PAHT-CF vs PETG-ESD — documented properties and sources
PropertyHigh-temperature CF nylon (PAHT-CF)PAESD-safe PETGPETG
Market snapshot
Listing priceUSD/kg; dated snapshots$59.98/kg median; $49.99–$69.98/kg across 2 dated product listings$102.99/kg median; $65.98–$140.00/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryHigh-temperature carbon-fibre nylon. Bambu Lab's PAHT-CF and Polymaker's PA612-CF15 both use a long-chain polyamide matrix for lower moisture uptake than PA6[1][2]PETG compounded with a conductive filler to bring surface resistivity into the static-dissipative range[3][4]
Densityg/cm³1.03 (Polymaker PA612-CF15) and 1.06 (Bambu Lab), ISO 1183[1][2]1.24 (Fiberon) and 1.28 (3DXTech), ISO 1183[3][4]
Typical priceUSD/kg1 kg-equivalent spools cluster near 60[1][5]1 kg-equivalent spools span 66–140; the middle of the market is about 103[5][6]
Price range across brandsUSD/kg50–70 across brands; Bambu Lab 50, Polymaker Fiberon PA612-CF15 70[1][5]66–140 across brands; Fiberon PETG-ESD 66, 3DXSTAT ESD-PETG 140[5][6]
Market availability1–5Available from several mainstream brands[1][5]Niche, a handful of specialist brands[5][6]
Spool sizes & diameters1.75 mm; 0.5 and 1 kg spools[5][1]1.75 mm; 0.5, 0.75, 1 and 3 kg spools[5][6]
Typical applicationsUnder-bonnet and near-motor parts needing 170 °C-plus heat deflection with less humidity drift than PA6[1][2]Electronics fixtures, trays and jigs handled around static-sensitive components[3][4]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[1]250–290 (Fiberon)[3]
Bed temperature°CNot documented70–80 (Fiberon); 70 (3DXTech)[3][4]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[1]Open frame is fine — Fiberon specifies room-temperature chamber[3]
Recommended chamber temperature°C45–60 (Bambu Lab)[1]Not documented
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[7][8]Textured PEI, satin or powder-coated sheets; on smooth PEI a glue stick acts as a release agent[9][10]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][11]Fiberon rates the material to 500 mm/s, equivalent to 40 on a 0.4 mm nozzle at 0.2 mm layer — a machine-limited headline rather than a measured melt rate[3][11]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[7]Needs the right surface or a thin adhesive — the problem is releasing the part, not sticking it[9][10]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[8]Moderate — retraction tuning needed; Polymaker names stringing as PETG's common quirk[10]
Overall printing difficulty1–5Expert / industrial hardware only[1][12]Intermediate — dry filament and a tuned profile; resistivity depends on getting the nozzle temperature right[3]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[1]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-CF15 and recommends hardened steel or ruby[2]Hardened steel required[3]
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-CF15[2]Moderately abrasive — conductive carbon filler[3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[12]Low — 3DXTech lists no special nozzle concerns and no minimum layer height for its ESD-PETG, only a 65 °C pre-dry[13]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[7]Slightly sensitive[14]
Hotend requirementMay require an all-metal hot end (Simplify3D)[7]No special hot-end required[14]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — 0.88 % saturated at 25 °C / 55 % RH for Bambu Lab PAHT-CF, a third of its PA6-CF; Polymaker's PA612-CF15 reaches 2.2 % equilibrium[1][2][15]Moderate (0.3–0.8 %) — the PETG matrix reaches 0.40 % saturated at 25 °C / 55 % RH and 3DXTech specifies a 65 °C, 4 h pre-dry[9][13]
Equilibrium moisture content at ~50 % RH%0.88 saturated at 25 °C / 55 % RH (Bambu Lab PAHT-CF); 2.2 equilibrium (Polymaker PA612-CF15)[1][2]0.41 equilibrium water absorption (Fiberon PETG-ESD)[3]
Drying temperature & time80 °C for 8–12 h (Bambu Lab)[1]65 °C for 3 h (Fiberon)[3]
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing and a rough surface[12]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA612-CF15 itself: at 2.57 % moisture tensile falls only 91.9 → 83.1 MPa and modulus 5137 → 3991 MPa — the PA612 backbone absorbs far less than PA6[2][16]Polymaker groups PETG with nylon, PVA and TPU as highly hygroscopic; no dry-versus-conditioned strength figures are published for this grade and the loss shows as bubbling and poor layer adhesion[12]
Storage requirementSealed below 20 % RH with desiccant[12]Sealed with desiccant; Polymaker groups PETG with the highly hygroscopic materials[12][10]
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[17][18]Not documented
Mechanical Properties
Tensile strength (XY)MPa92 ± 7 (Bambu Lab) and 91.9 ± 2.0 (Polymaker PA612-CF15, dry/annealed) printed XY, ISO 527; the Polymaker grade only falls to 83.1 ± 2.2 conditioned to 2.57 % moisture[1][2]36.1 ± 0.9 printed XY, ISO 527 (Fiberon); 3DXTech quotes 50 at break[3][4]
Young's modulusMPa3860 ± 230 (Bambu Lab) and 5137 ± 192 (Polymaker PA612-CF15, dry) printed XY, ISO 527; Polymaker 3991 ± 137 conditioned[1][2]1983 ± 75 printed XY, ISO 527 (Fiberon)[3]
Elongation at break%2.6 ± 0.2 dry (Polymaker PA612-CF15) to 8.4 ± 1.8 (Bambu Lab) printed XY, ISO 527; Polymaker 4.1 ± 0.3 conditioned[1][2]7.3 ± 0.7 printed XY, ISO 527 (Fiberon); 3DXTech quotes 13 at break[3][4]
Flexural strengthMPaNot documented54.0 ± 2.5 printed XY, ISO 178 (Fiberon)[3]
Flexural modulusMPa4230 ± 210 printed XY, ISO 178 (Bambu Lab)[1]1651 ± 141 printed XY, ISO 178 (Fiberon)[3]
Charpy impact, notchedkJ/m²8.1 ± 0.8 printed XY dry and 7.7 ± 0.5 conditioned, ISO 179 notched (Polymaker PA612-CF15)[2]5.7 ± 0.5 printed XY, ISO 179, notched (Fiberon)[3]
Other impact dataCharpy unnotched 57.5 ± 3.4 and notched 22.8 ± 1.8 printed XY (Bambu Lab, ISO 179)[1]Charpy unnotched 29.3 ± 2.2 printed XY (Fiberon, ISO 179)[3]
Layer adhesion / Z tensileMPa47 ± 5 (Bambu Lab) and 48.3 ± 3.9 (Polymaker PA612-CF15, dry) printed Z, ISO 527; Polymaker 35.6 ± 3.0 conditioned[1][2]20.7 ± 0.6 printed Z, ISO 527 (Fiberon)[3]
Brittleness1–5Moderate[1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre long-chain nylon filament[19]Not documented
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load with 110 °C continuous service; the long-chain PA612 matrix takes up 0.88 % at saturation, a third of the same maker's PA6-CF, so it holds dimension better[20][2]Below average — no ESD-grade creep test; unfilled PETG sagged from 12 to 17.1–20.4 mm over 5 days at 1.25 kg[21][22][23][24]
Fatigue / repeated-flex resistance1–5Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[20]Moderate — no ESD-grade S-N curve; unfilled printed PETG ran 79 000–193 000 cycles at 30 % of tensile strength[25]
Elasticity / flexibility1–5Rigid[1]Slightly flexible in thin sections[3]
Z strength as % of XY%51 (Bambu Lab) to 53 (Polymaker PA612-CF15), printed[1][2]57 (Fiberon, printed Z against XY tensile)[3]
Thermal Properties
HDT at 0.45 MPa°C175 (Polymaker PA612-CF15) and 194 (Bambu Lab), ISO 75 at 0.45 MPa[1][2]76 (ISO 75, 0.45 MPa, Fiberon)[3]
HDT at 1.8 MPa°C114 (Polymaker PA612-CF15) and 170 (Bambu Lab), ISO 75 at 1.8 MPa[1][2]72 (ISO 75, 1.8 MPa, Fiberon)[3]
Glass transition (Tg)°C70 (Bambu Lab, DSC)[1]77 (Fiberon) and 80 (3DXTech), DSC[3][4]
Melting point / Vicat°C210 (Polymaker PA612-CF15) and 225 (Bambu Lab) melting, DSC; Vicat 206 (Polymaker)[1][2]Amorphous — no melting point; Vicat 86 (Fiberon, ISO 306)[3]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[17]Flammable; no UL 94 rating published for standard grades[26]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[8]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[8]Withstands acids, alkalis, oils and UV exposure[10]
Water / humidity resistance in service1–5Absorbs water, properties shift — less than PA6 but more than PA12[16][1]Not documented
Food contactNot food-contact certified as filament[8]Not certified for food contact as filament[10]
Biodegradability / compostabilityNot biodegradable[8]Not biodegradable[10]
RecyclabilityNot accepted in household plastic collection[8]Not accepted in household plastic collection[10]
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker PA612-CF15, ANSI/ESD S11.11)[2]Surface resistivity falls with nozzle temperature: 7.0×10⁶–1.6×10⁷ ohm at 250 °C, 3.2×10⁵–4.7×10⁵ at 270 °C and below 1×10⁴ at 290 °C (Fiberon); 3DXTech quotes 10⁷–10⁹ ohm/sq[3][4]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[27]Moderate — measurable VOCs and UFPs, ventilation advised[27]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[27]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[27]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[27]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[27]Open a window / occasional ventilation[27]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[17]Conductive carbon filler is bound in the matrix; avoid inhaling sanding dust[3]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[7]Sands poorly — the material is tough and gums rather than powders[14]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[7]Cyanoacrylate; no common solvent welds PETG cleanly[14]
Vapour / chemical smoothingNo practical vapour smoothing[7]No practical vapour smoothing[14]
Support material pairingNot documentedPrints its own supports; Polymaker rates PolyDissolve S1 for PETG[14]
Dimensional accuracy & detailNot documentedNozzle temperature has to be held steady — it moves surface resistivity by three orders of magnitude[3]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[28]No common workshop solvent; 1,2-dichloroethane destroys it inside a week and dichloromethane — a carcinogen — dissolves the surface.[29][30]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[28]Acetone (+16 % weight over 1 year at 23 °C), ethyl acetate, toluene and DMF swell and soften it; methanol crazes it.[29]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[28]Dichloromethane brushed on is the only agent that smooths PETG — a controlled carcinogen, not workshop stock.[30]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet — PAHT-CF Bambu Lab · 2026-08 · tds
  2. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  3. Fiberon PETG-ESD Technical Data Sheet V1.1 Polymaker · 2026-08 · tds
  4. 3DXSTAT ESD-PETG Technical Data Sheet 3DXTech · 2026-08 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  8. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  9. Prusament PETG Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  10. PETG — material basics Polymaker Wiki · 2026-08 · doc
  11. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  12. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  13. 3DXSTAT ESD-PETG — product page (print recommendations) 3DXTech · 2026-08 · doc
  14. PET and PETG — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  15. Bambu Filament Technical Data Sheet — PA6-CF Bambu Lab · 2026-08 · tds
  16. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  17. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  18. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  19. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  20. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  21. PCTG vs PETG comparison — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  22. Extrudr PETG vs PCTG vs XPETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  23. Prusament PETG-CF vs PETG V0 vs PETG — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  24. BambuLab PETG Basic vs Translucent vs PETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  26. Prusament PETG V0 Technical Datasheet Prusa Polymers · 2026-08 · tds
  27. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  28. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  29. Eastman Spectar copolyester — Chemical resistance (unstressed bars, 1 year at 23 °C) Eastman Chemical Company · 2026-08 · tds
  30. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc