3D Printing Info

Filament comparison

PEKK vs TPU 85A

Compare printing settings, strength, heat resistance, dated prices and sources.

PEKK guideTPU 85A guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PEKK comparisonsMore TPU 85A comparisons
PEKK vs TPU 85A — documented properties and sources
PropertyPEKKHIGHTEMPTPU 85AFLEX
Market snapshot
Listing priceUSD/kg; dated snapshots$525.00/kg median; $332.50–$771.12/kg across 6 dated product listings$89.89/kg median; $31.99–$106.05/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryPolyether ketone ketone, amorphous grade — a polyaryletherketone that stays amorphous, so it does not need PEEK's crystallisation control. Stratasys sells it as Antero 800NA and Antero 840CN03; category numbers below are unfilled unless a carbon grade is named[1][2]Soft thermoplastic polyurethane at 82–85 Shore A[3][4][5]
Densityg/cm³1.28 unfilled (ASTM D792, Antero 800NA; 1.31 annealed) and 1.33 for CarbonX PEKK-A CF15 (ISO 1183)[2][1]1.11 (BASF Ultrafuse 85A) to 1.19 (NinjaFlex 85A), ISO 1183 / ASTM D792[5][3]
Typical priceUSD/kg1 kg-equivalent spools cluster near 550[6][7][8]1 kg-equivalent spools span 32–106; the middle of the market is about 90[6][9][3]
Price range across brandsUSD/kg333-771 across grades and formats; 3DXTech CarbonX PEKK-A+CF15 333 at 2 kg, 3D4Makers unfilled PEKK-A 485 at 2 kg, IEMAI 3D 500 at 1 kg, Kimya PEKK Carbon 771 at 500 g[6][7][8][10][11]32–106 across brands; Siraya Tech Flex TPU 85A 32 at 1 kg, add:north TPU Pro Matte 85A 72, Recreus Filaflex 82A 90 at 500 g, Proto-pasta Clear Flexible TPU 90, 3DXTech 3DXFLEX 85A 96, NinjaTek NinjaFlex 106[12][6][9][13][3]
Market availability1–5Niche, a handful of specialist brands[6][7][8]Available from several mainstream brands[6][12]
Spool sizes & diameters1.75 and 2.85 mm; 200 g to 2 kg spools, plus Stratasys canisters[6][7][2]1.75, 2.85 and 3 mm; 0.5, 1 and 2 kg spools[6][12][3]
Typical applicationsAerospace interior and structural parts; 3DXTech labels its carbon-filled PEKK-A grade AERO and Stratasys certifies Antero 800NA for outgassing and FST[1][2]Soft-touch grips, seals, wearables and anything that must compress and rebound[3][4]
Printing Parameters
Nozzle temperature°CNot documented200–220 (BASF Ultrafuse 85A, 210 typical)[5]
Bed temperature°C140 (3DXTech CarbonX PEKK-A CF15)[1]40 (BASF Ultrafuse 85A)[5]
Enclosure / chamber requirement1–5Actively heated chamber required[14][15]Open frame is fine[5]
Bed surface & adhesion aidNot documentedPEI sheet or painter's tape; Polymaker warns TPU can over-stick and advises a glue stick as a release agent[16][17]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented1.2–3.2 at the 15–40 mm/s BASF specifies on a 0.4 mm nozzle at 0.2 mm layer[5]
Warping tendency1–5Not documentedNone[5]
Bed-adhesion difficulty1–5Not documentedSticks to anything — Recreus states its 82A grade has excellent bed adhesion without a heated bed or additives[4]
Stringing / oozing tendency1–5Not documentedHigh — drying plus tuning needed[18][17]
Overall printing difficulty1–5Expert / industrial hardware only[14][15]Advanced — enclosure, hardware upgrades, tuning; at this hardness the filament will not push through a Bowden tube[3][4]
Extruder requirementNot documentedDirect drive only. NinjaTek calls its 85A grade ideal for direct-drive extruders and Recreus specifies direct-drive printers for 82A; BASF caps print speed at 15–40 mm/s with a nozzle of 0.4 mm or larger[3][4][5]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — the category spans unfilled PEKK, where brass is acceptable, and the carbon-filled aerospace grades that make up most of the market[1][2]Brass fine indefinitely[19]
Abrasiveness1–5Highly abrasive — most PEKK filament sold is carbon-filled; unfilled Antero 800NA and ThermaX PEKK-A are non-abrasive[1][2]Non-abrasive[19]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[20]High — jams from moisture, heat creep or particles[18][17]
Heat-creep / jam sensitivity1–5Not documentedVery high — softens in the cold zone readily; soft filament buckles between the drive gear and the melt zone[17][3]
Hotend requirementNot documentedNo special hot-end required, but a direct-drive extruder is (Simplify3D)[16]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Not documentedModerate — NinjaTek measures 0.22 % in 24 h (ASTM D570) and BASF specifies a 70 °C dry for at least 5 h[3][5]
Equilibrium moisture content at ~50 % RH%Not documented0.22 after 24 h water immersion (NinjaFlex 85A, ASTM D570) — an immersion figure, not an equilibrium moisture content at 50 % RH[3]
Drying temperature & timeNot documented70 °C for at least 5 h in a hot-air dryer or vacuum oven (BASF)[5]
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing and a rough surface[18]
Effect of moisture on strengthNo dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[20]Polymaker groups TPU with the highly hygroscopic materials; wet TPU prints with poor layer adhesion and weak, brittle layers[18]
Storage requirementNot documentedSealed with desiccant; often kept in a dryer during the print[18]
Mechanical Properties
Tensile strength (XY)MPa86.7-90.0 at yield and 73.0 at break (printed XZ, ASTM D638, Antero 800NA on the F900 and Fortus 450mc); 88.8 at break annealed; 126 at break for CarbonX PEKK-A CF15 (printed XY, ISO 527)[2][1]26 ultimate (NinjaFlex 85A, ASTM D638)[3]
Young's modulusMPa2640-3870 (printed XZ, ASTM D638, Antero 800NA; upper figure annealed); 9125 for CarbonX PEKK-A CF15 (printed XY, ISO 527)[2][1]12 (NinjaFlex 85A, ASTM D638) — two orders of magnitude below any rigid filament; NinjaTek's 95A Cheetah reaches 26 by the same method[3][21]
Elongation at break%6.1 at break (printed XZ, ASTM D638, Antero 800NA); 2.3 in ZX; 3.15 for CarbonX PEKK-A CF15 (ISO 527)[2][1]650 at break (Filaflex 82A) and 660 (NinjaFlex 85A); BASF measures 600 in XY and 320 in ZX[4][3][5]
Flexural strengthMPa136 at 5 % strain (printed XZ, ASTM D790, Antero 800NA); 178 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[2][1]Not documented
Flexural modulusMPa3200 (printed XZ, ASTM D790, Antero 800NA); 8817 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[2][1]Not documented
Other impact dataIzod notched 41.1 J/m XZ and 33.3 J/m ZX; unnotched 1730 J/m XZ against 203 J/m ZX (printed, ASTM D256/D4812, Antero 800NA)[2]Not documented
Layer adhesion / Z tensileMPa50.1-59.4 at yield (printed ZX, ASTM D638, Antero 800NA); 56.0 for the ESD grade Antero 840CN03[2][22]Not documented
Brittleness1–5Moderate unfilled — 6.1 % elongation at break in plane; brittle in the carbon-filled grades at 3.15 %[2][1]Very ductile — bends far before failing[3]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documented29 Shore D / 85 Shore A (BASF Ultrafuse 85A, ISO 7619-1); 85 Shore A (NinjaFlex, ASTM D2240); 82 A nominal for Filaflex[3][5][4]
Creep resistance / sustained load1–5Excellent — holds load for years. Antero 800NA still holds 82 % of its room-temperature ZX tensile strength at 104 °C and 63 % at 132 °C (printed, ASTM D638)[2]Poor — no 85A creep test; a printed 95A TPU bar crept from 74.5 to 82.7 mm over 5 days at 1.25 kg, and softer grades creep more[23]
Fatigue / repeated-flex resistance1–5Not documentedExcellent — living hinges viable[17]
Elasticity / flexibility1–5Rigid[1]Rubbery / highly elastic[3][4]
Z strength as % of XY%56-82 (Antero 800NA and 840CN03 printed on the F900 and Fortus 450mc, ZX against XZ tensile yield and break, ASTM D638)[2][22]53 — BASF measures 320 % elongation at break in ZX against 600 % in XY[5]
Wear resistance & frictionNot documentedAbrasion 0.08 g mass loss over 10 000 cycles (NinjaFlex, ASTM D4060); 82 mm³ (BASF, ISO 4649)[3][5]
Thermal Properties
HDT at 0.45 MPa°C158 (printed XY and ZX, ASTM D648 Method B at 66 psi, Antero 800NA); 285 for CarbonX PEKK-A CF15 (ISO 75 at 0.45 MPa)[2][1]Not documented
HDT at 1.8 MPa°C156-157 (printed, ASTM D648 Method B at 264 psi, Antero 800NA); moulded 147[2]Not documented
Glass transition (Tg)°C156 (ASTM D7426, Antero 800NA); 165 for CarbonX PEKK-A CF15 (DSC)[2][1]Not documented
Melting point / Vicat°C300 melt point (ASTM D7426 peak heat, Antero 800NA); 305 for CarbonX PEKK-A CF15 (DSC)[2][1]216 melting (NinjaFlex 85A, DSC)[3]
Thermal expansion (CTE)µm/m·K36.1 in XY and 50.2 in ZX (printed, 40-140 °C, ASTM E831, Antero 800NA); 47.4 and 51.2 for the ESD grade Antero 840CN03[2][22]Not documented
Environment & Chemical
UV resistance1–5Good — years with some colour shift. 1000 h of QUV cycling to ASTM G154 left Antero 800NA's yield strength unchanged at 57 MPa and raised stress at break 3.6 %[2]Good — years with some colour shift; Polymaker lists UV exposure among the conditions TPU withstands[17]
Chemical resistanceNot documentedWithstands industrial solvents and UV exposure (Polymaker)[17]
Food contactNot documentedNot food safe without specific certification (Polymaker)[17]
Biodegradability / compostabilityNot documentedNot biodegradable[17]
RecyclabilityNot documentedNot accepted in household plastic collection[17]
Electrical & ESD propertiesUnfilled PEKK is an insulator at above 1.4e14 ohm-cm (ASTM D257); CarbonX PEKK-A CF15 sits above 10^7 ohm/sq, and the Antero 840CN03 ESD grade is specified at 10^4-10^9 ohm-cm[2][1][22]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[24]Low hazard — minimal VOC and particle emission; TPU was not among the nine filaments in the chamber study[24]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[24]Open a window / occasional ventilation[24]
Dust & fibre handling hazardCarbon fibre is bound in the matrix; sanding dust should not be inhaled[1]Not documented
Post-Processing
Sanding & machiningNot documentedDifficult to sand or smooth; Polymaker limits post-processing to trimming or tumbling[17]
Gluing & solvent weldingNot documentedCyanoacrylate bonds TPU; no common solvent welds it[17]
Vapour / chemical smoothingNot documentedNo practical vapour smoothing[17]
Support material pairingNot documentedPolymaker warns TPU supports are often very difficult to remove[17]
Solvents & Solubility
Soluble inConcentrated sulphuric acid, as for PEEK; no common organic solvent touches a polyaryletherketone.[25][26]DMF, DMSO, NMP and THF dissolve TPU; acetone, MEK and cyclohexanone are partial solvents. All laboratory reagents.[27]
Softened or crazed byConcentrated sulphuric acid and liquid Freon are the entries Ensinger marks not resistant; acetone, MEK and toluene do nothing.[25]Toluene and benzene swell it up to +50 % by weight at 23 °C; esters swell it severely; ethanol and IPA soften it.[27]
Solvent welding & smoothing agentNone — no solvent softens a polyaryletherketone.[25]None practical — the true solvents (DMF, THF, NMP) are laboratory reagents and leave the joint swollen and weak.[27]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. CarbonX Carbon Fiber PEKK-A CF15 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  2. Antero 800NA — FDM Material Data Sheet (PEKK-based) Stratasys · 2025-08 · tds
  3. NinjaFlex 85A Technical Specifications NinjaTek · 2026-08 · tds
  4. Filaflex 82A product page (Shore hardness and elongation) Recreus · 2026-08 · vendor
  5. Ultrafuse TPU 85A Technical Data Sheet (Version 3.0) BASF Forward AM · 2022-08 · tds
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  8. Kimya PEKK-A Natural 1.75 mm 500 g igo3d · 2026-08 · vendor
  9. Siraya Tech Flex TPU 85A Filament — product page Siraya Tech · 2026-08 · vendor
  10. Kimya PEKK Carbon Grey 1.75 mm 500 g igo3d · 2026-08 · vendor
  11. IEMAI 3D PEKK 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  12. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  13. add:north TPU Pro Matte 85A product page add:north · 2026-08 · vendor
  14. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  15. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  16. Flexible (TPE/TPU) — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. TPU — material basics Polymaker Wiki · 2026-08 · doc
  18. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  19. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  20. THERMAX PEKK-A — product page (print recommendations) 3DXTech · 2026-08 · doc
  21. NinjaTek technical specs comparison chart (Cheetah, NinjaFlex, Armadillo, Alloy 910, Nylon 645) NinjaTek · 2026-08 · tds
  22. Antero 840CN03 — FDM Material Data Sheet (PEKK, ESD) Stratasys · 2024-08 · tds
  23. BambuLab TPU 95A HF vs Qidi TPU 95A HF — results spreadsheet My Tech Fun (Igor Gaspar) · 2024-02 · test
  24. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  25. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  26. The Effects of Sulfonated Poly(ether ether ketone) Ion Exchange Preparation Conditions on Membrane Properties Yee, Zhang & Ladewig, Membranes 3(3) 182–195 · 2013-07 · paper
  27. Elastollan — Chemical properties: swelling and chemical resistance BASF · 2026-08 · tds