Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PC (PC-GF) guideSoft TPU (below 85A) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC-GF comparisonsMore TPU soft comparisons
PC-GF vs TPU soft — documented properties and sources
PropertyGlass-fibre PC (PC-GF)PCSoft TPU (below 85A)FLEX
Market snapshot
Listing priceUSD/kg; dated snapshots$71.27/kg median; $71.27–$71.27/kg across 1 dated product listings$114.04/kg median; $109.80–$122.27/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryPolycarbonate reinforced with 30 wt% short glass fibre[1]Very soft thermoplastic elastomers below 85 Shore A. Fiberlogy's FiberFlex 30D measures 81 Shore A, the softest grade with a published datasheet found here[2]
Densityg/cm³1.17 (measured on a 100 % infill printed part, ISO 1183-A)[1]1.07 (Fiberlogy FiberFlex 30D, ISO 1183)[2]
Typical priceUSD/kg1 kg spools cluster near 71[3]1 kg-equivalent spools cluster near 115[4][5][6]
Price range across brandsUSD/kg71 — BASF Ultrafuse PC GF30 at igo3d is the only priced listing found; Owens Corning sells XSTRAND GF30-PC in 500 g and 1 kg[3][1]110–122 at 1 kg-equivalent; Recreus 70A 110 and 60A 116 at 500 g, NinjaTek Edge 83A 112, NinjaTek Chinchilla 75A 122; the Recreus 3 kg spools fall to 70–73[4][6][5]
Market availability1–5Niche, a handful of specialist brands — neither Polymaker's nor 3DXTech's polycarbonate range contains a glass-fibre grade, but BASF Forward AM and Owens Corning both sell one through European retail[3][1][7][8]Niche, a handful of specialist brands[2][9][4]
Spool sizes & diameters1.75 and 2.85 mm at +/- 0.05 mm; 500 g and 1 kg net spools[1]1.75, 2.85 and 3 mm; 0.5, 0.85, 1, 2 and 3 kg spools[2][4][10][5]
Typical applicationsFunctional prototyping for mechanical engineering, electronics and automotive[1]Highly compliant seals, soft grips and prosthetic liners[2]
Diameter tolerance± mm+/- 0.05 (Owens Corning XSTRAND)[1]Not documented
Printing Parameters
Nozzle temperature°C280-330 (Owens Corning XSTRAND GF30-PC)[1]Not documented
Bed temperature°C80-110 (Owens Corning XSTRAND GF30-PC)[1]50–70 (Fiberlogy FiberFlex 30D)[2]
Enclosure / chamber requirement1–5Enclosure required (passive) — as for unfilled PC[11][12]Open frame is fine[2]
Bed surface & adhesion aidPerforated plate, DimaFix or Magigoo PC glue (Owens Corning)[1]PEI sheet or painter's tape; Polymaker warns TPU can over-stick and advises a glue stick as a release agent[13][14]
Overall printing difficulty1–5Not documentedExpert / industrial hardware only — below 85 Shore A the filament buckles in almost any feed path that is not a short, constrained direct drive[10][14]
Extruder requirementOwens Corning specifies a nozzle above 0.4 mm and hardened steel nozzles and drive wheels[1]Direct drive only, with a constrained filament path; Bowden is not viable at this hardness[10][9]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Owens Corning states glass reinforcement shortens brass nozzle and drive-wheel life[1]Brass fine indefinitely[15]
Abrasiveness1–5Highly abrasive — 30 wt% glass fibre[1]Non-abrasive[15]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles; PC already absorbs water from the air and Prusa lists glass-filled composites as a higher clogging risk[16][17]High — jams from moisture, heat creep or particles; below 85 Shore A the filament buckles and compresses, and Simplify3D warns that raised feed rates most likely end in a jam[13][14][18]
Heat-creep / jam sensitivity1–5Not documentedVery high — softens in the cold zone readily[14]
Hotend requirementNot documentedNo special hot-end required, but a direct-drive extruder is (Simplify3D)[13]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Negligible (<0.1 % EMC) — Owens Corning measures below 0.1 % at 23 °C and 50 % RH (ISO 62)[1]Moderate[18]
Equilibrium moisture content at ~50 % RH%Below 0.1 at 23 °C and 50 % RH, and below 0.1 at saturation (ISO 62)[1]Not documented
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing and a rough surface[18]
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[19][18]Polymaker groups TPU with the highly hygroscopic materials; no dry-versus-conditioned figures are published[18]
Storage requirementNot documentedSealed with desiccant; often kept in a dryer during the print[18]
Mechanical Properties
Tensile strength (XY)MPa65 at break (printed, ISO 527 at 1 mm/min)[1]Not documented
Young's modulusMPa5400 (printed, ISO 527 at 1 mm/min)[1]Not documented
Elongation at break%2.5 at break (printed, ISO 527 at 1 mm/min)[1]870 at break (Fiberlogy FiberFlex 30D, ISO 527) — the highest elongation in the dataset[2]
Flexural strengthMPa113 at yield (printed, ISO 178 at 2 mm/min)[1]Not documented
Flexural modulusMPa5500 (printed, ISO 178 at 2 mm/min)[1]Not documented
Brittleness1–5Brittle — snaps with little warning; 2.5 % elongation at break[1]Very ductile — bends far before failing[2]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for a glass-fibre grade[20]81 Shore A and 30 Shore D (Fiberlogy FiberFlex 30D, ISO 7619)[2]
Creep resistance / sustained load1–5Excellent — holds load for years. Room-temperature tensile creep of moulded unfilled PC ran unbroken at 41 MPa until the test was stopped, and 30 wt% glass raises the tensile modulus from about 2.3 to 5.4 GPa[21][1]Poor — no creep test at this hardness; a printed 95A TPU bar crept from 74.5 to 82.7 mm over 5 days at 1.25 kg[22]
Fatigue / repeated-flex resistance1–5Not documentedExcellent — living hinges viable[14]
Elasticity / flexibility1–5Rigid[1]Rubbery / highly elastic[2]
Wear resistance & frictionNot documentedTear strength 95 kN/m (Fiberlogy FiberFlex 30D, ISO 34-1)[2]
Thermal Properties
HDT at 1.8 MPa°C137 (printed, ISO 75 Method A at 1.8 MPa)[1]Not documented
Glass transition (Tg)°C145 (DSC, ISO 11357)[1]Not documented
Melting point / Vicat°C270 stated as melting point (ISO 11357) — unusual for an amorphous polymer, but this is the published figure[1]170 melting (Fiberlogy FiberFlex 30D, DSC)[2]
Thermal expansion (CTE)µm/m·K26.2 in XY and 77.4 in Z (printed, ISO 11359-2) — a threefold anisotropy, and the lowest in-plane expansion of any polycarbonate here[1]Not documented
Flammability / UL 94UL 94 V-0 verified (Owens Corning)[1]Not documented
Environment & Chemical
UV resistance1–5Good — years with some colour shift. Owens Corning lists UV resistance as a product benefit but publishes no exposure data[1]Good — years with some colour shift; Polymaker lists UV exposure among the conditions TPU withstands[14]
Chemical resistanceNot documentedWithstands industrial solvents and UV exposure (Polymaker)[14]
Water / humidity resistance in service1–5Excellent — essentially unaffected; below 0.1 % water at saturation (ISO 62)[1]Not documented
Food contactNot documentedNot food safe without specific certification (Polymaker)[14]
Biodegradability / compostabilityNot documentedNot biodegradable[14]
RecyclabilityNot documentedNot accepted in household plastic collection[14]
Electrical & ESD propertiesElectrically insulating (Owens Corning)[1]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[23]Low hazard — minimal VOC and particle emission; TPU was not among the nine filaments in the chamber study[23]
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[23]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[23][12]Open a window / occasional ventilation[23]
Dust & fibre handling hazardOwens Corning warns that the glass reinforcement is abrasive when melted and advises sufficient ventilation and avoiding extrusion fumes[1]Not documented
Post-Processing
Sanding & machiningNot documentedDifficult to sand or smooth; Polymaker limits post-processing to trimming or tumbling[14]
Gluing & solvent weldingNot documentedCyanoacrylate bonds TPU; no common solvent welds it[14]
Vapour / chemical smoothingNot documentedNo practical vapour smoothing[14]
Support material pairingNot documentedPolymaker warns TPU supports are often very difficult to remove[14]
Dimensional accuracy & detailHigh dimensional stability is the headline benefit; the 26.2 um/m*K in-plane CTE is a third of unfilled PC's[1]Not documented
Solvents & Solubility
Soluble inDichloromethane and chloroform dissolve the matrix and leave the fibre; DMF and dioxane do the same (Covestro).[24]DMF, DMSO, NMP and THF dissolve TPU; acetone, MEK and cyclohexanone are partial solvents. All laboratory reagents.[25]
Softened or crazed byMethanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[24]Toluene and benzene swell it up to +50 % by weight at 23 °C; esters swell it severely; ethanol and IPA soften it.[25]
Solvent welding & smoothing agentDichloromethane cement welds the resin, but the fibre keeps the joint from flowing closed. Controlled carcinogen.[26]None practical — the true solvents (DMF, THF, NMP) are laboratory reagents and leave the joint swollen and weak.[25]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. XSTRAND GF30-PC Data Sheet Owens Corning · 2019-04 · tds
  2. FiberFlex 30D Technical Data Sheet Fiberlogy · 2026-08 · tds
  3. BASF Ultrafuse PC GF30 Black 2.85 mm 1.000 g igo3d · 2026-08 · vendor
  4. Recreus product catalogue Recreus · 2026-08 · vendor
  5. Chinchilla product page — print guidelines, spool sizes and price NinjaTek · 2026-08 · vendor
  6. NinjaFlex Edge product page — durometer, print guidelines and price NinjaTek · 2026-08 · vendor
  7. Polymaker product catalogue Polymaker · 2026-08 · vendor
  8. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  9. Filaflex 82A product page (Shore hardness and elongation) Recreus · 2026-08 · vendor
  10. NinjaFlex 85A Technical Specifications NinjaTek · 2026-08 · tds
  11. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  12. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  13. Flexible (TPE/TPU) — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  14. TPU — material basics Polymaker Wiki · 2026-08 · doc
  15. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  16. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  17. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  19. PC — material basics Polymaker Wiki · 2026-08 · doc
  20. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  21. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  22. BambuLab TPU 95A HF vs Qidi TPU 95A HF — results spreadsheet My Tech Fun (Igor Gaspar) · 2024-02 · test
  23. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  24. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  25. Elastollan — Chemical properties: swelling and chemical resistance BASF · 2026-08 · tds
  26. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds