Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PA12 (PA12-GF) guidePPA-CF (carbon-fibre polyphthalamide) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA12-GF comparisonsMore PPA-CF comparisons
PA12-GF vs PPA-CF — documented properties and sources
PropertyGlass-fibre PA12 (PA12-GF)PAPPA-CF (carbon-fibre polyphthalamide)PA
Market snapshot
Listing priceUSD/kg; dated snapshots$130.67/kg median; $46.00–$140.18/kg across 3 dated product listings$84.99/kg median; $21.99–$266.67/kg across 7 dated product listings
Identity & Market
Base polymer / chemistryPA12 reinforced with chopped glass fibre — 3DXTech's grade is nominally 30 wt%[1]Polyphthalamide — semi-aromatic nylon — with 10–15 wt% chopped carbon fibre; Bambu Lab lists the composition as semi-aromatic nylon plus carbon fibre, Raise3D and Siraya Tech state 15 wt%, Flashforge 10 %[2][3][4][5]
Densityg/cm³1.23 (ISO 1183)[1]1.15 (Raise3D) to 1.25 (Bambu Lab and IEMAI 3D), ISO 1183; Flashforge 1.21–1.23[2][3][4][6]
Typical priceUSD/kg1 kg-equivalent spools span 46–140; the middle of the market is about 88[7][8][9]1 kg-equivalent spools span 22–267; the middle of the market is about 85[10][11][12][13][14][15]
Price range across brandsUSD/kg46–140 across brands; IEMAI 3D 46, 3DXTech 131 at 750 g and 130 at 2 kg, PrimaCreator NylonPower Glass Fiber 140 at 500 g[7][8][9]22–267 across brands; CHCKX 22 on Amazon, IEMAI 3D 51, Siraya Tech 57 and 85, Bambu Lab 200 at 750 g, Raise3D 209, 3DXTech CarbonX HTN+CF 267 at 750 g[10][11][12][16][13][14][15]
Market availability1–5Available from several mainstream brands[7][8]Available from several mainstream brands[10][11][12][13][14]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75 and 2 kg spools[7][9]1.75 mm; 750 g, 1 kg, 2 kg and 2.5 kg spools[2][12][14]
Typical applicationsStiff, humidity-stable structural parts — the glass gives the modulus, the PA12 matrix limits the moisture drift[1][17]Under-bonnet automotive brackets, jigs and end-use parts that must stay stiff above the 100 °C working ceiling of PA6-CF[3][4]
Diameter tolerance± mmNot documented0.05 (Bambu Lab and Siraya Tech, 1.75 mm)[2][5]
Printing Parameters
Nozzle temperature°CNot documented280–310 (Bambu Lab and CHCKX); 280–320 (Siraya Tech)[2][5][15]
Bed temperature°CNot documented100–120 (Bambu Lab and CHCKX); Siraya Tech runs cooler at 70–90[2][5][15]
Enclosure / chamber requirement1–5Enclosure required (passive)[18]Enclosure required (passive) — Bambu Lab specifies a 50–80 °C chamber and Siraya Tech requires an enclosure, while Flashforge states its LUVOCOM-based grade prints on machines with no heated chamber[2][4][12]
Recommended chamber temperature°CNot documented50–80 (Bambu Lab); specimens were printed at a 52 °C chamber and Bambu Lab notes 70–80 °C raises Z properties[2]
Part cooling fanNot documentedBambu Lab turns the part fan on; Siraya Tech runs it off[2][5]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[19][18]Smooth or textured PEI plate with a glue stick, or a PVP glue coating[2][5]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented8–12 mm³/s at 300–320 °C (Siraya Tech)[5]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[19]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[18]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[18]Advanced — enclosure, hardware upgrades, tuning; a 320 °C hot end and a hardened nozzle are the entry requirements[2][5]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — no nozzle-life figure is published for a PA12-GF30 grade; Polymaker measures about 9 h of brass nozzle life on its comparable fibre-filled nylons[20]Hardened steel required — Siraya Tech and CHCKX specify hardened steel or better, Raise3D warns brass wears quickly[3][5][15]
Abrasiveness1–5Highly abrasive — standard GF composite[20]Highly abrasive — standard CF/GF composites and glow fills[3][5]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[21]Moderate — needs dry filament and a clean nozzle; Siraya Tech states nozzles below 0.4 mm will clog[5][12]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[19]Not documented
Hotend requirementMay require an all-metal hot end (Simplify3D)[19]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — the PA12 matrix takes up far less than PA6, on the evidence of Polymaker's 1.5 % for PA12-CF10 against 3.33 % for PA6-GF25[22][23]High (0.8–2 %) — 1.30 % saturated at 25 °C / 55 % RH for Bambu Lab and IEMAI 3D against 2.35 % for the same makers' PA6-CF, which is the whole reason to pay for PPA[2][6][24]
Equilibrium moisture content at ~50 % RH%Not documented1.30 saturated at 25 °C / 55 % RH (Bambu Lab and IEMAI 3D) against 2.35 for their PA6-CF; Siraya Tech 1.37 and 1.09 by ISO 62, Raise3D 0.6 by ISO 62 Method 1, Flashforge below 0.1 at 23 °C / 24 h[2][3][4][5][25][6][24]
Drying temperature & timeNot documented100–140 °C for 8–12 h (Bambu Lab, hotter is better within that range); Siraya Tech 100 °C for 4–6 h; Raise3D 80–100 °C for 6–12 h[2][3][5]
Effect of moisture on strengthPolymaker's PA12 grades change little between wet and dry, unlike PA6; the CoPA dry-to-wet blocks show the PA6-type response[17][26]Not documented
Storage requirementSealed below 20 % RH with desiccant[21]Sealed below 20 % RH with desiccant (Bambu Lab); Raise3D keeps the spool in a dry box throughout the print[2][3]
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[20][26]Not documented
Mechanical Properties
Tensile strength (XY)MPa82 at break (printed XY, ISO 527)[1]95–168 (printed XY, ISO 527): Siraya Tech 95, Flashforge 108–112, Siraya Tech Core 112, Raise3D 122 conditioned and annealed, Bambu Lab and IEMAI 3D 168[2][3][4][5][25][6]
Young's modulusMPa7800 (printed XY, ISO 527)[1]7100–11800 (printed XY): Flashforge 7100–8000, Raise3D and Siraya Tech 7800, Siraya Tech Core 9300, Bambu Lab and IEMAI 3D 11800[2][3][4][5][25][6]
Elongation at break%4.5 at break (printed XY, ISO 527) — nearly double the 2.4 % of Polymaker's PA6-GF25[1][23]1.9–5 at break (printed XY): Raise3D 1.9, Siraya Tech 2, Siraya Tech Core 2.25, Bambu Lab and IEMAI 3D 3.2, Flashforge 3.5–5[2][3][4][5][25][6]
Flexural strengthMPa94 (printed XY, ISO 178)[1]145–221 (printed XY, ISO 178): Siraya Tech 145, Siraya Tech Core 178, Raise3D 190, Bambu Lab and IEMAI 3D 208, Flashforge 210–221[2][3][4][5][25][6]
Flexural modulusMPa7550 (printed XY, ISO 178)[1]6500–9860 (printed XY, ISO 178): Flashforge 6500–7000, Siraya Tech 6800, Raise3D 8510, Siraya Tech Core 8700, Bambu Lab and IEMAI 3D 9860[2][3][4][5][25][6]
Charpy impact, notchedkJ/m²Not documented6.5 notched Charpy XY (Bambu Lab and IEMAI 3D, ISO 179); Raise3D 7.8 and Siraya Tech 11 by ISO 179 without stating notched[2][3][5][6]
Other impact dataNot documentedBambu Lab and IEMAI 3D unnotched Charpy 41.7 kJ/m² XY against 4.3 in Z; Flashforge Izod 9–11 kJ/m² XY against 2.5–3 in Z[2][4][6]
Layer adhesion / Z tensileMPaNot documented57 printed Z (Bambu Lab and IEMAI 3D, ISO 527); Raise3D measures 30.2 by a custom mono-layer method[2][3][6]
Brittleness1–5Moderate[1]Brittle — snaps with little warning; 2–3 % elongation at break is typical[2][3][5]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a glass-fibre PA12 filament[27]Not documented
Creep resistance / sustained load1–5Good. Ensinger lists high creep resistance for extruded PA66-GF30 stock, and the PA12 matrix absorbs far less water than PA6, so a PA12-GF part holds load better in a humid environment[27][18]Good — Flashforge cites outstanding creep resistance at high temperature and Raise3D high creep resistance, both against other nylons[3][4]
Fatigue / repeated-flex resistance1–5Good. Ensinger lists high fatigue strength as a headline property of extruded PA66-GF30 stock[27]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[2]
Z strength as % of XY%Not documented34 (Bambu Lab and IEMAI 3D, Z against XY tensile, ISO 527)[2][6]
Thermal Properties
HDT at 0.45 MPa°CNot documented188–227 (ISO 75 at 0.45 MPa): Raise3D 188, Flashforge 220, Bambu Lab and IEMAI 3D 227; Siraya Tech reaches 192–199 only after annealing, 84.5–97 unannealed[2][3][4][5][25][6]
HDT at 1.8 MPa°CNot documented113–196 (ISO 75 at 1.8 MPa): Raise3D 113, Bambu Lab and IEMAI 3D 196; Siraya Tech reaches 119–126 only after annealing, 82.5–84 unannealed[2][3][5][25][6]
Glass transition (Tg)°CNot documented80 (Siraya Tech, ASTM D3418) to 85 (Bambu Lab and IEMAI 3D, DSC)[2][5][6]
Melting point / Vicat°CNot documentedMelting point 231 (Raise3D) to 258 (Bambu Lab and IEMAI 3D); Vicat softening 230–238 (ISO 306)[2][3][5][25][6]
Continuous service temperature°CNot documented120 (Flashforge, IEC 60216, LUVOCOM PPA-CF)[4]
Annealing responseNot documentedBambu Lab anneals at 120–140 °C for 6–12 h; Raise3D at 80–100 °C for 8 h and warns of up to 0.5 % Z shrinkage. On Siraya Tech's grades annealing lifts HDT at 0.45 MPa from 84.5 to 192 °C while notched Charpy falls from 11 to 6.3 kJ/m²[2][3][5]
Thermal expansion (CTE)µm/m·K48.6 on extruded PA66-GF30 stock (ASTM D696; source states 2.7e-5 in/in/°F) — no figure is published for a glass-fibre PA12 filament[27]Not documented
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[20]Flammable; Bambu Lab lists water, carbon oxides and nitrogen oxides as combustion products. No UL 94 rating is published for the filament grades surveyed[2]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[18]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[18]Better than general nylon against weak acids, weak alkalis, most organic solvents and most oils and greases (Bambu Lab); not resistant to strong acids or strong alkalis[2]
Water / humidity resistance in service1–5Good — minor absorption relative to PA6-based composites[17]Good — minor absorption; 1.3 % saturated moisture is roughly half what PA6-CF takes up[2][24]
Food contactNot food-contact certified as filament[18]Not documented
Biodegradability / compostabilityNot biodegradable[18]Not documented
RecyclabilityNot accepted in household plastic collection[18]Not documented
Electrical & ESD propertiesSurface resistance above 10¹³ ohm/sq — insulating (ASTM D257)[1]Flashforge's data sheet gives a surface resistance of 10³ Ω or below (IEC 60093) for its LUVOCOM-based PPA-CF — the carbon loading makes it conductive rather than merely dissipative[4]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[28]Not documented
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[28]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[28]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[28]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[28]Not documented
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Chopped carbon fibre; dry sanding and cutting release respirable fibre-laden dust[29]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[19]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[19]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[19]Not documented
Support material pairingNot documentedBambu Lab pairs it with Support for PA/PET; Raise3D warns that PPA-CF used as its own support bonds permanently to the model once it takes up moisture, so supports must come off before annealing[2][3]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[30]Formic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[30]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[30]Zinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[30]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[30]None — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[30]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. FibreX PA12-GF30 Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  2. Bambu Filament Technical Data Sheet V1.0 — PPA-CF Bambu Lab · 2026-08 · tds
  3. Raise3D Industrial PPA CF Technical Data Sheet V2.0 Raise3D · 2022-04 · tds
  4. Flashforge PPA-CF Filament Technical Data Sheet (LUVOCOM PPA-CF, 10 % carbon fibre) Flashforge · 2026-08 · tds
  5. Siraya Tech Fibreheart PPA-CF Technical Data Sheet Siraya Tech · 2026-08 · tds
  6. IEMAI 3D CF-PPA Technical Data Sheet IEMAI 3D · 2025-04 · tds
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. IEMAI 3D GF-PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  9. PrimaCreator SELECT NylonPower Glass Fiber product page PrimaCreator · 2026-08 · vendor
  10. PPA-CF — Bambu Lab US Store Bambu Lab · 2026-08 · vendor
  11. Raise3D Industrial PPA CF Filament 1.75 mm (1 kg) — product listing MatterHackers · 2026-08 · vendor
  12. Fibreheart PPA-CF Filament — product page Siraya Tech · 2026-08 · vendor
  13. IEMAI 3D CF-PPA 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  14. CARBONX HTN+CF — product page 3DXTech · 2026-08 · vendor
  15. CHCKX PPA-CF 3D Printing Filament Matte Black 1 kg 1.75 mm 10 % Carbon Fiber — Amazon listing Amazon.com · 2026-08 · vendor
  16. Siraya Tech Fibreheart PPA-CF Core Filament — product page Siraya Tech · 2026-08 · vendor
  17. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  18. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  19. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  20. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  21. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  22. Fiberon PA12-CF10 Technical Data Sheet V1.1 Polymaker · 2025-02 · tds
  23. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  24. Bambu Filament Technical Data Sheet V3.0 — PA6-CF Bambu Lab · 2026-08 · tds
  25. Siraya Tech Fibreheart PPA-CF Core Technical Data Sheet Siraya Tech · 2026-08 · tds
  26. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  27. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  28. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  29. PET-CF / PPA-CF / PPS-CF / PA6-CF carbon fibre filament usage guide Bambu Lab Wiki · 2026-08 · doc
  30. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds