3D Printing Info

Filament comparison

PE vs PLA Stone

Compare printing settings, strength, heat resistance, dated prices and sources.

Polyethylene (PE) guideStone-filled PLA guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PE comparisonsMore PLA Stone comparisons
PE vs PLA Stone — documented properties and sources
PropertyPolyethylene (PE)POLYOLEFINStone-filled PLAPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$87.72/kg median; $87.72–$87.72/kg across 1 dated product listings$22.99/kg median; $15.99–$49.16/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryPolyethylene — the simplest polyolefin, non-polar and highly crystalline. The one retailed filament grade, Spectrum HDPE, uses what Spectrum calls Low Warp technology and is denser and stiffer than plain HDPE[1][2]PLA filled with stone or mineral powder — Formfutura StoneFil declares 40–50 wt% stone powder[3][4]
Densityg/cm³1.10 (Spectrum HDPE filament, ISO 1183) against 0.95 for extruded HDPE stock — the filament is a modified formulation[1][2]1.22 (Bambu Lab PLA Marble) and 1.50–1.70 (Formfutura StoneFil), ISO 1183[4][3]
Typical priceUSD/kg1 kg-equivalent spools cluster near 88[5]1 kg spools cluster near 21[6][7]
Price range across brandsUSD/kg87.72 — Spectrum's 500 g spools at 3DJAKE are the only PE filament listing found[5]16–49 across brands; SUNLU 16, ELEGOO 19, Polymaker 21, Bambu Lab 25, Prusament 38, Filament PM MarbleJet 49 on 0.5 kg spools[8][7][6][9][10][11]
Market availability1–5Niche, a handful of specialist brands — Spectrum HDPE in six colours is the only PE filament in the 3DJAKE and igo3d product sitemaps, at MatterHackers or at Printed Solid, but it is a normal stocked item rather than a special order[12][13][9][5]Stocked by most mainstream brands[6][7][8]
Spool sizes & diameters1.75 mm; 500 g spools in six colours[5][12]1.75 and 2.85 mm; 0.5 and 1 kg spools plus refills[7][3]
Typical applicationsChemically resistant containers, packaging prototypes and consumer goods where HDPE is the production material[1]Architectural models, sculpture and props with a matte mineral surface[4]
Printing Parameters
Nozzle temperature°C240-290 (Spectrum HDPE)[1]190–230 (Bambu Lab)[4]
Bed temperature°C80-100 (Spectrum HDPE)[1]35–45 (Bambu Lab)[4]
Enclosure / chamber requirement1–5Enclosure recommended — Spectrum recommends a closed chamber for larger prints[1]Open frame is fine[4]
Part cooling fan0-50 % part cooling (Spectrum HDPE)[1]Fan on[4]
Bed surface & adhesion aidSpectrum states no adhesive is necessary for its low-warp HDPE, depending on geometry[1]Not documented
Warping tendency1–5Moderate — needs adhesion aid or draught shield. Spectrum's low-warp grade is sold as printable on desktop machines, which is not true of plain polyethylene[1]Not documented
Bed-adhesion difficulty1–5Needs the right surface or a thin adhesive; Spectrum states no adhesive is necessary but recommends a closed chamber for large parts[1]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; Spectrum sells the grade as desktop-printable with no dry box and no hardened nozzle[1]Easy — minor profile tuning; 0.2 mm nozzles are not usable[14]
Extruder requirementNot documentedNozzles below 0.4 mm are not compatible (Bambu Lab)[14]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely — Spectrum states a ruby or hardened nozzle is not required[1]Brass acceptable; hardened steel for volume work — Bambu Lab's compatibility table says no hardened nozzle is needed while the note under the same table groups PLA Marble with particle-filled materials that should always use one[14]
Abrasiveness1–5Non-abrasive[1]Moderately abrasive — stone fill[14][3]
Nozzle clog risk1–5Low — Spectrum lists no drybox and no ruby or hardened nozzle for HDPE, and very low moisture absorption[1]Moderate — needs dry filament and a clean nozzle[14]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Negligible (<0.1 % EMC) — Spectrum lists very low moisture absorption and no dry box[1]Moderate — 0.44 % saturated at 25 °C / 55 % RH[4]
Equilibrium moisture content at ~50 % RH%Not documented0.44 saturated at 25 °C / 55 % RH (Bambu Lab)[4]
Drying temperature & timeNo drying step published; Spectrum lists a dry box as not required[1]Not documented
Effect of moisture on strengthNot applicable in practice — Spectrum lists very low moisture absorption and no drybox requirement for HDPE[1]Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[15]
Storage requirementStore dry at 18-25 °C out of sunlight; Spectrum quotes a 24-month shelf life[1]Not documented
Mechanical Properties
Tensile strength (XY)MPa29 at break (Spectrum HDPE, ISO 527; specimen type not stated) against 25.5 at yield on extruded HDPE stock (ASTM D638, from 3700 psi)[1][2]33 ± 4 printed XY, ISO 527 (Bambu Lab)[4]
Young's modulusMPa3500 (Spectrum HDPE, ISO 527) against 965 on extruded HDPE stock (ASTM D638, from 140,000 psi) — the filament grade is nearly four times stiffer than plain polyethylene[1][2]2330 ± 240 printed XY, ISO 527 (Bambu Lab)[4]
Elongation at break%18 at break (Spectrum HDPE, ISO 527) against above 100 on extruded stock (ASTM D638)[1][2]6.7 ± 0.5 printed XY, ISO 527 (Bambu Lab)[4]
Flexural strengthMPa27.6 on extruded HDPE stock (ASTM D790; converted from 4000 psi)[2]75 ± 5 printed XY, ISO 178 (Bambu Lab)[4]
Flexural modulusMPa3200 (Spectrum HDPE, ISO 178) against 965 on extruded stock (ASTM D790, from 140,000 psi)[1][2]2920 ± 180 printed XY, ISO 178 (Bambu Lab)[4]
Charpy impact, notchedkJ/m²Not documented9.5 ± 2.6 printed XY, ISO 179, notched (Bambu Lab)[4]
Other impact dataCharpy 10 kJ/m2 (Spectrum HDPE, ISO 179-1; notch condition not stated); Izod 104 J/m on extruded stock, converted from 1.94 ft-lb/in (ASTM D256)[1][2]Charpy unnotched 24.0 printed XY (Bambu Lab, ISO 179)[4]
Layer adhesion / Z tensileMPaNot documented30 ± 4 printed Z, ISO 527 (Bambu Lab)[4]
Brittleness1–5Tough — absorbs impact, yields before breaking; 18 % elongation at break on the filament and above 100 % on extruded stock[1][2]Brittle — snaps with little warning[4]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 67 and Rockwell R54 on extruded HDPE stock (ASTM D2240, D785); Spectrum quotes Rockwell 80 HRM for its filament (ISO 2039-2)[2][1]Not documented
Creep resistance / sustained load1–5Not documentedPoor — no stone-filled creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[16][17][18]
Fatigue / repeated-flex resistance1–5Good — Spectrum lists outstanding abrasion and crack resistance for its HDPE, but no repeated-flex or fatigue test data was found for any PE filament[1]Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and the mineral filler leaves a brittle compound[19][4]
Elasticity / flexibility1–5Slightly flexible in thin sections — Spectrum's low-warp grade has a 3.5 GPa tensile modulus; plain extruded HDPE at 965 MPa is genuinely semi-flexible[1][2]Rigid[4]
Z strength as % of XY%Not documented91 by tensile, 73 by flexural (printed, Bambu Lab)[4]
Thermal Properties
HDT at 0.45 MPa°C75 on extruded HDPE stock (ASTM D648 at 66 psi; converted from 167 °F)[2]56 (ISO 75, 0.45 MPa)[4]
HDT at 1.8 MPa°CNot documented53 (ISO 75, 1.8 MPa)[4]
Glass transition (Tg)°CNot documented56 (DSC)[4]
Melting point / Vicat°CNot documented156 peak melt (DSC); Formfutura gives a 120–170 melting range for StoneFil[4][3]
Continuous service temperature°C110 stated as heat resistance by Spectrum with no test standard given; extruded stock is rated 120 long-term maximum (converted from 248 °F) and brittle below -76[1][2]Not documented
Thermal expansion (CTE)µm/m·K117 (extruded HDPE stock, ASTM D696; source states 6.5e-5 in/in/°F)[2]Not documented
Environment & Chemical
UV resistance1–5Moderate — a season or two. Spectrum describes its HDPE as UV-stable and weather-resistant but publishes no exposure data[1]Degrades within weeks outdoors[20]
Chemical resistanceExcellent chemical resistance to acids, bases, oils and solvents (Spectrum); Ensinger lists broad chemical compatibility for HDPE stock[1][2]Not documented
Water / humidity resistance in service1–5Excellent — essentially unaffected; Ensinger lists low moisture absorption for HDPE stock and Spectrum very low absorption for the filament[1][2]Not documented
RecyclabilitySpectrum states the filament is fully recyclable; HDPE is resin code 2[1]Not documented
Health & Safety
Fume toxicity1–5Not documentedLow hazard — minimal VOC and particle emission[21]
Ventilation / filtration requirement1–5Not documentedNone needed in a normal room[21]
Dust & fibre handling hazardNot documentedFormfutura's SDS sets an occupational limit of 1 mg/m³ for the stone powder and lists it as both a fibre and a particulate — do not dry-sand without extraction[3]
Post-Processing
Sanding & machiningEasy to machine — Ensinger lists machinability as a headline property of HDPE stock[2]Sands to a stone-like matte surface[3]
Support material pairingNot documentedSupport for PLA (Bambu Lab)[4]
Dimensional accuracy & detailSpectrum lists a shiny surface finish and no adhesive requirement; shrinkage remains the limit on large flat parts[1]Matte mineral surface hides layer lines; 55° overhangs and 30 mm bridges as for plain PLA[4]
Solvents & Solubility
Soluble inNone at room temperature; xylene dissolves HDPE at about 105 °C and LDPE at 75 °C. Hot decalin does the same.[22][23]Chloroform dissolves the PLA matrix (10 % w/v, 2–4 h at 23 °C) and leaves the filler as loose sludge; laboratory reagent.[24]
Softened or crazed byToluene, xylene, styrene, chloroform, dichloromethane, MEK and trichloroethylene are all unsatisfactory at 21 °C.[23]Acetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[24][25]
Solvent welding & smoothing agentNone — polyethylene has no room-temperature solvent, so joints are made by heat welding.[23][22]Chloroform vapour attacks only the resin fraction, so the filler is left standing proud; no workshop-safe agent exists.[26][25]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Spectrum HDPE Technical Data Sheet Spectrum Filaments · 2025-10 · tds
  2. TECAFINE HDPE natural — stock shape properties Ensinger · 2026-08 · tds
  3. StoneFil safety data sheet Formfutura · 2026-08 · msds
  4. Bambu Filament Technical Data Sheet — PLA Marble Bambu Lab · 2026-08 · tds
  5. Spectrum HDPE Traffic Black, 1.75 mm / 500 g 3DJAKE · 2026-08 · vendor
  6. PLA Marble — product page Bambu Lab US Store · 2026-08 · vendor
  7. Polymaker product catalogue Polymaker · 2026-08 · vendor
  8. ELEGOO product catalogue ELEGOO · 2026-08 · vendor
  9. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  10. SUNLU High Speed PLA Marble 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  11. Filament PM PLA MarbleJet technical data sheet Filament PM (Plasty Mladec) · 2026-08 · tds
  12. 3DJAKE product catalogue 3DJAKE · 2026-08 · vendor
  13. igo3d product sitemap (17452 product URLs) igo3d · 2026-08 · vendor
  14. PLA Usage Guide Bambu Lab Wiki · 2026-08 · doc
  15. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  16. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  17. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  18. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  19. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  20. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  21. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  22. US 5,278,282 Polymer recycling by selective dissolution — xylene dissolution temperatures Nauman & Lynch, Rensselaer Polytechnic Institute · 1994-01 · paper
  23. HDPE Chemical Resistance Guide (21 °C and 60 °C) INEOS Olefins & Polymers USA · 2026-08 · tds
  24. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  25. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  26. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper