3D Printing Info

Filament comparison

PA12-CF vs PC-ESD

Compare printing settings, strength, heat resistance, dated prices and sources.

Carbon-fibre PA12 (PA12-CF) guideESD-safe PC guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA12-CF comparisonsMore PC-ESD comparisons
PA12-CF vs PC-ESD — documented properties and sources
PropertyCarbon-fibre PA12 (PA12-CF)PAESD-safe PCPC
Market snapshot
Listing priceUSD/kg; dated snapshots$109.98/kg median; $52.00–$180.00/kg across 4 dated product listings$180.00/kg median; $180.00–$180.00/kg across 1 dated product listings
Identity & Market
Base polymer / chemistryPA12 reinforced with chopped carbon fibre — Polymaker's grade is 10 wt%[1][2]Polycarbonate compounded with a conductive filler for static-dissipative parts[3]
Densityg/cm³1.06 (Polymaker Fiberon) and 1.16 (3DXTech), ISO 1183[1][2]1.24 (ISO 1183, 3DXTech); Stratasys specific gravity 1.195 (ASTM D792)[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 52–180; the middle of the market is about 110[5][6][7]1 kg-equivalent spools cluster near 180[6]
Price range across brandsUSD/kg52–180 across brands; IEMAI 3D 52, YXPOLYER 80 at 500 g, Polymaker Fiberon 140, 3DXTech CarbonX 180[5][6][8][7]180 at 3DXTech's 750 g pricing — the most expensive material in this group[6]
Market availability1–5Available from several mainstream brands[5][6]Special order, 1–2 makers worldwide[6]
Spool sizes & diameters1.75 mm; 0.5, 0.75 and 2 kg spools[5][6]1.75 and 2.85 mm; 750 g spools plus Stratasys-compatible cartridges[6]
Typical applicationsStiff parts that must stay dimensionally stable in changing humidity — Polymaker sells this grade specifically on low moisture sensitivity[9][1]Electronics fixtures and trays that need PC heat resistance and static dissipation together[3]
Printing Parameters
Nozzle temperature°C260–290 (Extrudr DURAPRO PA12 CF)[10]Not documented
Bed temperature°C110 (Extrudr DURAPRO PA12 CF)[10]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive)[11][1]Enclosure required (passive)[12][13]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[14][11]PEI with a glue stick or a commercial adhesive[15]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s12 at Extrudr's 150 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[10][16]Not documented
Warping tendency1–5Not documentedSevere — heated chamber needed[12][13]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[14]Needs a specific surface plus adhesive[15][17]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[11]Moderate — retraction tuning needed; Polymaker flags stringing as a common PC problem[17]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[11]Advanced — enclosure, hardware upgrades, tuning[12]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA12-CF10 and recommends hardened steel or ruby[1]Hardened steel required[3]
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA12-CF10[1]Moderately abrasive — conductive carbon filler[3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[18]Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a 120 °C pre-dry[19]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[14]Slightly sensitive[15]
Hotend requirementMay require an all-metal hot end (Simplify3D)[14]All-metal hot end required (Simplify3D)[15]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — 1.5 % equilibrium, the lowest of Polymaker's nylon composites and less than half its PA6-GF25[1][20]Low (0.1–0.3 %) — the PC matrix takes up 0.15–0.25 % and 3DXTech specifies a 120 °C, 4 h pre-dry[21][22][19]
Equilibrium moisture content at ~50 % RH%1.5 equilibrium water absorption (Polymaker Fiberon PA12-CF10)[1]Not documented
Drying temperature & time80–100 °C; storage below 20 % RH[18][1]Not documented
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing and a rough surface[18]
Effect of moisture on strengthPolymaker's own dry/wet blocks for PA12-CF10 change little: at 2.92 % moisture tensile falls 77.4 → 71.7 MPa and modulus 3311 → 3132 MPa, against a halving for its PA6 grades[1][9]No dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic and requires a 70–80 °C dry for 6–8 h; run wet, the loss shows as surface defects and poor layer adhesion[17][18]
Storage requirementSealed below 20 % RH with desiccant[18]Airtight containers with desiccant to prevent reabsorption[17]
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[23][24]Not documented
Mechanical Properties
Tensile strength (XY)MPa77.4 ± 1.1 printed XY dry (Polymaker Fiberon), 71.7 ± 0.7 conditioned to 2.92 % moisture, ISO 527; 3DXTech quotes 72 at break. Stratasys FDM Nylon 12CF spans 76.5-124 at break printed XZ across five machine and tip combinations (ASTM D638)[1][2][25]68 at break (printed XY, ISO 527, 3DXTech) — above the 58 of 3DXTech's unfilled ezPC; Stratasys prints 47.6-49.4 at yield in XZ (ASTM D638)[3][26][4]
Young's modulusMPa3311 ± 135 printed XY dry and 3132 ± 124 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 8000. Stratasys FDM Nylon 12CF spans 7910-15400 printed XZ against 2130-3000 in ZX (ASTM D638)[1][2][25]2300 (printed XY, ISO 527); Stratasys prints 1960 in XZ and 1810-1910 in ZX (ASTM D638)[3][4]
Elongation at break%4.2 ± 0.4 printed XY dry and 5.3 ± 0.3 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 2.1 at break[1][2]6 at break (printed XY, ISO 527), against 14 for the unfilled grade[3][26]
Flexural strengthMPa90 (printed XY, 3DXTech, ISO 178). Stratasys FDM Nylon 12CF spans 152-200 printed XZ against 61-73 in ZX (ASTM D790)[2][25]95 (printed XY, ISO 178); Stratasys prints 82.6-83.2 at break in XZ against 46.3-49.5 in ZX (ASTM D790)[3][4]
Flexural modulusMPa7900 (printed XY, 3DXTech, ISO 178)[2]2310 (printed XY, ISO 178)[3]
Charpy impact, notchedkJ/m²9.9 ± 0.7 printed XY dry and 10.2 ± 0.8 conditioned, ISO 179 notched (Polymaker Fiberon)[1]Not documented
Other impact dataIzod notched 102-138 J/m printed XZ against 22.4-45.5 J/m in ZX (Stratasys FDM Nylon 12CF, ASTM D256)[25]Not documented
Layer adhesion / Z tensileMPa52.2 ± 0.8 printed Z dry (Polymaker Fiberon) — 67 % of XY, unusually isotropic for a filled nylon; 42.1 ± 1.8 conditioned. Stratasys FDM Nylon 12CF gives 32.7-38.4 at break printed ZX (ASTM D638)[1][25]32.5-37.9 at yield printed ZX (Stratasys, ASTM D638 on the Fortus 450mc and F900)[4]
Brittleness1–5Moderate[1]Moderate[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre PA12 filament[27]Rockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for an ESD grade[28]
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load at 110 °C continuous service; the PA12 matrix takes up 1.5 % equilibrium moisture against PA6's several per cent, so a PA12-CF part drifts less in service[29][1]Excellent — holds load for years. Moulded unfilled PC was still running unbroken under 41 MPa tensile creep at room temperature when the test was stopped, and the conductive filler leaves the glass transition unchanged at 142 °C, so the creep mechanism is polycarbonate's[30][4]
Fatigue / repeated-flex resistance1–5Good. Stratasys sells unfilled FDM Nylon 12 specifically for repetitive-flex parts on the strength of its fatigue properties, and Ensinger reports improved fatigue strength for carbon-filled nylon compounds[29]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[3]
Z strength as % of XY%31-50 (Stratasys FDM Nylon 12CF, ZX against XZ tensile at break, ASTM D638, five machine and tip combinations) against 67 (Polymaker Fiberon PA12-CF10, printed Z against XY)[1][25]68-77 (Stratasys ZX against XZ tensile yield, ASTM D638)[4]
Thermal Properties
HDT at 0.45 MPa°C131 (ISO 75, 0.45 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 160 printed XY and 168 ZX, and 175 with unidirectional toolpaths (ASTM D648 at 66 psi)[1][25]143-146 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 66 psi); 135 moulded[4]
HDT at 1.8 MPa°C105 (ISO 75, 1.8 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 130 printed XY and 154 ZX (ASTM D648 at 264 psi)[1][25]140-144 printed in XY, XZ and ZX (Stratasys, ASTM D648 Method B at 264 psi); 124 moulded[4]
Glass transition (Tg)°C55 (DSC, Polymaker Fiberon)[1]143 (DSC, 3DXTech) and 142 (Stratasys, ASTM D7426)[3][4]
Melting point / Vicat°C171 melting (DSC); Vicat 170.2 (ISO 306)[1]Not documented
Continuous service temperature°CNot documented113 — Prusa publishes this as the temperature resistance of Prusament PC Blend[22]
Thermal expansion (CTE)µm/m·KStratasys FDM Nylon 12CF gives 116 on XY-built and 37 on ZX-built specimens over -50 to 20 °C, rising to 181 (XY) and 46 (ZX) above the 37.5 °C glass transition (ASTM E831); Extrudr quotes 100 for DURAPRO PA12 CF (ISO 11359-2)[10][25]68.4 on extruded unfilled PC stock (ASTM D696; source states 3.8e-5 in/in/°F); no figure is published for a conductive-filled grade[28]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[23]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[11]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[11]Withstands oils, solvents and fuels; Polymaker rates it good against weak acids[17]
Water / humidity resistance in service1–5Good — minor absorption; the most humidity-stable nylon composite here[9][1]Not documented
Food contactNot food-contact certified as filament[11]Bisphenol-A polycarbonate is not offered as food-contact filament[17]
Biodegradability / compostabilityNot biodegradable[11]Not biodegradable[17]
RecyclabilityNot accepted in household plastic collection[11]Mechanically recyclable but not accepted in household plastic collection[17]
Electrical & ESD propertiesSurface resistivity above 10¹² ohm — insulating (Polymaker Fiberon, ANSI/ESD S11.11)[1]Surface resistance 10⁷–10⁹ ohm/sq, the static-dissipative band (ASTM D257), against above 10¹³ for unfilled ezPC[3][26]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[31]Moderate — measurable VOCs and UFPs, ventilation advised[31]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[31]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[31]≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[31]
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[31]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[31]Ventilated room or enclosure recommended[31][12]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[23]Conductive carbon filler is bound in the matrix; avoid inhaling sanding dust[3]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[14]Sands and machines well; the toughness means it cuts rather than chips[15]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[14]Cyanoacrylate; dichloromethane solvent-welds PC but is a laboratory reagent[15]
Vapour / chemical smoothingNo practical vapour smoothing[14]No practical vapour smoothing[15]
Support material pairingNot documentedPrints its own supports; 3DXTech sells a dedicated PC break-away support[15]
Dimensional accuracy & detailPolymaker's own conditioning test found PA12-CF10 was the only nylon that did not grow past its original size after moisture conditioning[9]Not documented
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[32]Dichloromethane, chloroform, DMF and dioxane dissolve it outright (Covestro, 6 days at 23 °C). Laboratory reagents.[33]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[32]Methanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[33]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[32]Dichloromethane cement welds PC — 16.5 MPa lap shear at one week (IPS Weld-On 3). A controlled carcinogen.[34]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA12-CF10 Technical Data Sheet V1.1 Polymaker · 2025-02 · tds
  2. CarbonX CF PA12 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  3. 3DXSTAT ESD-PC Technical Data Sheet 3DXTech · 2026-08 · tds
  4. PC-ESD — FDM Material Data Sheet Stratasys · 2024-10 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. IEMAI 3D CF-PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  8. YXPOLYER PA12 CF 500 g — product page YXPOLYER · 2026-08 · vendor
  9. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  10. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  11. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  12. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  13. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  14. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  15. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. PC — material basics Polymaker Wiki · 2026-08 · doc
  18. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  19. 3DXSTAT ESD-PC — product page (print recommendations) 3DXTech · 2026-08 · doc
  20. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  21. Bambu Filament Technical Data Sheet V2.0 — PC Bambu Lab · 2026-08 · tds
  22. Prusament PC Blend Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  23. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  24. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  25. FDM Nylon 12CF — Material Data Sheet Stratasys · 2025-09 · tds
  26. ezPC Polycarbonate Technical Data Sheet 3DXTech · 2026-08 · tds
  27. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  28. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  29. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  30. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  31. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  32. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  33. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  34. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds