3D Printing Info

Filament comparison

PA12 vs PAHT-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

PA12 (Nylon 12) guideHigh-temperature CF nylon (PAHT-CF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA12 comparisonsMore PAHT-CF comparisons
PA12 vs PAHT-CF — documented properties and sources
PropertyPA12 (Nylon 12)PAHigh-temperature CF nylon (PAHT-CF)PA
Market snapshot
Listing priceUSD/kg; dated snapshots$64.33/kg median; $36.00–$170.67/kg across 3 dated product listings$59.98/kg median; $49.99–$69.98/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryPolyamide 12 — the longest-chain common nylon, with the fewest amide groups per unit mass and so the least moisture uptake[1][2]High-temperature carbon-fibre nylon. Bambu Lab's PAHT-CF and Polymaker's PA612-CF15 both use a long-chain polyamide matrix for lower moisture uptake than PA6[3][2]
Densityg/cm³1.01 specific gravity (Stratasys FDM Nylon 12, ASTM D792)[4]1.03 (Polymaker PA612-CF15) and 1.06 (Bambu Lab), ISO 1183[3][2]
Typical priceUSD/kg1 kg-equivalent spools span 36–171; the middle of the market is about 64[5][6]1 kg-equivalent spools cluster near 60[3][7]
Price range across brandsUSD/kg36–171 across brands; IEMAI 3D 36, Fiberlogy 64 at 3DJake, 3DXTech AmideX Nylon 12 171[5][8][6]50–70 across brands; Bambu Lab 50, Polymaker Fiberon PA612-CF15 70[3][7]
Market availability1–5Available from several mainstream brands[5][8]Available from several mainstream brands[3][7]
Spool sizes & diameters1.75 and 2.85 mm; 750 g and 1 kg spools[8][5]1.75 mm; 0.5 and 1 kg spools[7][3]
Typical applicationsDimensionally stable functional parts, ducting and living hinges where PA6 would move too much with humidity[1][9]Under-bonnet and near-motor parts needing 170 °C-plus heat deflection with less humidity drift than PA6[3][2]
Printing Parameters
Nozzle temperature°C260–290 (Extrudr DURAPRO PA12)[10]260–290 (Bambu Lab)[3]
Bed temperature°C110 (Extrudr DURAPRO PA12)[10]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive)[1]Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber[3]
Recommended chamber temperature°CNot documented45–60 (Bambu Lab)[3]
Part cooling fanPart cooling fan not required (Simplify3D)[11]Not documented
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[11][1]PEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[11][1]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s12 at Extrudr's 150 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[10][12]8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[3][12]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[11][1]Needs a specific surface plus adhesive[11]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[1]Moderate — retraction tuning needed[1]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[1]Expert / industrial hardware only[3][13]
Extruder requirementNot documented0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades[1]Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-CF15 and recommends hardened steel or ruby[2]
Abrasiveness1–5Non-abrasive when unfilled[1]Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-CF15[2]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[9][13]High — jams from moisture, heat creep or particles[13]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[11]Moderate — good heatbreak cooling needed[11]
Hotend requirementMay require an all-metal hot end (Simplify3D)[11]May require an all-metal hot end (Simplify3D)[11]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — Polymaker's PA12-CF10 reaches 1.5 % equilibrium against 3.33 % for its PA6-GF25, and Polymaker developed the PA12 grade specifically for lower moisture sensitivity[2][9]High (0.8–2 %) — 0.88 % saturated at 25 °C / 55 % RH for Bambu Lab PAHT-CF, a third of its PA6-CF; Polymaker's PA612-CF15 reaches 2.2 % equilibrium[3][2][14]
Equilibrium moisture content at ~50 % RH%Not documented0.88 saturated at 25 °C / 55 % RH (Bambu Lab PAHT-CF); 2.2 equilibrium (Polymaker PA612-CF15)[3][2]
Drying temperature & time60–80 °C for 8–12 h (Extrudr DURAPRO PA12); 100 °C for 8 h (Polymaker CoPA)[10][15]80 °C for 8–12 h (Bambu Lab)[3]
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[9]Not documented
Effect of moisture on strengthPolymaker states its PA12 grade changes little between wet and dry, unlike its PA6-based materials; the CoPA dry-to-wet reference shows what the PA6-type response looks like[9][15]Polymaker publishes dry and wet printed blocks for PA612-CF15 itself: at 2.57 % moisture tensile falls only 91.9 → 83.1 MPa and modulus 5137 → 3991 MPa — the PA612 backbone absorbs far less than PA6[2][9]
Storage requirementSealed below 20 % RH with desiccant[13]Sealed below 20 % RH with desiccant[13]
Hydrolysis at melt temperaturePolymaker requires a 100 °C dry for 8 h and storage below 20 % RH; no molecular-weight loss figure is published, and the published wet data is conditioning rather than melt hydrolysis[15][16]Polymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[17][15]
Mechanical Properties
Tensile strength (XY)MPa49.3 at yield and 33.4 at break printed XZ (Stratasys FDM Nylon 12, ASTM D638)[4]92 ± 7 (Bambu Lab) and 91.9 ± 2.0 (Polymaker PA612-CF15, dry/annealed) printed XY, ISO 527; the Polymaker grade only falls to 83.1 ± 2.2 conditioned to 2.57 % moisture[3][2]
Young's modulusMPa1510 printed XZ and 1250 ZX (Stratasys FDM Nylon 12, ASTM D638)[4]3860 ± 230 (Bambu Lab) and 5137 ± 192 (Polymaker PA612-CF15, dry) printed XY, ISO 527; Polymaker 3991 ± 137 conditioned[3][2]
Elongation at break%30 at break printed XZ against 6.5 in ZX (Stratasys FDM Nylon 12, ASTM D638)[4]2.6 ± 0.2 dry (Polymaker PA612-CF15) to 8.4 ± 1.8 (Bambu Lab) printed XY, ISO 527; Polymaker 4.1 ± 0.3 conditioned[3][2]
Flexural modulusMPaNot documented4230 ± 210 printed XY, ISO 178 (Bambu Lab)[3]
Charpy impact, notchedkJ/m²11 at +23 °C and 6.0 at -30 °C (Extrudr DuraPro PA12, ISO 179/1eA); unnotched does not break[10]8.1 ± 0.8 printed XY dry and 7.7 ± 0.5 conditioned, ISO 179 notched (Polymaker PA612-CF15)[2]
Other impact dataIzod notched 138 J/m printed XZ against 71.0 J/m in ZX (Stratasys FDM Nylon 12, ASTM D256)[4]Charpy unnotched 57.5 ± 3.4 and notched 22.8 ± 1.8 printed XY (Bambu Lab, ISO 179)[3]
Layer adhesion / Z tensileMPa41.8 at yield and 41.2 at break printed ZX (Stratasys FDM Nylon 12, ASTM D638) — higher than the XZ break figure, because XZ specimens draw and neck first[4]47 ± 5 (Bambu Lab) and 48.3 ± 3.9 (Polymaker PA612-CF15, dry) printed Z, ISO 527; Polymaker 35.6 ± 3.0 conditioned[3][2]
Brittleness1–5Tough — absorbs impact, yields before breaking[1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre long-chain nylon filament[18]
Creep resistance / sustained load1–5Moderate — the long-chain polyamides hold load better than PLA but below PC[1]Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load with 110 °C continuous service; the long-chain PA612 matrix takes up 0.88 % at saturation, a third of the same maker's PA6-CF, so it holds dimension better[19][2]
Fatigue / repeated-flex resistance1–5Excellent — living hinges viable. Stratasys sells FDM Nylon 12 specifically for repetitive-flex parts such as snap-fit clips and press-fit inserts on the strength of its fatigue properties[1][4]Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[19]
Elasticity / flexibility1–5Semi-flexible[9]Rigid[3]
Z strength as % of XY%85 (Stratasys FDM Nylon 12, ZX against XZ tensile yield, ASTM D638) — one of the least anisotropic unfilled filaments measured[4]51 (Bambu Lab) to 53 (Polymaker PA612-CF15), printed[3][2]
Thermal Properties
HDT at 0.45 MPa°C94.7 printed XY and 91.9 in XZ/ZX (Stratasys FDM Nylon 12, ASTM D648 at 66 psi)[4]175 (Polymaker PA612-CF15) and 194 (Bambu Lab), ISO 75 at 0.45 MPa[3][2]
HDT at 1.8 MPa°C84.3 printed XY and 75.3 in XZ/ZX (Stratasys FDM Nylon 12, ASTM D648 at 264 psi)[4]114 (Polymaker PA612-CF15) and 170 (Bambu Lab), ISO 75 at 1.8 MPa[3][2]
Glass transition (Tg)°C34.0 (Stratasys FDM Nylon 12, ASTM D7426 inflection point)[4]70 (Bambu Lab, DSC)[3]
Melting point / Vicat°CVicat A 142 (Extrudr DURAPRO PA12, ISO 306)[10]210 (Polymaker PA612-CF15) and 225 (Bambu Lab) melting, DSC; Vicat 206 (Polymaker)[3][2]
Continuous service temperature°CBounded by a Vicat softening point of 142 °C (Extrudr DURAPRO PA12); no loaded-bar service figure is published[10]Not documented
Thermal expansion (CTE)µm/m·K84-103 printed (Stratasys FDM Nylon 12, ASTM E831: 84.4 in XY and 85.6 in XZ/ZX over -50 to 10 °C, 89.1 over 10-45 °C, 98.2 over 45-70 °C); Extrudr quotes 100 for DURAPRO PA12 (ISO 11359-2)[10][4]Not documented
Flammability / UL 94Flammable; no UL 94 rating published for the unfilled grades surveyed[10]Flammable; no UL 94 rating published for the grades surveyed[17]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement[1]Months outdoors before embrittlement — unstabilised polyamide yellows under UV[1]
Chemical resistanceWithstands oils, fuels and alkalis[1]Withstands oils, fuels and alkalis[1]
Water / humidity resistance in service1–5Good — minor absorption; the least moisture-sensitive of the common nylons[9]Absorbs water, properties shift — less than PA6 but more than PA12[9][3]
Food contactNot food-contact certified as filament[1]Not food-contact certified as filament[1]
Biodegradability / compostabilityNot biodegradable[1]Not biodegradable[1]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[1]Not accepted in household plastic collection[1]
Electrical & ESD propertiesNot documentedSurface resistivity above 10¹² ohm — insulating (Polymaker PA612-CF15, ANSI/ESD S11.11)[2]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[20]Moderate — measurable VOCs and UFPs, ventilation advised[20]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon; total VOC reached nearly 200 µg/min, the highest of the nine filaments tested[20]Up to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[20]
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median — low for ultrafine particles despite the highest VOC mass of any filament tested[20]≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[20]
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament — the largest single-VOC emission rate measured in the study[20]Caprolactam, at up to 180 µg/min from nylon filament[20]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[20]Ventilated room or enclosure recommended[20]
Dust & fibre handling hazardNot documentedFibre is bound in the matrix; sanding dust should not be inhaled[17]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[11]Sands poorly — gums rather than powders[11]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[11]Cyanoacrylate; no common solvent welds polyamide[11]
Vapour / chemical smoothingNo practical vapour smoothing[11]No practical vapour smoothing[11]
Support material pairingPolymaker sells a break-away PolySupport matched to PA12[11]Not documented
Dimensional accuracy & detailHolds dimensions better than PA6 after conditioning — Polymaker singles its PA12 grade out on exactly this point[9]Not documented
Solvents & Solubility
Soluble inDissolved at 23 °C by formic acid, phenol, m-cresol, 96 % sulphuric acid or hexafluoroisopropanol — all laboratory reagents.[21][22]Formic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[21]
Softened or crazed byNot resistant to 10 % formic acid, phenol, chloroform or dichloromethane (Ensinger); zinc chloride stress-cracks nylon.[22][21]Zinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[21]
Solvent welding & smoothing agentNone — nylon's only solvents are formic acid, phenol and HFIP, all of which degrade the part they wet.[21]None — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[21]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  2. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  3. Bambu Filament Technical Data Sheet — PAHT-CF Bambu Lab · 2026-08 · tds
  4. FDM Nylon 12 — Material Data Sheet Stratasys · 2021-09 · tds
  5. Nylon PA12 — product listing 3DJake International · 2026-08 · vendor
  6. IEMAI 3D PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  7. Polymaker product catalogue Polymaker · 2026-08 · vendor
  8. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  9. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  10. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  11. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  12. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  13. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  14. Bambu Filament Technical Data Sheet — PA6-CF Bambu Lab · 2026-08 · tds
  15. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  16. PolyMide CoPA — Technical Data Sheet page Polymaker Wiki · 2026-08 · tds
  17. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  18. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  19. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  20. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  21. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  22. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds