± 3 printed Z, ISO 527 (Bambu Lab)[2]23.7 as printed, 22.5 annealed, printed Z, ISO 527 (Polymaker)[3]
Brittleness1–5Brittle — snaps with little warning; notched Charpy falls from 21.5 to 4.2 kJ/m² against unfilled Bambu Lab ABS[2][22]Very brittle — elongation at break 2.77 % in XY and 0.85 % in Z[3]
Creep resistance / sustained load1–5Good — no creep test found; chopped glass fibre lifts modulus to 3160 MPa against 2200 for unfilled Bambu Lab ABS[2][22]Poor — no GF-grade creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[23][24][25]
Fatigue / repeated-flex resistance1–5Below average — no S-N curve found; notched Charpy falls to 4.2 kJ/m² against 21.5 for unfilled Bambu Lab ABS[2][22]Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and elongation at break falls to 2.77 % in XY and 0.85 % in Z[26][3]
Elasticity / flexibility1–5Rigid[2]Rigid[3]
Z strength as % of XY%81 (Bambu Lab, printed Z against XY tensile)[2]47 as printed (23.7 Z against 50.1 XY), printed[3]
Wear resistance & frictionNot documentedeSUN describes high wear resistance and positions the grade for wear parts[4]
Thermal Properties
HDT at 0.45 MPa°C99 (ISO 75, 0.45 MPa, Bambu Lab) against 87 for unfilled Bambu Lab ABS[2][22]75.5 as printed, 114.7 after annealing (ISO 75, 0.45 MPa) — the point of the material[3]
HDT at 1.8 MPa°C88 (ISO 75, 1.8 MPa, Bambu Lab) against 84 for unfilled Bambu Lab ABS[2][22]59.7 as printed, 84 after annealing (ISO 75, 1.8 MPa)[3]
Glass transition (Tg)°CNot documented59.8 (DSC)[3]
Melting point / Vicat°CNot documented174.9 peak melt (DSC); Vicat 148.9 as printed, 148.3 annealed[3]
Annealing responseNot documentedAnnealing lifts HDT at 0.45 MPa from 75.5 to 114.7 °C and modulus from 3794 to 4207 MPa[3]
Environment & Chemical
UV resistance1–5Not documentedDegrades within weeks outdoors[27]
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[28]Not documented
Food contactNot food safe — Polymaker cites potential chemical leaching[16]Not documented
Biodegradability / compostabilityNot biodegradable[16]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[16]Not documented
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[29][13]Low hazard — minimal VOC and particle emission[29]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[29]Not documented
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[29]Not documented
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[29][13]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[29][13]None needed in a normal room[29]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Glass fibre is bound in the matrix; avoid inhaling sanding dust[30]
Post-Processing
Sanding & machiningSands well and takes filler before painting[16]Not documented
Painting & finishingPaints readily after light abrasion[16]Not documented
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[31][13]Not documented
Dimensional accuracy & detailBambu Lab describes a smooth matte finish with micro-spot gloss that blurs layer lines[2]Near-zero shrinkage — 0.05 % in X-Y and Z (Polymaker)[3]
Solvents & Solubility
Soluble inAcetone dissolves the resin and leaves the fibre as sludge; MEK, THF, ethyl acetate and chlorinated solvents do the same.[32][28]Chloroform dissolves the PLA matrix (10 % w/v, 2–4 h at 23 °C) and leaves the filler as loose sludge; laboratory reagent.[33]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[32][34]Acetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[33][35]
Solvent welding & smoothing agentAcetone vapour reaches only the resin fraction, so the fibre is left standing proud of the smoothed surface.[35][28]Chloroform vapour attacks only the resin fraction, so the filler is left standing proud; no workshop-safe agent exists.[36][35]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. FibreX ABS+GF10 Glass Fiber ABS Technical Data Sheet 3DXTech · 2026-08 · tds
  2. Bambu Filament Technical Data Sheet V1.0 — ABS-GF Bambu Lab · 2026-08 · tds
  3. Polymaker HT-PLA-GF Technical Data Sheet V1.1 Polymaker · 2026-08 · tds
  4. eSUN ePLA-GF Technical Data Sheet V1.0 (Nov 2023) eSUN (copy hosted on 3d.nice-cdn.com) · 2023-11 · tds
  5. Bambu Filament Technical Data Sheet V1.0 — PLA Galaxy Bambu Lab · 2026-08 · tds
  6. ABS-GF — product page Bambu Lab US Store · 2026-08 · vendor
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. Siraya Tech Fibreheart ABS-GF Filament product page Siraya Tech · 2026-08 · vendor
  9. SUNLU ABS-GF (ABS Glass Fiber) 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  10. Polymaker HT-PLA-GF — product page Polymaker Shop · 2026-08 · vendor
  11. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  12. Polymaker product catalogue Polymaker · 2026-08 · vendor
  13. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  14. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  15. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  16. ABS — material basics Polymaker Wiki · 2026-08 · doc
  17. FIBREX ABS+GF — product page (print recommendations) 3DXTech · 2026-08 · doc
  18. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  19. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  20. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  21. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  22. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  23. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  24. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  27. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  28. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  29. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  30. StoneFil safety data sheet Formfutura · 2026-08 · msds
  31. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  32. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  33. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  34. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  35. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  36. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper