3D Printing Info

Filament comparison

ABS-ESD vs PPS-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

ESD-safe ABS guideFibre-reinforced PPS guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS-ESD comparisonsMore PPS-CF comparisons
ABS-ESD vs PPS-CF — documented properties and sources
PropertyESD-safe ABSABSFibre-reinforced PPSHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$102.50/kg median; $47.00–$166.67/kg across 4 dated product listings$139.98/kg median; $119.98–$174.17/kg across 5 dated product listings
Identity & Market
Base polymer / chemistryABS compounded with a conductive carbon filler for static-dissipative parts[1]Carbon-fibre reinforced PPS — Polymaker's Fiberon grade is nominally 10 wt%[2]
Densityg/cm³1.09 (ISO 1183)[1]1.29 (Fiberon PPS-CF10) and 1.36 (Fiberon PPS-GF20), ISO 1183[2][3]
Typical priceUSD/kg1 kg-equivalent spools span 47–167; the middle of the market is about 103[4][5][6]1 kg-equivalent spools span 93–174; the middle of the market is about 140[7][8][9][10]
Price range across brandsUSD/kg47–167 across brands; IEMAI 47, YXPOLYER 65, 3DXTech 140 at 750 g pricing; the EMI-shielding ABS grade runs 167[4][5][6]93-174 across brands and formats; Polymaker Fiberon PPS-GF20 93 at 3 kg, IEMAI 3D CF-PPS 131 at 750 g, LEHVOSS Luvocom 3F PPS CF 9938 164 at 2.3 kg, Bambu Lab PPS-CF 174 at 750 g[7][8][9][10]
Market availability1–5Niche, a handful of specialist brands[4]Available from several mainstream brands[7][8][9]
Spool sizes & diameters1.75 and 2.85 mm; 750 g spools[4]1.75 mm; 0.5 kg spools[7]
Typical applicationsElectronics handling fixtures, trays and jigs used around static-sensitive parts[1]Chemical and automotive parts needing PPS chemistry with structural stiffness[2]
Printing Parameters
Enclosure / chamber requirement1–5Enclosure recommended[11]Enclosure required (passive) — Polymaker states its Fiberon PPS-CF10 needs no heated chamber, unlike the unfilled sulfones and PAEKs[2]
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[11][12]Not documented
Warping tendency1–5High — enclosure needed for reliable large parts[11]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[11]Not documented
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[13]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile[11]Expert / industrial hardware only[2]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[1]Hardened steel required[2]
Abrasiveness1–5Moderately abrasive — conductive carbon filler[1]Highly abrasive — standard CF composite[2]
Nozzle clog risk1–5Low — 3DXTech lists no special nozzle concerns and no minimum layer height for its ESD-ABS, only an 80 °C pre-dry[14]High — jams from moisture, heat creep or particles; Polymaker specifies hardened steel or ruby nozzles for carbon-filled PPS and Prusa lists composites as a higher clogging risk[15][16]
Heat-creep / jam sensitivity1–5Slightly sensitive[12]Not documented
Hotend requirementNo special hot-end required[12]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — the ABS matrix takes up 0.51–0.65 % saturated at 25 °C / 55 % RH and 3DXTech specifies a 80 °C, 4 h pre-dry[17][18][14]Low (0.1–0.3 %) — 0.225 % equilibrium for Fiberon PPS-CF10 and 0.11 % for PPS-GF20[2][3]
Equilibrium moisture content at ~50 % RH%Not documented0.225 equilibrium (Fiberon PPS-CF10); 0.11 (PPS-GF20)[2][3]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[19]Not documented
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures; absorbed water flashes to steam in the hotend and shows as bubbling and poor layer adhesion[19]No dry-versus-conditioned figures are published; equilibrium uptake is 0.225 % and Polymaker specifies a 100 °C, 10 h dry[2]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[19]Not documented
Mechanical Properties
Tensile strength (XY)MPa58 at break (printed XY, ISO 527) — the conductive filler raises strength above the unfilled grade's 42[1][20]59.4 ± 1.3 (PPS-CF10) and 64.1 ± 2.1 (PPS-GF20) printed XY, ISO 527[2][3]
Young's modulusMPa2130 (printed XY, ISO 527)[1]5446.7 ± 149.0 (PPS-CF10) and 4552.0 ± 54.6 (PPS-GF20) printed XY, ISO 527[2][3]
Elongation at break%4 at break (printed XY, ISO 527)[1]1.4 ± 0.1 (PPS-CF10) and 2.0 ± 0.2 (PPS-GF20) printed XY, ISO 527 — the lowest elongation in the dataset[2][3]
Flexural strengthMPa80 (printed XY, ISO 178)[1]Not documented
Flexural modulusMPa2275 (printed XY, ISO 178)[1]Not documented
Charpy impact, notchedkJ/m²Not documented5.3 ± 0.2 printed XY for PPS-CF10 and 7.3 ± 0.2 for PPS-GF20, ISO 179 notched[2][3]
Layer adhesion / Z tensileMPaNot documented32.0 ± 5.1 (PPS-CF10) and 22.9 ± 0.8 (PPS-GF20) printed Z, ISO 527[2][3]
Brittleness1–5Moderate[1]Very brittle — cracks or shatters easily; elongation at break 1.4 %[2]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell 105 (and R124) on extruded unfilled PPS stock (ASTM D785); no figure is published for a fibre-filled PPS filament[21]
Creep resistance / sustained load1–5Moderate — no creep test found; Tg of 105 °C keeps room-temperature service far below softening[1]Excellent — holds load for years. Ensinger lists high creep resistance for unfilled PPS stock and Spectrum states creep resistance is unchanged under continuous load at high temperature; the fibre raises heat deflection to 252 °C at 0.45 MPa[21][22][2]
Fatigue / repeated-flex resistance1–5Below average — no S-N curve found; elongation at break 4 %, well below unfilled ABS[1][20]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[2]
Z strength as % of XY%Not documented54 (PPS-CF10) and 36 (PPS-GF20), printed[2][3]
Thermal Properties
HDT at 0.45 MPa°CNot documented252.5 (PPS-CF10) and 236.3 (PPS-GF20), printed, ISO 75 at 0.45 MPa[2][3]
HDT at 1.8 MPa°CNot documented133 (PPS-CF10) and 125.8 (PPS-GF20), printed, ISO 75 at 1.8 MPa[2][3]
Glass transition (Tg)°C105 (DSC)[1]97.7 (PPS-CF10) and 95.0 (PPS-GF20), DSC[2][3]
Melting point / Vicat°CNot documented279.7 (PPS-CF10) and 279.6 (PPS-GF20) melting, DSC; Vicat 267.5 and 272.5 (ISO 306)[2][3]
Continuous service temperature°CNot documented170 long-term service on extruded PPS stock, converted from 338 °F; no figure published for the carbon-filled grade[21]
Environment & Chemical
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[23]Outstanding — PPS resists essentially all solvents below 200 °C[15]
Food contactNot food safe — Polymaker cites potential chemical leaching[13]Not documented
Biodegradability / compostabilityNot biodegradable[13]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[13]Not documented
Electrical & ESD propertiesSurface resistance 10⁷–10⁹ ohm/sq, the static-dissipative band (ASTM D257), against above 10¹³ for unfilled ABS[1][20]Surface resistivity above 10¹² ohm — insulating (ANSI/ESD S11.11)[2][3]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[24][11]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[24]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[24]Not documented
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[24]Not documented
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[24][11]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[24][11]Ventilated room or enclosure recommended[24]
Dust & fibre handling hazardConductive carbon filler is bound in the matrix; avoid inhaling sanding dust[1]Fibre is bound in the matrix; sanding dust should not be inhaled[2]
Post-Processing
Sanding & machiningSands well and takes filler before painting[13]Not documented
Painting & finishingPaints readily after light abrasion[13]Not documented
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[25][11]Not documented
Solvents & Solubility
Soluble inAcetone dissolves it — the basis of ABS slurry; so do MEK, THF, ethyl acetate, chloroform, dichloromethane and toluene.[26][23]None — PPS does not dissolve in any known solvent below 200 °C.[27][26]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[26][28]Nothing at 23 °C; Ensinger rates it only conditionally resistant to benzene, dichloromethane, toluene and pyridine.[26]
Solvent welding & smoothing agentAcetone: about 20 min of vapour at 80 °C over 5 mm of liquid. Prusa measured layer adhesion more than doubled.[29]None — no solvent welds or smooths PPS.[27]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. 3DXSTAT ESD-ABS Technical Data Sheet 3DXTech · 2026-08 · tds
  2. Fiberon PPS-CF10 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  3. Fiberon PPS-GF20 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  4. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  5. IEMAI ESD-ABS 3D Printing Filament product page IEMAI 3D · 2026-08 · vendor
  6. YXPOLYER ABS ESD product page YXPOLYER · 2026-08 · vendor
  7. Polymaker product catalogue Polymaker · 2026-08 · vendor
  8. Bambu Lab PPS-CF Black, spool (750 g) 3DJAKE · 2026-08 · vendor
  9. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  10. IEMAI 3D CF-PPS 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  11. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  12. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  13. ABS — material basics Polymaker Wiki · 2026-08 · doc
  14. 3DXSTAT ESD-ABS — product page (print recommendations) 3DXTech · 2026-08 · doc
  15. PPS — material basics Polymaker Wiki · 2026-08 · doc
  16. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  17. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  18. Polymaker ABS Pro Technical Data Sheet V1 (2026-05-29) Polymaker · 2026-05 · tds
  19. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  20. 3DXMAX ABS Technical Data Sheet 3DXTech · 2026-08 · tds
  21. TECATRON natural (PPS) — stock shape properties Ensinger · 2026-08 · tds
  22. Spectrum PPS AM230 Technical Data Sheet Spectrum Filaments · 2022-04 · tds
  23. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  24. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  25. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  26. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  27. PPS (Polyphenylene sulfide) — Knowledge Base Prusa Research · 2026-08 · doc
  28. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  29. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc