Compare printing settings, strength, heat resistance, dated prices and sources.

High-temperature CF nylon (PAHT-CF) guidePEEK guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PAHT-CF comparisonsMore PEEK comparisons
PAHT-CF vs PEEK — documented properties and sources
PropertyHigh-temperature CF nylon (PAHT-CF)PAPEEKHIGHTEMP
Market snapshot
Listing priceUSD/kg; dated snapshots$59.98/kg median; $49.99–$69.98/kg across 2 dated product listings$531.87/kg median; $296.14–$770.00/kg across 5 dated product listings
Identity & Market
Base polymer / chemistryHigh-temperature carbon-fibre nylon. Bambu Lab's PAHT-CF and Polymaker's PA612-CF15 both use a long-chain polyamide matrix for lower moisture uptake than PA6[1][2]Polyether ether ketone — a semi-crystalline polyaryletherketone[3]
Densityg/cm³1.03 (Polymaker PA612-CF15) and 1.06 (Bambu Lab), ISO 1183[1][2]1.30 (ISO 1183)[3][4]
Typical priceUSD/kg1 kg-equivalent spools cluster near 60[1][5]1 kg-equivalent spools span 296–770; the middle of the market is about 532[6][7][8]
Price range across brandsUSD/kg50–70 across brands; Bambu Lab 50, Polymaker Fiberon PA612-CF15 70[1][5]296-770 across brands and spool sizes; 3D4Makers recycled R-PEEK 296 at 750 g, IEMAI 3D 420 at 1 kg, LEHVOSS Luvocom 3F PEEK 9581 532 at 2 kg, 3DXTech ThermaX PEEK 770 at 500 g[6][7][8]
Market availability1–5Available from several mainstream brands[1][5]Niche, a handful of specialist brands[6][7][4]
Spool sizes & diameters1.75 mm; 0.5 and 1 kg spools[5][1]1.75 and 2.85 mm; 200 g to 2 kg spools[6][7][4]
Typical applicationsUnder-bonnet and near-motor parts needing 170 °C-plus heat deflection with less humidity drift than PA6[1][2]Aerospace brackets, semiconductor handling, sterilisable medical tooling and downhole parts[3]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[1]380-400 (3DXTech printed-specimen conditions); Victrex quotes a 340-450 melt range for AM 450 FIL[3][4]
Bed temperature°CNot documented130–140 (3DXTech)[3]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[1]Actively heated chamber required[9][10]
Recommended chamber temperature°C45–60 (Bambu Lab)[1]Not less than 150 for semi-crystalline printing (Victrex AM 450 FIL); bed above 150[4]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[11][12]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][13]Not documented
Warping tendency1–5Not documentedSevere — heated chamber needed[9]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[11]Very difficult — special plates or slurry required[9]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[12]Not documented
Overall printing difficulty1–5Expert / industrial hardware only[1][14]Expert / industrial hardware only[9][10]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[1]An all-metal hot end rated above 400 °C and a heated chamber; 3DXTech tests at 0.25 mm layer height on a 0.4 mm nozzle[3][9]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-CF15 and recommends hardened steel or ruby[2]Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[9]
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-CF15[2]Non-abrasive when unfilled[3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[14]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[15]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[11]Not documented
Hotend requirementMay require an all-metal hot end (Simplify3D)[11]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — 0.88 % saturated at 25 °C / 55 % RH for Bambu Lab PAHT-CF, a third of its PA6-CF; Polymaker's PA612-CF15 reaches 2.2 % equilibrium[1][2][16]Not documented
Equilibrium moisture content at ~50 % RH%0.88 saturated at 25 °C / 55 % RH (Bambu Lab PAHT-CF); 2.2 equilibrium (Polymaker PA612-CF15)[1][2]0.45 at saturation, 23 °C (ISO 62); 0.55 at 100 °C[4]
Drying temperature & time80 °C for 8–12 h (Bambu Lab)[1]120 °C for 5 h, target below 0.020 % moisture (Victrex AM 450 FIL)[4]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA612-CF15 itself: at 2.57 % moisture tensile falls only 91.9 → 83.1 MPa and modulus 5137 → 3991 MPa — the PA612 backbone absorbs far less than PA6[2][17]No dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[15]
Storage requirementSealed below 20 % RH with desiccant[14]Not documented
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[18][19]Not documented
Mechanical Properties
Tensile strength (XY)MPa92 ± 7 (Bambu Lab) and 91.9 ± 2.0 (Polymaker PA612-CF15, dry/annealed) printed XY, ISO 527; the Polymaker grade only falls to 83.1 ± 2.2 conditioned to 2.57 % moisture[1][2]60-100 (printed XY): Victrex AM 450 FIL 60-80 at yield and 3DXTech 100, both ISO 527; 98 at yield injection-moulded[3][4]
Young's modulusMPa3860 ± 230 (Bambu Lab) and 5137 ± 192 (Polymaker PA612-CF15, dry) printed XY, ISO 527; Polymaker 3991 ± 137 conditioned[1][2]3000-4000 (printed XY, ISO 527, Victrex AM 450 FIL); 3720 (3DXTech); 4000 injection-moulded[3][4]
Elongation at break%2.6 ± 0.2 dry (Polymaker PA612-CF15) to 8.4 ± 1.8 (Bambu Lab) printed XY, ISO 527; Polymaker 4.1 ± 0.3 conditioned[1][2]28 (printed XY, ISO 527) — remarkably ductile for a high-temperature polymer[3]
Flexural strengthMPaNot documented130 (printed XY, ISO 178)[3]
Flexural modulusMPa4230 ± 210 printed XY, ISO 178 (Bambu Lab)[1]2700 (printed XY, ISO 178)[3]
Charpy impact, notchedkJ/m²8.1 ± 0.8 printed XY dry and 7.7 ± 0.5 conditioned, ISO 179 notched (Polymaker PA612-CF15)[2]6.0 (injection-moulded, ISO 179/1eA); unnotched does not break[4]
Other impact dataCharpy unnotched 57.5 ± 3.4 and notched 22.8 ± 1.8 printed XY (Bambu Lab, ISO 179)[1]Izod notched 7.0 kJ/m2 injection-moulded (ISO 180/A). Printed anisotropy is extreme: VICTREX AM 200 on a Stratasys F900 gives Izod notched 1380-1530 J/m XZ against 30-62 J/m ZX (ASTM D256)[4][20]
Layer adhesion / Z tensileMPa47 ± 5 (Bambu Lab) and 48.3 ± 3.9 (Polymaker PA612-CF15, dry) printed Z, ISO 527; Polymaker 35.6 ± 3.0 conditioned[1][2]20-85 at yield (printed ZX, ISO 527, Victrex AM 450 FIL); the spread is set by chamber temperature and weld quality[4]
Brittleness1–5Moderate[1]Tough — absorbs impact, yields before breaking[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre long-chain nylon filament[21]Shore D 84.5 (injection-moulded, ISO 868); Rockwell M100 / R125 on extruded PEEK stock (ASTM D785)[4][22]
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load with 110 °C continuous service; the long-chain PA612 matrix takes up 0.88 % at saturation, a third of the same maker's PA6-CF, so it holds dimension better[23][2]Excellent — holds load for years. Victrex rates PEEK for long-term creep; injection-moulded flexural stress at 3.5 % strain falls only from 125 MPa at 23 °C to 85 MPa at 125 °C, and extruded stock is rated to 249 °C continuous[24][4][22]
Fatigue / repeated-flex resistance1–5Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[23]Excellent — living hinges viable. Victrex rates PEEK for long-term fatigue as well as creep[24]
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%51 (Bambu Lab) to 53 (Polymaker PA612-CF15), printed[1][2]71-84 (VICTREX AM 200 LMPAEK printed on the Stratasys F900 and Fortus 450mc, ZX against XZ tensile yield, ASTM D638); unfilled PEEK's own ZX spread is wider[20]
Thermal Properties
HDT at 0.45 MPa°C175 (Polymaker PA612-CF15) and 194 (Bambu Lab), ISO 75 at 0.45 MPa[1][2]140 (printed XY, ISO 75 at 0.45 MPa, 3DXTech)[3]
HDT at 1.8 MPa°C114 (Polymaker PA612-CF15) and 170 (Bambu Lab), ISO 75 at 1.8 MPa[1][2]152 (unannealed, ISO 75-2/Af, Victrex AM 450 FIL); 160 on extruded stock (ASTM D648 at 264 psi)[4][22]
Glass transition (Tg)°C70 (Bambu Lab, DSC)[1]143 (DSC, 3DXTech); Victrex gives onset 143 and midpoint 150 (ISO 11357-2)[3][4]
Melting point / Vicat°C210 (Polymaker PA612-CF15) and 225 (Bambu Lab) melting, DSC; Vicat 206 (Polymaker)[1][2]343 melting (ISO 11357-3, Victrex); VICTREX AM 200 LMPAEK melts at 303[4][20]
Continuous service temperature°CNot documented240 UL 746B relative thermal index, strength (RTI electrical 260, impact 180); Ensinger rates extruded PEEK stock at 249 long term[4][22]
Thermal expansion (CTE)µm/m·KNot documented37.8 (extruded PEEK stock, 23-60 °C, ASTM E831; source states 2.1e-5 in/in/°F), rising to 41.9 at 60-100 °C and 55.8 at 100-150 °C[22]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[18]UL 94 V-0 at 1.5 mm on the base resin; glow-wire flammability index 960 °C at 2.0 mm (IEC 60695-2-12)[3][4]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[12]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[12]Outstanding — resistant to almost all solvents and to steam sterilisation[3]
Water / humidity resistance in service1–5Absorbs water, properties shift — less than PA6 but more than PA12[17][1]Excellent — essentially unaffected; 0.45 % water at saturation and resistant to steam sterilisation[4][3]
Food contactNot food-contact certified as filament[12]Not documented
Biodegradability / compostabilityNot biodegradable[12]Not documented
RecyclabilityNot accepted in household plastic collection[12]Not documented
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker PA612-CF15, ANSI/ESD S11.11)[2]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[25]Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[25]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[25]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[25]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[25]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[25]Ventilated room or enclosure recommended[25]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[18]Not documented
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[11]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[11]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[11]Not documented
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[26]95–98 wt% sulphuric acid dissolves it — 10 g per 100 mL at 40–70 °C gives a dark red solution. Laboratory route only.[27][28]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[26]Concentrated nitric, hydrofluoric, hydrobromic and hydriodic acids attack it; DCM, DMSO and THF swell thin-walled sections.[29][28]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[26]None — no solvent softens PEEK, so parts are joined thermally or mechanically, never chemically.[29][28]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet — PAHT-CF Bambu Lab · 2026-08 · tds
  2. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  3. ThermaX PEEK Technical Data Sheet v3 3DXTech · 2026-08 · tds
  4. VICTREX AM 450 FIL — datasheet Victrex · 2025-12 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  8. IEMAI 3D PEEK 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  9. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  10. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  11. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  12. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  13. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  14. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  15. ThermaX PEEK — product page 3DXTech · 2026-08 · vendor
  16. Bambu Filament Technical Data Sheet — PA6-CF Bambu Lab · 2026-08 · tds
  17. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  18. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  19. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  20. VICTREX AM 200 — FDM Material Data Sheet Stratasys · 2024-04 · tds
  21. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  22. TECAPEEK natural (PEEK) — stock shape properties Ensinger · 2026-08 · tds
  23. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  24. PEEK polymers — product overview Victrex · 2026-08 · doc
  25. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  26. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  27. The Effects of Sulfonated Poly(ether ether ketone) Ion Exchange Preparation Conditions on Membrane Properties Yee, Zhang & Ladewig, Membranes 3(3) 182–195 · 2013-07 · paper
  28. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  29. What solvents are not compatible with PEEK? — fluidics technical FAQ IDEX Health & Science · 2026-08 · doc