3D Printing Info

Filament comparison

PA6-GF vs TPE SEBS

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PA6 (PA6-GF) guideTPE (SEBS) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA6-GF comparisonsMore TPE SEBS comparisons
PA6-GF vs TPE SEBS — documented properties and sources
PropertyGlass-fibre PA6 (PA6-GF)PATPE (SEBS)FLEX
Market snapshot
Listing priceUSD/kg; dated snapshots$59.98/kg median; $39.99–$130.00/kg across 6 dated product listings$98.25/kg median; $76.50–$120.00/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryPA6 reinforced with chopped glass fibre — Polymaker's grade is 25 wt%[1][2]Styrene-ethylene-butadiene-styrene thermoplastic elastomer — a styrenic rubber, not a polyurethane[3]
Densityg/cm³1.14 (Bambu Lab) and 1.20 (Polymaker Fiberon), ISO 1183[2][1]1.044 printed part density (BASF Ultrafuse TPS 90A, ISO 1183-1) — the lightest elastomer here[3]
Typical priceUSD/kg1 kg-equivalent spools span 40–130; the middle of the market is about 60[2][4][5]1 kg-equivalent spools cluster near 77[6]
Price range across brandsUSD/kg40–130 across brands; SUNLU 40, YXPOLYER 45, Polymaker Fiberon and Bambu Lab 60, 3DXTech FibreX 87, Obsidian Nylon 6+GF 130[4][2][7][5][8]77 for the Recreus 600 g spool; Proto-pasta only lists a 50 g coil, which prices at 120[6][9]
Market availability1–5Stocked by most mainstream brands[2][4][7][5][8]Niche, a handful of specialist brands[3][9][6]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75 and 1 kg spools[4][7][2]1.75 and 2.85 mm; 0.05 and 0.6 kg spools[3][6]
Typical applicationsStiff, heat-resistant structural parts where a matte finish and lower cost beat carbon fibre[2][1]Soft-touch overmoulds and skin-contact parts where a non-polyurethane elastomer is wanted[3]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab)[2]260–280 (BASF Ultrafuse TPS 90A) — far hotter than any TPU here[3]
Bed temperature°CNot documented70–90 (BASF Ultrafuse TPS 90A)[3]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[2]Open frame is fine[3]
Recommended chamber temperature°C45–60 (Bambu Lab)[2]Not documented
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[10][11]PEI sheet or painter's tape; Polymaker warns TPU can over-stick and advises a glue stick as a release agent[12][13]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s10 at Bambu Lab's 130 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][14]0.8–2.4 at the 10–30 mm/s BASF specifies on a 0.4 mm nozzle at 0.2 mm layer — the slowest material in this group[3]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[10]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[11]Not documented
Overall printing difficulty1–5Expert / industrial hardware only[2][15]Advanced — enclosure, hardware upgrades, tuning[3]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[2]Nozzle 0.4 mm or larger; BASF caps print speed at 10–30 mm/s[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA6-GF25 and recommends hardened steel or ruby[1]Brass fine indefinitely[16]
Abrasiveness1–5Highly abrasive — standard GF composite; Polymaker puts brass nozzle life at roughly 9 h on PA6-GF25[1]Non-abrasive[16]
Nozzle clog risk1–5Very high — frequent jams without careful setup[15]Moderate — needs dry filament and a clean nozzle; BASF caps print speed at 10–30 mm/s and Simplify3D warns that raised feed rates on flexibles most likely end in a jam[12][3]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[10]Not documented
Hotend requirementMay require an all-metal hot end (Simplify3D)[10]No special hot-end required, but a direct-drive extruder is (Simplify3D)[12]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Very high (>2 %) — 2.56 % saturated at 25 °C / 55 % RH (Bambu Lab) and 3.33 % equilibrium (Polymaker Fiberon), the highest in the dataset[2][1]Negligible (<0.1 % EMC) — BASF states drying is not necessary, unique among the elastomers here[3]
Equilibrium moisture content at ~50 % RH%2.56 saturated at 25 °C / 55 % RH (Bambu Lab); 3.33 equilibrium (Polymaker Fiberon PA6-GF25)[2][1]Not documented
Drying temperature & time80 °C for 8–12 h (Bambu Lab)[2]None — BASF states Ultrafuse TPS 90A arrives in a printable condition and drying is not necessary[3]
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[17]Bubbling and popping at the nozzle, stringing and a rough surface[15]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA6-GF25 itself: at 4.57 % moisture tensile falls 80.1 → 40.2 MPa and modulus 5357 → 1794 MPa, while notched Charpy rises 10.0 → 28.0 kJ/m²[1][17]Not applicable — the SEBS chemistry has no amide or ester linkages to take up water, and BASF specifies no drying at all[3]
Storage requirementSealed below 20 % RH with desiccant[15]Sealed with desiccant; often kept in a dryer during the print[15]
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[18][19]Not documented
Mechanical Properties
Tensile strength (XY)MPa75 ± 6 (Bambu Lab) and 80.1 ± 1.8 (Polymaker Fiberon, dry/annealed) printed XY, ISO 527; Fiberon falls to 40.2 ± 2.1 conditioned to 4.57 % moisture. Stratasys FDM PA6/66-GF30-FR gives 60.2-61.1 at break and 61.7-62.3 at yield printed XZ (ASTM D638)[2][1][20]Not documented
Young's modulusMPa2850 ± 260 (Bambu Lab) and 5357 ± 211 (Polymaker Fiberon, dry) printed XY, ISO 527; Fiberon falls to 1794 ± 84 conditioned. Stratasys FDM PA6/66-GF30-FR gives 5600-5830 printed XZ against 3050-3140 in ZX (ASTM D638)[2][1][20]Not documented
Elongation at break%2.4 ± 0.2 dry (Polymaker Fiberon) to 3.9 ± 0.8 (Bambu Lab) printed XY, ISO 527; the Fiberon grade rises to 4.2 ± 0.7 conditioned[2][1]Not documented
Flexural modulusMPa3670 ± 140 printed XY, ISO 178 (Bambu Lab)[2]Not documented
Charpy impact, notchedkJ/m²10.0 ± 0.7 printed XY dry and 28.0 ± 1.0 conditioned, ISO 179 notched (Polymaker Fiberon); Bambu Lab 7.2 ± 2.3[1][2]Not documented
Other impact dataCharpy unnotched 27.2 ± 2.2 printed XY (Bambu Lab, ISO 179). Stratasys FDM PA6/66-GF30-FR gives Izod notched 74.6-77.1 J/m printed XZ against 17.2-22.1 in ZX (ASTM D256)[2][20]Not documented
Layer adhesion / Z tensileMPa27 ± 5 (Bambu Lab) and 60.7 ± 1.1 (Polymaker Fiberon, dry) printed Z, ISO 527 — the two makers differ by more than a factor of two; Fiberon falls to 26.3 ± 1.5 conditioned. Stratasys FDM PA6/66-GF30-FR gives 23.7-24.4 at break printed ZX (ASTM D638)[2][1][20]Not documented
Brittleness1–5Brittle — snaps with little warning; elongation at break 2.4 % in XY[1]Very ductile — bends far before failing[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785)[21]89 Shore A and 29 Shore D (BASF Ultrafuse TPS 90A, ISO 7619-1)[3]
Creep resistance / sustained load1–5Good. Ensinger lists high creep resistance as a headline property of extruded PA66-GF30 stock; the rating is held below Excellent because equilibrium moisture uptake of 3.33 % softens the matrix in service[21][1]Poor — no SEBS creep test; a printed 95A TPU bar crept from 74.5 to 82.7 mm over 5 days at 1.25 kg[22]
Fatigue / repeated-flex resistance1–5Good. Ensinger lists high fatigue strength as a headline property of extruded PA66-GF30 stock[21]Excellent — living hinges viable[13]
Elasticity / flexibility1–5Rigid[2]Rubbery / highly elastic[3]
Z strength as % of XY%36 (Bambu Lab) to 76 (Polymaker Fiberon), printed; Stratasys FDM PA6/66-GF30-FR gives 39-41 (ZX against XZ tensile at break, ASTM D638)[2][1][20]Not documented
Wear resistance & frictionNot documentedAbrasion 111 mm³ (ISO 4649) — the poorest abrasion resistance in this group, well behind TPU[3]
Thermal Properties
HDT at 0.45 MPa°C182 (Bambu Lab) and 191 (Polymaker Fiberon), ISO 75 at 0.45 MPa. Stratasys FDM PA6/66-GF30-FR gives 161 printed XY and 185 XZ (ASTM D648 at 66 psi)[2][1][20]Not documented
HDT at 1.8 MPa°C157 (Polymaker Fiberon) and 158 (Bambu Lab), ISO 75 at 1.8 MPa[2][1]Not documented
Glass transition (Tg)°C67 (Bambu Lab) and 70.4 (Polymaker Fiberon), DSC; Stratasys measures 51.5 on FDM PA6/66-GF30-FR (ASTM D7426)[2][1][20]Not documented
Melting point / Vicat°C214.5 (Polymaker Fiberon) and 219 (Bambu Lab) melting, DSC; Vicat 210–212 (ISO 306)[2][1]242–249 melting (BASF Ultrafuse TPS 90A, ISO 11357-3)[3]
Thermal expansion (CTE)µm/m·K48.6 on extruded PA66-GF30 stock (ASTM D696; source states 2.7e-5 in/in/°F). Stratasys measures much higher on printed FDM PA6/66-GF30-FR — 95.4 over -20 to 5 °C and 214 over 25 to 80 °C in XY (ASTM E831)[21][20]Not documented
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[18]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[11]Good — years with some colour shift; Polymaker lists UV exposure among the conditions TPU withstands[13]
Chemical resistanceWithstands oils, fuels and alkalis[11]Withstands industrial solvents and UV exposure (Polymaker)[13]
Water / humidity resistance in service1–5Absorbs water, properties shift[17]Excellent — essentially unaffected[3]
Food contactNot food-contact certified as filament[11]Not food safe without specific certification (Polymaker)[13]
Biodegradability / compostabilityNot biodegradable[11]Not biodegradable[13]
RecyclabilityNot accepted in household plastic collection[11]Not accepted in household plastic collection[13]
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker Fiberon, ANSI/ESD S11.11)[1]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[23]Low hazard — minimal VOC and particle emission; TPU was not among the nine filaments in the chamber study[23]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[23]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[23]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[23]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[23]Open a window / occasional ventilation[23]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Not documented
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[10]Difficult to sand or smooth; Polymaker limits post-processing to trimming or tumbling[13]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[10]Cyanoacrylate bonds TPU; no common solvent welds it[13]
Vapour / chemical smoothingNo practical vapour smoothing[10]No practical vapour smoothing[13]
Support material pairingNot documentedPolymaker warns TPU supports are often very difficult to remove[13]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[24]Toluene dissolves SEBS at room temperature — Kraton quotes solution viscosity at 25 % mass in toluene, 25 °C.[25]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[24]Soaking in hydrocarbon solvents and oils deteriorates it; short exposures are tolerated. Resists water, acids and bases.[25]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[24]Toluene will weld it, though the joint stays soft; no workshop-safe agent, and vapour smoothing is not practical.[25]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  2. Bambu Filament Technical Data Sheet — PA6-GF Bambu Lab · 2026-08 · tds
  3. Ultrafuse TPS 90A Technical Data Sheet (Version 1.1, SEBS) BASF Forward AM · 2020-12 · tds
  4. Polymaker product catalogue Polymaker · 2026-08 · vendor
  5. SUNLU Nylon-6 Glass Fiber (PA6-GF) 3D Printer Filament 1 kg — product page SUNLU · 2026-08 · vendor
  6. Recreus product catalogue Recreus · 2026-08 · vendor
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. YXPOLYER PA6-GF Black 1 kg — product page YXPOLYER · 2026-08 · vendor
  9. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  10. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  11. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  12. Flexible (TPE/TPU) — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  13. TPU — material basics Polymaker Wiki · 2026-08 · doc
  14. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  15. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  16. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  17. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  18. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  19. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  20. FDM PA6/66-GF30-FR — Material Data Sheet Stratasys · 2026-07 · tds
  21. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  22. BambuLab TPU 95A HF vs Qidi TPU 95A HF — results spreadsheet My Tech Fun (Igor Gaspar) · 2024-02 · test
  23. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  24. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  25. KRATON polymers Grade Range — chemical resistance and toluene solution data Kraton Corporation · 2025-07 · tds