3D Printing Info

Filament comparison

PC-FR vs PP-GF

Compare printing settings, strength, heat resistance, dated prices and sources.

Flame-retardant PC (PC-FR) guideGlass-fibre PP (PP-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PC-FR comparisonsMore PP-GF comparisons
PC-FR vs PP-GF — documented properties and sources
PropertyFlame-retardant PC (PC-FR)PCGlass-fibre PP (PP-GF)POLYOLEFIN
Market snapshot
Listing priceUSD/kg; dated snapshots$87.50/kg median; $54.99–$224.00/kg across 4 dated product listings$49.09/kg median; $46.27–$86.01/kg across 3 dated product listings
Identity & Market
Base polymer / chemistryFlame-retardant polycarbonate. Polymaker builds its grade on Covestro's Makrolon family and rates it UL 94 V-0[1][2]Polypropylene reinforced with chopped glass fibre[3][4]
Densityg/cm³1.18 (Bambu Lab) and 1.2 (Polymaker), ISO 1183[2][1]1.12 (Prusament PP Glass Fiber, ISO 1183) — the glass lifts it above water[3]
Typical priceUSD/kg1 kg-equivalent spools span 55–224; the two mainstream 1 kg grades are 55 and the industrial grades 120–224[2][5]1 kg-equivalent spools cluster near 49[6][7][8]
Price range across brandsUSD/kg55–224 across brands; Bambu Lab and Polymaker 55, 3DXTech FR PC/ABS 120, 3DXLABS FR-PC 224[2][5][9]46-86 across brands; BCN3D PP GF30 46 at 700 g, BASF Ultrafuse PP GF30 49 at 2.2 kg, Prusament PP Glass Fiber 86 at 850 g[6][7][8]
Market availability1–5Available from several mainstream brands[2][5][9]Available from several mainstream brands[6][7][8]
Spool sizes & diameters1.75 mm; 0.75 and 1 kg spools[5][9][2]1.75 and 2.85 mm; 700 g, 850 g and 2.2 kg spools[6][7][8]
Typical applicationsElectrical enclosures, transport interiors and battery housings that must meet a flammability rating[1][2]Stiff, chemically resistant parts where PP-CF's cost or conductivity is unwanted[4]
Diameter tolerance± mm±0.03 (Bambu Lab PC FR)[2]±0.04 (Prusament)[3]
Printing Parameters
Nozzle temperature°C260–280 (Bambu Lab); 250–270 (Polymaker)[2][1]245 ± 10 (Prusament) — 25 °C below the carbon-fibre grade[3][10]
Bed temperature°C90–110 (Bambu Lab); 90–105 (Polymaker)[2][1]95 ± 10 (Prusament)[3]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber, Polymaker 70–100 °C[2][1]Enclosure recommended — Simplify3D lists an enclosure as a hardware requirement and Polymaker advises one below 70 °C ambient to stop warping and cracking[11][12]
Recommended chamber temperature°C45–60 (Bambu Lab); 70–100 (Polymaker)[2][1]Not documented
Part cooling fan0–60 % (Bambu Lab)[2]Off — Prusa runs 0 % except 100 % on bridges[3]
Bed surface & adhesion aidSmooth or textured PEI plate (Bambu Lab)[2]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s24 at Bambu Lab's 300 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][13]4 at Prusa's 50 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[3][13]
Warping tendency1–5Severe — heated chamber needed[1][14]High — enclosure needed for reliable large parts; Prusa recommends a brim[3]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[15][16]Very difficult — special plates or slurry required[3]
Stringing / oozing tendency1–5Moderate — retraction tuning needed; Polymaker flags stringing as a common PC problem[16]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[2][14]Advanced — enclosure, hardware upgrades, tuning; hardened nozzle mandatory[3]
Extruder requirementNot documentedPrusa states a hardened nozzle is necessary and recommends a brim[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[14]Hardened steel required[3]
Abrasiveness1–5Non-abrasive[1]Highly abrasive — standard GF composite[3]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a 6 h pre-dry at 80 °C[17]Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[18]
Heat-creep / jam sensitivity1–5Slightly sensitive[15]Not documented
Hotend requirementAll-metal hot end required (Simplify3D)[15]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low (0.1–0.3 %) — 0.12 % saturated at 25 °C / 55 % RH (Bambu Lab), half that of unfilled Bambu Lab PC[2][19]Low (0.1–0.3 %) — 0.11 % at both 24 h and 7 days, higher than the carbon-fibre grade's 0.04 % but still very low[3][10]
Equilibrium moisture content at ~50 % RH%0.12 saturated at 25 °C / 55 % RH (Bambu Lab)[2]0.11 after 24 h and 0.11 after 7 days at 24 °C / 22 % RH (Prusa Polymers)[3]
Drying temperature & time75 °C for 6 h (Polymaker)[1]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[20]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[16][20]Not applicable in practice at 0.11 % equilibrium uptake[3]
Storage requirementAirtight containers with desiccant to prevent reabsorption[16]No special storage needed[3]
Mechanical Properties
Tensile strength (XY)MPa60 ± 4 (Bambu Lab) and 67 ± 4.5 (Polymaker) printed XY, ISO 527[2][1]46.6 ± 1.3 filament tensile yield (Prusament, ISO 527) — more than double the carbon-fibre grade's 21[3][10]
Young's modulusMPa1670 ± 40 (Bambu Lab) and 2634 ± 182 (Polymaker) printed XY, ISO 527[2][1]Not documented
Elongation at break%2.4 ± 0.3 (Bambu Lab) and 3.49 ± 0.7 (Polymaker) at break, printed XY, ISO 527 — the retardant roughly halves unfilled PC's elongation[2][1][21]Not documented
Flexural strengthMPa96.6 ± 1.3 printed XY, ISO 178 (Polymaker)[1]Not documented
Flexural modulusMPa2518 ± 53 printed XY, ISO 178 (Polymaker)[1]Not documented
Charpy impact, notchedkJ/m²11.7 ± 1.6 printed XY, ISO 179, notched (Polymaker)[1]7.9 ± 0.4 printed horizontal and 9.9 ± 0.8 printed vertical XZ (ISO 179-1, notched)[3]
Other impact dataNotched Charpy 7.5 ± 1.6 kJ/m² at −30 °C printed XY (Polymaker, ISO 179-1/1eA)[1]Not documented
Layer adhesion / Z tensileMPa21 ± 3 (Bambu Lab) and 46 ± 4.8 (Polymaker) printed Z, ISO 527[2][1]Not documented
Brittleness1–5Moderate[2][1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for a flame-retardant filament[22]Rockwell R102 (and M95) on extruded unfilled PP stock (ASTM D785); no figure is published for a glass-fibre PP filament[23]
Creep resistance / sustained load1–5Good. Moulded unfilled PC sustained 41 MPa tensile creep at room temperature without breaking, but the retardant package drops the glass transition to 115 °C in Polymaker's grade, so the unfilled rating is not carried over in full[24][1]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%35 (Bambu Lab) to 69 (Polymaker), printed[2][1]Not documented
Thermal Properties
HDT at 0.45 MPa°C110 (Polymaker) and 113 (Bambu Lab), ISO 75 at 0.45 MPa[1][2]138.3 (ISO 75, 0.45 MPa)[3]
HDT at 1.8 MPa°C107 (Polymaker) and 108 (Bambu Lab), ISO 75 at 1.8 MPa[1][2]112.6 (ISO 75, 1.8 MPa)[3]
Glass transition (Tg)°C115 (Polymaker) and 145 (Bambu Lab), DSC[1][2]Not documented
Melting point / Vicat°CAmorphous — no melting point; Vicat 114 (Bambu Lab, ISO 306)[2]Not documented
Continuous service temperature°C113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[25]Not documented
Thermal expansion (CTE)µm/m·K68.4 on extruded unfilled PC stock (ASTM D696; source states 3.8e-5 in/in/°F); no figure is published for a flame-retardant grade[22]Not documented
Flammability / UL 94UL 94 V-0 (Polymaker PolyMax PC-FR); 3DXTech rates its FR PC/ABS V-0 at 1.5 mm on the base resin[1][26]Not documented
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors unless stabilised[16]Not documented
Chemical resistanceWithstands oils, solvents and fuels; Polymaker rates it good against weak acids[16]Excellent against acids, alkalis and most solvents[12]
Water / humidity resistance in service1–5Not documentedExcellent — essentially unaffected[3]
Food contactBisphenol-A polycarbonate is not offered as food-contact filament[16]Not documented
Biodegradability / compostabilityNot biodegradable[16]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[16]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[27]Low hazard — minimal VOC and particle emission. Inferred: no polyolefin was among the nine filaments in the Azimi chamber study, so this is a family-level judgement rather than a measurement[27]
Ultrafine-particle emission rateparticles/min≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[27]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[27][14]Open a window / occasional ventilation. Inferred — no polyolefin was measured in the chamber study[27]
Dust & fibre handling hazardNot documentedGlass fibre is bound in the matrix; avoid inhaling sanding dust[3]
Post-Processing
Sanding & machiningSands and machines well; the toughness means it cuts rather than chips[15]Not documented
Gluing & solvent weldingCyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[15]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[15]Not documented
Support material pairingPrints its own supports; 3DXTech sells a dedicated PC break-away support[15]Not documented
Solvents & Solubility
Soluble inDichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[28]None at room temperature; chloroform dissolves the matrix at 60 °C and xylene at about 118 °C, leaving the fibre.[29][30]
Softened or crazed byMethanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[28]Xylene, decalin, CCl4 and chlorobenzene are heavily absorbed at 20 °C; oleum, chlorosulphonic acid and bromine destroy it.[29]
Solvent welding & smoothing agentDichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[31]None — nothing softens PP at room temperature, so joints have to be welded thermally rather than chemically.[29]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PolyMax PC-FR Technical Data Sheet V5.5 Polymaker · 2024-11 · tds
  2. Bambu Filament Technical Data Sheet V1.0 — PC FR Bambu Lab · 2026-08 · tds
  3. Prusament PP Glass Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  4. Prusament PP Glass Fiber — material page Prusa Polymers · 2026-08 · doc
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. BASF Ultrafuse PP GF30 Black 2.85 mm 2.200 g igo3d · 2026-08 · vendor
  7. BCN3D PP GF30 Black 2.85 mm 700 g igo3d · 2026-08 · vendor
  8. Prusa Prusament PP Glass Fiber Natural (NFC), 1.75 mm / 850 g 3DJAKE · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. Prusament PP Carbon Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  11. Polypropylene — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  12. PP — material basics Polymaker Wiki · 2026-08 · doc
  13. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  14. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  15. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  16. PC — material basics Polymaker Wiki · 2026-08 · doc
  17. 3DXTech Firewire FR-PC/ABS product page 3DXTech · 2026-08 · vendor
  18. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  19. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  20. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  21. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  22. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  23. TECAFINE PP natural — stock shape properties Ensinger · 2026-08 · tds
  24. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  25. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  26. Firewire Flame Retardant PC/ABS Technical Data Sheet Rev 3.0 3DXTech · 2026-08 · tds
  27. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  28. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  29. Pro-fax and Moplen polypropylene — Chemical Resistance Guide (20, 60 and 100 °C) LyondellBasell · 2026-08 · tds
  30. US 5,278,282 Polymer recycling by selective dissolution — xylene dissolution temperatures Nauman & Lynch, Rensselaer Polytechnic Institute · 1994-01 · paper
  31. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds