3D Printing Info

Filament comparison

PA12-CF vs POM

Compare printing settings, strength, heat resistance, dated prices and sources.

Carbon-fibre PA12 (PA12-CF) guidePOM (acetal) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA12-CF comparisonsMore POM comparisons
PA12-CF vs POM — documented properties and sources
PropertyCarbon-fibre PA12 (PA12-CF)PAPOM (acetal)ENGINEERING
Market snapshot
Listing priceUSD/kg; dated snapshots$109.98/kg median; $52.00–$180.00/kg across 4 dated product listingsNot documented
Identity & Market
Base polymer / chemistryPA12 reinforced with chopped carbon fibre — Polymaker's grade is 10 wt%[1][2]Polyoxymethylene, normally the copolymer POM-C. Apium's filament grade is POM-C with antistatic additives; no unfilled POM filament was found on sale[3][4]
Densityg/cm³1.06 (Polymaker Fiberon) and 1.16 (3DXTech), ISO 1183[1][2]1.41 (extruded POM-C stock)[3]
Typical priceUSD/kg1 kg-equivalent spools span 52–180; the middle of the market is about 110[5][6][7]Not documented
Price range across brandsUSD/kg52–180 across brands; IEMAI 3D 52, YXPOLYER 80 at 500 g, Polymaker Fiberon 140, 3DXTech CarbonX 180[5][6][8][7]Not documented
Market availability1–5Available from several mainstream brands[5][6]Special order, 1-2 makers worldwide — Apium sells a POM-C ESD filament through its own shop and states its printers are the only ones able to process POM-C; no POM filament appears in the 3DJAKE or igo3d product sitemaps, at MatterHackers or at Printed Solid[4][9][10][11]
Spool sizes & diameters1.75 mm; 0.5, 0.75 and 2 kg spools[5][6]Not documented
Typical applicationsStiff parts that must stay dimensionally stable in changing humidity — Polymaker sells this grade specifically on low moisture sensitivity[12][1]Gears, bushings, bearings, conveyor and food-machinery parts; Apium markets its POM-C ESD grade for semiconductor insulators, aerospace fasteners and sliding parts[3][4]
Printing Parameters
Nozzle temperature°C260–290 (Extrudr DURAPRO PA12 CF)[13]Not documented
Bed temperature°C110 (Extrudr DURAPRO PA12 CF)[13]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive)[14][1]Not documented
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[15][14]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s12 at Extrudr's 150 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[13][16]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[15]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[14]Not documented
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[14]Not documented
Extruder requirementNot documentedApium states that the adaptive heating system on its industrial machines is what makes POM-C printable, and that no other 3D printer can process it[4]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA12-CF10 and recommends hardened steel or ruby[1]Not documented
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA12-CF10[1]Not documented
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[17]Not documented
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[15]Not documented
Hotend requirementMay require an all-metal hot end (Simplify3D)[15]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — 1.5 % equilibrium, the lowest of Polymaker's nylon composites and less than half its PA6-GF25[1][18]Low (0.1-0.3 %) — extruded POM-C stock takes up 0.18 % in 24 h and 0.80 % at saturation (ASTM D570)[3]
Equilibrium moisture content at ~50 % RH%1.5 equilibrium water absorption (Polymaker Fiberon PA12-CF10)[1]Not documented
Drying temperature & time80–100 °C; storage below 20 % RH[17][1]Not documented
Effect of moisture on strengthPolymaker's own dry/wet blocks for PA12-CF10 change little: at 2.92 % moisture tensile falls 77.4 → 71.7 MPa and modulus 3311 → 3132 MPa, against a halving for its PA6 grades[1][12]Not documented
Storage requirementSealed below 20 % RH with desiccant[17]Not documented
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[19][20]Not documented
Mechanical Properties
Tensile strength (XY)MPa77.4 ± 1.1 printed XY dry (Polymaker Fiberon), 71.7 ± 0.7 conditioned to 2.92 % moisture, ISO 527; 3DXTech quotes 72 at break. Stratasys FDM Nylon 12CF spans 76.5-124 at break printed XZ across five machine and tip combinations (ASTM D638)[1][2][21]66.9 at break and 64.1 at yield (extruded POM-C stock, ASTM D638; converted from 9700 and 9300 psi)[3]
Young's modulusMPa3311 ± 135 printed XY dry and 3132 ± 124 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 8000. Stratasys FDM Nylon 12CF spans 7910-15400 printed XZ against 2130-3000 in ZX (ASTM D638)[1][2][21]2275 (extruded POM-C stock, ASTM D638; converted from 330,000 psi)[3]
Elongation at break%4.2 ± 0.4 printed XY dry and 5.3 ± 0.3 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 2.1 at break[1][2]40 at break and 9 at yield (extruded POM-C stock, ASTM D638)[3]
Flexural strengthMPa90 (printed XY, 3DXTech, ISO 178). Stratasys FDM Nylon 12CF spans 152-200 printed XZ against 61-73 in ZX (ASTM D790)[2][21]89.6 (extruded POM-C stock, ASTM D790; converted from 13,000 psi)[3]
Flexural modulusMPa7900 (printed XY, 3DXTech, ISO 178)[2]2758 (extruded POM-C stock, ASTM D790; converted from 400,000 psi)[3]
Charpy impact, notchedkJ/m²9.9 ± 0.7 printed XY dry and 10.2 ± 0.8 conditioned, ISO 179 notched (Polymaker Fiberon)[1]Not documented
Other impact dataIzod notched 102-138 J/m printed XZ against 22.4-45.5 J/m in ZX (Stratasys FDM Nylon 12CF, ASTM D256)[21]Izod 53 J/m on extruded POM-C stock, converted from 1.0 ft-lb/in[3]
Layer adhesion / Z tensileMPa52.2 ± 0.8 printed Z dry (Polymaker Fiberon) — 67 % of XY, unusually isotropic for a filled nylon; 42.1 ± 1.8 conditioned. Stratasys FDM Nylon 12CF gives 32.7-38.4 at break printed ZX (ASTM D638)[1][21]Not documented
Brittleness1–5Moderate[1]Tough — absorbs impact, yields before breaking; extruded stock elongates 40 % before failing. No printed figure is published[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre PA12 filament[22]Rockwell 86 (and R120) — the source names only the R scale on extruded POM-C stock (ASTM D785)[3]
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load at 110 °C continuous service; the PA12 matrix takes up 1.5 % equilibrium moisture against PA6's several per cent, so a PA12-CF part drifts less in service[23][1]Not documented
Fatigue / repeated-flex resistance1–5Good. Stratasys sells unfilled FDM Nylon 12 specifically for repetitive-flex parts on the strength of its fatigue properties, and Ensinger reports improved fatigue strength for carbon-filled nylon compounds[23]Not documented
Elasticity / flexibility1–5Rigid[1]Not documented
Z strength as % of XY%31-50 (Stratasys FDM Nylon 12CF, ZX against XZ tensile at break, ASTM D638, five machine and tip combinations) against 67 (Polymaker Fiberon PA12-CF10, printed Z against XY)[1][21]Not documented
Wear resistance & frictionNot documentedWear factor 65e-10 in3*min/(ft*lb*h) and a dynamic coefficient of friction of 0.21 at 40 psi and 50 fpm (ASTM D3702, extruded stock) — the properties that make acetal the default gear and bushing plastic; Apium lists good sliding properties as the reason for its grade[3][4]
Thermal Properties
HDT at 0.45 MPa°C131 (ISO 75, 0.45 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 160 printed XY and 168 ZX, and 175 with unidirectional toolpaths (ASTM D648 at 66 psi)[1][21]158 (extruded POM-C stock, ASTM D648 at 66 psi; converted from 316 °F)[3]
HDT at 1.8 MPa°C105 (ISO 75, 1.8 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 130 printed XY and 154 ZX (ASTM D648 at 264 psi)[1][21]110 (extruded POM-C stock, ASTM D648 at 264 psi; converted from 230 °F)[3]
Glass transition (Tg)°C55 (DSC, Polymaker Fiberon)[1]Not documented
Melting point / Vicat°C171 melting (DSC); Vicat 170.2 (ISO 306)[1]165 melting (extruded POM-C stock; converted from 329 °F)[3]
Continuous service temperature°CNot documented91 long term and 141 intermittent (extruded POM-C stock; converted from 195 °F and 285 °F)[3]
Thermal expansion (CTE)µm/m·KStratasys FDM Nylon 12CF gives 116 on XY-built and 37 on ZX-built specimens over -50 to 20 °C, rising to 181 (XY) and 46 (ZX) above the 37.5 °C glass transition (ASTM E831); Extrudr quotes 100 for DURAPRO PA12 CF (ISO 11359-2)[13][21]84.6 (extruded POM-C stock, ASTM D696; source states 4.7e-5 in/in/°F)[3]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[19]UL 94 HB on extruded POM-C stock[3]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[14]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[14]Good chemical resistance, particularly to bases; Apium lists resistance to bases as a headline property[3][4]
Water / humidity resistance in service1–5Good — minor absorption; the most humidity-stable nylon composite here[12][1]Good — minor absorption; 0.80 % water at saturation (ASTM D570, extruded stock)[3]
Food contactNot food-contact certified as filament[14]Not documented
Biodegradability / compostabilityNot biodegradable[14]Not documented
RecyclabilityNot accepted in household plastic collection[14]Not documented
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker Fiberon, ANSI/ESD S11.11)[1]Volume resistance 1e14 ohm-cm, dielectric strength 500 V/mil and dielectric constant 3.7 at 60 Hz on extruded stock (ASTM D257, D149, D150); Apium's filament grade adds antistatic agents[3][4]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[24]Not documented
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[24]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[24]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[24]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[24]Not documented
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[19]Not documented
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[15]Easy to machine — Ensinger lists machinability as a headline property of POM-C stock[3]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[15]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[15]Not documented
Dimensional accuracy & detailPolymaker's own conditioning test found PA12-CF10 was the only nylon that did not grow past its original size after moisture conditioning[12]Not documented
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[25]Hexafluoroisopropanol dissolves it at room temperature; NMP and DMF only when hot. Laboratory reagents.[26]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[25]Acids, oxidants, halogens and hot concentrated zinc chloride attack it; alcohols, ketones and esters do not.[26][27]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[25]None — no solvent softens POM below its melting point, which is why it is bolted or heat-welded rather than glued.[26]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA12-CF10 Technical Data Sheet V1.1 Polymaker · 2025-02 · tds
  2. CarbonX CF PA12 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  3. TECAFORM AH natural (POM-C) — stock shape properties Ensinger · 2026-08 · tds
  4. POM-C ESD 3D printing — material page Apium 3D Technologies · 2026-08 · doc
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. IEMAI 3D CF-PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  8. YXPOLYER PA12 CF 500 g — product page YXPOLYER · 2026-08 · vendor
  9. 3DJAKE product catalogue 3DJAKE · 2026-08 · vendor
  10. igo3d product sitemap (17452 product URLs) igo3d · 2026-08 · vendor
  11. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  12. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  13. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  14. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  15. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  18. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  19. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  20. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  21. FDM Nylon 12CF — Material Data Sheet Stratasys · 2025-09 · tds
  22. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  23. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  24. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  25. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  26. Resistance of Ultramid, Ultraform and Ultradur to chemicals (TI-KTU/AS-28 e) BASF · 2000-10 · tds
  27. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds