3D Printing Info

Filament comparison

PEI 1010 vs PLA-PHA

Compare printing settings, strength, heat resistance, dated prices and sources.

PEI (ULTEM 1010) guidePLA/PHA blend guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PEI 1010 comparisonsMore PLA-PHA comparisons
PEI 1010 vs PLA-PHA — documented properties and sources
PropertyPEI (ULTEM 1010)HIGHTEMPPLA/PHA blendPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$281.22/kg median; $195.00–$698.00/kg across 6 dated product listings$76.40/kg median; $76.40–$76.40/kg across 1 dated product listings
Identity & Market
Base polymer / chemistryPolyetherimide, ULTEM 1010 grade — the higher-temperature, food- and medical-contact PEI[1][2]PLA blended with polyhydroxyalkanoate, a bacterially fermented bio-polyester[3]
Densityg/cm³1.27 (ISO 1183, 3DXTech and Prusament); 1.29 specific gravity on moulded plaques (ASTM D792, Stratasys)[1][2][4]1.2 (ISO 1183)[3]
Typical priceUSD/kg1 kg-equivalent spools span 195–698; the middle of the market is about 270[5][6][7][8][9]Not documented
Price range across brandsUSD/kg195-698 across brands and grades; 3DXTech ThermaX PEI 1010 195 at 2 kg, IEMAI 3D 223 at 1 kg, 3D4Makers 270 at 2 kg, Prusament 292 at 500 g, Kimya 347 at 500 g, 3DXTech ESD-PEI 1010 698 at 500 g[5][6][7][8][9]Not documented
Market availability1–5Niche, a handful of specialist brands[5][6][7][8]Niche, a handful of specialist brands[3][10]
Spool sizes & diameters1.75 and 2.85 mm; 200 g to 2 kg spools, plus Stratasys canisters[5][8][4]1.75 and 2.85 mm; 750 g and 2200 g spools[3]
Typical applicationsAutoclavable tooling, food-contact fixtures and parts that must hold load near 200 °C[2]General-purpose printing where PLA's brittleness is the limiting factor[3]
Printing Parameters
Nozzle temperature°C410 ± 10 (Prusament) — the hottest nozzle in the dataset[2]195–220 (colorFabb)[3]
Bed temperature°C140–160 (Prusament); 130–140 (3DXTech)[2][1]50–60 (colorFabb)[3]
Enclosure / chamber requirement1–5Actively heated chamber required — Prusa specifies 90 °C[2]Open frame is fine[3]
Recommended chamber temperature°C90 (Prusament)[2]Not documented
Part cooling fanNot documented0–100 %; colorFabb states the blend runs on both heated and unheated beds[3][11]
Bed surface & adhesion aidPA nylon sheet or powder-coated sheet with high-temperature glue (Prusament)[2]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented3.2–8 at colorFabb's 40–100 mm/s, on a 0.4 mm nozzle at 0.2 mm layer[11][12]
Warping tendency1–5Severe — heated chamber needed[2]Not documented
Overall printing difficulty1–5Expert / industrial hardware only[2][13]Beginner — prints on any machine out of the box[3]
Extruder requirementA hot end rated to 420 °C, a heated chamber and a high-temperature bed; Prusa dries the filament at 150 °C for 6–8 h before printing[2]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[2]Brass fine indefinitely[3]
Abrasiveness1–5Non-abrasive when unfilled[1]Non-abrasive[3]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 150 °C pre-dry before every print[14]Very low — unfilled PLA blend; Prusa lists no drybox and no hardened nozzle for PLA[15]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Not documentedModerate — the PLA matrix takes up 0.40–0.51 % saturated; colorFabb publishes no figure for the blend[16][17]
Equilibrium moisture content at ~50 % RH%0.4 in 24 h and 0.7 in 7 days at 24 °C and 22 % RH (Prusament)[2]Not documented
Drying temperature & time150 °C for 6–8 h (Prusament) — the hottest drying schedule in the dataset[2]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published; 3DXTech mandates a 150 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[14]Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[18]
Mechanical Properties
Tensile strength (XY)MPa79-95 printed in plane: Stratasys 79.2 (F900 T14) to 91.6 (F3300 N500) at break in XZ, ASTM D638; Prusament 95 +/- 3.5 at yield printed horizontal, ISO 527-1; 3DXTech quotes 56 (ISO 527)[4][2][1]62–64 (ISO 527-1A, colorFabb; two grades quoted)[3]
Young's modulusMPa2300-3040 printed in plane: Prusament 2300 +/- 100 horizontal (ISO 527-1), Stratasys 2920-3040 in XZ (ASTM D638); 3DXTech quotes 2500[4][2][1]2960–3070 (ISO 527-1A, colorFabb)[3]
Elongation at break%4.0-4.1 at break in XZ (ASTM D638, Stratasys); Prusament gives 6.6 +/- 0.7 at yield printed horizontal (ISO 527-1); 3DXTech quotes 3[4][2][1]4 and 11 (ISO 527-1A, colorFabb; two grades quoted)[3]
Flexural strengthMPa128 at 5 % strain (F900 T14) and 144 at break (F3300) printed XZ, ASTM D790; Prusament 98 +/- 6.5 horizontal and 138 +/- 5.3 vertical (ISO 178); 3DXTech quotes 110[4][2][1]Not documented
Flexural modulusMPa2910-3260 printed XZ (ASTM D790, Stratasys); Prusament 2300 horizontal and 2700 vertical (ISO 178); 3DXTech quotes 2510[4][2][1]2500–3300 flexural modulus (ISO 178, colorFabb)[3]
Charpy impact, notchedkJ/m²3.4 ± 0.9 printed horizontal and 3.6 ± 0.4 printed vertical, ISO 179-1 notched (Prusament)[2]2.8–3.7 (ISO 179, notched, colorFabb)[3]
Other impact dataIzod notched 26.6-36.3 J/m XZ against 21.7-27.2 J/m ZX; unnotched 260-406 J/m XZ against 68-116 J/m ZX (printed, ASTM D256/D4812, Stratasys). Charpy unnotched 19.7 +/- 4.3 horizontal and 39 +/- 10 vertical (Prusament, ISO 179-1)[4][2]Not documented
Layer adhesion / Z tensileMPa28-37 at break (printed ZX, ASTM D638, Stratasys F900 and F3300) against 72 +/- 5 at yield printed vertical (ISO 527-1, Prusament on the Pro HT90 with a 0.6 mm nozzle and 90 °C chamber) — a fourfold spread driven by chamber temperature and bead size[4][2]Not documented
Brittleness1–5Brittle — snaps with little warning; notched Charpy only 3.4 kJ/m²[2]Moderate — colorFabb positions the blend as tougher and less brittle than its generic PLA grades[3]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 83.5 (Prusa Polymers method); Rockwell M110 / R126 on extruded PEI stock (ASTM D785)[2][19]Not documented
Creep resistance / sustained load1–5Excellent — holds load for years. Printed coupons hold 215 °C heat deflection at 1.8 MPa (ASTM D648) and extruded PEI stock is rated 170 °C long-term service[4][19]Poor — no PLA/PHA creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[20][21][22]
Fatigue / repeated-flex resistance1–5Not documentedBelow average — no S-N curve for the blend; colorFabb positions it as tougher and less brittle than its generic PLA, which ran 38 000–49 000 cycles at 30 % of tensile strength[23][3]
Elasticity / flexibility1–5Rigid[2]Rigid[3]
Z strength as % of XY%36-40 (Stratasys ZX against XZ tensile at break, ASTM D638) against 76 (Prusament vertical against horizontal tensile yield, ISO 527-1)[4][2]Not documented
Thermal Properties
HDT at 0.45 MPa°C207 (Prusament, ISO 75 at 0.45 MPa) to 217 (printed XY 216.9 and XZ 217.1, ASTM D648 Method B at 66 psi, Stratasys); 3DXTech quotes 208[2][4][1]Not documented
HDT at 1.8 MPa°C194 (Prusament, ISO 75 at 1.8 MPa) to 215 (printed XY 215.1 and XZ 214.5, ASTM D648 Method B at 264 psi, Stratasys) — the highest heat deflection in the dataset[2][4]Not documented
Glass transition (Tg)°C209 (moulded plaque, ASTM D7426 inflection point, Stratasys); 217 (DSC, 3DXTech)[4][1]Not documented
Melting point / Vicat°CNot documentedAbove 155 melting (ISO 3146-C)[3]
Continuous service temperature°C170 long-term service on extruded PEI stock, converted from 338 °F; 200 short term[19]Not documented
Thermal expansion (CTE)µm/m·K36.1 (printed XY, -50 to 60 °C, ASTM E831), falling to 29.8 over 60-205 °C; ZX gives 32.5 over -50 to 110 °C and 16.2 over 110-165 °C[4]Not documented
Flammability / UL 94UL 94 V-0 at 1.5 mm, rated on the base resin[1]Not documented
Environment & Chemical
UV resistance1–5Not documentedDegrades within weeks outdoors[24]
Biodegradability / compostabilityNot documentedcolorFabb states the PHA component is 100 % biodegradable[3]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[25]Low hazard — minimal VOC and particle emission[25]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[25]None needed in a normal room[25]
Solvents & Solubility
Soluble inChlorinated hydrocarbons — dichloromethane and chloroform — are solvents for polyetherimide. Laboratory reagents.[26][27]Chloroform dissolves the PLA phase (10 % w/v, 2–4 h at 23 °C); THF and DMF need 65 °C. Laboratory reagents.[28]
Softened or crazed byAcetone, MEK, benzene, toluene and butyl acetate craze or stress-crack it; alcohols, fuels and dilute acids do not.[27][26]Acetone, ethyl acetate and toluene plasticise it but dissolve <1 % even at 65 °C; submersion in acetone crazes and destroys parts.[28][29]
Solvent welding & smoothing agentDichloromethane is the only welding route, and it is a controlled carcinogen rather than a workshop material.[26][27]Chloroform vapour smooths and welds PLA at the cost of tensile strength; acetone does not smooth it at all.[30][29]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. ThermaX PEI 1010 Technical Data Sheet v4 3DXTech · 2026-08 · tds
  2. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  3. PLA/PHA technical data sheet colorFabb · 2026-08 · tds
  4. ULTEM 1010 Resin — FDM Material Data Sheet Stratasys · 2026-06 · tds
  5. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  6. Kimya PEI-1010 Amber Yellow 1.75 mm 500 g igo3d · 2026-08 · vendor
  7. Prusa Prusament PEI 1010 Natural (NFC), 1.75 mm / 500 g 3DJAKE · 2026-08 · vendor
  8. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  9. IEMAI 3D PEI 1010 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  10. woodFill technical data sheet colorFabb · 2026-08 · tds
  11. glowFill technical data sheet colorFabb · 2026-08 · tds
  12. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  13. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  14. THERMAX PEI 1010 — product page (print recommendations) 3DXTech · 2026-08 · doc
  15. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  16. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  17. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  18. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  19. TECAPEI natural (PEI) — stock shape properties Ensinger · 2026-08 · tds
  20. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  21. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  22. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  23. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  24. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  25. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  26. Radel PPSU, Veradel PESU, Acudel modified PPSU Design Guide — environmental stress cracking tables Solvay Specialty Polymers · 2026-08 · tds
  27. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  28. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  29. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  30. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper