3D Printing Info

Filament comparison

PA6 vs PLA HS

Compare printing settings, strength, heat resistance, dated prices and sources.

PA6 (Nylon 6) guideHigh-Speed PLA guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA6 comparisonsMore PLA HS comparisons
PA6 vs PLA HS — documented properties and sources
PropertyPA6 (Nylon 6)PAHigh-Speed PLAPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$104.00/kg median; $38.99–$136.00/kg across 3 dated product listings$19.99/kg median; $11.49–$32.99/kg across 10 dated product listings
Identity & Market
Base polymer / chemistryPolyamide 6, ring-opened from caprolactam — the most hygroscopic of the common nylons[1][2]PLA with rheology and crystallisation tuned for high volumetric flow; melt index 15.4 g/10 min vs 7–11 for standard PLA[3][4]
Densityg/cm³1.06 (ISO 1183, 3DXTech iOn PA6 alloy)[5]1.23 (ISO 1183, at 21.5 °C)[3]
Typical priceUSD/kg1 kg-equivalent spools span 39–136; the middle of the market is about 104, though budget unfilled PA6 has now arrived at 39[6][7]Mainstream 1 kg spools cluster near 20[8][9][10]
Price range across brandsUSD/kg39–136 across brands; YXPOLYER 39, 3DXTech iOn Nylon 6 Alloy 104, WearX Nylon 6 136. Unfilled PA6 filament stays rare — most PA6 reaches the market glass- or carbon-filled[6][7]11–33 across brands; budget house brands 11–18, Prusament 33[11][12][13]
Market availability1–5Niche, a handful of specialist brands[6]Stocked by most mainstream brands[14][10][15]
Spool sizes & diameters1.75 and 2.85 mm; 500 g and 750 g spools[6]1.75 mm; 1 kg spools[8][10]
Typical applicationsWear parts, bushings and gears where PA6's toughness and abrasion resistance matter more than dimensional stability[1]Large or repetitive prints on printers that can sustain high flow[16][14]
Diameter tolerance± mmNot documented±0.03 (Bambu Lab PLA Basic, rated to 258 mm/s)[17]
Printing Parameters
Nozzle temperature°C220–260 (Polymaker); 225–265 (Simplify3D)[1][18]210–230 for high-speed work; 190–210 at classic speeds[3][14]
Bed temperature°C70–100 (Polymaker); 70–90 (Simplify3D)[1][18]30–60 (Polymaker); 35–45 (Bambu Lab)[3][19]
Enclosure / chamber requirement1–5Enclosure required (passive)[20][1]Open frame is fine[3]
Part cooling fanPart cooling fan not required (Simplify3D)[18]Fan on[3]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[18][1]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented≈24 at 300 mm/s with a 0.4 mm nozzle and 0.2 mm layer; 30 % more flow than regular PLA at the same temperature[3][14][16][21]
Warping tendency1–5Not documentedNone[3]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[18][1]Sticks to anything[22]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[1]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning; the filament must be kept dry throughout the print[1][23]Easy — minor profile tuning; needs a printer that can actually reach the flow rate[14][3]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades[1]Brass fine indefinitely[24]
Abrasiveness1–5Non-abrasive when unfilled[1]Non-abrasive[25][24]
Nozzle clog risk1–5Very high — frequent jams without careful setup; wet nylon pops and cracks in the melt[26][23]Very low[24]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[18]Moderate — good heatbreak cooling needed; PLA softens below 60 °C[27]
Hotend requirementMay require an all-metal hot end (Simplify3D)[18]No special hot-end required[22]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Very high (>2 %) — Polymaker groups nylon with PVA as the most moisture-prone class, and its own PA6-based composites reach 2.35–3.33 % equilibrium[23][28]Moderate — 0.40 % equilibrium at 23 °C / 70 % RH[3]
Equilibrium moisture content at ~50 % RH%Not documented0.40 equilibrium at 23 °C / 70 % RH (Polymaker PolySonic)[3]
Drying temperature & time100 °C for 8 h (Polymaker CoPA); storage below 20 % RH[20][29]55 °C for 6 h; 50 °C for 8 h (Bambu Lab)[3][19]
Symptoms when wetPopping and cracking during extrusion, then defects that Polymaker describes as very hard to diagnose[26]Bubbling and popping at the nozzle, stringing, rough surface and weak layers[23]
Effect of moisture on strengthMeasured dry against wet on printed specimens at 6.16 % moisture (Polymaker CoPA): tensile 78.0 → 34.3 MPa, Young's modulus 2703 → 724 MPa, flexural strength 109.8 → 22.6 MPa, while notched Charpy rises 6.9 → 27.7 kJ/m² and elongation 12.7 → 13.2 %[20][26]Polymaker rates PLA low-sensitivity — the loss shows as poor layer adhesion and brittle layers rather than a published strength figure[23]
Storage requirementSealed below 20 % RH with desiccant; Polymaker says nylon often needs to stay in a dryer while printing[29][23]Sealed with desiccant below 20 % RH; shelf life at ambient is long[19][22]
Hydrolysis at melt temperaturePolymaker requires a 100 °C dry for 8 h and storage below 20 % RH; no molecular-weight loss figure is published, and the published wet data is conditioning rather than melt hydrolysis[20][29]Not documented
Mechanical Properties
Tensile strength (XY)MPa62 at break (printed XY, ISO 527, 3DXTech iOn PA6 alloy); Stratasys FDM Nylon 6 conditioned to 20 °C / 50 % RH gives 67.6 ultimate and 49.3 at yield printed XZ (ASTM D638)[5][30]43.9 at 300 mm/s and 46.0 at 46.7 mm/s (printed XY, ISO 527); 58.6 on My Tech Fun bars for Creality Hyper PLA[3][31]
Young's modulusMPa2110 (printed XY, ISO 527, 3DXTech iOn PA6 alloy); Stratasys FDM Nylon 6 conditioned gives 2232 printed XZ and 1817 ZX (ASTM D638)[5][30]2650 at 300 mm/s, 2878 at classic speed (printed XY, ISO 527)[3]
Elongation at break%9 at break (printed XY, ISO 527, 3DXTech iOn PA6 alloy); Stratasys FDM Nylon 6 conditioned gives 38 printed XZ against 3.2 in ZX (ASTM D638)[5][30]15.1 at 300 mm/s, 21.5 at classic speed (printed XY, ISO 527)[3]
Flexural strengthMPa78 (printed XY, ISO 178, 3DXTech iOn PA6 alloy); Stratasys FDM Nylon 6 conditioned gives 97.2 printed XZ and 82 ZX (ASTM D790)[5][30]71.4 at 300 mm/s, 76.5 at classic speed (printed XY, ISO 178)[3]
Flexural modulusMPa2200 (printed XY, ISO 178, 3DXTech iOn PA6 alloy); Stratasys FDM Nylon 6 conditioned gives 2196 printed XZ and 1879 ZX (ASTM D790)[5][30]2798 at 300 mm/s, 2868 at classic speed (printed XY, ISO 178)[3]
Charpy impact, notchedkJ/m²Not documented5.0 at 300 mm/s, 6.1 at classic speed (printed XY, ISO 179, notched)[3]
Other impact dataIzod notched 106 J/m printed XZ against 43 J/m in ZX; unnotched 2873 against 192 J/m (Stratasys FDM Nylon 6, conditioned 20 °C / 50 % RH, ASTM D256 Method A) — a 15x anisotropy unnotched[30]Printing at 300 mm/s instead of 46.7 mm/s costs 4.6 % tensile strength and 18 % notched Charpy[3]
Layer adhesion / Z tensileMPa36.5 ultimate and 28.9 at yield printed ZX (Stratasys FDM Nylon 6, conditioned 20 °C / 50 % RH, ASTM D638)[30]32.4 at 300 mm/s, 37.3 at classic speed (printed Z, ISO 527); 35.3 for Creality Hyper PLA vs 23.0 for average PLA on identical bars[3][31]
Brittleness1–5Tough — absorbs impact, yields before breaking[1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 86 and Rockwell 85 (108) — the source does not name the scales on extruded unfilled PA66 stock (ASTM D2240, D785); no figure is published for a PA6 filament[32]78.7 Shore D measured on printed bars for Sunlu PLA Meta (My Tech Fun), against 75.3 for the same maker's plain PLA[33]
Creep resistance / sustained load1–5Moderate[1]Poor — 12 mm bar sagged to 17.7 mm over 6 days at 1.25 kg[31]
Fatigue / repeated-flex resistance1–5Excellent — living hinges viable[1]Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength (R = 0.2)[34][27]
Elasticity / flexibility1–5Semi-flexible[26]Rigid[3]
Z strength as % of XY%54 (Stratasys FDM Nylon 6 conditioned, ZX against XZ ultimate tensile, ASTM D638); 59 on the yield figures[30]74 at 300 mm/s, 81 at classic speed (printed)[3]
Wear resistance & friction3DXTech sells a dedicated wear-resistant PA6 grade; abrasion resistance is the usual reason to choose PA6 over PA12[6]Not documented
Thermal Properties
HDT at 0.45 MPa°CNot documented53 (ISO 75, 0.45 MPa)[3]
HDT at 1.8 MPa°C93 (Stratasys FDM Nylon 6, conditioned, ASTM D648 at 264 psi)[30]52 (ISO 75, 1.8 MPa)[3]
Glass transition (Tg)°C105 (DSC, 3DXTech iOn PA6 alloy)[5]59 (DSC)[3]
Melting point / Vicat°CNot documented164 peak melt (DSC); crystallisation 96 °C, Vicat 61 °C[3]
Continuous service temperature°CNot documented53 — loaded bars begin to move at this temperature[31]
Thermal expansion (CTE)µm/m·K81.0 on extruded unfilled PA66 stock (ASTM D696; source states 4.5e-5 in/in/°F); no figure is published for a PA6 filament, and PA6 and PA66 expand almost identically[32]96–99 for plain printed PLA (fibre Bragg grating, 25–50 °C); no grade-specific measurement published[35]
Flammability / UL 94Flammable; no UL 94 rating published for the unfilled filament grades surveyed[5]Flammable; no UL 94 rating published by the major brands[19][4]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows and chalks under UV[1]Degrades within weeks outdoors[27][36]
Chemical resistanceWithstands oils, fuels and alkalis — the usual reason to choose a polyamide[1]Good against weak acids, oils and grease; poor against strong acids and alkalis[3]
Water / humidity resistance in service1–5Absorbs water, properties shift — a conditioned part is measurably softer and larger than the same part dry[26][20]Good — insoluble in water[19]
Food contactPolymaker notes medical-grade variants exist, but standard filament is not food-contact certified[1]Base resin is food-contact grade, but printed layer grooves harbour bacteria; Prusa advises against food use[27]
Biodegradability / compostabilityNot biodegradable[1]Industrially compostable only — needs sustained 55 °C; not home compostable[37][27]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[1]Mechanically recyclable; not accepted in household plastic collection[37]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[2]Low hazard — minimal VOC and particle emission[2]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon; total VOC reached nearly 200 µg/min, the highest of the nine filaments tested[2]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median — low for ultrafine particles despite the highest VOC mass of any filament tested[2]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament — the largest single-VOC emission rate measured in the study[2]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[2]None needed in a normal room[2]
Post-Processing
Sanding & machiningSands poorly — the toughness makes it gum rather than powder[18]Wet sanding — dry sanding heats the surface by friction and smears it[36][27]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[18]Cyanoacrylate for most joints; some grades partially dissolve and bond with acetone[27][38]
Vapour / chemical smoothingNo practical vapour smoothing[18]No practical vapour smoothing — only chloroform, hot benzene or THF, which are laboratory-only[27]
Support material pairingPVA dissolves cleanly against nylon; Polymaker sells a break-away PolySupport for PA12[18]PolySupport and PolyDissolve S1 (Polymaker)[3]
Dimensional accuracy & detailParts grow as they absorb moisture after printing; Polymaker declines to publish a standard dimensional allowance because it depends on geometry and infill[26]Not documented
Solvents & Solubility
Soluble inDissolved at 23 °C by formic acid above ~50 %, phenol, m-cresol, 96 % sulphuric acid or hexafluoroisopropanol — laboratory reagents.[39]Chloroform: 10 % w/v in 2–4 h at 23 °C, every grade and morphology; THF and DMF only at 65 °C. Laboratory reagents.[40]
Softened or crazed byZinc chloride solutions stress-crack it — 10 % marginal, 37 % not resistant; alcoholic calcium chloride dissolves it.[39]Acetone, ethyl acetate and toluene plasticise it but dissolve <1 % even at 65 °C; submersion in acetone crazes and destroys parts.[40][41]
Solvent welding & smoothing agentNone — nylon's only solvents are formic acid, phenol and HFIP, all of which degrade the part they wet.[39]Chloroform vapour smooths and welds PLA at the cost of tensile strength; acetone does not smooth it at all.[42][41]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  2. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  3. PolySonic PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  4. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  5. iOn PA6-based Nylon Alloy Technical Data Sheet v2.0 3DXTech · 2026-08 · tds
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. YXPOLYER PA6 Black 1 kg — product page YXPOLYER · 2026-08 · vendor
  8. PolySonic PLA 1.75mm/1kg — product page Polymaker Shop · 2026-08 · vendor
  9. Overture High Speed PLA 1.75mm Overture3D · 2026-08 · vendor
  10. High Speed PLA filament collection Anycubic Official Store · 2026-08 · vendor
  11. PLA Meta filament collection Sunlu Official Store · 2026-08 · vendor
  12. QIDI PLA Rapido 1.75mm 1kg 3D Printers Depot · 2026-08 · vendor
  13. Prusament PLA Prusa Pro Green 1kg (NFC) Prusa Research · 2026-08 · vendor
  14. PolySonic PLA — product page Polymaker · 2026-08 · vendor
  15. Creality PLA filament collection Creality Official Store · 2026-08 · vendor
  16. Polymaker Launches New High-Speed 3D Printing Filament — PolySonic PLA & PLA Pro Polymaker · 2023-11 · doc
  17. PLA Basic — product page Bambu Lab US Store · 2026-08 · vendor
  18. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  19. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  20. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  21. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  22. PLA — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  23. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  24. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  25. Prusament PLA — material page Prusa Polymers · 2026-08 · doc
  26. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  27. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  28. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  29. PolyMide CoPA — Technical Data Sheet page Polymaker Wiki · 2026-08 · tds
  30. FDM Nylon 6 — data sheet (conditioned 20 °C / 50 % RH) Stratasys · 2017-11 · tds
  31. Creality Hyper PLA filament review — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  32. TECAMID 66 natural (PA66) — stock shape properties Ensinger · 2026-08 · tds
  33. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  34. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  35. Characterization of Thermal Expansion Coefficient of 3D Printing Polymeric Materials Using Fiber Bragg Grating Sensors Materials 17(18):4668 · 2024-09 · paper
  36. Prusament PLA Technical Data Sheet v1.0 Prusa Polymers · 2018-09 · tds
  37. Filamentive PLA (recycled) — product page Filamentive · 2026-08 · vendor
  38. Prusament rPLA Corn Pigment 1kg — product page Prusa Research · 2026-08 · vendor
  39. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  40. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  41. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  42. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper