3D Printing Info

Filament comparison

PC vs PLA-PHA

Compare printing settings, strength, heat resistance, dated prices and sources.

Polycarbonate (PC) guidePLA/PHA blend guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC comparisonsMore PLA-PHA comparisons
PC vs PLA-PHA — documented properties and sources
PropertyPolycarbonate (PC)PCPLA/PHA blendPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$39.99/kg median; $29.99–$92.00/kg across 9 dated product listings$76.40/kg median; $76.40–$76.40/kg across 1 dated product listings
Identity & Market
Base polymer / chemistryBisphenol-A polycarbonate — an amorphous engineering thermoplastic[1][2]PLA blended with polyhydroxyalkanoate, a bacterially fermented bio-polyester[3]
Densityg/cm³1.19 (Polymaker) to 1.22 (Prusament), ISO 1183; Bambu Lab 1.20; Stratasys specific gravity 1.20 (ASTM D792)[1][4][5][6]1.2 (ISO 1183)[3]
Typical priceUSD/kg1 kg spools cluster near 40[5][7][8]Not documented
Price range across brandsUSD/kg30–92 across brands; Polymaker PolyLite 30, Bambu Lab 40, Polymaker PolyMax 52, Prusament 59, 3DXTech ezPC 64 and 3DXMAX PC 92[7][5][8][9]Not documented
Market availability1–5Available from several mainstream brands[5][7][9][8]Niche, a handful of specialist brands[3][10]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75, 0.9, 1 and 3 kg spools[7][9][8]1.75 and 2.85 mm; 750 g and 2200 g spools[3]
Typical applicationsLight guides, lenses, under-bonnet automotive parts and impact-loaded housings that must hold shape above 110 °C[2][1]General-purpose printing where PLA's brittleness is the limiting factor[3]
Diameter tolerance± mm±0.03 (Prusament PC Blend)[4]Not documented
Printing Parameters
Nozzle temperature°C250–280 across brands; Prusament 275 ± 10, Bambu Lab 260–280, Polymaker 250–270. Polymaker's material guide gives a wider 260–310 for PC and its composites[4][5][1][2]195–220 (colorFabb)[3]
Bed temperature°C90–115; Prusament 110 ± 10, Bambu Lab 90–110, Polymaker 90–105[4][5][1]50–60 (colorFabb)[3]
Enclosure / chamber requirement1–5Enclosure required (passive) — Polymaker specifies a 70–100 °C chamber, Bambu Lab 45–60 °C and rules out its P1P and A-series machines[1][5][11]Open frame is fine[3]
Recommended chamber temperature°C70–100 (Polymaker); 45–60 (Bambu Lab)[1][5]Not documented
Part cooling fanOff or very low — Polymaker specifies off, Prusament 20 % within a 0–30 % range, Bambu Lab 0–60 %[1][4][5]0–100 %; colorFabb states the blend runs on both heated and unheated beds[3][12]
Bed surface & adhesion aidTextured PEI with glue when needed (Polymaker); smooth or textured PEI (Bambu Lab)[1][13]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s24 at Bambu Lab's 300 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer; Polymaker allows 50–200 mm/s and its material guide advises 30–60 for layer adhesion[5][1][2][14]3.2–8 at colorFabb's 40–100 mm/s, on a 0.4 mm nozzle at 0.2 mm layer[12][14]
Warping tendency1–5Severe — heated chamber needed[1][2][11]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[1][11]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[2]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[2][11]Beginner — prints on any machine out of the box[3]
Extruder requirementAll-metal hotend rated to 300 °C; Polymaker advises larger nozzles and high chamber temperatures to improve bonding[2]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[11]Brass fine indefinitely[3]
Abrasiveness1–5Non-abrasive[1]Non-abrasive[3]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle[2]Very low — unfilled PLA blend; Prusa lists no drybox and no hardened nozzle for PLA[15]
Heat-creep / jam sensitivity1–5Slightly sensitive[16]Not documented
Hotend requirementAll-metal hot end required (Simplify3D); Polymaker advises a hot end rated above 300 °C[16][2]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low — 0.25 % saturated at 25 °C / 55 % RH (Bambu Lab); Prusa measures 0.15 % after 7 days at 22 % RH. Polymaker nonetheless calls PC highly hygroscopic in service[5][4][2]Moderate — the PLA matrix takes up 0.40–0.51 % saturated; colorFabb publishes no figure for the blend[17][18]
Equilibrium moisture content at ~50 % RH%0.25 saturated at 25 °C / 55 % RH (Bambu Lab); 0.15 after 7 days at 24 °C / 22 % RH (Prusa)[5][4]Not documented
Drying temperature & time80 °C for 8 h (Bambu Lab); 75 °C for 6 h (Polymaker); 70–80 °C for 6–8 h (Polymaker material guide)[5][1][2]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing, rough surface and weak layers[19]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[2][19]Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[19]
Storage requirementAirtight containers with desiccant to prevent reabsorption[2]Not documented
Mechanical Properties
Tensile strength (XY)MPa53.4 (PolyMax) to 69.1 (PolyLite) printed XY, ISO 527; Bambu Lab 62 +/- 2 and Prusament 63 +/- 1 at yield; Stratasys 62.3-64.6 at yield printed XZ, ASTM D638 (its PC White table duplicates the Antero 840CN03 figures and was not used)[1][20][5][4][21][6]62–64 (ISO 527-1A, colorFabb; two grades quoted)[3]
Young's modulusMPa2110 (Bambu Lab) to 2497 (PolyLite) printed XY, ISO 527; Prusament 1900, 3DXTech 2180[5][1][4][21]2960–3070 (ISO 527-1A, colorFabb)[3]
Elongation at break%3.8 (Bambu Lab) to 4.8 (PolyLite) at break, printed XY, ISO 527; 3DXTech quotes 14 at break, Prusament 5.8 at yield[5][1][21][4]4 and 11 (ISO 527-1A, colorFabb; two grades quoted)[3]
Flexural strengthMPa81.3 (PolyMax) to 108 (Bambu Lab) printed XY, ISO 178; Prusament 88 ± 1, PolyLite 106.1[20][5][4][1]Not documented
Flexural modulusMPa2050 (PolyMax) to 2640 (PolyLite) printed XY, ISO 178; Prusament 2100[20][1][4]2500–3300 flexural modulus (ISO 178, colorFabb)[3]
Charpy impact, notchedkJ/m²4.1 (PolyLite) to 21.3 (PolyMax) printed XY, ISO 179, notched; Prusament 12 ± 1[1][20][4]2.8–3.7 (ISO 179, notched, colorFabb)[3]
Other impact dataCharpy unnotched does not break on Prusa's pendulum in either orientation (ISO 179-1); PolyMax PC retains 9.2 kJ/m2 notched at -30 °C. Stratasys PC Black gives 85.3 MPa flexural strength at break in ZX against no break in XZ (ASTM D790, printed)[4][20][6]Not documented
Layer adhesion / Z tensileMPa37.1-45.3 at yield printed ZX (Stratasys PC Black and Red, ASTM D638); 41.4 (PolyMax) to 56 (Bambu Lab) printed Z; Prusa's interlayer adhesion test gives 21 +/- 2[4][20][5][6]Not documented
Brittleness1–5Tough — absorbs impact, yields before breaking[2][4]Moderate — colorFabb positions the blend as tougher and less brittle than its generic PLA grades[3]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 79 (Prusa Polymers method) and Shore D 79 on extruded PC stock (ASTM D2240); Rockwell 70 (118) — the source does not name the scales[4][22]Not documented
Creep resistance / sustained load1–5Excellent — holds load for years. Room-temperature tensile creep of moulded PC was still running unbroken at 41 MPa when the experiment was stopped for time; specimens failed within the test window only at 47-52 MPa (ASTM D638)[23]Poor — no PLA/PHA creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[24][25][26]
Fatigue / repeated-flex resistance1–5Good[4][2]Below average — no S-N curve for the blend; colorFabb positions it as tougher and less brittle than its generic PLA, which ran 38 000–49 000 cycles at 30 % of tensile strength[27][3]
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%59-73 (Stratasys PC Black and Red, ZX against XZ tensile yield, ASTM D638); 76 for PolyLite PC and 90 for Bambu Lab (printed Z against XY tensile)[5][1][6]Not documented
Thermal Properties
HDT at 0.45 MPa°C110 (PolyMax PC-FR) to 114 (PolyMax PC), ISO 75 at 0.45 MPa; Bambu Lab 112, PolyLite 111, Prusament 113. Stratasys FDM PC reaches 144 printed (ASTM D648 Method B at 66 psi)[20][1][5][4][6]Not documented
HDT at 1.8 MPa°C93 (Prusament) to 117 (Bambu Lab), ISO 75 at 1.8 MPa; PolyLite 107, PolyMax 99. Stratasys FDM PC reaches 141 printed (ASTM D648 Method B at 264 psi)[4][5][1][20][6]Not documented
Glass transition (Tg)°C113 (Polymaker, DSC), 142.5 (Stratasys, ASTM D7426 inflection point) and 145 (Bambu Lab, DSC); Polymaker's material guide quotes 150[1][5][2][6]Not documented
Melting point / Vicat°CAmorphous — no melting point; Vicat 117–120 (Polymaker, ISO 306); decomposition above 360 °C[1][20]Above 155 melting (ISO 3146-C)[3]
Continuous service temperature°C113 — Prusa publishes this as the temperature resistance of Prusament PC Blend; extruded PC stock is rated 121 long term (converted from 250 °F)[4][22]Not documented
Annealing response90 °C for 2 h (Polymaker)[1]Not documented
Thermal expansion (CTE)µm/m·K51.6 in XY over -50 to 30 °C, falling to 35.8 over 30-75 °C and 11.5 over 75-130 °C; 49.2 in XZ over -50 to 120 °C (printed, ASTM E831). Extruded PC stock gives 68.4 (ASTM D696)[6][22]Not documented
Flammability / UL 94Flammable; no UL 94 rating on standard PC, though V-0 grades exist[28][1]Not documented
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors — unstabilised PC yellows and embrittles under UV[2]Degrades within weeks outdoors[29]
Chemical resistanceWithstands oils, solvents and fuels; Polymaker rates it good against weak acids[2]Not documented
Water / humidity resistance in service1–5Good — minor absorption[5]Not documented
Food contactBisphenol-A polycarbonate is not offered as food-contact filament[2]Not documented
Biodegradability / compostabilityNot biodegradable[2]colorFabb states the PHA component is 100 % biodegradable[3]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[2]Not documented
Electrical & ESD propertiesSurface resistance above 10¹³ ohm/sq — an electrical insulator, which Polymaker lists as a headline advantage[21][2]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[30]Low hazard — minimal VOC and particle emission[30]
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[30]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[30][11]None needed in a normal room[30]
Post-Processing
Sanding & machiningSands and machines well; the toughness means it cuts rather than chips[16]Not documented
Painting & finishingOptical clarity survives printing, so transparent parts are usually left unpainted[2]Not documented
Gluing & solvent weldingCyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[16]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[16]Not documented
Support material pairingPrints its own supports; 3DXTech sells a dedicated PC break-away support[16]Not documented
Dimensional accuracy & detailWarping is the dominant accuracy limit; light transmission 89 % on PolyLite PC (GB/T 2410)[1][2]Not documented
Solvents & Solubility
Soluble inDichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[31]Chloroform dissolves the PLA phase (10 % w/v, 2–4 h at 23 °C); THF and DMF need 65 °C. Laboratory reagents.[32]
Softened or crazed byMethanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[31]Acetone, ethyl acetate and toluene plasticise it but dissolve <1 % even at 65 °C; submersion in acetone crazes and destroys parts.[32][33]
Solvent welding & smoothing agentDichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[34]Chloroform vapour smooths and welds PLA at the cost of tensile strength; acetone does not smooth it at all.[35][33]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  2. PC — material basics Polymaker Wiki · 2026-08 · doc
  3. PLA/PHA technical data sheet colorFabb · 2026-08 · tds
  4. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  5. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  6. PC (Polycarbonate) — FDM Material Data Sheet Stratasys · 2026-04 · tds
  7. Polymaker product catalogue Polymaker · 2026-08 · vendor
  8. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. woodFill technical data sheet colorFabb · 2026-08 · tds
  11. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  12. glowFill technical data sheet colorFabb · 2026-08 · tds
  13. Bambu Filament Technical Data Sheet V1.0 — PC FR Bambu Lab · 2026-08 · tds
  14. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  15. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  16. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  18. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  19. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  20. PolyMax PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  21. ezPC Polycarbonate Technical Data Sheet 3DXTech · 2026-08 · tds
  22. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  23. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  24. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  27. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  28. PolyMax PC-FR Technical Data Sheet V5.5 Polymaker · 2024-11 · tds
  29. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  30. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  31. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  32. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  33. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  34. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds
  35. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper