3D Printing Info

Filament comparison

PA12 vs PC-ESD

Compare printing settings, strength, heat resistance, dated prices and sources.

PA12 (Nylon 12) guideESD-safe PC guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA12 comparisonsMore PC-ESD comparisons
PA12 vs PC-ESD — documented properties and sources
PropertyPA12 (Nylon 12)PAESD-safe PCPC
Market snapshot
Listing priceUSD/kg; dated snapshots$64.33/kg median; $36.00–$170.67/kg across 3 dated product listings$180.00/kg median; $180.00–$180.00/kg across 1 dated product listings
Identity & Market
Base polymer / chemistryPolyamide 12 — the longest-chain common nylon, with the fewest amide groups per unit mass and so the least moisture uptake[1][2]Polycarbonate compounded with a conductive filler for static-dissipative parts[3]
Densityg/cm³1.01 specific gravity (Stratasys FDM Nylon 12, ASTM D792)[4]1.24 (ISO 1183, 3DXTech); Stratasys specific gravity 1.195 (ASTM D792)[3][5]
Typical priceUSD/kg1 kg-equivalent spools span 36–171; the middle of the market is about 64[6][7]1 kg-equivalent spools cluster near 180[8]
Price range across brandsUSD/kg36–171 across brands; IEMAI 3D 36, Fiberlogy 64 at 3DJake, 3DXTech AmideX Nylon 12 171[6][8][7]180 at 3DXTech's 750 g pricing — the most expensive material in this group[8]
Market availability1–5Available from several mainstream brands[6][8]Special order, 1–2 makers worldwide[8]
Spool sizes & diameters1.75 and 2.85 mm; 750 g and 1 kg spools[8][6]1.75 and 2.85 mm; 750 g spools plus Stratasys-compatible cartridges[8]
Typical applicationsDimensionally stable functional parts, ducting and living hinges where PA6 would move too much with humidity[1][9]Electronics fixtures and trays that need PC heat resistance and static dissipation together[3]
Printing Parameters
Nozzle temperature°C260–290 (Extrudr DURAPRO PA12)[10]Not documented
Bed temperature°C110 (Extrudr DURAPRO PA12)[10]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive)[1]Enclosure required (passive)[11][12]
Part cooling fanPart cooling fan not required (Simplify3D)[13]Not documented
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[13][1]PEI with a glue stick or a commercial adhesive[14]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s12 at Extrudr's 150 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[10][15]Not documented
Warping tendency1–5Not documentedSevere — heated chamber needed[11][12]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[13][1]Needs a specific surface plus adhesive[14][16]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[1]Moderate — retraction tuning needed; Polymaker flags stringing as a common PC problem[16]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[1]Advanced — enclosure, hardware upgrades, tuning[11]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades[1]Hardened steel required[3]
Abrasiveness1–5Non-abrasive when unfilled[1]Moderately abrasive — conductive carbon filler[3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[9][17]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a 120 °C pre-dry[18]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[13]Slightly sensitive[14]
Hotend requirementMay require an all-metal hot end (Simplify3D)[13]All-metal hot end required (Simplify3D)[14]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — Polymaker's PA12-CF10 reaches 1.5 % equilibrium against 3.33 % for its PA6-GF25, and Polymaker developed the PA12 grade specifically for lower moisture sensitivity[2][9]Low (0.1–0.3 %) — the PC matrix takes up 0.15–0.25 % and 3DXTech specifies a 120 °C, 4 h pre-dry[19][20][18]
Drying temperature & time60–80 °C for 8–12 h (Extrudr DURAPRO PA12); 100 °C for 8 h (Polymaker CoPA)[10][21]Not documented
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[9]Bubbling and popping at the nozzle, stringing and a rough surface[17]
Effect of moisture on strengthPolymaker states its PA12 grade changes little between wet and dry, unlike its PA6-based materials; the CoPA dry-to-wet reference shows what the PA6-type response looks like[9][21]No dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[16][17]
Storage requirementSealed below 20 % RH with desiccant[17]Airtight containers with desiccant to prevent reabsorption[16]
Hydrolysis at melt temperaturePolymaker requires a 100 °C dry for 8 h and storage below 20 % RH; no molecular-weight loss figure is published, and the published wet data is conditioning rather than melt hydrolysis[21][22]Not documented
Mechanical Properties
Tensile strength (XY)MPa49.3 at yield and 33.4 at break printed XZ (Stratasys FDM Nylon 12, ASTM D638)[4]68 at break (printed XY, ISO 527, 3DXTech) — above the 58 of 3DXTech's unfilled ezPC; Stratasys prints 47.6-49.4 at yield in XZ (ASTM D638)[3][23][5]
Young's modulusMPa1510 printed XZ and 1250 ZX (Stratasys FDM Nylon 12, ASTM D638)[4]2300 (printed XY, ISO 527); Stratasys prints 1960 in XZ and 1810-1910 in ZX (ASTM D638)[3][5]
Elongation at break%30 at break printed XZ against 6.5 in ZX (Stratasys FDM Nylon 12, ASTM D638)[4]6 at break (printed XY, ISO 527), against 14 for the unfilled grade[3][23]
Flexural strengthMPaNot documented95 (printed XY, ISO 178); Stratasys prints 82.6-83.2 at break in XZ against 46.3-49.5 in ZX (ASTM D790)[3][5]
Flexural modulusMPaNot documented2310 (printed XY, ISO 178)[3]
Charpy impact, notchedkJ/m²11 at +23 °C and 6.0 at -30 °C (Extrudr DuraPro PA12, ISO 179/1eA); unnotched does not break[10]Not documented
Other impact dataIzod notched 138 J/m printed XZ against 71.0 J/m in ZX (Stratasys FDM Nylon 12, ASTM D256)[4]Not documented
Layer adhesion / Z tensileMPa41.8 at yield and 41.2 at break printed ZX (Stratasys FDM Nylon 12, ASTM D638) — higher than the XZ break figure, because XZ specimens draw and neck first[4]32.5-37.9 at yield printed ZX (Stratasys, ASTM D638 on the Fortus 450mc and F900)[5]
Brittleness1–5Tough — absorbs impact, yields before breaking[1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for an ESD grade[24]
Creep resistance / sustained load1–5Moderate — the long-chain polyamides hold load better than PLA but below PC[1]Excellent — holds load for years. Moulded unfilled PC was still running unbroken under 41 MPa tensile creep at room temperature when the test was stopped, and the conductive filler leaves the glass transition unchanged at 142 °C, so the creep mechanism is polycarbonate's[25][5]
Fatigue / repeated-flex resistance1–5Excellent — living hinges viable. Stratasys sells FDM Nylon 12 specifically for repetitive-flex parts such as snap-fit clips and press-fit inserts on the strength of its fatigue properties[1][4]Not documented
Elasticity / flexibility1–5Semi-flexible[9]Rigid[3]
Z strength as % of XY%85 (Stratasys FDM Nylon 12, ZX against XZ tensile yield, ASTM D638) — one of the least anisotropic unfilled filaments measured[4]68-77 (Stratasys ZX against XZ tensile yield, ASTM D638)[5]
Thermal Properties
HDT at 0.45 MPa°C94.7 printed XY and 91.9 in XZ/ZX (Stratasys FDM Nylon 12, ASTM D648 at 66 psi)[4]143-146 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 66 psi); 135 moulded[5]
HDT at 1.8 MPa°C84.3 printed XY and 75.3 in XZ/ZX (Stratasys FDM Nylon 12, ASTM D648 at 264 psi)[4]140-144 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 264 psi); 124 moulded[5]
Glass transition (Tg)°C34.0 (Stratasys FDM Nylon 12, ASTM D7426 inflection point)[4]143 (DSC, 3DXTech) and 142 (Stratasys, ASTM D7426)[3][5]
Melting point / Vicat°CVicat A 142 (Extrudr DURAPRO PA12, ISO 306)[10]Not documented
Continuous service temperature°CBounded by a Vicat softening point of 142 °C (Extrudr DURAPRO PA12); no loaded-bar service figure is published[10]113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[20]
Thermal expansion (CTE)µm/m·K84-103 printed (Stratasys FDM Nylon 12, ASTM E831: 84.4 in XY and 85.6 in XZ/ZX over -50 to 10 °C, 89.1 over 10-45 °C, 98.2 over 45-70 °C); Extrudr quotes 100 for DURAPRO PA12 (ISO 11359-2)[10][4]68.4 on extruded unfilled PC stock (ASTM D696; source states 3.8e-5 in/in/°F); no figure is published for a conductive-filled grade[24]
Flammability / UL 94Flammable; no UL 94 rating published for the unfilled grades surveyed[10]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement[1]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[1]Withstands oils, solvents and fuels; Polymaker rates it good against weak acids[16]
Water / humidity resistance in service1–5Good — minor absorption; the least moisture-sensitive of the common nylons[9]Not documented
Food contactNot food-contact certified as filament[1]Bisphenol-A polycarbonate is not offered as food-contact filament[16]
Biodegradability / compostabilityNot biodegradable[1]Not biodegradable[16]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[1]Mechanically recyclable but not accepted in household plastic collection[16]
Electrical & ESD propertiesNot documentedSurface resistance 10⁷–10⁹ ohm/sq, the static-dissipative band (ASTM D257), against above 10¹³ for unfilled ezPC[3][23]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[26]Moderate — measurable VOCs and UFPs, ventilation advised[26]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon; total VOC reached nearly 200 µg/min, the highest of the nine filaments tested[26]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median — low for ultrafine particles despite the highest VOC mass of any filament tested[26]≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[26]
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament — the largest single-VOC emission rate measured in the study[26]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[26]Ventilated room or enclosure recommended[26][11]
Dust & fibre handling hazardNot documentedConductive carbon filler is bound in the matrix; avoid inhaling sanding dust[3]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[13]Sands and machines well; the toughness means it cuts rather than chips[14]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[13]Cyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[14]
Vapour / chemical smoothingNo practical vapour smoothing[13]No practical vapour smoothing[14]
Support material pairingPolymaker sells a break-away PolySupport matched to PA12[13]Prints its own supports; 3DXTech sells a dedicated PC break-away support[14]
Dimensional accuracy & detailHolds dimensions better than PA6 after conditioning — Polymaker singles its PA12 grade out on exactly this point[9]Not documented
Solvents & Solubility
Soluble inDissolved at 23 °C by formic acid, phenol, m-cresol, 96 % sulphuric acid or hexafluoroisopropanol — all laboratory reagents.[27][28]Dichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[29]
Softened or crazed byNot resistant to 10 % formic acid, phenol, chloroform or dichloromethane (Ensinger); zinc chloride stress-cracks nylon.[28][27]Methanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[29]
Solvent welding & smoothing agentNone — nylon's only solvents are formic acid, phenol and HFIP, all of which degrade the part they wet.[27]Dichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[30]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  2. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  3. 3DXSTAT ESD-PC Technical Data Sheet 3DXTech · 2026-08 · tds
  4. FDM Nylon 12 — Material Data Sheet Stratasys · 2021-09 · tds
  5. PC-ESD — FDM Material Data Sheet Stratasys · 2024-10 · tds
  6. Nylon PA12 — product listing 3DJake International · 2026-08 · vendor
  7. IEMAI 3D PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  8. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  9. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  10. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  11. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  12. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  13. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  14. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  15. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  16. PC — material basics Polymaker Wiki · 2026-08 · doc
  17. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  18. 3DXSTAT ESD-PC — product page (print recommendations) 3DXTech · 2026-08 · doc
  19. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  20. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  21. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  22. PolyMide CoPA — Technical Data Sheet page Polymaker Wiki · 2026-08 · tds
  23. ezPC Polycarbonate Technical Data Sheet 3DXTech · 2026-08 · tds
  24. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  25. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  26. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  27. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  28. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  29. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  30. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds