PP-GF vs PPS-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PP (PP-GF) guideFibre-reinforced PPS guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PP-GF comparisonsMore PPS-CF comparisons
PP-GF vs PPS-CF — documented properties and sources
PropertyGlass-fibre PP (PP-GF)POLYOLEFINFibre-reinforced PPSHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$49.09/kg median; $46.27–$86.01/kg across 3 dated product listings$139.98/kg median; $119.98–$174.17/kg across 5 dated product listings
Identity & Market
Base polymer / chemistryPolypropylene reinforced with chopped glass fibre[1][2]Carbon-fibre reinforced PPS — Polymaker's Fiberon grade is nominally 10 wt%[3]
Densityg/cm³1.12 (Prusament PP Glass Fiber, ISO 1183) — the glass lifts it above water[1]1.29 (Fiberon PPS-CF10) and 1.36 (Fiberon PPS-GF20), ISO 1183[3][4]
Typical priceUSD/kg1 kg-equivalent spools cluster near 49[5][6][7]1 kg-equivalent spools span 93–174; the middle of the market is about 140[8][9][10][11]
Price range across brandsUSD/kg46-86 across brands; BCN3D PP GF30 46 at 700 g, BASF Ultrafuse PP GF30 49 at 2.2 kg, Prusament PP Glass Fiber 86 at 850 g[5][6][7]93-174 across brands and formats; Polymaker Fiberon PPS-GF20 93 at 3 kg, IEMAI 3D CF-PPS 131 at 750 g, LEHVOSS Luvocom 3F PPS CF 9938 164 at 2.3 kg, Bambu Lab PPS-CF 174 at 750 g[8][9][10][11]
Market availability1–5Available from several mainstream brands[5][6][7]Available from several mainstream brands[8][9][10]
Spool sizes & diameters1.75 and 2.85 mm; 700 g, 850 g and 2.2 kg spools[5][6][7]1.75 mm; 0.5 kg spools[8]
Typical applicationsStiff, chemically resistant parts where PP-CF's cost or conductivity is unwanted[2]Chemical and automotive parts needing PPS chemistry with structural stiffness[3]
Diameter tolerance± mm±0.04 (Prusament)[1]Not documented
Printing Parameters
Nozzle temperature°C245 ± 10 (Prusament) — 25 °C below the carbon-fibre grade[1][12]Not documented
Bed temperature°C95 ± 10 (Prusament)[1]Not documented
Enclosure / chamber requirement1–5Enclosure recommended — Simplify3D lists an enclosure as a hardware requirement and Polymaker advises one below 70 °C ambient to stop warping and cracking[13][14]Enclosure required (passive) — Polymaker states its Fiberon PPS-CF10 needs no heated chamber, unlike the unfilled sulfones and PAEKs[3]
Part cooling fanOff — Prusa runs 0 % except 100 % on bridges[1]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s4 at Prusa's 50 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][15]Not documented
Warping tendency1–5High — enclosure needed for reliable large parts; Prusa recommends a brim[1]Not documented
Bed-adhesion difficulty1–5Very difficult — special plates or slurry required[1]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning; hardened nozzle mandatory[1]Expert / industrial hardware only[3]
Extruder requirementPrusa states a hardened nozzle is necessary and recommends a brim[1]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[1]Hardened steel required[3]
Abrasiveness1–5Highly abrasive — standard GF composite[1]Highly abrasive — standard CF composite[3]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[16]High — jams from moisture, heat creep or particles; Polymaker specifies hardened steel or ruby nozzles for carbon-filled PPS and Prusa lists composites as a higher clogging risk[17][16]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low (0.1–0.3 %) — 0.11 % at both 24 h and 7 days, higher than the carbon-fibre grade's 0.04 % but still very low[1][12]Low (0.1–0.3 %) — 0.225 % equilibrium for Fiberon PPS-CF10 and 0.11 % for PPS-GF20[3][4]
Equilibrium moisture content at ~50 % RH%0.11 after 24 h and 0.11 after 7 days at 24 °C / 22 % RH (Prusa Polymers)[1]0.225 equilibrium (Fiberon PPS-CF10); 0.11 (PPS-GF20)[3][4]
Effect of moisture on strengthNot applicable in practice at 0.11 % equilibrium uptake[1]No dry-versus-conditioned figures are published; equilibrium uptake is 0.225 % and Polymaker specifies a 100 °C, 10 h dry[3]
Storage requirementNo special storage needed[1]Not documented
Mechanical Properties
Tensile strength (XY)MPa46.6 ± 1.3 filament tensile yield (Prusament, ISO 527) — more than double the carbon-fibre grade's 21[1][12]59.4 ± 1.3 (PPS-CF10) and 64.1 ± 2.1 (PPS-GF20) printed XY, ISO 527[3][4]
Young's modulusMPaNot documented5446.7 ± 149.0 (PPS-CF10) and 4552.0 ± 54.6 (PPS-GF20) printed XY, ISO 527[3][4]
Elongation at break%Not documented1.4 ± 0.1 (PPS-CF10) and 2.0 ± 0.2 (PPS-GF20) printed XY, ISO 527 — the lowest elongation in the dataset[3][4]
Charpy impact, notchedkJ/m²7.9 ± 0.4 printed horizontal and 9.9 ± 0.8 printed vertical XZ (ISO 179-1, notched)[1]5.3 ± 0.2 printed XY for PPS-CF10 and 7.3 ± 0.2 for PPS-GF20, ISO 179 notched[3][4]
Layer adhesion / Z tensileMPaNot documented32.0 ± 5.1 (PPS-CF10) and 22.9 ± 0.8 (PPS-GF20) printed Z, ISO 527[3][4]
Brittleness1–5Moderate[1]Very brittle — cracks or shatters easily; elongation at break 1.4 %[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell R102 (and M95) on extruded unfilled PP stock (ASTM D785); no figure is published for a glass-fibre PP filament[18]Rockwell 105 (and R124) on extruded unfilled PPS stock (ASTM D785); no figure is published for a fibre-filled PPS filament[19]
Creep resistance / sustained load1–5Not documentedExcellent — holds load for years. Ensinger lists high creep resistance for unfilled PPS stock and Spectrum states creep resistance is unchanged under continuous load at high temperature; the fibre raises heat deflection to 252 °C at 0.45 MPa[19][20][3]
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%Not documented54 (PPS-CF10) and 36 (PPS-GF20), printed[3][4]
Thermal Properties
HDT at 0.45 MPa°C138.3 (ISO 75, 0.45 MPa)[1]252.5 (PPS-CF10) and 236.3 (PPS-GF20), printed, ISO 75 at 0.45 MPa[3][4]
HDT at 1.8 MPa°C112.6 (ISO 75, 1.8 MPa)[1]133 (PPS-CF10) and 125.8 (PPS-GF20), printed, ISO 75 at 1.8 MPa[3][4]
Glass transition (Tg)°CNot documented97.7 (PPS-CF10) and 95.0 (PPS-GF20), DSC[3][4]
Melting point / Vicat°CNot documented279.7 (PPS-CF10) and 279.6 (PPS-GF20) melting, DSC; Vicat 267.5 and 272.5 (ISO 306)[3][4]
Continuous service temperature°CNot documented170 long-term service on extruded PPS stock, converted from 338 °F; no figure published for the carbon-filled grade[19]
Environment & Chemical
Chemical resistanceExcellent against acids, alkalis and most solvents[14]Outstanding — PPS resists essentially all solvents below 200 °C[17]
Water / humidity resistance in service1–5Excellent — essentially unaffected[1]Not documented
Electrical & ESD propertiesNot documentedSurface resistivity above 10¹² ohm — insulating (ANSI/ESD S11.11)[3][4]
Health & Safety
Fume toxicity1–5Low hazard — minimal VOC and particle emission. Inferred: no polyolefin was among the nine filaments in the Azimi chamber study, so this is a family-level judgement rather than a measurement[21]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[21]
Ventilation / filtration requirement1–5Open a window / occasional ventilation. Inferred — no polyolefin was measured in the chamber study[21]Ventilated room or enclosure recommended[21]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Fibre is bound in the matrix; sanding dust should not be inhaled[3]
Solvents & Solubility
Soluble inNone at room temperature; chloroform dissolves the matrix at 60 °C and xylene at about 118 °C, leaving the fibre.[22][23]None — PPS does not dissolve in any known solvent below 200 °C.[24][25]
Softened or crazed byXylene, decalin, CCl4 and chlorobenzene are heavily absorbed at 20 °C; oleum, chlorosulphonic acid and bromine destroy it.[22]Nothing at 23 °C; Ensinger rates it only conditionally resistant to benzene, dichloromethane, toluene and pyridine.[25]
Solvent welding & smoothing agentNone — nothing softens PP at room temperature, so joints have to be welded thermally rather than chemically.[22]None — no solvent welds or smooths PPS.[24]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Prusament PP Glass Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  2. Prusament PP Glass Fiber — material page Prusa Polymers · 2026-08 · doc
  3. Fiberon PPS-CF10 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  4. Fiberon PPS-GF20 Technical Data Sheet V1.1 Polymaker · 2025-07 · tds
  5. BASF Ultrafuse PP GF30 Black 2.85 mm 2.200 g igo3d · 2026-08 · vendor
  6. BCN3D PP GF30 Black 2.85 mm 700 g igo3d · 2026-08 · vendor
  7. Prusa Prusament PP Glass Fiber Natural (NFC), 1.75 mm / 850 g 3DJAKE · 2026-08 · vendor
  8. Polymaker product catalogue Polymaker · 2026-08 · vendor
  9. Bambu Lab PPS-CF Black, spool (750 g) 3DJAKE · 2026-08 · vendor
  10. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  11. IEMAI 3D CF-PPS 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  12. Prusament PP Carbon Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  13. Polypropylene — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  14. PP — material basics Polymaker Wiki · 2026-08 · doc
  15. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  16. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  17. PPS — material basics Polymaker Wiki · 2026-08 · doc
  18. TECAFINE PP natural — stock shape properties Ensinger · 2026-08 · tds
  19. TECATRON natural (PPS) — stock shape properties Ensinger · 2026-08 · tds
  20. Spectrum PPS AM230 Technical Data Sheet Spectrum Filaments · 2022-04 · tds
  21. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  22. Pro-fax and Moplen polypropylene — Chemical Resistance Guide (20, 60 and 100 °C) LyondellBasell · 2026-08 · tds
  23. US 5,278,282 Polymer recycling by selective dissolution — xylene dissolution temperatures Nauman & Lynch, Rensselaer Polytechnic Institute · 1994-01 · paper
  24. PPS (Polyphenylene sulfide) — Knowledge Base Prusa Research · 2026-08 · doc
  25. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds