PA12-CF vs PLA-GF

Compare printing settings, strength, heat resistance, dated prices and sources.

Carbon-fibre PA12 (PA12-CF) guideGlass-fibre PLA (PLA-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA12-CF comparisonsMore PLA-GF comparisons
PA12-CF vs PLA-GF — documented properties and sources
PropertyCarbon-fibre PA12 (PA12-CF)PAGlass-fibre PLA (PLA-GF)PLA
Market snapshot
Listing priceUSD/kg; dated snapshots$109.98/kg median; $52.00–$180.00/kg across 4 dated product listings$44.99/kg median; $29.99–$59.99/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryPA12 reinforced with chopped carbon fibre — Polymaker's grade is 10 wt%[1][2]PLA filled with chopped glass fibre — 12 wt% (Polymaker HT-PLA-GF), 15–20 wt% (eSUN PLA-GF). Bambu Lab PLA Galaxy uses glass microspheres, not fibre, and is not equivalent[3][4][5]
Densityg/cm³1.06 (Polymaker Fiberon) and 1.16 (3DXTech), ISO 1183[1][2]1.31 (eSUN) to 1.337 (Polymaker), ISO 1183 / GB/T 1033[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 52–180; the middle of the market is about 110[6][7][8]1 kg spools cluster near 30[9][10]
Price range across brandsUSD/kg52–180 across brands; IEMAI 3D 52, YXPOLYER 80 at 500 g, Polymaker Fiberon 140, 3DXTech CarbonX 180[6][7][11][8]30–60 across brands; Polymaker 30, Proto-pasta 60[9][10]
Market availability1–5Available from several mainstream brands[6][7]Niche, a handful of specialist brands[9][10][4]
Spool sizes & diameters1.75 mm; 0.5, 0.75 and 2 kg spools[6][7]1.75 mm; 0.5 and 1 kg spools[10][6]
Typical applicationsStiff parts that must stay dimensionally stable in changing humidity — Polymaker sells this grade specifically on low moisture sensitivity[12][1]Stiff brackets and fixtures; the Polymaker grade is aimed at parts annealed for heat resistance[3]
Printing Parameters
Nozzle temperature°C260–290 (Extrudr DURAPRO PA12 CF)[13]210–230 (Polymaker HT-PLA-GF)[3]
Bed temperature°C110 (Extrudr DURAPRO PA12 CF)[13]25–60 (Polymaker HT-PLA-GF)[3]
Enclosure / chamber requirement1–5Enclosure required (passive)[14][1]Open frame is fine[3]
Part cooling fanNot documentedFan on — eSUN specifies 100 %[4]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[15][14]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s12 at Extrudr's 150 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[13][16]28 at Polymaker's stated 350 mm/s on a 0.4 mm nozzle at 0.2 mm layer; eSUN prints its specimens at 60 mm/s[3][4][16]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[15]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[14]Not documented
Shrinkage%Not documented0.05 in X-Y and Z, 0.10 diagonal (Polymaker HT-PLA-GF)[3]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[14]Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA12-CF10 and recommends hardened steel or ruby[1]Hardened steel required[3]
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA12-CF10[1]Highly abrasive — standard GF composite[3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[17]Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[18]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[15]Not documented
Hotend requirementMay require an all-metal hot end (Simplify3D)[15]Hardened steel or ruby nozzle; Polymaker's own slicer preset sets a minimum nozzle hardness of 40 HRC[3]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — 1.5 % equilibrium, the lowest of Polymaker's nylon composites and less than half its PA6-GF25[1][19]Moderate — the PLA matrix takes up 0.40–0.51 % saturated; no glass-filled grade publishes its own figure[20][21]
Equilibrium moisture content at ~50 % RH%1.5 equilibrium water absorption (Polymaker Fiberon PA12-CF10)[1]Not documented
Drying temperature & time80–100 °C; storage below 20 % RH[17][1]60 °C for 6 h (Polymaker HT-PLA-GF)[3]
Effect of moisture on strengthPolymaker's own dry/wet blocks for PA12-CF10 change little: at 2.92 % moisture tensile falls 77.4 → 71.7 MPa and modulus 3311 → 3132 MPa, against a halving for its PA6 grades[1][12]Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[17]
Storage requirementSealed below 20 % RH with desiccant[17]Not documented
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[22][23]Not documented
Mechanical Properties
Tensile strength (XY)MPa77.4 ± 1.1 printed XY dry (Polymaker Fiberon), 71.7 ± 0.7 conditioned to 2.92 % moisture, ISO 527; 3DXTech quotes 72 at break. Stratasys FDM Nylon 12CF spans 76.5-124 at break printed XZ across five machine and tip combinations (ASTM D638)[1][2][24]50.1 as printed and 50.2 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 59.3 by GB/T 1040[3][4]
Young's modulusMPa3311 ± 135 printed XY dry and 3132 ± 124 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 8000. Stratasys FDM Nylon 12CF spans 7910-15400 printed XZ against 2130-3000 in ZX (ASTM D638)[1][2][24]3794 as printed, 4207 annealed, printed XY, ISO 527 (Polymaker)[3]
Elongation at break%4.2 ± 0.4 printed XY dry and 5.3 ± 0.3 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 2.1 at break[1][2]2.77 as printed, 2.3 annealed, printed XY, ISO 527 (Polymaker); eSUN quotes 7.99[3][4]
Flexural strengthMPa90 (printed XY, 3DXTech, ISO 178). Stratasys FDM Nylon 12CF spans 152-200 printed XZ against 61-73 in ZX (ASTM D790)[2][24]86.4 printed XY, ISO 178 (Polymaker)[3]
Flexural modulusMPa7900 (printed XY, 3DXTech, ISO 178)[2]3685 printed XY, ISO 178 (Polymaker); eSUN quotes 4415 flexural modulus by GB/T 9341[3][4]
Charpy impact, notchedkJ/m²9.9 ± 0.7 printed XY dry and 10.2 ± 0.8 conditioned, ISO 179 notched (Polymaker Fiberon)[1]5.31 ± 0.46 as printed and 4.92 ± 0.50 annealed (printed XY, ISO 179, notched); Z 4.28 ± 0.18[3]
Other impact dataIzod notched 102-138 J/m printed XZ against 22.4-45.5 J/m in ZX (Stratasys FDM Nylon 12CF, ASTM D256)[24]Izod 10.16 kJ/m² (eSUN, GB/T 1843)[4]
Layer adhesion / Z tensileMPa52.2 ± 0.8 printed Z dry (Polymaker Fiberon) — 67 % of XY, unusually isotropic for a filled nylon; 42.1 ± 1.8 conditioned. Stratasys FDM Nylon 12CF gives 32.7-38.4 at break printed ZX (ASTM D638)[1][24]23.7 as printed, 22.5 annealed, printed Z, ISO 527 (Polymaker)[3]
Brittleness1–5Moderate[1]Very brittle — elongation at break 2.77 % in XY and 0.85 % in Z[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre PA12 filament[25]Not documented
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load at 110 °C continuous service; the PA12 matrix takes up 1.5 % equilibrium moisture against PA6's several per cent, so a PA12-CF part drifts less in service[26][1]Poor — no GF-grade creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[27][28][29]
Fatigue / repeated-flex resistance1–5Good. Stratasys sells unfilled FDM Nylon 12 specifically for repetitive-flex parts on the strength of its fatigue properties, and Ensinger reports improved fatigue strength for carbon-filled nylon compounds[26]Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and elongation at break falls to 2.77 % in XY and 0.85 % in Z[30][3]
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%31-50 (Stratasys FDM Nylon 12CF, ZX against XZ tensile at break, ASTM D638, five machine and tip combinations) against 67 (Polymaker Fiberon PA12-CF10, printed Z against XY)[1][24]47 as printed (23.7 Z against 50.1 XY), printed[3]
Wear resistance & frictionNot documentedeSUN describes high wear resistance and positions the grade for wear parts[4]
Thermal Properties
HDT at 0.45 MPa°C131 (ISO 75, 0.45 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 160 printed XY and 168 ZX, and 175 with unidirectional toolpaths (ASTM D648 at 66 psi)[1][24]75.5 as printed, 114.7 after annealing (ISO 75, 0.45 MPa) — the point of the material[3]
HDT at 1.8 MPa°C105 (ISO 75, 1.8 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 130 printed XY and 154 ZX (ASTM D648 at 264 psi)[1][24]59.7 as printed, 84 after annealing (ISO 75, 1.8 MPa)[3]
Glass transition (Tg)°C55 (DSC, Polymaker Fiberon)[1]59.8 (DSC)[3]
Melting point / Vicat°C171 melting (DSC); Vicat 170.2 (ISO 306)[1]174.9 peak melt (DSC); Vicat 148.9 as printed, 148.3 annealed[3]
Annealing responseNot documentedAnnealing lifts HDT at 0.45 MPa from 75.5 to 114.7 °C and modulus from 3794 to 4207 MPa[3]
Thermal expansion (CTE)µm/m·KStratasys FDM Nylon 12CF gives 116 on XY-built and 37 on ZX-built specimens over -50 to 20 °C, rising to 181 (XY) and 46 (ZX) above the 37.5 °C glass transition (ASTM E831); Extrudr quotes 100 for DURAPRO PA12 CF (ISO 11359-2)[13][24]Not documented
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[22]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[14]Degrades within weeks outdoors[31]
Chemical resistanceWithstands oils, fuels and alkalis[14]Not documented
Water / humidity resistance in service1–5Good — minor absorption; the most humidity-stable nylon composite here[12][1]Not documented
Food contactNot food-contact certified as filament[14]Not documented
Biodegradability / compostabilityNot biodegradable[14]Not documented
RecyclabilityNot accepted in household plastic collection[14]Not documented
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker Fiberon, ANSI/ESD S11.11)[1]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[32]Low hazard — minimal VOC and particle emission[32]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[32]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[32]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[32]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[32]None needed in a normal room[32]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[22]Glass fibre is bound in the matrix; avoid inhaling sanding dust[33]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[15]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[15]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[15]Not documented
Dimensional accuracy & detailPolymaker's own conditioning test found PA12-CF10 was the only nylon that did not grow past its original size after moisture conditioning[12]Near-zero shrinkage — 0.05 % in X-Y and Z (Polymaker)[3]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[34]Chloroform dissolves the PLA matrix (10 % w/v, 2–4 h at 23 °C) and leaves the filler as loose sludge; laboratory reagent.[35]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[34]Acetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[35][36]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[34]Chloroform vapour attacks only the resin fraction, so the filler is left standing proud; no workshop-safe agent exists.[37][36]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA12-CF10 Technical Data Sheet V1.1 Polymaker · 2025-02 · tds
  2. CarbonX CF PA12 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  3. Polymaker HT-PLA-GF Technical Data Sheet V1.1 Polymaker · 2026-08 · tds
  4. eSUN ePLA-GF Technical Data Sheet V1.0 (Nov 2023) eSUN (copy hosted on 3d.nice-cdn.com) · 2023-11 · tds
  5. Bambu Filament Technical Data Sheet V1.0 — PLA Galaxy Bambu Lab · 2026-08 · tds
  6. Polymaker product catalogue Polymaker · 2026-08 · vendor
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. IEMAI 3D CF-PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  9. Polymaker HT-PLA-GF — product page Polymaker Shop · 2026-08 · vendor
  10. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  11. YXPOLYER PA12 CF 500 g — product page YXPOLYER · 2026-08 · vendor
  12. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  13. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  14. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  15. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  18. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  19. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  20. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  21. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  22. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  23. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  24. FDM Nylon 12CF — Material Data Sheet Stratasys · 2025-09 · tds
  25. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  26. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  27. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  28. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  29. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  30. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  31. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  32. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  33. StoneFil safety data sheet Formfutura · 2026-08 · msds
  34. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  35. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  36. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  37. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper