3D Printing Info

Filament comparison

ABS-ESD vs PEI 1010

Compare printing settings, strength, heat resistance, dated prices and sources.

ESD-safe ABS guidePEI (ULTEM 1010) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS-ESD comparisonsMore PEI 1010 comparisons
ABS-ESD vs PEI 1010 — documented properties and sources
PropertyESD-safe ABSABSPEI (ULTEM 1010)HIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$102.50/kg median; $47.00–$166.67/kg across 4 dated product listings$281.22/kg median; $195.00–$698.00/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryABS compounded with a conductive carbon filler for static-dissipative parts[1]Polyetherimide, ULTEM 1010 grade — the higher-temperature, food- and medical-contact PEI[2][3]
Densityg/cm³1.09 (ISO 1183)[1]1.27 (ISO 1183, 3DXTech and Prusament); 1.29 specific gravity on moulded plaques (ASTM D792, Stratasys)[2][3][4]
Typical priceUSD/kg1 kg-equivalent spools span 47–167; the middle of the market is about 103[5][6][7]1 kg-equivalent spools span 195–698; the middle of the market is about 270[5][8][9][10][11]
Price range across brandsUSD/kg47–167 across brands; IEMAI 47, YXPOLYER 65, 3DXTech 140 at 750 g pricing; the EMI-shielding ABS grade runs 167[5][6][7]195-698 across brands and grades; 3DXTech ThermaX PEI 1010 195 at 2 kg, IEMAI 3D 223 at 1 kg, 3D4Makers 270 at 2 kg, Prusament 292 at 500 g, Kimya 347 at 500 g, 3DXTech ESD-PEI 1010 698 at 500 g[5][8][9][10][11]
Market availability1–5Niche, a handful of specialist brands[5]Niche, a handful of specialist brands[5][8][9][10]
Spool sizes & diameters1.75 and 2.85 mm; 750 g spools[5]1.75 and 2.85 mm; 200 g to 2 kg spools, plus Stratasys canisters[5][10][4]
Typical applicationsElectronics handling fixtures, trays and jigs used around static-sensitive parts[1]Autoclavable tooling, food-contact fixtures and parts that must hold load near 200 °C[3]
Printing Parameters
Nozzle temperature°CNot documented410 ± 10 (Prusament) — the hottest nozzle in the dataset[3]
Bed temperature°CNot documented140–160 (Prusament); 130–140 (3DXTech)[3][2]
Enclosure / chamber requirement1–5Enclosure recommended[12]Actively heated chamber required — Prusa specifies 90 °C[3]
Recommended chamber temperature°CNot documented90 (Prusament)[3]
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[12][13]PA nylon sheet or powder-coated sheet with high-temperature glue (Prusament)[3]
Warping tendency1–5High — enclosure needed for reliable large parts[12]Severe — heated chamber needed[3]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[12]Not documented
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[14]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile[12]Expert / industrial hardware only[3][15]
Extruder requirementNot documentedA hot end rated to 420 °C, a heated chamber and a high-temperature bed; Prusa dries the filament at 150 °C for 6–8 h before printing[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[1]Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[3]
Abrasiveness1–5Moderately abrasive — conductive carbon filler[1]Non-abrasive when unfilled[2]
Nozzle clog risk1–5Low — 3DXTech lists no special nozzle concerns and no minimum layer height for its ESD-ABS, only an 80 °C pre-dry[16]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 150 °C pre-dry before every print[17]
Heat-creep / jam sensitivity1–5Slightly sensitive[13]Not documented
Hotend requirementNo special hot-end required[13]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — the ABS matrix takes up 0.51–0.65 % saturated at 25 °C / 55 % RH and 3DXTech specifies a 80 °C, 4 h pre-dry[18][19][16]Not documented
Equilibrium moisture content at ~50 % RH%Not documented0.4 in 24 h and 0.7 in 7 days at 24 °C and 22 % RH (Prusament)[3]
Drying temperature & timeNot documented150 °C for 6–8 h (Prusament) — the hottest drying schedule in the dataset[3]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[20]Not documented
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures; absorbed water flashes to steam in the hotend and shows as bubbling and poor layer adhesion[20]No dry-versus-conditioned figures are published; 3DXTech mandates a 150 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[17]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[20]Not documented
Mechanical Properties
Tensile strength (XY)MPa58 at break (printed XY, ISO 527) — the conductive filler raises strength above the unfilled grade's 42[1][21]79-95 printed in plane: Stratasys 79.2 (F900 T14) to 91.6 (F3300 N500) at break in XZ, ASTM D638; Prusament 95 +/- 3.5 at yield printed horizontal, ISO 527-1; 3DXTech quotes 56 (ISO 527)[4][3][2]
Young's modulusMPa2130 (printed XY, ISO 527)[1]2300-3040 printed in plane: Prusament 2300 +/- 100 horizontal (ISO 527-1), Stratasys 2920-3040 in XZ (ASTM D638); 3DXTech quotes 2500[4][3][2]
Elongation at break%4 at break (printed XY, ISO 527)[1]4.0-4.1 at break in XZ (ASTM D638, Stratasys); Prusament gives 6.6 +/- 0.7 at yield printed horizontal (ISO 527-1); 3DXTech quotes 3[4][3][2]
Flexural strengthMPa80 (printed XY, ISO 178)[1]128 at 5 % strain (F900 T14) and 144 at break (F3300) printed XZ, ASTM D790; Prusament 98 +/- 6.5 horizontal and 138 +/- 5.3 vertical (ISO 178); 3DXTech quotes 110[4][3][2]
Flexural modulusMPa2275 (printed XY, ISO 178)[1]2910-3260 printed XZ (ASTM D790, Stratasys); Prusament 2300 horizontal and 2700 vertical (ISO 178); 3DXTech quotes 2510[4][3][2]
Charpy impact, notchedkJ/m²Not documented3.4 ± 0.9 printed horizontal and 3.6 ± 0.4 printed vertical, ISO 179-1 notched (Prusament)[3]
Other impact dataNot documentedIzod notched 26.6-36.3 J/m XZ against 21.7-27.2 J/m ZX; unnotched 260-406 J/m XZ against 68-116 J/m ZX (printed, ASTM D256/D4812, Stratasys). Charpy unnotched 19.7 +/- 4.3 horizontal and 39 +/- 10 vertical (Prusament, ISO 179-1)[4][3]
Layer adhesion / Z tensileMPaNot documented28-37 at break (printed ZX, ASTM D638, Stratasys F900 and F3300) against 72 +/- 5 at yield printed vertical (ISO 527-1, Prusament on the Pro HT90 with a 0.6 mm nozzle and 90 °C chamber) — a fourfold spread driven by chamber temperature and bead size[4][3]
Brittleness1–5Moderate[1]Brittle — snaps with little warning; notched Charpy only 3.4 kJ/m²[3]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedShore D 83.5 (Prusa Polymers method); Rockwell M110 / R126 on extruded PEI stock (ASTM D785)[3][22]
Creep resistance / sustained load1–5Moderate — no creep test found; Tg of 105 °C keeps room-temperature service far below softening[1]Excellent — holds load for years. Printed coupons hold 215 °C heat deflection at 1.8 MPa (ASTM D648) and extruded PEI stock is rated 170 °C long-term service[4][22]
Fatigue / repeated-flex resistance1–5Below average — no S-N curve found; elongation at break 4 %, well below unfilled ABS[1][21]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%Not documented36-40 (Stratasys ZX against XZ tensile at break, ASTM D638) against 76 (Prusament vertical against horizontal tensile yield, ISO 527-1)[4][3]
Thermal Properties
HDT at 0.45 MPa°CNot documented207 (Prusament, ISO 75 at 0.45 MPa) to 217 (printed XY 216.9 and XZ 217.1, ASTM D648 Method B at 66 psi, Stratasys); 3DXTech quotes 208[3][4][2]
HDT at 1.8 MPa°CNot documented194 (Prusament, ISO 75 at 1.8 MPa) to 215 (printed XY 215.1 and XZ 214.5, ASTM D648 Method B at 264 psi, Stratasys) — the highest heat deflection in the dataset[3][4]
Glass transition (Tg)°C105 (DSC)[1]209 (moulded plaque, ASTM D7426 inflection point, Stratasys); 217 (DSC, 3DXTech)[4][2]
Continuous service temperature°CNot documented170 long-term service on extruded PEI stock, converted from 338 °F; 200 short term[22]
Thermal expansion (CTE)µm/m·KNot documented36.1 (printed XY, -50 to 60 °C, ASTM E831), falling to 29.8 over 60-205 °C; ZX gives 32.5 over -50 to 110 °C and 16.2 over 110-165 °C[4]
Flammability / UL 94Not documentedUL 94 V-0 at 1.5 mm, rated on the base resin[2]
Environment & Chemical
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[23]Not documented
Food contactNot food safe — Polymaker cites potential chemical leaching[14]Not documented
Biodegradability / compostabilityNot biodegradable[14]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[14]Not documented
Electrical & ESD propertiesSurface resistance 10⁷–10⁹ ohm/sq, the static-dissipative band (ASTM D257), against above 10¹³ for unfilled ABS[1][21]Not documented
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[24][12]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[24]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[24]Not documented
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[24]Not documented
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[24][12]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[24][12]Ventilated room or enclosure recommended[24]
Dust & fibre handling hazardConductive carbon filler is bound in the matrix; avoid inhaling sanding dust[1]Not documented
Post-Processing
Sanding & machiningSands well and takes filler before painting[14]Not documented
Painting & finishingPaints readily after light abrasion[14]Not documented
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[25][12]Not documented
Solvents & Solubility
Soluble inAcetone dissolves it — the basis of ABS slurry; so do MEK, THF, ethyl acetate, chloroform, dichloromethane and toluene.[26][23]Chlorinated hydrocarbons — dichloromethane and chloroform — are solvents for polyetherimide. Laboratory reagents.[27][26]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[26][28]Acetone, MEK, benzene, toluene and butyl acetate craze or stress-crack it; alcohols, fuels and dilute acids do not.[26][27]
Solvent welding & smoothing agentAcetone: about 20 min of vapour at 80 °C over 5 mm of liquid. Prusa measured layer adhesion more than doubled.[29]Dichloromethane is the only welding route, and it is a controlled carcinogen rather than a workshop material.[27][26]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. 3DXSTAT ESD-ABS Technical Data Sheet 3DXTech · 2026-08 · tds
  2. ThermaX PEI 1010 Technical Data Sheet v4 3DXTech · 2026-08 · tds
  3. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  4. ULTEM 1010 Resin — FDM Material Data Sheet Stratasys · 2026-06 · tds
  5. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  6. IEMAI ESD-ABS 3D Printing Filament product page IEMAI 3D · 2026-08 · vendor
  7. YXPOLYER ABS ESD product page YXPOLYER · 2026-08 · vendor
  8. Kimya PEI-1010 Amber Yellow 1.75 mm 500 g igo3d · 2026-08 · vendor
  9. Prusa Prusament PEI 1010 Natural (NFC), 1.75 mm / 500 g 3DJAKE · 2026-08 · vendor
  10. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  11. IEMAI 3D PEI 1010 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  12. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  13. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  14. ABS — material basics Polymaker Wiki · 2026-08 · doc
  15. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  16. 3DXSTAT ESD-ABS — product page (print recommendations) 3DXTech · 2026-08 · doc
  17. THERMAX PEI 1010 — product page (print recommendations) 3DXTech · 2026-08 · doc
  18. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  19. Polymaker ABS Pro Technical Data Sheet V1 (2026-05-29) Polymaker · 2026-05 · tds
  20. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  21. 3DXMAX ABS Technical Data Sheet 3DXTech · 2026-08 · tds
  22. TECAPEI natural (PEI) — stock shape properties Ensinger · 2026-08 · tds
  23. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  24. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  25. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  26. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  27. Radel PPSU, Veradel PESU, Acudel modified PPSU Design Guide — environmental stress cracking tables Solvay Specialty Polymers · 2026-08 · tds
  28. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  29. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc