Compare printing settings, strength, heat resistance, dated prices and sources.

Polypropylene (PP) guideFibre-reinforced PPS guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PP comparisonsMore PPS-CF comparisons
PP vs PPS-CF — documented properties and sources
PropertyPolypropylene (PP)POLYOLEFINFibre-reinforced PPSHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$46.56/kg median; $31.99–$53.00/kg across 4 dated product listings$139.98/kg median; $119.98–$174.17/kg across 5 dated product listings
Identity & Market
Base polymer / chemistryPolypropylene — a semi-crystalline polyolefin with no polar groups, so it neither absorbs water nor bonds to most bed surfaces[1][2]Carbon-fibre reinforced PPS — Polymaker's Fiberon grade is nominally 10 wt%[3]
Densityg/cm³0.91 (Prusa PP composite, ISO 1183) — the lightest common filament[4]1.29 (Fiberon PPS-CF10) and 1.36 (Fiberon PPS-GF20), ISO 1183[3][5]
Typical priceUSD/kg1 kg-equivalent spools span 27–53; the middle of the market is about 44[6][7][8][9]1 kg-equivalent spools span 93–174; the middle of the market is about 140[10][11][12][13]
Price range across brandsUSD/kg27–53 across brands; Reli3D 32 on Amazon, SUNLU 44 at 0.8 kg, Fiberlogy 49 at 750 g, IEMAI 3D 53, and the 3DJake PP listing spans 27–49[6][14][7][8][9]93-174 across brands and formats; Polymaker Fiberon PPS-GF20 93 at 3 kg, IEMAI 3D CF-PPS 131 at 750 g, LEHVOSS Luvocom 3F PPS CF 9938 164 at 2.3 kg, Bambu Lab PPS-CF 174 at 750 g[10][11][12][13]
Market availability1–5Available from several mainstream brands[14][7][6]Available from several mainstream brands[10][11][12]
Spool sizes & diameters1.75 and 2.85 mm; 0.75 kg spools are common[7]1.75 mm; 0.5 kg spools[10]
Typical applicationsLiving hinges, chemical-resistant containers, automotive clips and packaging prototypes[1]Chemical and automotive parts needing PPS chemistry with structural stiffness[3]
Printing Parameters
Nozzle temperature°C210–230 (Braskem-type PE/PP window); Formfutura's Centaur PP melts at 205 ± 15 °C[1]Not documented
Enclosure / chamber requirement1–5Enclosure recommended — Simplify3D lists an enclosure as a hardware requirement and Polymaker advises one below 70 °C ambient to stop warping and cracking[15][2]Enclosure required (passive) — Polymaker states its Fiberon PPS-CF10 needs no heated chamber, unlike the unfilled sulfones and PAEKs[3]
Part cooling fanPart cooling fan required (Simplify3D)[15]Not documented
Bed surface & adhesion aidPacking tape, a polypropylene sheet, or a PP-specific adhesive such as Magigoo PP — ordinary PLA and ABS adhesives do not hold it[15][2]Not documented
Warping tendency1–5High — enclosure needed for reliable large parts; PP's crystallinity drives shrinkage and Prusa recommends a brim on its PP grades[4][16]Not documented
Bed-adhesion difficulty1–5Very difficult — special plates or slurry required. PP bonds to almost nothing; a polypropylene-specific tape or adhesive is the normal answer[4][2]Not documented
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[2]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning; bed adhesion is the whole problem[2][4]Expert / industrial hardware only[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades — Simplify3D states no special hotend is required[15]Hardened steel required[3]
Abrasiveness1–5Non-abrasive when unfilled[15]Highly abrasive — standard CF composite[3]
Nozzle clog risk1–5Low — Simplify3D lists no special hotend requirement for PP and clogging is not among its listed drawbacks[17][15]High — jams from moisture, heat creep or particles; Polymaker specifies hardened steel or ruby nozzles for carbon-filled PPS and Prusa lists composites as a higher clogging risk[18][19]
Heat-creep / jam sensitivity1–5Slightly sensitive[15]Not documented
Hotend requirementNo special hot-end required (Simplify3D)[15]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Negligible (<0.1 % EMC) — Prusa measures 0.03 % in 24 h and 0.04 % in 7 days on its PP composite, the lowest figures it publishes for any filament[4]Low (0.1–0.3 %) — 0.225 % equilibrium for Fiberon PPS-CF10 and 0.11 % for PPS-GF20[3][5]
Equilibrium moisture content at ~50 % RH%0.03 after 24 h and 0.04 after 7 days at 24 °C / 22 % RH (Prusa Polymers, measured on its PP composite)[4]0.225 equilibrium (Fiberon PPS-CF10); 0.11 (PPS-GF20)[3][5]
Drying temperature & timeNo drying step is published for PP; uptake is below the level that affects printing[4]Not documented
Symptoms when wetBubbling and popping at the nozzle; Polymaker still advises a 70 °C dry for 4–6 h despite the low uptake[2]Not documented
Effect of moisture on strengthNot applicable in practice — with equilibrium uptake at 0.04 %, there is no moisture-driven strength loss to measure. Polymaker's sensitivity tiers put polyolefins below even PLA[4][17]No dry-versus-conditioned figures are published; equilibrium uptake is 0.225 % and Polymaker specifies a 100 °C, 10 h dry[3]
Storage requirementNo special storage needed[4]Not documented
Mechanical Properties
Tensile strength (XY)MPa12 at yield (Formfutura Centaur PP, ASTM D638)[1]59.4 ± 1.3 (PPS-CF10) and 64.1 ± 2.1 (PPS-GF20) printed XY, ISO 527[3][5]
Young's modulusMPa724 on extruded PP stock (ASTM D638; converted from 105,000 psi)[20]5446.7 ± 149.0 (PPS-CF10) and 4552.0 ± 54.6 (PPS-GF20) printed XY, ISO 527[3][5]
Elongation at break%Above 600 at break (Formfutura Centaur PP, ASTM D638)[1]1.4 ± 0.1 (PPS-CF10) and 2.0 ± 0.2 (PPS-GF20) printed XY, ISO 527 — the lowest elongation in the dataset[3][5]
Flexural strengthMPa31.0 on extruded PP stock (ASTM D790; converted from 4500 psi)[20]Not documented
Flexural modulusMPa402 flexural modulus (Formfutura Centaur PP, ASTM D790) — an order of magnitude below any rigid filament[1]Not documented
Charpy impact, notchedkJ/m²Not documented5.3 ± 0.2 printed XY for PPS-CF10 and 7.3 ± 0.2 for PPS-GF20, ISO 179 notched[3][5]
Other impact dataIzod notched 112 J/m on extruded PP stock, converted from 2.1 ft-lb/in (ASTM D256)[20]Not documented
Layer adhesion / Z tensileMPaNot documented32.0 ± 5.1 (PPS-CF10) and 22.9 ± 0.8 (PPS-GF20) printed Z, ISO 527[3][5]
Brittleness1–5Very ductile — bends far before failing[1]Very brittle — cracks or shatters easily; elongation at break 1.4 %[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell R102 (and M95) on extruded PP stock (ASTM D785)[20]Rockwell 105 (and R124) on extruded unfilled PPS stock (ASTM D785); no figure is published for a fibre-filled PPS filament[21]
Creep resistance / sustained load1–5Below average[1]Excellent — holds load for years. Ensinger lists high creep resistance for unfilled PPS stock and Spectrum states creep resistance is unchanged under continuous load at high temperature; the fibre raises heat deflection to 252 °C at 0.45 MPa[21][22][3]
Fatigue / repeated-flex resistance1–5Excellent — living hinges viable, the classic polypropylene application[1]Not documented
Elasticity / flexibility1–5Semi-flexible[1]Rigid[3]
Z strength as % of XY%Not documented54 (PPS-CF10) and 36 (PPS-GF20), printed[3][5]
Thermal Properties
HDT at 0.45 MPa°C74 on extruded PP stock (ASTM D648 at 66 psi; converted from 165 °F)[20]252.5 (PPS-CF10) and 236.3 (PPS-GF20), printed, ISO 75 at 0.45 MPa[3][5]
HDT at 1.8 MPa°CNot documented133 (PPS-CF10) and 125.8 (PPS-GF20), printed, ISO 75 at 1.8 MPa[3][5]
Glass transition (Tg)°CNot documented97.7 (PPS-CF10) and 95.0 (PPS-GF20), DSC[3][5]
Melting point / Vicat°C205 ± 15 melting (Formfutura Centaur PP)[1]279.7 (PPS-CF10) and 279.6 (PPS-GF20) melting, DSC; Vicat 267.5 and 272.5 (ISO 306)[3][5]
Continuous service temperature°CBounded by a melting point of 205 ± 15 °C and by the 158 °C heat deflection of the carbon-filled grade; no loaded-bar service figure is published for unfilled PP[1][4]170 long-term service on extruded PPS stock, converted from 338 °F; no figure published for the carbon-filled grade[21]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[4]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polypropylene chalks under UV[2]Not documented
Chemical resistanceExcellent against acids, alkalis and most solvents — the usual reason to choose PP[2]Outstanding — PPS resists essentially all solvents below 200 °C[18]
Water / humidity resistance in service1–5Excellent — essentially unaffected[4]Not documented
Food contactPolypropylene is a common food-packaging polymer, but no filament here carries a food-contact certification[2]Not documented
Biodegradability / compostabilityNot biodegradable[2]Not documented
RecyclabilityMechanically recyclable as resin code 5, but printed waste is not accepted in household collection[2]Not documented
Electrical & ESD propertiesNot documentedSurface resistivity above 10¹² ohm — insulating (ANSI/ESD S11.11)[3][5]
Health & Safety
Fume toxicity1–5Low hazard — minimal VOC and particle emission. Inferred: no polyolefin was among the nine filaments in the Azimi chamber study, so this is a family-level judgement rather than a measurement[23]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[23]
Ventilation / filtration requirement1–5Open a window / occasional ventilation. Inferred — no polyolefin was measured in the chamber study[23]Ventilated room or enclosure recommended[23]
Dust & fibre handling hazardNot documentedFibre is bound in the matrix; sanding dust should not be inhaled[3]
Post-Processing
Sanding & machiningSands poorly — the waxy surface loads abrasive paper[15]Not documented
Painting & finishingPaint and adhesives do not key to untreated PP; flame or plasma treatment is normally needed first[2]Not documented
Gluing & solvent weldingNothing common bonds untreated PP; flame or plasma treatment is needed before adhesives key[2]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[15]Not documented
Support material pairingPrints its own supports; no soluble support is rated for PP[15]Not documented
Dimensional accuracy & detailShrinkage and warping dominate; the low modulus means parts flex rather than hold tolerance[4]Not documented
Solvents & Solubility
Soluble inNone at room temperature; chloroform dissolves it at 60 °C and xylene at about 118 °C — the xylene-solubles route.[24][25]None — PPS does not dissolve in any known solvent below 200 °C.[26][27]
Softened or crazed byXylene, decalin, CCl4 and chlorobenzene are heavily absorbed at 20 °C; oleum, chlorosulphonic acid and bromine destroy it.[24]Nothing at 23 °C; Ensinger rates it only conditionally resistant to benzene, dichloromethane, toluene and pyridine.[27]
Solvent welding & smoothing agentNone — nothing softens PP at room temperature, so joints have to be welded thermally rather than chemically.[24]None — no solvent welds or smooths PPS.[26]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Centaur PP Technical Data Sheet Formfutura · 2026-08 · tds
  2. PP — material basics Polymaker Wiki · 2026-08 · doc
  3. Fiberon PPS-CF10 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  4. Prusament PP Carbon Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  5. Fiberon PPS-GF20 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  6. SUNLU product catalogue SUNLU · 2026-08 · vendor
  7. Fiberlogy PP Natural — product page 3DJake International · 2026-08 · vendor
  8. Reli3D Low Warp PP Filament 1.75 mm 1 kg Black — Amazon listing Amazon.com · 2026-08 · vendor
  9. IEMAI 3D PP 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  10. Polymaker product catalogue Polymaker · 2026-08 · vendor
  11. Bambu Lab PPS-CF Black, spool (750 g) 3DJAKE · 2026-08 · vendor
  12. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  13. IEMAI 3D CF-PPS 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  14. PP filament listing 3DJake International · 2026-08 · vendor
  15. Polypropylene — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  16. Prusament PP Glass Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  17. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  18. PPS — material basics Polymaker Wiki · 2026-08 · doc
  19. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  20. TECAFINE PP natural — stock shape properties Ensinger · 2026-08 · tds
  21. TECATRON natural (PPS) — stock shape properties Ensinger · 2026-08 · tds
  22. Spectrum PPS AM230 Technical Data Sheet Spectrum Filaments · 2022-04 · tds
  23. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  24. Pro-fax and Moplen polypropylene — Chemical Resistance Guide (20, 60 and 100 °C) LyondellBasell · 2026-08 · tds
  25. US 5,278,282 Polymer recycling by selective dissolution — xylene dissolution temperatures Nauman & Lynch, Rensselaer Polytechnic Institute · 1994-01 · paper
  26. PPS (Polyphenylene sulfide) — Knowledge Base Prusa Research · 2026-08 · doc
  27. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds