3D Printing Info

Filament comparison

PC-GF vs PEKK

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PC (PC-GF) guidePEKK guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC-GF comparisonsMore PEKK comparisons
PC-GF vs PEKK — documented properties and sources
PropertyGlass-fibre PC (PC-GF)PCPEKKHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$71.27/kg median; $71.27–$71.27/kg across 1 dated product listings$525.00/kg median; $332.50–$771.12/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryPolycarbonate reinforced with 30 wt% short glass fibre[1]Polyether ketone ketone, amorphous grade — a polyaryletherketone that stays amorphous, so it does not need PEEK's crystallisation control. Stratasys sells it as Antero 800NA and Antero 840CN03; category numbers below are unfilled unless a carbon grade is named[2][3]
Densityg/cm³1.17 (measured on a 100 % infill printed part, ISO 1183-A)[1]1.28 unfilled (ASTM D792, Antero 800NA; 1.31 annealed) and 1.33 for CarbonX PEKK-A CF15 (ISO 1183)[3][2]
Typical priceUSD/kg1 kg spools cluster near 71[4]1 kg-equivalent spools cluster near 550[5][6][7]
Price range across brandsUSD/kg71 — BASF Ultrafuse PC GF30 at igo3d is the only priced listing found; Owens Corning sells XSTRAND GF30-PC in 500 g and 1 kg[4][1]333-771 across grades and formats; 3DXTech CarbonX PEKK-A+CF15 333 at 2 kg, 3D4Makers unfilled PEKK-A 485 at 2 kg, IEMAI 3D 500 at 1 kg, Kimya PEKK Carbon 771 at 500 g[5][6][7][8][9]
Market availability1–5Niche, a handful of specialist brands — neither Polymaker's nor 3DXTech's polycarbonate range contains a glass-fibre grade, but BASF Forward AM and Owens Corning both sell one through European retail[4][1][10][5]Niche, a handful of specialist brands[5][6][7]
Spool sizes & diameters1.75 and 2.85 mm at +/- 0.05 mm; 500 g and 1 kg net spools[1]1.75 and 2.85 mm; 200 g to 2 kg spools, plus Stratasys canisters[5][6][3]
Typical applicationsFunctional prototyping for mechanical engineering, electronics and automotive[1]Aerospace interior and structural parts; 3DXTech labels its carbon-filled PEKK-A grade AERO and Stratasys certifies Antero 800NA for outgassing and FST[2][3]
Diameter tolerance± mm+/- 0.05 (Owens Corning XSTRAND)[1]Not documented
Printing Parameters
Nozzle temperature°C280-330 (Owens Corning XSTRAND GF30-PC)[1]Not documented
Bed temperature°C80-110 (Owens Corning XSTRAND GF30-PC)[1]140 (3DXTech CarbonX PEKK-A CF15)[2]
Enclosure / chamber requirement1–5Enclosure required (passive) — as for unfilled PC[11][12]Actively heated chamber required[13][14]
Bed surface & adhesion aidPerforated plate, DimaFix or Magigoo PC glue (Owens Corning)[1]Not documented
Overall printing difficulty1–5Not documentedExpert / industrial hardware only[13][14]
Extruder requirementOwens Corning specifies a nozzle above 0.4 mm and hardened steel nozzles and drive wheels[1]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Owens Corning states glass reinforcement shortens brass nozzle and drive-wheel life[1]Hardened steel required — the category spans unfilled PEKK, where brass is acceptable, and the carbon-filled aerospace grades that make up most of the market[2][3]
Abrasiveness1–5Highly abrasive — 30 wt% glass fibre[1]Highly abrasive — most PEKK filament sold is carbon-filled; unfilled Antero 800NA and ThermaX PEKK-A are non-abrasive[2][3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles; PC already absorbs water from the air and Prusa lists glass-filled composites as a higher clogging risk[15][16]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[17]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Negligible (<0.1 % EMC) — Owens Corning measures below 0.1 % at 23 °C and 50 % RH (ISO 62)[1]Not documented
Equilibrium moisture content at ~50 % RH%Below 0.1 at 23 °C and 50 % RH, and below 0.1 at saturation (ISO 62)[1]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[18][19]No dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[17]
Mechanical Properties
Tensile strength (XY)MPa65 at break (printed, ISO 527 at 1 mm/min)[1]86.7-90.0 at yield and 73.0 at break (printed XZ, ASTM D638, Antero 800NA on the F900 and Fortus 450mc); 88.8 at break annealed; 126 at break for CarbonX PEKK-A CF15 (printed XY, ISO 527)[3][2]
Young's modulusMPa5400 (printed, ISO 527 at 1 mm/min)[1]2640-3870 (printed XZ, ASTM D638, Antero 800NA; upper figure annealed); 9125 for CarbonX PEKK-A CF15 (printed XY, ISO 527)[3][2]
Elongation at break%2.5 at break (printed, ISO 527 at 1 mm/min)[1]6.1 at break (printed XZ, ASTM D638, Antero 800NA); 2.3 in ZX; 3.15 for CarbonX PEKK-A CF15 (ISO 527)[3][2]
Flexural strengthMPa113 at yield (printed, ISO 178 at 2 mm/min)[1]136 at 5 % strain (printed XZ, ASTM D790, Antero 800NA); 178 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[3][2]
Flexural modulusMPa5500 (printed, ISO 178 at 2 mm/min)[1]3200 (printed XZ, ASTM D790, Antero 800NA); 8817 for CarbonX PEKK-A CF15 (printed XY, ISO 178)[3][2]
Other impact dataNot documentedIzod notched 41.1 J/m XZ and 33.3 J/m ZX; unnotched 1730 J/m XZ against 203 J/m ZX (printed, ASTM D256/D4812, Antero 800NA)[3]
Layer adhesion / Z tensileMPaNot documented50.1-59.4 at yield (printed ZX, ASTM D638, Antero 800NA); 56.0 for the ESD grade Antero 840CN03[3][20]
Brittleness1–5Brittle — snaps with little warning; 2.5 % elongation at break[1]Moderate unfilled — 6.1 % elongation at break in plane; brittle in the carbon-filled grades at 3.15 %[3][2]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for a glass-fibre grade[21]Not documented
Creep resistance / sustained load1–5Excellent — holds load for years. Room-temperature tensile creep of moulded unfilled PC ran unbroken at 41 MPa until the test was stopped, and 30 wt% glass raises the tensile modulus from about 2.3 to 5.4 GPa[22][1]Excellent — holds load for years. Antero 800NA still holds 82 % of its room-temperature ZX tensile strength at 104 °C and 63 % at 132 °C (printed, ASTM D638)[3]
Elasticity / flexibility1–5Rigid[1]Rigid[2]
Z strength as % of XY%Not documented56-82 (Antero 800NA and 840CN03 printed on the F900 and Fortus 450mc, ZX against XZ tensile yield and break, ASTM D638)[3][20]
Thermal Properties
HDT at 0.45 MPa°CNot documented158 (printed XY and ZX, ASTM D648 Method B at 66 psi, Antero 800NA); 285 for CarbonX PEKK-A CF15 (ISO 75 at 0.45 MPa)[3][2]
HDT at 1.8 MPa°C137 (printed, ISO 75 Method A at 1.8 MPa)[1]156-157 (printed, ASTM D648 Method B at 264 psi, Antero 800NA); moulded 147[3]
Glass transition (Tg)°C145 (DSC, ISO 11357)[1]156 (ASTM D7426, Antero 800NA); 165 for CarbonX PEKK-A CF15 (DSC)[3][2]
Melting point / Vicat°C270 stated as melting point (ISO 11357) — unusual for an amorphous polymer, but this is the published figure[1]300 melt point (ASTM D7426 peak heat, Antero 800NA); 305 for CarbonX PEKK-A CF15 (DSC)[3][2]
Thermal expansion (CTE)µm/m·K26.2 in XY and 77.4 in Z (printed, ISO 11359-2) — a threefold anisotropy, and the lowest in-plane expansion of any polycarbonate here[1]36.1 in XY and 50.2 in ZX (printed, 40-140 °C, ASTM E831, Antero 800NA); 47.4 and 51.2 for the ESD grade Antero 840CN03[3][20]
Flammability / UL 94UL 94 V-0 verified (Owens Corning)[1]Not documented
Environment & Chemical
UV resistance1–5Good — years with some colour shift. Owens Corning lists UV resistance as a product benefit but publishes no exposure data[1]Good — years with some colour shift. 1000 h of QUV cycling to ASTM G154 left Antero 800NA's yield strength unchanged at 57 MPa and raised stress at break 3.6 %[3]
Water / humidity resistance in service1–5Excellent — essentially unaffected; below 0.1 % water at saturation (ISO 62)[1]Not documented
Electrical & ESD propertiesElectrically insulating (Owens Corning)[1]Unfilled PEKK is an insulator at above 1.4e14 ohm-cm (ASTM D257); CarbonX PEKK-A CF15 sits above 10^7 ohm/sq, and the Antero 840CN03 ESD grade is specified at 10^4-10^9 ohm-cm[3][2][20]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[23]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[23]
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[23]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[23][12]Ventilated room or enclosure recommended[23]
Dust & fibre handling hazardOwens Corning warns that the glass reinforcement is abrasive when melted and advises sufficient ventilation and avoiding extrusion fumes[1]Carbon fibre is bound in the matrix; sanding dust should not be inhaled[2]
Post-Processing
Dimensional accuracy & detailHigh dimensional stability is the headline benefit; the 26.2 um/m*K in-plane CTE is a third of unfilled PC's[1]Not documented
Solvents & Solubility
Soluble inDichloromethane and chloroform dissolve the matrix and leave the fibre; DMF and dioxane do the same (Covestro).[24]Concentrated sulphuric acid, as for PEEK; no common organic solvent touches a polyaryletherketone.[25][26]
Softened or crazed byMethanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[24]Concentrated sulphuric acid and liquid Freon are the entries Ensinger marks not resistant; acetone, MEK and toluene do nothing.[25]
Solvent welding & smoothing agentDichloromethane cement welds the resin, but the fibre keeps the joint from flowing closed. Controlled carcinogen.[27]None — no solvent softens a polyaryletherketone.[25]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. XSTRAND GF30-PC Data Sheet Owens Corning · 2019-04 · tds
  2. CarbonX Carbon Fiber PEKK-A CF15 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  3. Antero 800NA — FDM Material Data Sheet (PEKK-based) Stratasys · 2025-08 · tds
  4. BASF Ultrafuse PC GF30 Black 2.85 mm 1.000 g igo3d · 2026-08 · vendor
  5. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  6. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  7. Kimya PEKK-A Natural 1.75 mm 500 g igo3d · 2026-08 · vendor
  8. Kimya PEKK Carbon Grey 1.75 mm 500 g igo3d · 2026-08 · vendor
  9. IEMAI 3D PEKK 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  10. Polymaker product catalogue Polymaker · 2026-08 · vendor
  11. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  12. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  13. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  14. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  15. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  16. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. THERMAX PEKK-A — product page (print recommendations) 3DXTech · 2026-08 · doc
  18. PC — material basics Polymaker Wiki · 2026-08 · doc
  19. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  20. Antero 840CN03 — FDM Material Data Sheet (PEKK, ESD) Stratasys · 2024-08 · tds
  21. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  22. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  23. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  24. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  25. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  26. The Effects of Sulfonated Poly(ether ether ketone) Ion Exchange Preparation Conditions on Membrane Properties Yee, Zhang & Ladewig, Membranes 3(3) 182–195 · 2013-07 · paper
  27. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds