PC-FR vs TPU 85A

Compare printing settings, strength, heat resistance, dated prices and sources.

Flame-retardant PC (PC-FR) guideTPU 85A guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC-FR comparisonsMore TPU 85A comparisons
PC-FR vs TPU 85A — documented properties and sources
PropertyFlame-retardant PC (PC-FR)PCTPU 85AFLEX
Market snapshot
Listing priceUSD/kg; dated snapshots$87.50/kg median; $54.99–$224.00/kg across 4 dated product listings$89.89/kg median; $31.99–$106.05/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryFlame-retardant polycarbonate. Polymaker builds its grade on Covestro's Makrolon family and rates it UL 94 V-0[1][2]Soft thermoplastic polyurethane at 82–85 Shore A[3][4][5]
Densityg/cm³1.18 (Bambu Lab) and 1.2 (Polymaker), ISO 1183[2][1]1.11 (BASF Ultrafuse 85A) to 1.19 (NinjaFlex 85A), ISO 1183 / ASTM D792[5][3]
Typical priceUSD/kg1 kg-equivalent spools span 55–224; the two mainstream 1 kg grades are 55 and the industrial grades 120–224[2][6]1 kg-equivalent spools span 32–106; the middle of the market is about 90[7][8][3]
Price range across brandsUSD/kg55–224 across brands; Bambu Lab and Polymaker 55, 3DXTech FR PC/ABS 120, 3DXLABS FR-PC 224[2][6][7]32–106 across brands; Siraya Tech Flex TPU 85A 32 at 1 kg, add:north TPU Pro Matte 85A 72, Recreus Filaflex 82A 90 at 500 g, Proto-pasta Clear Flexible TPU 90, 3DXTech 3DXFLEX 85A 96, NinjaTek NinjaFlex 106[9][7][8][10][3]
Market availability1–5Available from several mainstream brands[2][6][7]Available from several mainstream brands[7][9]
Spool sizes & diameters1.75 mm; 0.75 and 1 kg spools[6][7][2]1.75, 2.85 and 3 mm; 0.5, 1 and 2 kg spools[7][9][3]
Typical applicationsElectrical enclosures, transport interiors and battery housings that must meet a flammability rating[1][2]Soft-touch grips, seals, wearables and anything that must compress and rebound[3][4]
Diameter tolerance± mm±0.03 (Bambu Lab PC FR)[2]Not documented
Printing Parameters
Nozzle temperature°C260–280 (Bambu Lab); 250–270 (Polymaker)[2][1]200–220 (BASF Ultrafuse 85A, 210 typical)[5]
Bed temperature°C90–110 (Bambu Lab); 90–105 (Polymaker)[2][1]40 (BASF Ultrafuse 85A)[5]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber, Polymaker 70–100 °C[2][1]Open frame is fine[5]
Recommended chamber temperature°C45–60 (Bambu Lab); 70–100 (Polymaker)[2][1]Not documented
Part cooling fan0–60 % (Bambu Lab)[2]Not documented
Bed surface & adhesion aidSmooth or textured PEI plate (Bambu Lab)[2]PEI sheet or painter's tape; Polymaker warns TPU can over-stick and advises a glue stick as a release agent[11][12]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s24 at Bambu Lab's 300 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][13]1.2–3.2 at the 15–40 mm/s BASF specifies on a 0.4 mm nozzle at 0.2 mm layer[5]
Warping tendency1–5Severe — heated chamber needed[1][14]None[5]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[15][16]Sticks to anything — Recreus states its 82A grade has excellent bed adhesion without a heated bed or additives[4]
Stringing / oozing tendency1–5Moderate — retraction tuning needed; Polymaker flags stringing as a common PC problem[16]High — drying plus tuning needed[17][12]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[2][14]Advanced — enclosure, hardware upgrades, tuning; at this hardness the filament will not push through a Bowden tube[3][4]
Extruder requirementNot documentedDirect drive only. NinjaTek calls its 85A grade ideal for direct-drive extruders and Recreus specifies direct-drive printers for 82A; BASF caps print speed at 15–40 mm/s with a nozzle of 0.4 mm or larger[3][4][5]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[14]Brass fine indefinitely[18]
Abrasiveness1–5Non-abrasive[1]Non-abrasive[18]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a 6 h pre-dry at 80 °C[19]High — jams from moisture, heat creep or particles[17][12]
Heat-creep / jam sensitivity1–5Slightly sensitive[15]Very high — softens in the cold zone readily; soft filament buckles between the drive gear and the melt zone[12][3]
Hotend requirementAll-metal hot end required (Simplify3D)[15]No special hot-end required, but a direct-drive extruder is (Simplify3D)[11]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low (0.1–0.3 %) — 0.12 % saturated at 25 °C / 55 % RH (Bambu Lab), half that of unfilled Bambu Lab PC[2][20]Moderate — NinjaTek measures 0.22 % in 24 h (ASTM D570) and BASF specifies a 70 °C dry for at least 5 h[3][5]
Equilibrium moisture content at ~50 % RH%0.12 saturated at 25 °C / 55 % RH (Bambu Lab)[2]0.22 after 24 h water immersion (NinjaFlex 85A, ASTM D570) — an immersion figure, not an equilibrium moisture content at 50 % RH[3]
Drying temperature & time75 °C for 6 h (Polymaker)[1]70 °C for at least 5 h in a hot-air dryer or vacuum oven (BASF)[5]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[17]Bubbling and popping at the nozzle, stringing and a rough surface[17]
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[16][17]Polymaker groups TPU with the highly hygroscopic materials; wet TPU prints with poor layer adhesion and weak, brittle layers[17]
Storage requirementAirtight containers with desiccant to prevent reabsorption[16]Sealed with desiccant; often kept in a dryer during the print[17]
Mechanical Properties
Tensile strength (XY)MPa60 ± 4 (Bambu Lab) and 67 ± 4.5 (Polymaker) printed XY, ISO 527[2][1]26 ultimate (NinjaFlex 85A, ASTM D638)[3]
Young's modulusMPa1670 ± 40 (Bambu Lab) and 2634 ± 182 (Polymaker) printed XY, ISO 527[2][1]12 (NinjaFlex 85A, ASTM D638) — two orders of magnitude below any rigid filament; NinjaTek's 95A Cheetah reaches 26 by the same method[3][21]
Elongation at break%2.4 ± 0.3 (Bambu Lab) and 3.49 ± 0.7 (Polymaker) at break, printed XY, ISO 527 — the retardant roughly halves unfilled PC's elongation[2][1][22]650 at break (Filaflex 82A) and 660 (NinjaFlex 85A); BASF measures 600 in XY and 320 in ZX[4][3][5]
Flexural strengthMPa96.6 ± 1.3 printed XY, ISO 178 (Polymaker)[1]Not documented
Flexural modulusMPa2518 ± 53 printed XY, ISO 178 (Polymaker)[1]Not documented
Charpy impact, notchedkJ/m²11.7 ± 1.6 printed XY, ISO 179, notched (Polymaker)[1]Not documented
Other impact dataNotched Charpy 7.5 ± 1.6 kJ/m² at −30 °C printed XY (Polymaker, ISO 179-1/1eA)[1]Not documented
Layer adhesion / Z tensileMPa21 ± 3 (Bambu Lab) and 46 ± 4.8 (Polymaker) printed Z, ISO 527[2][1]Not documented
Brittleness1–5Moderate[2][1]Very ductile — bends far before failing[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for a flame-retardant filament[23]29 Shore D / 85 Shore A (BASF Ultrafuse 85A, ISO 7619-1); 85 Shore A (NinjaFlex, ASTM D2240); 82 A nominal for Filaflex[3][5][4]
Creep resistance / sustained load1–5Good. Moulded unfilled PC sustained 41 MPa tensile creep at room temperature without breaking, but the retardant package drops the glass transition to 115 °C in Polymaker's grade, so the unfilled rating is not carried over in full[24][1]Poor — no 85A creep test; a printed 95A TPU bar crept from 74.5 to 82.7 mm over 5 days at 1.25 kg, and softer grades creep more[25]
Fatigue / repeated-flex resistance1–5Not documentedExcellent — living hinges viable[12]
Elasticity / flexibility1–5Rigid[1]Rubbery / highly elastic[3][4]
Z strength as % of XY%35 (Bambu Lab) to 69 (Polymaker), printed[2][1]53 — BASF measures 320 % elongation at break in ZX against 600 % in XY[5]
Wear resistance & frictionNot documentedAbrasion 0.08 g mass loss over 10 000 cycles (NinjaFlex, ASTM D4060); 82 mm³ (BASF, ISO 4649)[3][5]
Thermal Properties
HDT at 0.45 MPa°C110 (Polymaker) and 113 (Bambu Lab), ISO 75 at 0.45 MPa[1][2]Not documented
HDT at 1.8 MPa°C107 (Polymaker) and 108 (Bambu Lab), ISO 75 at 1.8 MPa[1][2]Not documented
Glass transition (Tg)°C115 (Polymaker) and 145 (Bambu Lab), DSC[1][2]Not documented
Melting point / Vicat°CAmorphous — no melting point; Vicat 114 (Bambu Lab, ISO 306)[2]216 melting (NinjaFlex 85A, DSC)[3]
Continuous service temperature°C113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[26]Not documented
Thermal expansion (CTE)µm/m·K68.4 on extruded unfilled PC stock (ASTM D696; source states 3.8e-5 in/in/°F); no figure is published for a flame-retardant grade[23]Not documented
Flammability / UL 94UL 94 V-0 (Polymaker PolyMax PC-FR); 3DXTech rates its FR PC/ABS V-0 at 1.5 mm on the base resin[1][27]Not documented
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors unless stabilised[16]Good — years with some colour shift; Polymaker lists UV exposure among the conditions TPU withstands[12]
Chemical resistanceWithstands oils, solvents and fuels; Polymaker rates it good against weak acids[16]Withstands industrial solvents and UV exposure (Polymaker)[12]
Food contactBisphenol-A polycarbonate is not offered as food-contact filament[16]Not food safe without specific certification (Polymaker)[12]
Biodegradability / compostabilityNot biodegradable[16]Not biodegradable[12]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[16]Not accepted in household plastic collection[12]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[28]Low hazard — minimal VOC and particle emission; TPU was not among the nine filaments in the chamber study[28]
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[28]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[28][14]Open a window / occasional ventilation[28]
Post-Processing
Sanding & machiningSands and machines well; the toughness means it cuts rather than chips[15]Difficult to sand or smooth; Polymaker limits post-processing to trimming or tumbling[12]
Gluing & solvent weldingCyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[15]Cyanoacrylate bonds TPU; no common solvent welds it[12]
Vapour / chemical smoothingNo practical vapour smoothing[15]No practical vapour smoothing[12]
Support material pairingPrints its own supports; 3DXTech sells a dedicated PC break-away support[15]Polymaker warns TPU supports are often very difficult to remove[12]
Solvents & Solubility
Soluble inDichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[29]DMF, DMSO, NMP and THF dissolve TPU; acetone, MEK and cyclohexanone are partial solvents. All laboratory reagents.[30]
Softened or crazed byMethanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[29]Toluene and benzene swell it up to +50 % by weight at 23 °C; esters swell it severely; ethanol and IPA soften it.[30]
Solvent welding & smoothing agentDichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[31]None practical — the true solvents (DMF, THF, NMP) are laboratory reagents and leave the joint swollen and weak.[30]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PolyMax PC-FR Technical Data Sheet V5.5 Polymaker · 2024-11 · tds
  2. Bambu Filament Technical Data Sheet V1.0 — PC FR Bambu Lab · 2026-08 · tds
  3. NinjaFlex 85A Technical Specifications NinjaTek · 2026-08 · tds
  4. Filaflex 82A product page (Shore hardness and elongation) Recreus · 2026-08 · vendor
  5. Ultrafuse TPU 85A Technical Data Sheet (Version 3.0) BASF Forward AM · 2022-08 · tds
  6. Polymaker product catalogue Polymaker · 2026-08 · vendor
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. Siraya Tech Flex TPU 85A Filament — product page Siraya Tech · 2026-08 · vendor
  9. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  10. add:north TPU Pro Matte 85A product page add:north · 2026-08 · vendor
  11. Flexible (TPE/TPU) — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  12. TPU — material basics Polymaker Wiki · 2026-08 · doc
  13. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  14. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  15. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  16. PC — material basics Polymaker Wiki · 2026-08 · doc
  17. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  18. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  19. 3DXTech Firewire FR-PC/ABS product page 3DXTech · 2026-08 · vendor
  20. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  21. NinjaTek technical specs comparison chart (Cheetah, NinjaFlex, Armadillo, Alloy 910, Nylon 645) NinjaTek · 2026-08 · tds
  22. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  23. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  24. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  25. BambuLab TPU 95A HF vs Qidi TPU 95A HF — results spreadsheet My Tech Fun (Igor Gaspar) · 2024-02 · test
  26. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  27. Firewire Flame Retardant PC/ABS Technical Data Sheet Rev 3.0 3DXTech · 2026-08 · tds
  28. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  29. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  30. Elastollan — Chemical properties: swelling and chemical resistance BASF · 2026-08 · tds
  31. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds