3D Printing Info

Filament comparison

PETG-ESD vs PPA-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

ESD-safe PETG guidePPA-CF (carbon-fibre polyphthalamide) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PETG-ESD comparisonsMore PPA-CF comparisons
PETG-ESD vs PPA-CF — documented properties and sources
PropertyESD-safe PETGPETGPPA-CF (carbon-fibre polyphthalamide)PA
Market snapshot
Listing priceUSD/kg; dated snapshots$102.99/kg median; $65.98–$140.00/kg across 2 dated product listings$84.99/kg median; $21.99–$266.67/kg across 7 dated product listings
Identity & Market
Base polymer / chemistryPETG compounded with a conductive filler to bring surface resistivity into the static-dissipative range[1][2]Polyphthalamide — semi-aromatic nylon — with 10–15 wt% chopped carbon fibre; Bambu Lab lists the composition as semi-aromatic nylon plus carbon fibre, Raise3D and Siraya Tech state 15 wt%, Flashforge 10 %[3][4][5][6]
Densityg/cm³1.24 (Fiberon) and 1.28 (3DXTech), ISO 1183[1][2]1.15 (Raise3D) to 1.25 (Bambu Lab and IEMAI 3D), ISO 1183; Flashforge 1.21–1.23[3][4][5][7]
Typical priceUSD/kg1 kg-equivalent spools span 66–140; the middle of the market is about 103[8][9]1 kg-equivalent spools span 22–267; the middle of the market is about 85[10][11][12][13][14][15]
Price range across brandsUSD/kg66–140 across brands; Fiberon PETG-ESD 66, 3DXSTAT ESD-PETG 140[8][9]22–267 across brands; CHCKX 22 on Amazon, IEMAI 3D 51, Siraya Tech 57 and 85, Bambu Lab 200 at 750 g, Raise3D 209, 3DXTech CarbonX HTN+CF 267 at 750 g[10][11][12][16][13][14][15]
Market availability1–5Niche, a handful of specialist brands[8][9]Available from several mainstream brands[10][11][12][13][14]
Spool sizes & diameters1.75 mm; 0.5, 0.75, 1 and 3 kg spools[8][9]1.75 mm; 750 g, 1 kg, 2 kg and 2.5 kg spools[3][12][14]
Typical applicationsElectronics fixtures, trays and jigs handled around static-sensitive components[1][2]Under-bonnet automotive brackets, jigs and end-use parts that must stay stiff above the 100 °C working ceiling of PA6-CF[4][5]
Diameter tolerance± mmNot documented0.05 (Bambu Lab and Siraya Tech, 1.75 mm)[3][6]
Printing Parameters
Nozzle temperature°C250–290 (Fiberon)[1]280–310 (Bambu Lab and CHCKX); 280–320 (Siraya Tech)[3][6][15]
Bed temperature°C70–80 (Fiberon); 70 (3DXTech)[1][2]100–120 (Bambu Lab and CHCKX); Siraya Tech runs cooler at 70–90[3][6][15]
Enclosure / chamber requirement1–5Open frame is fine — Fiberon specifies room-temperature chamber[1]Enclosure required (passive) — Bambu Lab specifies a 50–80 °C chamber and Siraya Tech requires an enclosure, while Flashforge states its LUVOCOM-based grade prints on machines with no heated chamber[3][5][12]
Recommended chamber temperature°CNot documented50–80 (Bambu Lab); specimens were printed at a 52 °C chamber and Bambu Lab notes 70–80 °C raises Z properties[3]
Part cooling fanNot documentedBambu Lab turns the part fan on; Siraya Tech runs it off[3][6]
Bed surface & adhesion aidTextured PEI, satin or powder-coated sheets; on smooth PEI a glue stick acts as a release agent[17][18]Smooth or textured PEI plate with a glue stick, or a PVP glue coating[3][6]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sFiberon rates the material to 500 mm/s, equivalent to 40 on a 0.4 mm nozzle at 0.2 mm layer — a machine-limited headline rather than a measured melt rate[1][19]8–12 mm³/s at 300–320 °C (Siraya Tech)[6]
Bed-adhesion difficulty1–5Needs the right surface or a thin adhesive — the problem is releasing the part, not sticking it[17][18]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed; Polymaker names stringing as PETG's common quirk[18]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; resistivity depends on getting the nozzle temperature right[1]Advanced — enclosure, hardware upgrades, tuning; a 320 °C hot end and a hardened nozzle are the entry requirements[3][6]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[1]Hardened steel required — Siraya Tech and CHCKX specify hardened steel or better, Raise3D warns brass wears quickly[4][6][15]
Abrasiveness1–5Moderately abrasive — conductive carbon filler[1]Highly abrasive — standard CF/GF composites and glow fills[4][6]
Nozzle clog risk1–5Low — 3DXTech lists no special nozzle concerns and no minimum layer height for its ESD-PETG, only a 65 °C pre-dry[20]Moderate — needs dry filament and a clean nozzle; Siraya Tech states nozzles below 0.4 mm will clog[6][12]
Heat-creep / jam sensitivity1–5Slightly sensitive[21]Not documented
Hotend requirementNo special hot-end required[21]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate (0.3–0.8 %) — the PETG matrix reaches 0.40 % saturated at 25 °C / 55 % RH and 3DXTech specifies a 65 °C, 4 h pre-dry[17][20]High (0.8–2 %) — 1.30 % saturated at 25 °C / 55 % RH for Bambu Lab and IEMAI 3D against 2.35 % for the same makers' PA6-CF, which is the whole reason to pay for PPA[3][7][22]
Equilibrium moisture content at ~50 % RH%0.41 equilibrium water absorption (Fiberon PETG-ESD)[1]1.30 saturated at 25 °C / 55 % RH (Bambu Lab and IEMAI 3D) against 2.35 for their PA6-CF; Siraya Tech 1.37 and 1.09 by ISO 62, Raise3D 0.6 by ISO 62 Method 1, Flashforge below 0.1 at 23 °C / 24 h[3][4][5][6][23][7][22]
Drying temperature & time65 °C for 3 h (Fiberon)[1]100–140 °C for 8–12 h (Bambu Lab, hotter is better within that range); Siraya Tech 100 °C for 4–6 h; Raise3D 80–100 °C for 6–12 h[3][4][6]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[24]Not documented
Effect of moisture on strengthPolymaker groups PETG with nylon, PVA and TPU as highly hygroscopic; no dry-versus-conditioned strength figures are published for this grade and the loss shows as bubbling and poor layer adhesion[24]Not documented
Storage requirementSealed with desiccant; Polymaker groups PETG with the highly hygroscopic materials[24][18]Sealed below 20 % RH with desiccant (Bambu Lab); Raise3D keeps the spool in a dry box throughout the print[3][4]
Mechanical Properties
Tensile strength (XY)MPa36.1 ± 0.9 printed XY, ISO 527 (Fiberon); 3DXTech quotes 50 at break[1][2]95–168 (printed XY, ISO 527): Siraya Tech 95, Flashforge 108–112, Siraya Tech Core 112, Raise3D 122 conditioned and annealed, Bambu Lab and IEMAI 3D 168[3][4][5][6][23][7]
Young's modulusMPa1983 ± 75 printed XY, ISO 527 (Fiberon)[1]7100–11800 (printed XY): Flashforge 7100–8000, Raise3D and Siraya Tech 7800, Siraya Tech Core 9300, Bambu Lab and IEMAI 3D 11800[3][4][5][6][23][7]
Elongation at break%7.3 ± 0.7 printed XY, ISO 527 (Fiberon); 3DXTech quotes 13 at break[1][2]1.9–5 at break (printed XY): Raise3D 1.9, Siraya Tech 2, Siraya Tech Core 2.25, Bambu Lab and IEMAI 3D 3.2, Flashforge 3.5–5[3][4][5][6][23][7]
Flexural strengthMPa54.0 ± 2.5 printed XY, ISO 178 (Fiberon)[1]145–221 (printed XY, ISO 178): Siraya Tech 145, Siraya Tech Core 178, Raise3D 190, Bambu Lab and IEMAI 3D 208, Flashforge 210–221[3][4][5][6][23][7]
Flexural modulusMPa1651 ± 141 printed XY, ISO 178 (Fiberon)[1]6500–9860 (printed XY, ISO 178): Flashforge 6500–7000, Siraya Tech 6800, Raise3D 8510, Siraya Tech Core 8700, Bambu Lab and IEMAI 3D 9860[3][4][5][6][23][7]
Charpy impact, notchedkJ/m²5.7 ± 0.5 printed XY, ISO 179, notched (Fiberon)[1]6.5 notched Charpy XY (Bambu Lab and IEMAI 3D, ISO 179); Raise3D 7.8 and Siraya Tech 11 by ISO 179 without stating notched[3][4][6][7]
Other impact dataCharpy unnotched 29.3 ± 2.2 printed XY (Fiberon, ISO 179)[1]Bambu Lab and IEMAI 3D unnotched Charpy 41.7 kJ/m² XY against 4.3 in Z; Flashforge Izod 9–11 kJ/m² XY against 2.5–3 in Z[3][5][7]
Layer adhesion / Z tensileMPa20.7 ± 0.6 printed Z, ISO 527 (Fiberon)[1]57 printed Z (Bambu Lab and IEMAI 3D, ISO 527); Raise3D measures 30.2 by a custom mono-layer method[3][4][7]
Brittleness1–5Moderate[1]Brittle — snaps with little warning; 2–3 % elongation at break is typical[3][4][6]
Creep resistance / sustained load1–5Below average — no ESD-grade creep test; unfilled PETG sagged from 12 to 17.1–20.4 mm over 5 days at 1.25 kg[25][26][27][28]Good — Flashforge cites outstanding creep resistance at high temperature and Raise3D high creep resistance, both against other nylons[4][5]
Fatigue / repeated-flex resistance1–5Moderate — no ESD-grade S-N curve; unfilled printed PETG ran 79 000–193 000 cycles at 30 % of tensile strength[29]Not documented
Elasticity / flexibility1–5Slightly flexible in thin sections[1]Rigid[3]
Z strength as % of XY%57 (Fiberon, printed Z against XY tensile)[1]34 (Bambu Lab and IEMAI 3D, Z against XY tensile, ISO 527)[3][7]
Thermal Properties
HDT at 0.45 MPa°C76 (ISO 75, 0.45 MPa, Fiberon)[1]188–227 (ISO 75 at 0.45 MPa): Raise3D 188, Flashforge 220, Bambu Lab and IEMAI 3D 227; Siraya Tech reaches 192–199 only after annealing, 84.5–97 unannealed[3][4][5][6][23][7]
HDT at 1.8 MPa°C72 (ISO 75, 1.8 MPa, Fiberon)[1]113–196 (ISO 75 at 1.8 MPa): Raise3D 113, Bambu Lab and IEMAI 3D 196; Siraya Tech reaches 119–126 only after annealing, 82.5–84 unannealed[3][4][6][23][7]
Glass transition (Tg)°C77 (Fiberon) and 80 (3DXTech), DSC[1][2]80 (Siraya Tech, ASTM D3418) to 85 (Bambu Lab and IEMAI 3D, DSC)[3][6][7]
Melting point / Vicat°CAmorphous — no melting point; Vicat 86 (Fiberon, ISO 306)[1]Melting point 231 (Raise3D) to 258 (Bambu Lab and IEMAI 3D); Vicat softening 230–238 (ISO 306)[3][4][6][23][7]
Continuous service temperature°CNot documented120 (Flashforge, IEC 60216, LUVOCOM PPA-CF)[5]
Annealing responseNot documentedBambu Lab anneals at 120–140 °C for 6–12 h; Raise3D at 80–100 °C for 8 h and warns of up to 0.5 % Z shrinkage. On Siraya Tech's grades annealing lifts HDT at 0.45 MPa from 84.5 to 192 °C while notched Charpy falls from 11 to 6.3 kJ/m²[3][4][6]
Flammability / UL 94Flammable; no UL 94 rating published for standard grades[30]Flammable; Bambu Lab lists water, carbon oxides and nitrogen oxides as combustion products. No UL 94 rating is published for the filament grades surveyed[3]
Environment & Chemical
Chemical resistanceWithstands acids, alkalis, oils and UV exposure[18]Better than general nylon against weak acids, weak alkalis, most organic solvents and most oils and greases (Bambu Lab); not resistant to strong acids or strong alkalis[3]
Water / humidity resistance in service1–5Not documentedGood — minor absorption; 1.3 % saturated moisture is roughly half what PA6-CF takes up[3][22]
Food contactNot certified for food contact as filament[18]Not documented
Biodegradability / compostabilityNot biodegradable[18]Not documented
RecyclabilityNot accepted in household plastic collection[18]Not documented
Electrical & ESD propertiesSurface resistivity falls with nozzle temperature: 7.0×10⁶–1.6×10⁷ ohm at 250 °C, 3.2×10⁵–4.7×10⁵ at 270 °C and below 1×10⁴ at 290 °C (Fiberon); 3DXTech quotes 10⁷–10⁹ ohm/sq[1][2]Flashforge's data sheet gives a surface resistance of 10³ Ω or below (IEC 60093) for its LUVOCOM-based PPA-CF — the carbon loading makes it conductive rather than merely dissipative[5]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[31]Not documented
Ventilation / filtration requirement1–5Open a window / occasional ventilation[31]Not documented
Dust & fibre handling hazardConductive carbon filler is bound in the matrix; avoid inhaling sanding dust[1]Chopped carbon fibre; dry sanding and cutting release respirable fibre-laden dust[32]
Post-Processing
Sanding & machiningSands poorly — the material is tough and gums rather than powders[21]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds PETG cleanly[21]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[21]Not documented
Support material pairingPrints its own supports; Polymaker rates PolyDissolve S1 for PETG[21]Bambu Lab pairs it with Support for PA/PET; Raise3D warns that PPA-CF used as its own support bonds permanently to the model once it takes up moisture, so supports must come off before annealing[3][4]
Dimensional accuracy & detailNozzle temperature has to be held steady — it moves surface resistivity by three orders of magnitude[1]Not documented
Solvents & Solubility
Soluble inNo common workshop solvent; 1,2-dichloroethane destroys it inside a week and dichloromethane — a carcinogen — dissolves the surface.[33][34]Formic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[35]
Softened or crazed byAcetone (+16 % weight over 1 year at 23 °C), ethyl acetate, toluene and DMF swell and soften it; methanol crazes it.[33]Zinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[35]
Solvent welding & smoothing agentDichloromethane brushed on is the only agent that smooths PETG — a controlled carcinogen, not workshop stock.[34]None — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[35]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PETG-ESD Technical Data Sheet V1.1 Polymaker · 2026-08 · tds
  2. 3DXSTAT ESD-PETG Technical Data Sheet 3DXTech · 2026-08 · tds
  3. Bambu Filament Technical Data Sheet V1.0 — PPA-CF Bambu Lab · 2026-08 · tds
  4. Raise3D Industrial PPA CF Technical Data Sheet V2.0 Raise3D · 2022-04 · tds
  5. Flashforge PPA-CF Filament Technical Data Sheet (LUVOCOM PPA-CF, 10 % carbon fibre) Flashforge · 2026-08 · tds
  6. Siraya Tech Fibreheart PPA-CF Technical Data Sheet Siraya Tech · 2026-08 · tds
  7. IEMAI 3D CF-PPA Technical Data Sheet IEMAI 3D · 2025-04 · tds
  8. Polymaker product catalogue Polymaker · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. PPA-CF — Bambu Lab US Store Bambu Lab · 2026-08 · vendor
  11. Raise3D Industrial PPA CF Filament 1.75 mm (1 kg) — product listing MatterHackers · 2026-08 · vendor
  12. Fibreheart PPA-CF Filament — product page Siraya Tech · 2026-08 · vendor
  13. IEMAI 3D CF-PPA 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  14. CARBONX HTN+CF — product page 3DXTech · 2026-08 · vendor
  15. CHCKX PPA-CF 3D Printing Filament Matte Black 1 kg 1.75 mm 10 % Carbon Fiber — Amazon listing Amazon.com · 2026-08 · vendor
  16. Siraya Tech Fibreheart PPA-CF Core Filament — product page Siraya Tech · 2026-08 · vendor
  17. Prusament PETG Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  18. PETG — material basics Polymaker Wiki · 2026-08 · doc
  19. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  20. 3DXSTAT ESD-PETG — product page (print recommendations) 3DXTech · 2026-08 · doc
  21. PET and PETG — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  22. Bambu Filament Technical Data Sheet V3.0 — PA6-CF Bambu Lab · 2026-08 · tds
  23. Siraya Tech Fibreheart PPA-CF Core Technical Data Sheet Siraya Tech · 2026-08 · tds
  24. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  25. PCTG vs PETG comparison — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. Extrudr PETG vs PCTG vs XPETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  27. Prusament PETG-CF vs PETG V0 vs PETG — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  28. BambuLab PETG Basic vs Translucent vs PETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  29. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  30. Prusament PETG V0 Technical Datasheet Prusa Polymers · 2026-08 · tds
  31. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  32. PET-CF / PPA-CF / PPS-CF / PA6-CF carbon fibre filament usage guide Bambu Lab Wiki · 2026-08 · doc
  33. Eastman Spectar copolyester — Chemical resistance (unstressed bars, 1 year at 23 °C) Eastman Chemical Company · 2026-08 · tds
  34. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  35. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds