3D Printing Info

Filament comparison

PEEK vs PLA Matte

Compare printing settings, strength, heat resistance, dated prices and sources.

PEEK guideMatte PLA guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PEEK comparisonsMore PLA Matte comparisons
PEEK vs PLA Matte — documented properties and sources
PropertyPEEKHIGHTEMPMatte PLAPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$531.87/kg median; $296.14–$770.00/kg across 5 dated product listings$19.09/kg median; $10.99–$32.16/kg across 10 dated product listings
Identity & Market
Base polymer / chemistryPolyether ether ketone — a semi-crystalline polyaryletherketone[1]PLA compounded with a mineral filler — Fiberlogy names chalk — that scatters light into a diffuse finish[2][3]
Densityg/cm³1.30 (ISO 1183)[1][4]1.31 (Bambu Lab, ISO 1183) to 1.38 (Fiberlogy PLA Mineral, method not stated) — above plain PLA from the filler[3][2]
Typical priceUSD/kg1 kg-equivalent spools span 296–770; the middle of the market is about 532[5][6][7]Mainstream 1 kg spools cluster near 21[8][9][10]
Price range across brandsUSD/kg296-770 across brands and spool sizes; 3D4Makers recycled R-PEEK 296 at 750 g, IEMAI 3D 420 at 1 kg, LEHVOSS Luvocom 3F PEEK 9581 532 at 2 kg, 3DXTech ThermaX PEEK 770 at 500 g[5][6][7]11–32 across brands; budget house brands 11–19, Fiberlogy PLA Mineral 32[11][9][12]
Market availability1–5Niche, a handful of specialist brands[5][6][4]Stocked by most mainstream brands[11][10][8]
Spool sizes & diameters1.75 and 2.85 mm; 200 g to 2 kg spools[5][6][4]1.75 mm; 1 kg spools plus spool-less refills[8][13]
Typical applicationsAerospace brackets, semiconductor handling, sterilisable medical tooling and downhole parts[1]Display models and visible parts where a matte, non-reflective finish matters[3]
Diameter tolerance± mmNot documented±0.03 (Bambu Lab)[14]
Printing Parameters
Nozzle temperature°C380-400 (3DXTech printed-specimen conditions); Victrex quotes a 340-450 melt range for AM 450 FIL[1][4]190–230 (Bambu Lab); 190–210 (Fiberlogy PLA Mineral)[3][2]
Bed temperature°C130–140 (3DXTech)[1]35–45 (Bambu Lab); 60 (Fiberlogy)[3][2]
Enclosure / chamber requirement1–5Actively heated chamber required[15][16]Open frame is fine[3][2]
Recommended chamber temperature°CNot less than 150 for semi-crystalline printing (Victrex AM 450 FIL); bed above 150[4]Not documented
Part cooling fanNot documentedFan on; Fiberlogy specifies 75–100 %[3][2]
Bed surface & adhesion aidNot documentedCool plate, high-temperature plate or textured PEI with glue (Bambu Lab); smooth PEI, textured PEI or glass (Fiberlogy)[3][2]
Warping tendency1–5Severe — heated chamber needed[15]None[3]
Bed-adhesion difficulty1–5Very difficult — special plates or slurry required[15]Sticks to anything[17]
Overall printing difficulty1–5Expert / industrial hardware only[15][16]Beginner — prints on any machine out of the box[3][2]
Extruder requirementAn all-metal hot end rated above 400 °C and a heated chamber; 3DXTech tests at 0.25 mm layer height on a 0.4 mm nozzle[1][15]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[15]Brass fine indefinitely[18][3][2]
Abrasiveness1–5Non-abrasive when unfilled[1]Slightly abrasive — mineral filler pushes density from 1.24 to 1.31–1.38[2][3][19]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[20]Very low[18]
Heat-creep / jam sensitivity1–5Not documentedModerate — good heatbreak cooling needed; PLA softens below 60 °C[21]
Hotend requirementNot documentedNo special hot-end required[17]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Not documentedModerate — 0.40 % saturated at 25 °C / 55 % RH[3]
Equilibrium moisture content at ~50 % RH%0.45 at saturation, 23 °C (ISO 62); 0.55 at 100 °C[4]0.40 saturated at 25 °C / 55 % RH (Bambu Lab)[3]
Drying temperature & time120 °C for 5 h, target below 0.020 % moisture (Victrex AM 450 FIL)[4]50 °C for 8 h in a forced-air dryer, or 60–70 °C for 12 h on an X1 heatbed; Fiberlogy specifies 50 °C for 6 h[3][2][22]
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing, rough surface and weak layers[23]
Effect of moisture on strengthNo dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[20]Polymaker rates PLA low-sensitivity — the loss shows as poor layer adhesion and brittle layers rather than a published strength figure[23]
Storage requirementNot documentedSealed with desiccant below 20 % RH; shelf life at ambient is long[19][17]
Mechanical Properties
Tensile strength (XY)MPa60-100 (printed XY): Victrex AM 450 FIL 60-80 at yield and 3DXTech 100, both ISO 527; 98 at yield injection-moulded[1][4]30 (printed XY, ISO 527, Bambu Lab); 35.1 on My Tech Fun bars for PolyTerra PLA[3][24]
Young's modulusMPa3000-4000 (printed XY, ISO 527, Victrex AM 450 FIL); 3720 (3DXTech); 4000 injection-moulded[1][4]1960 (Bambu Lab, printed XY, ISO 527); Fiberlogy PLA Mineral quotes 3500 (ISO 527, specimen type not stated)[3][2]
Elongation at break%28 (printed XY, ISO 527) — remarkably ductile for a high-temperature polymer[1]14.8 (printed XY, ISO 527)[3]
Flexural strengthMPa130 (printed XY, ISO 178)[1]53 (printed XY, ISO 178) — 30 % below PLA Basic at 76[3][19]
Flexural modulusMPa2700 (printed XY, ISO 178)[1]2360 (printed XY, ISO 178)[3]
Charpy impact, notchedkJ/m²6.0 (injection-moulded, ISO 179/1eA); unnotched does not break[4]6.3 (printed XY, ISO 179, notched); unnotched 19.2[3]
Other impact dataIzod notched 7.0 kJ/m2 injection-moulded (ISO 180/A). Printed anisotropy is extreme: VICTREX AM 200 on a Stratasys F900 gives Izod notched 1380-1530 J/m XZ against 30-62 J/m ZX (ASTM D256)[4][25]Izod 6.1 kJ/m² on My Tech Fun printed bars for PolyTerra PLA[24]
Layer adhesion / Z tensileMPa20-85 at yield (printed ZX, ISO 527, Victrex AM 450 FIL); the spread is set by chamber temperature and weld quality[4]22 (printed Z, ISO 527); flexural Z falls to 29 against 53 in XY; 12.9 on My Tech Fun layer-adhesion bars[3][24]
Brittleness1–5Tough — absorbs impact, yields before breaking[1]Brittle — snaps with little warning[3]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 84.5 (injection-moulded, ISO 868); Rockwell M100 / R125 on extruded PEEK stock (ASTM D785)[4][26]Not documented
Creep resistance / sustained load1–5Excellent — holds load for years. Victrex rates PEEK for long-term creep; injection-moulded flexural stress at 3.5 % strain falls only from 125 MPa at 23 °C to 85 MPa at 125 °C, and extruded stock is rated to 249 °C continuous[27][4][26]Poor — 12 mm bar sagged to 18.7 mm over 5 days at 1.25 kg[24]
Fatigue / repeated-flex resistance1–5Excellent — living hinges viable. Victrex rates PEEK for long-term fatigue as well as creep[27]Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength (R = 0.2)[28][21]
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%71-84 (VICTREX AM 200 LMPAEK printed on the Stratasys F900 and Fortus 450mc, ZX against XZ tensile yield, ASTM D638); unfilled PEEK's own ZX spread is wider[25]73 by tensile, 55 by flexural (printed, Bambu Lab)[3]
Thermal Properties
HDT at 0.45 MPa°C140 (printed XY, ISO 75 at 0.45 MPa, 3DXTech)[1]58 (Bambu Lab) and 48 (Fiberlogy PLA Mineral), ISO 75 at 0.45 MPa[3][2]
HDT at 1.8 MPa°C152 (unannealed, ISO 75-2/Af, Victrex AM 450 FIL); 160 on extruded stock (ASTM D648 at 264 psi)[4][26]52 (ISO 75, 1.8 MPa)[3]
Glass transition (Tg)°C143 (DSC, 3DXTech); Victrex gives onset 143 and midpoint 150 (ISO 11357-2)[1][4]61 (DSC)[3]
Melting point / Vicat°C343 melting (ISO 11357-3, Victrex); VICTREX AM 200 LMPAEK melts at 303[4][25]163 peak melt (DSC); Vicat 63 °C[3]
Continuous service temperature°C240 UL 746B relative thermal index, strength (RTI electrical 260, impact 180); Ensinger rates extruded PEEK stock at 249 long term[4][26]54 — loaded bars begin to move at this temperature[24]
Annealing responseNot documented50–60 °C for 6–12 h; some prints deform or warp, and a forced-air oven is required[3]
Thermal expansion (CTE)µm/m·K37.8 (extruded PEEK stock, 23-60 °C, ASTM E831; source states 2.1e-5 in/in/°F), rising to 41.9 at 60-100 °C and 55.8 at 100-150 °C[26]Not documented
Flammability / UL 94UL 94 V-0 at 1.5 mm on the base resin; glow-wire flammability index 960 °C at 2.0 mm (IEC 60695-2-12)[1][4]Flammable; no UL 94 rating published by the major brands[19][29]
Environment & Chemical
UV resistance1–5Not documentedDegrades within weeks outdoors[21][30]
Chemical resistanceOutstanding — resistant to almost all solvents and to steam sterilisation[1]Good against weak acids, oils and grease; poor against strong acids and alkalis; dissolved by chloroform, THF and hot benzene[29][21]
Water / humidity resistance in service1–5Excellent — essentially unaffected; 0.45 % water at saturation and resistant to steam sterilisation[4][1]Good — insoluble in water[19]
Food contactNot documentedBase resin is food-contact grade, but printed layer grooves harbour bacteria; Prusa advises against food use[21]
Biodegradability / compostabilityNot documentedIndustrially compostable only — needs sustained 55 °C; not home compostable[31][21]
RecyclabilityNot documentedMechanically recyclable; not accepted in household plastic collection[31]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[32]Low hazard — minimal VOC and particle emission[32]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[32]None needed in a normal room[32]
Post-Processing
Sanding & machiningNot documentedWet sanding — dry sanding heats the surface by friction and smears it[30][21]
Gluing & solvent weldingNot documentedCyanoacrylate for most joints; some grades partially dissolve and bond with acetone[21][33]
Vapour / chemical smoothingNot documentedNo practical vapour smoothing — only chloroform, hot benzene or THF, which are laboratory-only[21]
Support material pairingNot documentedSupport for PLA (Bambu Lab)[3]
Dimensional accuracy & detailNot documentedMatte surface hides layer lines; 55° overhangs and 30 mm bridges as for plain PLA[3]
Solvents & Solubility
Soluble in95–98 wt% sulphuric acid dissolves it — 10 g per 100 mL at 40–70 °C gives a dark red solution. Laboratory route only.[34][35]Chloroform: 10 % w/v in 2–4 h at 23 °C, every grade and morphology; THF and DMF only at 65 °C. Laboratory reagents.[36]
Softened or crazed byConcentrated nitric, hydrofluoric, hydrobromic and hydriodic acids attack it; DCM, DMSO and THF swell thin-walled sections.[37][35]Acetone, ethyl acetate and toluene plasticise it but dissolve <1 % even at 65 °C; submersion in acetone crazes and destroys parts.[36][38]
Solvent welding & smoothing agentNone — no solvent softens PEEK, so parts are joined thermally or mechanically, never chemically.[37][35]Chloroform vapour smooths and welds PLA at the cost of tensile strength; acetone does not smooth it at all.[39][38]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. ThermaX PEEK Technical Data Sheet v3 3DXTech · 2026-08 · tds
  2. PLA Mineral — product and technical data Fiberlogy · 2026-08 · tds
  3. Bambu Filament Technical Data Sheet V3.0 — PLA Matte Bambu Lab · 2026-08 · tds
  4. VICTREX AM 450 FIL — datasheet Victrex · 2025-12 · tds
  5. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  6. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  7. IEMAI 3D PEEK 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  8. Polymaker Panchroma Matte PLA — product listing 3DJake International · 2026-08 · vendor
  9. Overture Matte PLA 1.75mm Overture3D · 2026-08 · vendor
  10. Matte PLA filament collection Anycubic Official Store · 2026-08 · vendor
  11. Matte PLA filament collection Sunlu Official Store · 2026-08 · vendor
  12. Fiberlogy PLA Mineral — product listing 3DJake International · 2026-08 · vendor
  13. Extrudr PLA NX2 Matt — product listing 3DJake International · 2026-08 · vendor
  14. PLA Basic — product page Bambu Lab US Store · 2026-08 · vendor
  15. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  16. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  17. PLA — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  19. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  20. ThermaX PEEK — product page 3DXTech · 2026-08 · vendor
  21. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  22. Filament Drying Recommendations Bambu Lab Wiki · 2026-08 · doc
  23. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  24. PolyTerra PLA vs PLA+ — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. VICTREX AM 200 — FDM Material Data Sheet Stratasys · 2024-04 · tds
  26. TECAPEEK natural (PEEK) — stock shape properties Ensinger · 2026-08 · tds
  27. PEEK polymers — product overview Victrex · 2026-08 · doc
  28. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  29. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  30. Prusament PLA Technical Data Sheet v1.0 Prusa Polymers · 2018-09 · tds
  31. Filamentive PLA (recycled) — product page Filamentive · 2026-08 · vendor
  32. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  33. Prusament rPLA Corn Pigment 1kg — product page Prusa Research · 2026-08 · vendor
  34. The Effects of Sulfonated Poly(ether ether ketone) Ion Exchange Preparation Conditions on Membrane Properties Yee, Zhang & Ladewig, Membranes 3(3) 182–195 · 2013-07 · paper
  35. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  36. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  37. What solvents are not compatible with PEEK? — fluidics technical FAQ IDEX Health & Science · 2026-08 · doc
  38. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  39. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper