3D Printing Info

Filament comparison

PA-CF ESD vs TPU 95A

Compare printing settings, strength, heat resistance, dated prices and sources.

ESD-safe CF nylon guideTPU 95A guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA-CF ESD comparisonsMore TPU 95A comparisons
PA-CF ESD vs TPU 95A — documented properties and sources
PropertyESD-safe CF nylonPATPU 95AFLEX
Market snapshot
Listing priceUSD/kg; dated snapshots$129.98/kg median; $129.98–$129.98/kg across 1 dated product listings$39.99/kg median; $23.00–$106.05/kg across 15 dated product listings
Identity & Market
Base polymer / chemistryCarbon-filled polyamide compounded to a static-dissipative resistivity — Polymaker's grade uses a PA612 matrix[1]Thermoplastic polyurethane, polyester or polyether based, at about 92–95 Shore A[2][3]
Densityg/cm³1.10 (ISO 1183)[1]1.20–1.25 (ISO 1183); Prusament 1.25, Polymaker 1.20–1.24, Bambu Lab 1.22[2][3][4]
Typical priceUSD/kg1 kg-equivalent spools cluster near 130[5]1 kg spools cluster near 35; the specialist and industrial brands run to 106[5][6][4][7][8][9]
Price range across brandsUSD/kg130 at Polymaker's 0.5 kg pricing[5]23–106 across brands; IEMAI 3D 23, LANDU 24, Siraya Tech 25, PS Imports 25, PrimaCreator 32, Bambu Lab 35–42, Polymaker 40–50, add:north 72, Recreus 90, 3DXTech 96, NinjaTek Cheetah 106[6][10][5][11][7][8][12][13][14][9]
Market availability1–5Special order, 1–2 makers worldwide[5]Ubiquitous, every brand and retailer[5][11][6][10][7][8]
Spool sizes & diameters1.75 mm; 0.5 kg spools[5]1.75 and 2.85 mm; 0.5, 0.75 and 1 kg spools[5][11]
Typical applicationsElectronics jigs and trays that also need nylon toughness and heat resistance[1]Gaskets, phone cases, tyres, vibration mounts and protective covers[15]
Diameter tolerance± mmNot documented±0.06 (Prusament) — the loosest tolerance Prusa publishes, because soft filament deforms in the gauge[3]
Printing Parameters
Nozzle temperature°CNot documented210–240; Polymaker 210–230, Prusament 230 ± 10, Bambu Lab HF 220–240[2][3][4]
Bed temperature°CNot documented25–65; Prusament 65 ± 10, Bambu Lab 30–35, Polymaker 25–60[3][4][2]
Enclosure / chamber requirement1–5Enclosure required (passive)[16]Open frame is fine[2]
Part cooling fanNot documentedFan on[2][4]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[17][16]PEI sheet or painter's tape; Polymaker warns TPU can over-stick and advises a glue stick as a release agent[18][15]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented2.4 at Polymaker's 30–50 mm/s and 2.4 at Prusa's 30 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer; Bambu Lab's high-flow grade lifts the cap to 200 mm/s (16 mm³/s)[2][3][4]
Warping tendency1–5Not documentedNone[2]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[17]Sticks to most surfaces[2]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[16]Moderate — retraction tuning needed; Polymaker specifies 3–6 mm retraction, well above the 1–3 mm used for rigid filaments[2]
Overall printing difficulty1–5Expert / industrial hardware only[16][19]Intermediate — dry filament and a tuned profile; the speed ceiling is the main constraint[2][3]
Extruder requirementNot documentedDirect drive strongly preferred. BASF rates its 95A grade as running on both direct-drive and Bowden machines, but every maker caps speed at 15–50 mm/s unless the grade is specifically high-flow[20][2][3]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-ESD and recommends hardened steel or ruby[1]Brass fine indefinitely[21]
Abrasiveness1–5Highly abrasive — carbon-filled nylon composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-ESD[1]Non-abrasive[21]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[19]Moderate — needs dry filament and a clean nozzle[19]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[17]High — all-metal hotend and strong cooling needed; soft filament buckles in the cold zone if it slows[15]
Hotend requirementMay require an all-metal hot end (Simplify3D)[17]No special hot-end required, but a direct-drive extruder is (Simplify3D)[18]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — the PA612 matrix sits between PA6 and PA12[22][23]Low (0.1–0.3 %) by Prusa's measurement at 0.04 % in 7 days, but Polymaker measures 0.82 % equilibrium and groups TPU with the highly hygroscopic materials[3][2][19]
Equilibrium moisture content at ~50 % RH%Not documented0.82 equilibrium (Polymaker); 0.02 after 24 h and 0.04 after 7 days at 22 % RH (Prusa)[2][3]
Drying temperature & timeNot documented70 °C for 8 h (Polymaker); 70 °C for 8 h or an 80–90 °C heatbed for 12 h (Bambu Lab)[2][4]
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing, rough surface and weak layers[19]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA612-ESD itself: at 4.64 % moisture tensile falls 84.3 → 73.6 MPa and modulus 4294 → 3731 MPa[1][23]Polymaker groups TPU with nylon, PVA and PETG as highly hygroscopic and says these often need to stay in a dryer while printing; no dry-versus-conditioned figures are published[19]
Storage requirementSealed below 20 % RH with desiccant[19]Sealed with desiccant; often kept in a dryer during the print[19]
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[24][25]Not documented
Mechanical Properties
Tensile strength (XY)MPa84.3 ± 2.3 printed XY dry (annealed 100 °C/16 h), 73.6 ± 2.3 conditioned to 4.64 % moisture, ISO 527[1]41.4 ± 1.3 printed (Prusament, ISO 37); NinjaTek Cheetah 39 ultimate (ASTM D638)[3][26]
Young's modulusMPa4293.7 ± 116.4 printed XY dry and 3730.8 ± 156.2 conditioned, ISO 527[1]Not documented
Elongation at break%3.0 ± 0.1 printed XY dry and 4.2 ± 0.4 conditioned, ISO 527[1]551 ± 24 printed (Polymaker, ISO 37); the filament itself stretches 7264 % before break (Prusa, ISO 527)[2][3]
Charpy impact, notchedkJ/m²5.9 ± 0.4 printed XY dry and 4.9 ± 0.3 conditioned, ISO 179 notched[1]Not documented
Other impact dataCharpy unnotched 24.1 ± 2.4 printed XY and 4.5 ± 0.2 printed Z (ISO 179)[1]Not documented
Layer adhesion / Z tensileMPa21.5 ± 2.7 printed Z dry — only a quarter of XY, the most anisotropic nylon composite here; 19.2 ± 1.6 conditioned[1]9.5 ± 0.2 (Prusament interlayer adhesion, ISO 527)[3]
Brittleness1–5Brittle — snaps with little warning; elongation 3.0 % in XY and 1.4 % in Z[1]Very ductile — bends far before failing[2][3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a conductive carbon-filled nylon filament[27]92 ± 0.4 Shore A and 39 ± 0.7 Shore D (Prusament); 95A (Polymaker, ISO 7619-1); 91 Shore A / 40 Shore D (Fiberlogy FiberFlex 40D, ISO 7619); 95A (NinjaTek Cheetah, ASTM D2240); 94.5 A measured on a printed Bambu Lab 95A part and 96.2 A on a Qidi one (My Tech Fun)[3][2][28][26][29]
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load at 110 °C continuous service; the PA612 matrix here still takes up 4.64 % moisture at conditioning, which softens it[30][1]Poor — deforms under load at room temperature; a loaded bar crept from 74.5 to 82.7 mm over 5 days[29]
Fatigue / repeated-flex resistance1–5Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[30]Excellent — living hinges viable[15]
Elasticity / flexibility1–5Rigid[1]Rubbery / highly elastic[2][3]
Z strength as % of XY%26 (printed Z against XY tensile)[1]Not documented
Wear resistance & frictionNot documentedAbrasion resistance is a headline property; BASF measures 64 mm³ loss by ISO 4649 on its 92A grade[20]
Thermal Properties
HDT at 0.45 MPa°C157.0 (ISO 75, 0.45 MPa)[1]Not documented
HDT at 1.8 MPa°C125.4 (ISO 75, 1.8 MPa)[1]Not documented
Glass transition (Tg)°C41.8 (DSC)[1]Not documented
Melting point / Vicat°C187.3 melting (DSC); Vicat 190.0 (ISO 306)[1]144 melting (BASF 95A, ISO 11357-3); Bambu Lab 183, Polymaker's modulus at 100 % elongation 8.9 MPa[20][4]
Continuous service temperature°CNot documentedBounded by a melting point of 144–183 °C; no loaded-bar service figure is published for TPU[20][4]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[24]Flammable; no UL 94 rating published for the grades surveyed[2]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[16]Good — years with some colour shift; Polymaker lists UV exposure among the conditions TPU withstands[15]
Chemical resistanceWithstands oils, fuels and alkalis[16]Good resistance to oils and common solvents (BASF)[20]
Food contactNot food-contact certified as filament[16]Not food safe without specific certification (Polymaker)[15]
Biodegradability / compostabilityNot biodegradable[16]Not biodegradable[15]
RecyclabilityNot accepted in household plastic collection[16]Not accepted in household plastic collection[15]
Electrical & ESD propertiesStatic-dissipative — the reason the grade exists; Polymaker's insulating nylon composites sit above 10¹² ohm by contrast[1][22]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[31]Low hazard — minimal VOC and particle emission; TPU was not among the nine filaments in the chamber study[31]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[31]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[31]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[31]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[31]Open a window / occasional ventilation[31]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[24]Not documented
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[17]Sanding is impractical — the surface tears rather than abrades[15]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[17]Cyanoacrylate bonds TPU; no common solvent welds it[15]
Vapour / chemical smoothingNo practical vapour smoothing[17]No practical vapour smoothing[15]
Support material pairingNot documentedPolymaker warns TPU supports are often very difficult to remove; PolyDissolve S1 is rated for TPU[15]
Dimensional accuracy & detailNot documentedStringing and elephant-foot are the accuracy limits; retraction has to be long and slow[2]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[32]DMF, DMSO, NMP and THF dissolve TPU; acetone, MEK and cyclohexanone are partial solvents. All laboratory reagents.[33]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[32]Toluene and benzene swell it up to +50 % by weight at 23 °C; esters swell it severely; ethanol and IPA soften it.[33]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[32]None practical — the true solvents (DMF, THF, NMP) are laboratory reagents and leave the joint swollen and weak.[33]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA612-ESD Technical Data Sheet V1.0 Polymaker · 2025-06 · tds
  2. PolyFlex TPU95 Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  3. Prusament TPU 95A Technical Datasheet v1.0 Prusa Polymers · 2025-05 · tds
  4. Bambu Filament Technical Data Sheet — TPU 95A HF Bambu Lab · 2026-08 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  7. LANDU TPU 3D Printer Filament 1.75 mm 95A Black 1 kg — Amazon listing Amazon.com · 2026-08 · vendor
  8. IEMAI 3D TPU 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  9. Cheetah product page — print guidelines, spool sizes and price NinjaTek · 2026-08 · vendor
  10. TPU for AMS — product page Bambu Lab US Store · 2026-08 · vendor
  11. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  12. Siraya Tech Flex TPU 95A Filament — product page Siraya Tech · 2026-08 · vendor
  13. PrimaCreator EasyPrint FLEX TPU 95A product page PrimaCreator · 2026-08 · vendor
  14. add:north TPU Pro Matte 95A product page add:north · 2026-08 · vendor
  15. TPU — material basics Polymaker Wiki · 2026-08 · doc
  16. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  17. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. Flexible (TPE/TPU) — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  19. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  20. Ultrafuse TPU 95A Technical Data Sheet (Version 2.0) BASF Forward AM · 2022-08 · tds
  21. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  22. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  23. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  24. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  25. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  26. NinjaTek technical specs comparison chart (Cheetah, NinjaFlex, Armadillo, Alloy 910, Nylon 645) NinjaTek · 2026-08 · tds
  27. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  28. FiberFlex 40D Technical Data Sheet Fiberlogy · 2026-08 · tds
  29. BambuLab TPU 95A HF vs Qidi TPU 95A HF — results spreadsheet My Tech Fun (Igor Gaspar) · 2024-02 · test
  30. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  31. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  32. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  33. Elastollan — Chemical properties: swelling and chemical resistance BASF · 2026-08 · tds